Premix Thermoplastics PRE-ELEC® PE 1292 price 1620 per MT

Physical Properties
Density
1.03 g/cc
Thickness
406 microns
Linear Mold Shrinkage
0.015 - 0.025 cm/cm @Thickness 4.00 mm
Melt Flow
1.5 g/10 min @Load 5.00 kg, Temperature 190 °C
Melt Flow
6.0 g/10 min @Load 10.0 kg, Temperature 190 °C
High Load Melt Index
35 g/10 min @Load 21.6 kg, Temperature 190 °C

Mechanical Properties
Film Tensile Strength at Yield, MD
31.0 MPa
Film Elongation at Break, MD
70 %
Film Elongation at Yield, MD
12 %
Modulus of Elasticity
1.10 GPa @Thickness 4.00 mm
Izod Impact, Notched
0.500 J/cm @Thickness 4.00 mm, Temperature -20.0 °C
Izod Impact, Notched
0.850 J/cm @Thickness 4.00 mm, Temperature 23.0 °C
Izod Impact, Unnotched
NB @Thickness 4.00 mm, Temperature 23.0 °C
Izod Impact, Unnotched
NB @Thickness 4.00 mm, Temperature -20.0 °C
Film Tensile Strength at Break, MD
17.0 MPa

Thermal Properties
Deflection Temperature at 0.46 MPa (66 psi)
84.0 °C @Thickness 4.00 mm
Vicat Softening Point
128 °C @Thickness 4.00 mm

Electrical Properties
Volume Resistivity
<= 10000 ohm-cm
Surface Resistance
<= 1e+05

Processing Properties
Middle Barrel Temperature
200 °C
Middle Barrel Temperature
210 °C
Middle Barrel Temperature
220 °C
Middle Barrel Temperature
220 °C
Middle Barrel Temperature
230 °C
Middle Barrel Temperature
230 °C
Die Temperature
220 °C
Die Temperature
230 °C
Die Temperature
230 °C
Die Temperature
240 °C
Die Temperature
240 °C
Melt Temperature
200 - 250 °C
Mold Temperature
40.0 - 60.0 °C
Roll Temperature
50.0 °C
Roll Temperature
60.0 °C
Roll Temperature
70.0 °C
Drying Temperature
80.0 °C @Time 7200 - 14400 sec
Moisture Content
<= 0.15 %
Injection Pressure
60.0 - 80.0 MPa
Shelf Life
12.0 Month

Descriptive Properties
Appearance
Granule
Color
Black
Injection Speed
Moderate

Alternative products

Premix Thermoplastics PRE-ELEC® PP 1386 accurate 80%

$ 1983/MT

Density: 0.980 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.010 - 0.012 cm/cm
Melt Flow: 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C
Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 230 °C

Premix Thermoplastics PRE-ELEC® CP 1318 (discontinued **) accurate 86%

$ 1990/MT

Density: 1.10 g/cc
Melt Flow: 1.0 g/10 min @Load 5.00 kg, Temperature 190 °C
High Load Melt Index: 26 g/10 min @Load 21.6 kg, Temperature 190 °C
Hardness, Shore A: 94
Hardness, Shore D: 46

Premix Thermoplastics PRE-ELEC® ABS 1410 accurate 70%

$ 1659/MT

Density: 1.10 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm @Thickness 4.00 mm
Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 220 °C
Hardness, Shore D: 76 @Thickness 4.00 mm

Premix Thermoplastics PRE-ELEC® PET 1451 accurate 60%

$ 1744/MT

Density: 1.33 g/cc
Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C
High Load Melt Index: 28 g/10 min @Load 21.6 kg, Temperature 200 °C
Film Tensile Strength at Yield, MD: 32.0 MPa

Premix Thermoplastics PRE-ELEC® PS 1326 accurate 80%

$ 1686/MT

Density: 1.08 g/cc
Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
Melt Flow: 1.2 g/10 min @Load 5.00 kg, Temperature 200 °C
High Load Melt Index: 45 g/10 min @Load 21.6 kg, Temperature 200 °C
Hardness, Shore A: 99

Premix Thermoplastics PRE-ELEC® PE 1294 accurate 93%

$ 1531/MT

Density: 1.01 g/cc
Linear Mold Shrinkage: 0.015 - 0.025 cm/cm
Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 190 °C
High Load Melt Index: 70 g/10 min @Load 21.6 kg, Temperature 190 °C

Premix Thermoplastics PRE-ELEC® ESD 7100 accurate 34%

$ 1451/MT

Density: 1.07 g/cc
Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C
High Load Melt Index: 20 g/10 min @Load 21.6 kg, Temperature 200 °C
Hardness, Shore D: 73 @Thickness 1.00 mm

Premix Thermoplastics PRE-ELEC® PE 1291 accurate 89%

$ 1521/MT

Density: 1.04 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.015 - 0.025 cm/cm
Melt Flow: 0.80 g/10 min @Load 10.0 kg, Temperature 190 °C
High Load Melt Index: 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C

Premix Thermoplastics PRE-ELEC® PS 1324 accurate 86%

$ 1584/MT

Density: 1.08 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
Melt Flow: 0.20 g/10 min @Load 5.00 kg, Temperature 200 °C
High Load Melt Index: 18 g/10 min @Load 21.6 kg, Temperature 200 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tanker price. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Premix Thermoplastics PRE-ELEC® PE 1292

Seller from Madrid – 2021-06-30:

Seller from Madrid work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1620 per MT

Seller from Bogotá – 2021-02-28:

Seller from Bogotá work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2163 per MT