Premix Thermoplastics PRE-ELEC® ABS 1410 price 1659 per MT

Physical Properties
Density
1.10 g/cc
Thickness
406 microns
Linear Mold Shrinkage
0.0050 - 0.0080 cm/cm @Thickness 4.00 mm
Melt Flow
15 g/10 min @Load 10.0 kg, Temperature 220 °C

Mechanical Properties
Hardness, Shore D
76 @Thickness 4.00 mm
Film Tensile Strength at Yield, MD
36.0 MPa
Film Elongation at Break, MD
8.0 %
Film Elongation at Break, TD
4.0 %
Film Elongation at Yield, MD
4.0 %
Modulus of Elasticity
2.00 GPa @Thickness 4.00 mm
Izod Impact, Notched
0.900 J/cm @Thickness 4.00 mm, Temperature 23.0 °C
Izod Impact, Unnotched
5.50 J/cm @Thickness 4.00 mm, Temperature 23.0 °C
Film Tensile Strength at Break, MD
29.0 MPa
Film Tensile Strength at Break, TD
30.0 MPa

Thermal Properties
Deflection Temperature at 0.46 MPa (66 psi)
88.0 °C @Thickness 4.00 mm
Deflection Temperature at 1.8 MPa (264 psi)
73.0 °C @Thickness 4.00 mm
Vicat Softening Point
91.0 °C @Thickness 4.00 mm
Vicat Softening Point
104 °C @Thickness 4.00 mm

Electrical Properties
Volume Resistivity
<= 1e+05
Surface Resistance
<= 1.00e+6 ohm

Processing Properties
Middle Barrel Temperature
200 °C
Middle Barrel Temperature
210 °C
Middle Barrel Temperature
220 °C
Middle Barrel Temperature
230 °C
Middle Barrel Temperature
240 °C
Middle Barrel Temperature
240 °C
Die Temperature
220 °C
Die Temperature
230 °C
Die Temperature
230 °C
Die Temperature
240 °C
Die Temperature
240 °C
Melt Temperature
220 - 260 °C
Mold Temperature
60.0 - 90.0 °C
Roll Temperature
60.0 °C
Roll Temperature
80.0 °C
Roll Temperature
90.0 °C
Drying Temperature
80.0 - 100 °C @Time 7200 - 14400 sec
Moisture Content
<= 0.15 %
Injection Pressure
75.01 - 120.0 MPa
Shelf Life
12.0 Month

Descriptive Properties
Appearance
Granule
Color
Black
Injection Speed
Moderate

Alternative products

Premix Thermoplastics PRE-ELEC® PP 1386 accurate 80%

$ 1983/MT

Density: 0.980 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 230 °C

Premix Thermoplastics PRE-ELEC® CP 1318 (discontinued **) accurate 80%

$ 1990/MT

Density: 1.10 g/cc
Melt Flow: 1.0 g/10 min @Load 5.00 kg, Temperature 190 °C
High Load Melt Index: 26 g/10 min @Load 21.6 kg, Temperature 190 °C
Hardness, Shore A: 94
Hardness, Shore D: 46

Premix Thermoplastics PRE-ELEC® ESD 1100 (discontinued **) accurate 37%

$ 1525/MT

Density: 1.25 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm
Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C
High Load Melt Index: 35 g/10 min @Load 21.6 kg, Temperature 200 °C

Premix Thermoplastics PRE-ELEC® PET 1451 accurate 57%

$ 1744/MT

Density: 1.33 g/cc
Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C
High Load Melt Index: 28 g/10 min @Load 21.6 kg, Temperature 200 °C
Film Tensile Strength at Yield, MD: 32.0 MPa

Premix Thermoplastics PRE-ELEC® PS 1326 accurate 80%

$ 1686/MT

Density: 1.08 g/cc
Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
Melt Flow: 1.2 g/10 min @Load 5.00 kg, Temperature 200 °C
High Load Melt Index: 45 g/10 min @Load 21.6 kg, Temperature 200 °C
Hardness, Shore A: 99

Premix Thermoplastics PRE-ELEC® PE 1294 accurate 80%

$ 1531/MT

Density: 1.01 g/cc
Linear Mold Shrinkage: 0.015 - 0.025 cm/cm
Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 190 °C
High Load Melt Index: 70 g/10 min @Load 21.6 kg, Temperature 190 °C

Premix Thermoplastics PRE-ELEC® PE 1291 accurate 76%

$ 1521/MT

Density: 1.04 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.015 - 0.025 cm/cm
Melt Flow: 0.80 g/10 min @Load 10.0 kg, Temperature 190 °C
High Load Melt Index: 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C

Premix Thermoplastics PRE-ELEC® PE 1292 accurate 84%

$ 1620/MT

Density: 1.03 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.015 - 0.025 cm/cm @Thickness 4.00 mm
Melt Flow: 1.5 g/10 min @Load 5.00 kg, Temperature 190 °C
Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 190 °C

Premix Thermoplastics PRE-ELEC® PS 1324 accurate 80%

$ 1584/MT

Density: 1.08 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
Melt Flow: 0.20 g/10 min @Load 5.00 kg, Temperature 200 °C
High Load Melt Index: 18 g/10 min @Load 21.6 kg, Temperature 200 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, tankers for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Premix Thermoplastics PRE-ELEC® ABS 1410

Seller from Ho Chi Minh City – 2021-04-16:

Seller from Ho Chi Minh City work with company: Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2289 per MT

Seller from Hechi – 2021-03-19:

Seller from Hechi work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1659 per MT