Premix Thermoplastics PRE-ELEC® PS 1324 price 1584 per MT

Physical Properties
Density
1.08 g/cc
Thickness
406 microns
Linear Mold Shrinkage
0.0040 - 0.0060 cm/cm
Melt Flow
0.20 g/10 min @Load 5.00 kg, Temperature 200 °C
High Load Melt Index
18 g/10 min @Load 21.6 kg, Temperature 200 °C

Mechanical Properties
Hardness, Shore A
99
Hardness, Shore D
73
Film Tensile Strength at Yield, MD
20.0 MPa
Film Tensile Strength at Yield, TD
18.0 MPa
Film Elongation at Break, MD
80 %
Film Elongation at Break, TD
65 %
Film Elongation at Yield, MD
4.0 %
Film Elongation at Yield, TD
4.0 %
Modulus of Elasticity
1.80 GPa
Izod Impact, Notched
0.900 J/cm @Thickness 4.00 mm, Temperature -20.0 °C
Izod Impact, Notched
1.30 J/cm @Thickness 4.00 mm, Temperature 23.0 °C
Izod Impact, Unnotched
4.00 J/cm @Thickness 4.00 mm, Temperature -20.0 °C
Izod Impact, Unnotched
8.00 J/cm @Thickness 4.00 mm, Temperature 23.0 °C
Film Tensile Strength at Break, MD
22.0 MPa
Film Tensile Strength at Break, TD
20.0 MPa

Thermal Properties
Deflection Temperature at 0.46 MPa (66 psi)
84.0 °C
Vicat Softening Point
97.0 °C

Electrical Properties
Volume Resistivity
<= 10000 ohm-cm
Surface Resistance
<= 1e+05

Processing Properties
Middle Barrel Temperature
210 °C
Middle Barrel Temperature
220 °C
Middle Barrel Temperature
220 °C
Middle Barrel Temperature
230 °C
Middle Barrel Temperature
230 °C
Middle Barrel Temperature
230 °C
Die Temperature
220 °C
Die Temperature
230 °C
Die Temperature
230 °C
Die Temperature
230 °C
Die Temperature
230 °C
Roll Temperature
60.0 °C
Roll Temperature
80.0 °C
Roll Temperature
90.0 °C
Drying Temperature
60.0 - 80.0 °C @Time 10800 - 14400 sec
Moisture Content
<= 0.15 %
Shelf Life
12.0 Month

Descriptive Properties
Appearance
Granule
Bending Strength, cycles, min
1000
Bending Strength, cycles, min
1000
Color
Black

Alternative products

Premix Thermoplastics PRE-ELEC® PP 1386 accurate 83%

$ 1983/MT

Density: 0.980 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 230 °C

Premix Thermoplastics PRE-ELEC® CP 1318 (discontinued **) accurate 83%

$ 1990/MT

Density: 1.10 g/cc
Melt Flow: 1.0 g/10 min @Load 5.00 kg, Temperature 190 °C
High Load Melt Index: 26 g/10 min @Load 21.6 kg, Temperature 190 °C
Hardness, Shore A: 94
Hardness, Shore D: 46

Premix Thermoplastics PRE-ELEC® ABS 1410 accurate 46%

$ 1659/MT

Density: 1.10 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm @Thickness 4.00 mm
Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 220 °C
Hardness, Shore D: 76 @Thickness 4.00 mm

Premix Thermoplastics PRE-ELEC® PET 1451 accurate 57%

$ 1744/MT

Density: 1.33 g/cc
Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C
High Load Melt Index: 28 g/10 min @Load 21.6 kg, Temperature 200 °C
Film Tensile Strength at Yield, MD: 32.0 MPa

Premix Thermoplastics PRE-ELEC® PS 1326 accurate 88%

$ 1686/MT

Density: 1.08 g/cc
Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
Melt Flow: 1.2 g/10 min @Load 5.00 kg, Temperature 200 °C
High Load Melt Index: 45 g/10 min @Load 21.6 kg, Temperature 200 °C
Hardness, Shore A: 99

Premix Thermoplastics PRE-ELEC® PE 1294 accurate 59%

$ 1531/MT

Density: 1.01 g/cc
Linear Mold Shrinkage: 0.015 - 0.025 cm/cm
Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 190 °C
High Load Melt Index: 70 g/10 min @Load 21.6 kg, Temperature 190 °C

Premix Thermoplastics PRE-ELEC® PE 1291 accurate 61%

$ 1521/MT

Density: 1.04 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.015 - 0.025 cm/cm
Melt Flow: 0.80 g/10 min @Load 10.0 kg, Temperature 190 °C
High Load Melt Index: 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C

Premix Thermoplastics PRE-ELEC® ESD 7120 accurate 17%

$ 1756/MT

Density: 1.07 g/cc
Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
Melt Flow: 7.0 g/10 min @Load 5.00 kg, Temperature 200 °C
Hardness, Shore D: 73
Tensile Strength, Ultimate: 23.0 MPa

Premix Thermoplastics PRE-ELEC® PE 1292 accurate 59%

$ 1620/MT

Density: 1.03 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.015 - 0.025 cm/cm @Thickness 4.00 mm
Melt Flow: 1.5 g/10 min @Load 5.00 kg, Temperature 190 °C
Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 190 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, vessels for sale greece. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Premix Thermoplastics PRE-ELEC® PS 1324

Seller from Chittagong – 2021-05-16:

Seller from Chittagong work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2571 per MT

Seller from Delhi – 2021-04-11:

Seller from Delhi work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2532 per MT

Seller from Jakarta – 2021-05-30:

Seller from Jakarta work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1584 per MT