Physical Properties
Density
1.75 - 1.80 g/cc
Water Absorption
<= 0.040 % @Time 86400 sec
Linear Mold Shrinkage, Flow
0.020 - 0.030 cm/cm
Melt Flow
4.0 - 6.0 g/10 min @Load 10.0 kg, Temperature 230 °C

Mechanical Properties
Hardness, Shore D
72 - 78
Tensile Strength at Break
30.0 - 50.0 MPa @Thickness 2.00 mm
Tensile Strength, Yield
50.0 - 60.0 MPa @Thickness 2.00 mm
Elongation at Break
20 - 300 %
Elongation at Yield
5.0 - 10 %
Tensile Modulus
1.70 - 2.50 GPa @Thickness 2.00 mm
Izod Impact, Notched
1.50 - 2.50 J/cm @Thickness 4.00 mm
Coefficient of Friction, Dynamic
0.15 - 0.35
Coefficient of Friction, Static
0.20 - 0.40
Taber Abrasion, mg/1000 Cycles
5.0 - 10

Thermal Properties
CTE, linear, Parallel to Flow
140 µm/m-°C @Temperature 0.000 - 40.0 °C
Specific Heat Capacity
1.20 J/g-°C @Temperature 23.0 °C
Specific Heat Capacity
1.60 J/g-°C @Temperature 100 °C
Thermal Conductivity
0.200 W/m-K @Temperature 23.0 °C
Melting Point
170 - 174 °C
Crystallization Temperature
137 - 145 °C
Vicat Softening Point
135 - 145 °C
Glass Transition Temp, Tg
-40.0 °C
Flammability, UL94
V-0 @Thickness 0.100 mm
Oxygen Index
44 % @Thickness 3.00 mm

Electrical Properties
Volume Resistivity
>= 1.00e+14 ohm-cm
Surface Resistance
>= 1.00e+14 ohm
Dielectric Constant
7.0 - 10 @Frequency 1000 Hz
Dielectric Strength
20.0 - 25.0 kV/mm @Thickness 1.00 mm

Descriptive Properties
Availability
Africa & Middle East
Availability
Asia Pacific
Availability
Europe
Availability
Latin America
Availability
North America
Processing Technique
Compression Molding; Extrusion

Alternative products

Celanese Hostaform® M10AE POM, Unfilled accurate 99%

$ 1463/MT

Density: 1.41 g/cc
Water Absorption at Saturation: 0.650 %
Melt Flow: 0.900 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 65.0 MPa
Elongation at Break: 25.0 %

Fujipoly Industries Zebra® 1002 Carbon Solid Self-Supported Connectors accurate 99%

$ 1726/MT

Hardness, Shore A: 10
Hardness, Shore A: 25
Hardness, Shore A: 55
Hardness, Shore A: 73
Tensile Strength, Yield: 2.90 MPa

Celanese Hostaform® C 27021 GV3/30 POM, 30% Glass Reinforced accurate 99%

$ 1494/MT

Density: 1.59 g/cc
Water Absorption at Saturation: 0.900 %
Melt Flow: 16.0 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 38.0 MPa
Elongation at Break: 12.0 %

Celanese Hostaform® C 9021 GV3/30 POM, 30% Glass Reinforced accurate 99%

$ 2043/MT

Density: 1.59 g/cc
Density of Compound: 1.37 g/cc
Water Absorption at Saturation: 0.900 %
Melt Flow: 7.50 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 38.0 MPa

Celanese Hostaform® C 13021 RM POM, Tribological accurate 99%

$ 1871/MT

Density: 1.41 g/cc
Water Absorption at Saturation: 0.650 %
Linear Mold Shrinkage, Flow: 0.0200 cm/cm
Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
Melt Flow: 12.5 g/10 min @Load 2.16 kg, Temperature 190 °C

Solvay Specialty Polymers Solef® 32008 Polyvinylidene Fluoride (PVDF) accurate 99%

$ 1506/MT

Density: 1.75 - 1.80 g/cc
Water Absorption: <= 0.040 % @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.020 - 0.030 cm/cm
Melt Flow: 3.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Hardness, Shore D: 47

Celanese VANDAR 4602Z PBT, Unfilled accurate 99%

$ 1628/MT

Specific Gravity: 1.25 g/cc
Density: 1.25 g/cc
Water Absorption: 0.100 % @Temperature 22.8 °C
Moisture Absorption: 0.200 %
Linear Mold Shrinkage, Flow: 0.0170 - 0.0220 cm/cm

Celanese Hostaform® C 2521 XAP² ™ POM (Unverified Data**) accurate 99%

$ 1996/MT

Density: 1.41 g/cc
Density of Compound: 1.20 g/cc
Water Absorption: 0.65 %
Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
Tensile Strength, Yield: 62.0 MPa

Solvay Specialty Polymers Solef® 31508 Polyvinylidene Fluoride (PVDF) accurate 99%

$ 1520/MT

Density: 1.75 - 1.80 g/cc
Water Absorption: <= 0.040 % @Time 86400 sec
Linear Mold Shrinkage, Flow: 0.020 - 0.030 cm/cm
Melt Flow: 3.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
Hardness, Shore D: 53

Celanese Hostaform® C 9021 LS POM, UV Resistant accurate 99%

$ 1596/MT

Density: 1.41 g/cc
Water Absorption at Saturation: 0.650 %
Linear Mold Shrinkage, Flow: 0.0200 cm/cm
Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, vessels for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF)

Seller from Chengdu – 2021-06-25:

Seller from Chengdu work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2081 per MT

Seller from Santiago – 2021-05-10:

Seller from Santiago work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2188 per MT

Seller from Melbourne – 2021-06-14:

Seller from Melbourne work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1506 per MT

Seller from Bangkok – 2021-05-01:

Seller from Bangkok work with company: Solvay, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $2244 per MT