DuPont Performance Polymers Crastin® LW9020FR BK851 PBT (Unverified Data**) price 2244 per MT

Physical Properties
Density
1.50 g/cc
Filler Content
20 %

Mechanical Properties
Tensile Strength at Break
100 MPa @Temperature 23.0 °C
Elongation at Break
2.0 % @Temperature 23.0 °C
Tensile Modulus
7.80 GPa @Temperature 23.0 °C
Flexural Strength
140 MPa @Temperature 23.0 °C
Izod Impact, Notched (ISO)
5.50 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
3.50 J/cm² @Temperature 23.0 °C
Charpy Impact, Notched
0.650 J/cm² @Temperature 23.0 °C

Thermal Properties
Melting Point
225 °C
Deflection Temperature at 1.8 MPa (264 psi)
170 °C
UL RTI, Electrical
140 °C @Thickness 0.750 mm
UL RTI, Electrical
140 °C @Thickness 1.50 mm
UL RTI, Electrical
140 °C @Thickness 3.00 mm
UL RTI, Electrical
140 °C @Thickness 6.00 mm
UL RTI, Mechanical with Impact
115 °C @Thickness 1.50 mm
UL RTI, Mechanical with Impact
115 °C @Thickness 0.750 mm
UL RTI, Mechanical with Impact
120 °C @Thickness 6.00 mm
UL RTI, Mechanical with Impact
120 °C @Thickness 3.00 mm
UL RTI, Mechanical without Impact
120 °C @Thickness 0.750 mm
UL RTI, Mechanical without Impact
120 °C @Thickness 1.50 mm
UL RTI, Mechanical without Impact
130 °C @Thickness 3.00 mm
UL RTI, Mechanical without Impact
130 °C @Thickness 6.00 mm
Flammability, UL94
V-0 @Thickness 6.00 mm
Flammability, UL94
V-0 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 3.00 mm
Flammability, UL94
V-0 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 3.00 mm
Flammability, UL94
V-0 @Thickness 6.00 mm

Processing Properties
Melt Temperature
250 °C
Melt Temperature
240 - 260 °C
Mold Temperature
80.0 °C
Mold Temperature
30.0 - 130 °C
Drying Temperature
110 - 130 °C
Dry Time
2.00 - 4.00 hour
Moisture Content
<= 0.040 %

Descriptive Properties
Appearance
Black Color
Drying Recommended
Yes
Features
Appearance, Pleasing Surface
Features
Chemical Resistance, Good
Features
Dimensional Stability, Good
Features
Flame Retardant
Features
Moisture Absorption, Low
Features
Processability, Good
Features
Warp Resistant
Features
Warpage, Low
Filler
Glass fiber reinforcement
Forms
Pellets
Generic
PBT Alloy
Material Status
Current
Part Marking Code
>PBT+ASA-GF20FR(17)<
Polymer Family
Polyester
Polymer Type
PBT
Processing Method
Injection Molding
Product Category
Flame Retardant Resins
Product Category
Glass Reinforced Resins
Product Category
Low Warp Resins
Region Available - Global
Yes
Resin Identification
PBT+ASA-GF20FR(17)
RoHS Compliance
Contact Manufacturer
Uses
Housings
Uses
Industrial Applications

Alternative products

DuPont Performance Polymers Crastin® 6134 NC010 PBT (Unverified Data**) accurate 72%

$ 1467/MT

Density: 1.30 g/cc
Melt Flow: 33 g/10 min @Load 2.16 kg, Temperature 250 °C
Melt Flow: 33.5 g/10 min @Load 2.16 kg, Temperature 250 °C
Tensile Strength, Yield: 59.0 MPa @Temperature 23.0 °C
Elongation at Break: 45 % @Temperature 23.0 °C

DuPont Performance Polymers Crastin® S650FR BK851 PBT (Unverified Data**) accurate 72%

$ 2393/MT

Density: 1.46 g/cc
Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.016 cm/cm @Thickness 2.00 mm
Tensile Strength, Yield: 65.0 MPa @Temperature 23.0 °C
Elongation at Break: 7.2 % @Temperature 23.0 °C

DuPont Performance Polymers Crastin® HR5315HF BK503 PBT (Unverified Data**) accurate 72%

$ 1689/MT

Density: 1.37 g/cc
Filler Content: 15 %
Water Absorption: 0.080 % @Temperature 23.0 °C
Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.011 cm/cm @Thickness 2.00 mm

DuPont Performance Polymers Crastin® LW9030 BK851 PBT (Unverified Data**) accurate 86%

$ 2170/MT

Density: 1.44 g/cc
Filler Content: 30 %
Tensile Strength at Break: 125 MPa @Temperature 23.0 °C
Elongation at Break: 2.0 % @Temperature 23.0 °C
Tensile Modulus: 9.20 GPa @Temperature 23.0 °C

DuPont Performance Polymers Crastin® S600F40 BK851 PBT (Unverified Data**) accurate 72%

$ 1695/MT

Density: 1.31 g/cc
Tensile Strength, Yield: 58.0 MPa @Temperature 23.0 °C
Elongation at Break: 20 % @Temperature 23.0 °C
Elongation at Break: 30 % @Temperature 23.0 °C
Elongation at Yield: 6.0 % @Temperature 23.0 °C

DuPont Performance Polymers Crastin® CE2056 NC010 PBT accurate 72%

$ 1759/MT

Density: 1.272 g/cc
Linear Mold Shrinkage, Flow: 0.026 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.023 cm/cm @Thickness 2.00 mm
Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 250 °C
Melt Flow: 6.5 g/10 min @Load 2.16 kg, Temperature 250 °C

DuPont Performance Polymers Crastin® LW9320 BK851 PBT (Unverified Data**) accurate 86%

$ 1717/MT

Density: 1.34 g/cc
Filler Content: 20 %
Tensile Strength at Break: 115 MPa @Temperature 23.0 °C
Elongation at Break: 2.3 % @Temperature 23.0 °C
Tensile Modulus: 7.30 GPa @Temperature 23.0 °C

DuPont Performance Polymers Crastin® HR5330HF BK503 PBT (Unverified Data**) accurate 72%

$ 1488/MT

Density: 1.50 g/cc
Filler Content: 30 %
Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 2.00 mm
Linear Mold Shrinkage, Transverse: 0.010 cm/cm @Thickness 2.00 mm
Tensile Strength at Break: 120 MPa @Temperature 23.0 °C

DuPont Performance Polymers Crastin® SK603 BK851 PBT (Unverified Data**) accurate 86%

$ 1647/MT

Density: 1.45 g/cc
Filler Content: 20 %
Tensile Strength at Break: 113 MPa @Temperature 23.0 °C
Elongation at Break: 3.0 % @Temperature 23.0 °C
Tensile Modulus: 6.90 GPa @Temperature 23.0 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, cargo vessels for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for DuPont Performance Polymers Crastin® LW9020FR BK851 PBT (Unverified Data**)

Seller from Bengalūru – 2021-07-18:

Seller from Bengalūru work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2244 per MT

Seller from Guangzhou – 2021-08-15:

Seller from Guangzhou work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2509 per MT