$ 1673/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 48
- Tensile Strength: 40.0 MPa
- Tensile Strength: 55.0 MPa
$ 2033/MT
- Density: 1.53 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 102 cm³/g
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
$ 2380/MT
- Density: 1.14 g/cc
- Hardness, Shore A: 76
- Tensile Strength, Ultimate: 30.0 MPa
- Tensile Strength, Yield: 4.30 MPa @Strain 100 %
- Tensile Strength, Yield: 8.30 MPa @Strain 300 %
$ 1630/MT
- Density: 1.48 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 92
- Linear Mold Shrinkage, Flow: 0.0027 cm/cm
$ 1746/MT
- Density: 1.25 g/cc
- Hardness, Shore A: 94
- Hardness, Shore D: 41
- Tensile Strength: 50.0 MPa
- Elongation at Break: 600 %
$ 1733/MT
- Density: 1.53 g/cc
- Water Absorption: 0.20 %
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 102 cm³/g
$ 2095/MT
- Density: 1.53 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Viscosity Test: 105 cm³/g
- Tensile Strength, Ultimate: 130 MPa
- Elongation at Break: 3.0 %
$ 1638/MT
- Density: 1.21 g/cc
- Hardness, Shore A: 90
- Tensile Strength: 40.0 MPa
- Tensile Strength: 50.0 MPa
- Tensile Strength: 4.00 MPa @Strain 20.0 %
$ 1798/MT
- Density: 1.13 g/cc
- Hardness, Shore A: 91
- Hardness, Shore D: 42
- Tensile Strength, Ultimate: 37.0 MPa
- Tensile Strength, Yield: 1.70 MPa @Strain 300 %
$ 1729/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 94
- Tensile Strength: 5.70 MPa
- Tensile Strength: 10.0 MPa
- Tensile Strength: 22.5 MPa
$ 2262/MT
- Density: 1.56 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 80 cm³/g
- Linear Mold Shrinkage, Flow: 0.0029 cm/cm
$ 2065/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 75
- Tensile Strength: 35.0 MPa
- Tensile Strength: 50.0 MPa
- Tensile Strength: 2.00 MPa @Strain 20.0 %
$ 1788/MT
- Density: 1.30 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.25 %
- Viscosity Test: 160 cm³/g
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
$ 1561/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 85
- Tensile Strength: 2.00 MPa
- Tensile Strength: 5.00 MPa
- Tensile Strength: 10.5 MPa
$ 1563/MT
- Density: 1.12 g/cc @Thickness 2.00 mm
- Hardness, Shore A: 86 @Thickness 2.00 mm
- Tensile Strength, Ultimate: 52.0 MPa @Thickness 2.00 mm
- Tensile Strength, Yield: 7.60 MPa @Strain 100 %
- Tensile Strength, Yield: 19.0 MPa @Strain 300 %, Thickness 0.760 mm
$ 1886/MT
- Density: 1.50 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 120
- Viscosity Measurement: 70 @Temperature 290 °C
$ 2403/MT
- Density: 1.45 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 115
- Viscosity Measurement: 70 @Temperature 290 °C
$ 1851/MT
- Density: 1.23 g/cc
- Hardness, Shore D: 60
- Tensile Strength: 40.0 MPa
- Tensile Strength: 55.0 MPa
- Tensile Strength: 13.0 MPa @Strain 20.0 %
$ 1448/MT
- Bulk Density: 0.600 - 0.900 g/cc
- Density: 1.47 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 105
$ 1922/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 60
- Tensile Strength: 30.0 MPa
- Tensile Strength: 1.00 MPa @Strain 20.0 %
- Tensile Strength: 2.50 MPa @Strain 100 %
$ 2181/MT
- Density: 1.55 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 116 cm³/g
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
$ 1797/MT
- Density: 1.39 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 107
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
$ 1583/MT
- Bulk Density: 0.600 - 0.900 g/cc
- Density: 1.45 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 107
$ 1838/MT
- Bulk Density: 0.600 - 0.900 g/cc
- Density: 1.60 - 1.70 g/cc
- Melting Point: 220 - 230 °C
- Decomposition Temperature: >= 290 °C
- Commercial Status: Europe
- Ignition Temperature: >350°C
$ 2049/MT
- Density: 1.25 g/cc
- Hardness, Shore D: 64
- Tensile Strength, Ultimate: 39.0 MPa
- Tensile Strength, Yield: 27.0 MPa @Strain 100 %
- Tensile Strength, Yield: 37.0 MPa @Strain 300 %
$ 1785/MT
- Density: 1.21 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Ultimate: 46.0 MPa
- Tensile Strength, Yield: 5.80 MPa @Strain 100 %
- Tensile Strength, Yield: 11.0 MPa @Strain 300 %
$ 1805/MT
- Density: 1.18 g/cc
- Hardness, Shore D: 64
- Tensile Strength, Ultimate: 41.0 MPa
- Tensile Strength, Yield: 25.0 MPa @Strain 100 %
- Tensile Strength, Yield: 33.0 MPa @Strain 300 %
$ 1552/MT
- Density: 1.28 g/cc
- Hardness, Shore D: 64
- Tensile Strength: 45.0 MPa
- Elongation at Break: 350 %
- Tear Strength: 200 kN/m
$ 2532/MT
- Density: 1.27 g/cc
- Hardness, Shore A: 88
- Tensile Strength, Ultimate: 33.0 MPa
- Tensile Strength, Yield: 7.00 MPa @Strain 100 %
- Tensile Strength, Yield: 15.5 MPa @Strain 300 %
$ 1576/MT
- Density: 1.30 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.25 %
- Viscosity Test: 130 cm³/g
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
$ 1883/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 88
- Hardness, Shore D: 37
- Tensile Strength: 38.0 MPa
- Tensile Strength: 50.0 MPa
$ 2013/MT
- Density: 1.32 g/cc
- Density: 1.55 g/cc
- Viscosity Measurement: 0.55
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 118
$ 2200/MT
- Density: 1.14 g/cc
- Hardness, Shore A: 95
- Hardness, Shore D: 47
- Tensile Strength, Ultimate: 36.0 MPa
- Tensile Strength, Yield: 12.0 MPa @Strain 100 %
$ 1545/MT
- Density: 1.47 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 105 cm³/g
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
$ 1900/MT
- Density: 1.23 g/cc
- Hardness, Shore A: 85
- Tensile Strength: 55.0 MPa
- Tensile Strength: 2.00 MPa @Strain 20.0 %
- Tensile Strength: 5.00 MPa @Strain 100 %
$ 1776/MT
- Density: 1.33 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 110
- Viscosity Measurement: 70 @Temperature 290 °C
$ 1587/MT
- Density: 1.30 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.25 %
- Viscosity Test: 107 cm³/g
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
$ 1608/MT
- Density: 1.35 g/cc
- Hardness, Shore D: 64
- Tensile Strength: 65.0 MPa
- Elongation at Break: 20 %
- Charpy Impact Unnotched: 8.00 J/cm² @Temperature -30.0 °C
$ 1751/MT
- Density: 1.17 g/cc
- Hardness, Shore A: 65
- Tensile Strength: 20.0 MPa
- Tensile Strength: 20.0 MPa
- Tensile Strength: 1.00 MPa @Strain 20.0 %
$ 1683/MT
- Density: 1.12 g/cc @Thickness 2.00 mm
- Hardness, Shore A: 86 @Thickness 2.00 mm
- Tensile Strength, Ultimate: 52.0 MPa @Thickness 2.00 mm
- Tensile Strength, Yield: 7.60 MPa @Strain 100 %
- Tensile Strength, Yield: 19.0 MPa @Strain 300 %
$ 1630/MT
- Density: 1.24 g/cc
- Hardness, Shore D: 64
- Tensile Strength, Ultimate: 40.0 MPa
- Tensile Strength, Yield: 26.0 MPa @Strain 100 %
- Tensile Strength, Yield: 38.0 MPa @Strain 300 %
$ 1928/MT
- Density: 1.61 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0147 cm/cm
$ 1531/MT
- Density: 1.44 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Tensile Strength at Break: 105 MPa
- Tensile Strength, Ultimate: 105 MPa
- Elongation at Break: 3.5 %
$ 1448/MT
- Density: 1.28 g/cc
- Hardness, Shore A: 95
- Tensile Strength, Ultimate: 34.5 MPa
- Tensile Strength, Yield: 21.0 MPa @Strain 100 %
- Tensile Strength, Yield: 30.0 MPa @Strain 300 %
$ 1512/MT
- Transmission, Visible: 40 % @Wavelength 700 nm
- Transmission, Visible: 40 % @Wavelength 2300 nm
- Transmission, Visible: 60 % @Wavelength 1700 nm
- Transmission, Visible: 65 % @Wavelength 2100 nm
- Transmission, Visible: 70 % @Wavelength 1300 nm
- Commercial Status: Europe
$ 2387/MT
- Density: 1.29 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 139
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
$ 1470/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 82
- Tensile Strength: 40.0 MPa
- Tensile Strength: 50.0 MPa
- Tensile Strength: 2.00 MPa @Strain 20.0 %
$ 1746/MT
- Density: 1.21 g/cc
- Hardness, Shore A: 86
- Tensile Strength: 40.0 MPa
- Tensile Strength: 50.0 MPa
- Tensile Strength: 2.80 MPa @Strain 20.0 %
$ 2269/MT
- Density: 1.21 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Ultimate: 31.3 MPa
- Tensile Strength, Yield: 6.30 MPa @Strain 100 %
- Tensile Strength, Yield: 12.8 MPa @Strain 300 %
$ 1635/MT
- Density: 1.38 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 94 cm³/g
- Linear Mold Shrinkage, Flow: 0.0041 cm/cm
$ 1464/MT
- Density: 1.23 g/cc
- Hardness, Shore A: 85
- Tensile Strength: 35.0 MPa
- Tensile Strength: 50.0 MPa
- Tensile Strength: 3.50 MPa @Strain 20.0 %
$ 1920/MT
- Bulk Density: 0.600 - 0.900 g/cc
- Density: 1.73 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 90
$ 2122/MT
- Density: 1.17 g/cc
- Hardness, Shore A: 70
- Tensile Strength: 30.0 MPa
- Tensile Strength: 45.0 MPa
- Tensile Strength: 1.50 MPa @Strain 20.0 %
$ 1444/MT
- Density: 1.55 g/cc
- Viscosity Measurement: 0.55
- Linear Mold Shrinkage: 0.0040 cm/cm
- Hardness, Rockwell R: 118
- Tensile Strength at Break: 145 MPa
$ 1590/MT
- Density: 1.24 g/cc
- Hardness, Shore D: 60
- Tensile Strength, Ultimate: 43.0 MPa
- Tensile Strength, Yield: 24.0 MPa @Strain 100 %
- Tensile Strength, Yield: 42.0 MPa @Strain 300 %
$ 1703/MT
- Density: 1.13 g/cc @Thickness 2.00 mm
- Hardness, Shore A: 90 @Thickness 2.00 mm
- Tensile Strength, Ultimate: 55.0 MPa @Thickness 2.00 mm
- Tensile Strength, Yield: 9.00 MPa @Strain 100 %
- Tensile Strength, Yield: 25.0 MPa @Strain 300 %
$ 1823/MT
- Density: 1.22 g/cc
- Hardness, Shore D: 52
- Tensile Strength: 40.0 MPa
- Tensile Strength: 50.0 MPa
- Tensile Strength: 11.0 MPa @Strain 20.0 %
$ 1460/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 87
- Hardness, Shore D: 39
- Tensile Strength: 30.0 MPa
- Tensile Strength: 35.0 MPa
$ 1750/MT
- Density: 1.26 g/cc
- Hardness, Shore D: 74
- Tensile Strength, Ultimate: 41.0 MPa
- Tensile Strength, Yield: 36.0 MPa @Strain 100 %
- Tensile Strength, Yield: 39.0 MPa @Strain 300 %
$ 1445/MT
- Density: 1.26 g/cc
- Hardness, Shore D: 53
- Tensile Strength: 50.0 MPa
- Elongation at Break: 500 %
- Tear Strength: 150 kN/m
$ 1637/MT
- Density: 1.24 g/cc
- Hardness, Shore D: 64
- Tensile Strength: 40.0 MPa
- Tensile Strength: 55.0 MPa
- Tensile Strength: 17.0 MPa @Strain 20.0 %
$ 1503/MT
- Density: 1.27 g/cc
- Hardness, Shore D: 58
- Tensile Strength: 20.0 MPa
- Tensile Strength: 30.0 MPa
- Tensile Strength: 13.0 MPa @Strain 20.0 %
$ 1738/MT
- Density: 1.25 g/cc
- Hardness, Shore D: 60
- Tensile Strength: 45.0 MPa
- Tensile Strength: 15.0 MPa @Strain 20.0 %
- Tensile Strength: 18.0 MPa @Strain 100 %
$ 1456/MT
- Density: 1.44 g/cc
- Density: 1.70 g/cc
- Viscosity Measurement: 0.52
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Rockwell R: 116
$ 1843/MT
- Density: 1.39 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Tensile Strength, Ultimate: 98.0 MPa
- Elongation at Break: 2.8 %
$ 2145/MT
- Density: 1.47 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 111 cm³/g
- Tensile Strength, Ultimate: 120 MPa
$ 2021/MT
- Density: 1.68 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 118
- Tensile Strength at Break: 125 MPa
- Tensile Strength at Break: 50.0 MPa @Temperature 120 °C
$ 2104/MT
- Density: 1.18 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Ultimate: 37.0 MPa
- Tensile Strength, Yield: 1.10 MPa @Strain 300 %
- Tensile Strength, Yield: 5.20 MPa @Strain 100 %
$ 1788/MT
- Density: 1.23 g/cc
- Hardness, Shore A: 89
- Hardness, Shore D: 37
- Tensile Strength: 20.0 MPa
- Tensile Strength: 35.0 MPa
$ 1630/MT
- Density: 1.53 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0044 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0124 cm/cm
$ 1994/MT
- Density: 1.23 g/cc
- Hardness, Shore A: 81
- Tensile Strength: 2.30 MPa
- Tensile Strength: 5.00 MPa
- Tensile Strength: 8.50 MPa
$ 1838/MT
- Density: 1.21 g/cc
- Hardness, Shore A: 78
- Tensile Strength: 2.80 MPa
- Tensile Strength: 5.50 MPa
- Tensile Strength: 9.50 MPa
$ 2158/MT
- Density: 1.11 g/cc
- Hardness, Shore A: 88
- Hardness, Shore D: 39
- Tensile Strength: 30.0 MPa
- Tensile Strength: 45.0 MPa
$ 1974/MT
- Density: 1.44 g/cc
- Tensile Strength at Break: 97.0 MPa
- Elongation at Break: 2.7 %
- Flexural Modulus: 6.30 GPa
- Izod Impact, Notched (ISO): 5.00 kJ/m²
$ 1929/MT
- Density: 1.45 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 107 cm³/g
- Linear Mold Shrinkage, Flow: 0.0039 cm/cm
$ 2101/MT
- Density: 1.23 g/cc
- Hardness, Shore D: 65
- Tensile Strength: 40.0 MPa
- Tensile Strength: 40.0 MPa
- Tensile Strength: 12.0 MPa @Strain 20.0 %
$ 1705/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 83
- Tensile Strength: 40.0 MPa
- Tensile Strength: 55.0 MPa
- Tensile Strength: 2.00 MPa @Strain 20.0 %
$ 1746/MT
- Density: 1.23 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 48
- Tensile Strength, Ultimate: 42.0 MPa
- Tensile Strength, Yield: 14.0 MPa @Strain 100 %
$ 1550/MT
- Density: 1.21 g/cc
- Hardness, Shore A: 93
- Hardness, Shore D: 41
- Tensile Strength, Ultimate: 41.0 MPa
- Tensile Strength, Yield: 10.0 MPa @Strain 100 %
$ 1484/MT
- Density: 1.13 g/cc
- Hardness, Shore A: 77
- Tensile Strength: 1.00 MPa
- Tensile Strength: 4.50 MPa
- Tensile Strength: 10.0 MPa
$ 1884/MT
- Density: 1.70 g/cc
- Viscosity Measurement: 0.52
- Linear Mold Shrinkage: 0.0020 cm/cm
- Hardness, Rockwell R: 118
- Tensile Strength at Break: 170 MPa
$ 2295/MT
- Density: 1.42 g/cc
- Water Absorption: 0.20 %
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 113 cm³/g
$ 1618/MT
- Bulk Density: 0.600 - 0.900 g/cc
- Density: 1.51 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 108
$ 1602/MT
- Density: 1.38 g/cc
- Hardness, Shore D: 70
- Tensile Strength: 70.0 MPa
- Elongation at Break: 15 %
- Charpy Impact Unnotched: 9.00 J/cm² @Temperature -30.0 °C
$ 2408/MT
- Density: 1.15 g/cc
- Hardness, Shore A: 89
- Tensile Strength: 4.80 MPa
- Tensile Strength: 7.60 MPa
- Tensile Strength: 16.5 MPa
$ 1455/MT
- Bulk Density: 0.600 - 0.900 g/cc
- Density: 1.30 g/cc
- Viscosity Measurement: 115
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.019 cm/cm
$ 1843/MT
- Density: 1.26 g/cc
- Hardness, Shore D: 75
- Tensile Strength: 40.0 MPa
- Tensile Strength: 25.0 MPa @Strain 20.0 %
- Tensile Strength: 30.0 MPa @Strain 100 %
$ 2548/MT
- Density: 1.24 g/cc
- Hardness, Shore A: 93
- Hardness, Shore D: 41
- Tensile Strength: 55.0 MPa
- Tensile Strength: 5.00 MPa @Strain 20.0 %
$ 1566/MT
- Density: 1.27 g/cc
- Hardness, Shore D: 50
- Tensile Strength: 30.0 MPa
- Elongation at Break: 65 %
- Charpy Impact Unnotched: 16.0 J/cm² @Temperature -30.0 °C
$ 1883/MT
- Bulk Density: 0.600 - 0.900 g/cc
- Density: 1.53 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 102
$ 1651/MT
- Density: 1.56 g/cc
- Viscosity Test: 87 cm³/g
- Melt Flow: 50 g/10 min @Load 2.16 kg, Temperature 275 °C
- Tensile Strength, Ultimate: 135 MPa
- Elongation at Break: 1.8 %
$ 1559/MT
- Density: 1.52 g/cc
- Viscosity Test: 92 cm³/g
- Tensile Strength, Ultimate: 140 MPa
- Elongation at Break: 3.2 %
- Flexural Strength: 212 MPa
$ 1638/MT
- Density: 1.26 g/cc
- Hardness, Shore D: 64
- Tensile Strength: 45.0 MPa
- Tensile Strength: 22.0 MPa @Strain 20.0 %
- Tensile Strength: 23.0 MPa @Strain 100 %
$ 1969/MT
- Density: 1.47 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 104
- Viscosity Measurement: 70 @Temperature 290 °C
$ 1877/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Ultimate: 39.0 MPa
- Tensile Strength, Yield: 1.30 MPa @Strain 300 %
- Tensile Strength, Yield: 6.60 MPa @Strain 100 %
$ 2090/MT
- Density: 1.27 g/cc
- Hardness, Shore A: 88
- Tensile Strength, Ultimate: 33.0 MPa
- Tensile Strength, Yield: 7.00 MPa @Strain 100 %
- Tensile Strength, Yield: 15.5 MPa @Strain 300 %
$ 1654/MT
- Density: 1.53 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 87 cm³/g
- Linear Mold Shrinkage, Flow: 0.0036 cm/cm
$ 1596/MT
- Density: 1.58 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Tensile Strength at Break: 132 MPa
- Tensile Strength, Ultimate: 130 MPa
$ 1798/MT
- Bulk Density: 0.600 - 0.900 g/cc
- Density: 1.37 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 115
$ 1780/MT
- Density: 1.21 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 46
- Tensile Strength, Ultimate: 40.0 MPa
- Tensile Strength, Yield: 13.0 MPa @Strain 100 %
$ 1782/MT
- Density: 1.21 g/cc
- Hardness, Shore A: 91
- Hardness, Shore D: 42
- Tensile Strength: 40.0 MPa
- Tensile Strength: 55.0 MPa
$ 2038/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 61
- Tensile Strength: 50.0 MPa
- Tensile Strength: 2.00 MPa @Strain 20.0 %
- Tensile Strength: 4.00 MPa @Strain 100 %
$ 1935/MT
- Density: 1.51 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 108
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm
$ 2010/MT
- Density: 1.35 g/cc
- Hardness, Shore D: 64
- Tensile Strength: 65.0 MPa
- Elongation at Break: 20 %
- Modulus of Elasticity: 1.90 GPa
$ 1779/MT
- Density: 1.55 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 101
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
$ 2100/MT
- Density: 1.21 g/cc
- Hardness, Shore A: 78
- Tensile Strength, Ultimate: 31.0 MPa
- Tensile Strength, Yield: 4.80 MPa @Strain 100 %
- Tensile Strength, Yield: 8.30 MPa @Strain 300 %
$ 1643/MT
- Density: 1.39 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 104
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
$ 1819/MT
- Bulk Density: 0.600 - 0.900 g/cc
- Density: 1.41 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 100
$ 1776/MT
- Density: 1.37 g/cc
- Hardness, Shore D: 67
- Tensile Strength: 65.0 MPa
- Tensile Strength: 35.0 MPa @Strain 5.00 %, Temperature 60.0 °C
- Tensile Strength: 40.0 MPa @Strain 5.00 %, Temperature 40.0 °C
$ 2330/MT
- Density: 1.24 g/cc
- Hardness, Shore A: 96
- Hardness, Shore D: 48
- Tensile Strength: 50.0 MPa
- Tensile Strength: 8.00 MPa @Strain 20.0 %
$ 1446/MT
- Density: 1.36 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 100
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
$ 1490/MT
- Water Vapor Transmission: 135 g/m²/day
- Oxygen Transmission Rate: 1200 cc/m²/day
- Thickness: 10.0 - 120 microns
- Dart Drop Total Energy: 240 J/cm
- Commercial Status: Europe
$ 1731/MT
- Density: 1.68 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 98 cm³/g
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 275 °C
$ 2166/MT
- Density: 1.22 g/cc
- Hardness, Shore D: 50
- Tensile Strength: 40.0 MPa
- Tensile Strength: 50.0 MPa
- Tensile Strength: 6.00 MPa @Strain 20.0 %
$ 2078/MT
- Density: 1.65 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 105 cm³/g
- Tensile Strength at Break: 154 MPa
$ 2173/MT
- Density: 1.27 g/cc
- Hardness, Shore A: 84
- Tensile Strength, Ultimate: 35.9 MPa
- Tensile Strength, Yield: 8.50 MPa @Strain 100 %
- Tensile Strength, Yield: 19.7 MPa @Strain 300 %
$ 2125/MT
- Density: 1.54 g/cc
- Viscosity Test: 89 cm³/g
- Melt Flow: 27 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Ultimate: 140 MPa
- Elongation at Break: 2.5 %
$ 2060/MT
- Density: 1.11 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Ultimate: 32.0 MPa
- Tensile Strength, Yield: 5.50 MPa @Strain 100 %
- Tensile Strength, Yield: 10.0 MPa @Strain 300 %
$ 1623/MT
- Density: 1.23 g/cc
- Hardness, Shore D: 57
- Tensile Strength: 43.0 MPa
- Tensile Strength: 50.0 MPa
- Tensile Strength: 12.0 MPa @Strain 20.0 %
$ 1521/MT
- Density: 1.424 g/cc
- Density: 1.61 g/cc
- Viscosity Measurement: 0.55
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 118
$ 1493/MT
- Density: 1.24 g/cc
- Hardness, Shore D: 73
- Tensile Strength, Ultimate: 40.0 MPa
- Tensile Strength, Yield: 36.0 MPa @Strain 100 %
- Tensile Strength, Yield: 37.0 MPa @Strain 300 %
$ 1706/MT
- Density: 1.19 g/cc @Thickness 2.00 mm
- Hardness, Shore A: 85 @Thickness 2.00 mm
- Tensile Strength, Ultimate: 67.0 MPa @Thickness 2.00 mm
- Tensile Strength, Yield: 6.00 MPa @Strain 100 %
- Tensile Strength, Yield: 15.0 MPa @Strain 300 %, Thickness 0.760 mm
$ 1914/MT
- Density: 1.65 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 108
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
$ 2478/MT
- Density: 1.68 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 105 cm³/g
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 2185/MT
- Density: 1.18 g/cc
- Hardness, Shore A: 80
- Tensile Strength: 35.0 MPa
- Tensile Strength: 50.0 MPa
- Tensile Strength: 2.00 MPa @Strain 20.0 %
$ 1492/MT
- Density: 1.45 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.25 %
- Viscosity Measurement: 123
- Viscosity Measurement: 70 @Temperature 290 °C
$ 2423/MT
- Density: 1.17 g/cc
- Hardness, Shore D: 60
- Tensile Strength, Ultimate: 40.0 MPa
- Tensile Strength, Yield: 22.0 MPa @Strain 100 %
- Tensile Strength, Yield: 33.0 MPa @Strain 300 %
$ 2233/MT
- Density: 1.45 g/cc
- Water Absorption: 0.20 %
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 110 cm³/g
$ 1834/MT
- Density: 1.39 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 104 cm³/g
- Linear Mold Shrinkage, Flow: 0.0039 cm/cm
$ 1719/MT
- Density: 1.25 g/cc
- Hardness, Shore D: 60
- Tensile Strength, Ultimate: 43.0 MPa
- Tensile Strength, Yield: 22.0 MPa @Strain 100 %
- Tensile Strength, Yield: 36.0 MPa @Strain 300 %
$ 1747/MT
- Density: 1.11 g/cc
- Hardness, Shore A: 75
- Tensile Strength: 0.800 MPa
- Tensile Strength: 2.70 MPa
- Tensile Strength: 7.70 MPa
$ 1737/MT
- Density: 1.42 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 111 cm³/g
- Linear Mold Shrinkage: 0.0050 cm/cm
$ 1475/MT
- Density: 1.25 - 1.27 g/cc
- Melt Flow: 8.3 - 13.8 g/10 min
- Hardness, Shore D: 32
- Melting Point: 110 - 120 °C
- Vicat Softening Point: 91.0 °C
- Commercial Status: Europe
$ 1947/MT
- Density: 1.24 - 1.26 g/cc
- Water Vapor Transmission: 98.0 g/m²/day
- Oxygen Transmission Rate: 860 cc/m²/day
- Melt Flow: <= 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Melt Flow: 2.4 - 5.2 g/10 min @Load 5.00 kg, Temperature 190 °C
$ 1460/MT
- Density: 1.58 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 112 cm³/g
- Linear Mold Shrinkage: 0.0030 cm/cm
$ 2482/MT
- Density: 1.67 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 118
- Tensile Strength at Break: 135 MPa
- Tensile Strength at Break: 60.0 MPa @Temperature 120 °C
$ 2172/MT
- Bulk Density: 0.600 - 0.900 g/cc
- Density: 1.53 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 102
$ 2209/MT
- Density: 1.68 g/cc
- Viscosity Measurement: 0.49
- Linear Mold Shrinkage: 0.0030 cm/cm
- Hardness, Rockwell R: 118
- Tensile Strength at Break: 130 MPa
$ 2218/MT
- Density: 1.37 g/cc
- Hardness, Shore D: 67
- Tensile Strength: 60.0 MPa
- Elongation at Break: 30 %
- Modulus of Elasticity: 1.80 GPa
$ 2078/MT
- Bulk Density: 0.600 - 0.900 g/cc
- Density: 1.20 - 1.35 g/cc
- Specific Heat Capacity: 1.50 J/g-°C
- Melting Point: 220 - 230 °C
- Decomposition Temperature: >= 290 °C
$ 1852/MT
- Density: 1.73 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.12 %
- Viscosity Test: 90 cm³/g
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm
$ 2129/MT
- Density: 1.23 g/cc
- Hardness, Shore A: 92
- Hardness, Shore D: 41
- Tensile Strength, Ultimate: 37.0 MPa
- Tensile Strength, Yield: 11.0 MPa @Strain 100 %
$ 2505/MT
- Density: 1.11 g/cc @Thickness 2.00 mm
- Hardness, Shore A: 80 @Thickness 2.00 mm
- Tensile Strength, Ultimate: 48.0 MPa @Thickness 2.00 mm
- Tensile Strength, Yield: 4.80 MPa @Strain 100 %
- Tensile Strength, Yield: 12.0 MPa @Strain 300 %, Thickness 0.760 mm
$ 1911/MT
- Density: 1.24 g/cc
- Hardness, Shore A: 98
- Hardness, Shore D: 54
- Tensile Strength, Ultimate: 42.0 MPa
- Tensile Strength, Yield: 19.0 MPa @Strain 100 %
$ 1696/MT
- Density: 1.30 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.25 %
- Water Vapor Transmission: 10.0 g/m²/day
- Viscosity Test: 130 cm³/g
$ 2231/MT
- Density: 1.19 g/cc
- Hardness, Shore D: 73
- Tensile Strength, Ultimate: 45.0 MPa
- Tensile Strength, Yield: 32.0 MPa @Strain 100 %
- Tensile Strength, Yield: 38.0 MPa @Strain 300 %
$ 2240/MT
- Density: 1.23 g/cc
- Hardness, Shore A: 93
- Tensile Strength, Ultimate: 37.5 MPa
- Tensile Strength, Yield: 11.8 MPa @Strain 100 %
- Tensile Strength, Yield: 24.4 MPa @Strain 300 %
$ 1507/MT
- Density: 1.12 g/cc @Thickness 2.00 mm
- Hardness, Shore A: 86 @Thickness 2.00 mm
- Tensile Strength, Ultimate: 52.0 MPa @Thickness 2.00 mm
- Tensile Strength, Yield: 7.60 MPa @Strain 100 %
- Tensile Strength, Yield: 19.0 MPa @Strain 300 %
$ 1566/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 82
- Tensile Strength, Ultimate: 36.0 MPa
- Tensile Strength, Yield: 1.10 MPa @Strain 300 %
- Tensile Strength, Yield: 5.50 MPa @Strain 100 %
$ 1787/MT
- Density: 1.17 g/cc
- Hardness, Shore A: 60
- Tensile Strength: 20.0 MPa
- Tensile Strength: 35.0 MPa
- Tensile Strength: 1.00 MPa @Strain 20.0 %
$ 1522/MT
- Density: 1.24 - 1.26 g/cc
- Water Vapor Transmission: 84.0 g/m²/day
- Oxygen Transmission Rate: 670 cc/m²/day
- Melt Flow: <= 2.0 g/10 min
- Hardness, Shore D: 59
$ 1610/MT
- Density: 1.48 g/cc
- Viscosity Test: 86 cm³/g
- Melt Flow: 65 g/10 min @Load 2.16 kg, Temperature 275 °C
- Tensile Strength, Ultimate: 110 MPa
- Elongation at Break: 1.9 %
$ 1445/MT
- Density: 1.53 g/cc
- Water Absorption: 0.20 %
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 101 cm³/g
$ 2288/MT
- Density: 1.26 g/cc
- Hardness, Shore A: 80
- Tensile Strength, Ultimate: 31.0 MPa
- Tensile Strength, Yield: 6.60 MPa @Strain 100 %
- Tensile Strength, Yield: 16.6 MPa @Strain 300 %
$ 2078/MT
- Density: 1.37 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 135
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
$ 1648/MT
- Density: 1.28 g/cc
- Hardness, Shore D: 61
- Tensile Strength: 45.0 MPa
- Elongation at Break: 450 %
- Tear Strength: 180 kN/m
$ 2091/MT
- Density: 1.76 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.12 %
- Viscosity Test: 75 cm³/g
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
$ 2473/MT
- Density: 1.16 g/cc @Thickness 2.00 mm
- Hardness, Shore A: 83 @Thickness 2.00 mm
- Tensile Strength, Ultimate: 38.0 MPa @Thickness 2.00 mm
- Tensile Strength, Yield: 5.90 MPa @Strain 100 %
- Tensile Strength, Yield: 13.0 MPa @Strain 300 %, Thickness 0.760 mm
$ 2260/MT
- Density: 1.76 g/cc
- Viscosity Test: 75 cm³/g
- Melt Flow: 110 g/10 min @Load 10.0 kg, Temperature 275 °C
- Tensile Strength, Ultimate: 170 MPa
- Elongation at Break: 1.4 %
$ 2165/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 85
- Tensile Strength, Ultimate: 34.0 MPa
- Tensile Strength, Yield: 6.90 MPa @Strain 100 %
- Tensile Strength, Yield: 14.0 MPa @Strain 300 %
$ 1968/MT
- Bulk Density: 0.600 - 0.900 g/cc
- Density: 1.51 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 117
$ 1752/MT
- Density: 1.14 g/cc @Thickness 2.00 mm
- Hardness, Shore A: 75 @Thickness 2.00 mm
- Tensile Strength, Ultimate: 41.0 MPa @Thickness 2.00 mm
- Tensile Strength, Yield: 4.80 MPa @Strain 100 %
- Tensile Strength, Yield: 11.0 MPa @Strain 300 %
$ 2190/MT
- Density: 1.41 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 98
- Linear Mold Shrinkage, Flow: 0.0063 cm/cm
$ 2386/MT
- Density: 1.39 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 105 cm³/g
- Linear Mold Shrinkage, Flow: 0.0016 cm/cm
$ 1644/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 65
- Tensile Strength: 25.0 MPa
- Tensile Strength: 40.0 MPa
- Tensile Strength: 1.50 MPa @Strain 20.0 %
$ 1771/MT
- Density: 1.25 - 1.27 g/cc
- Melt Flow: 2.7 - 4.9 g/10 min
- Surface Tension: 34 dynes/cm
- Hardness, Shore D: 32
- Tensile Strength: 34.0 MPa
$ 1671/MT
- Density: 1.25 - 1.27 g/cc
- Water Vapor Transmission: 140 g/m²/day
- Oxygen Transmission Rate: 1600 cc/m²/day
- Melt Flow: 2.7 - 4.9 g/10 min
- Hardness, Shore D: 32
$ 2088/MT
- Density: 1.37 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 100 cm³/g
- Linear Mold Shrinkage, Flow: 0.0095 cm/cm
$ 1471/MT
- Density: 1.14 g/cc
- Hardness, Shore A: 63
- Tensile Strength, Ultimate: 23.0 MPa
- Tensile Strength, Yield: 2.60 MPa @Strain 100 %
- Tensile Strength, Yield: 4.70 MPa @Strain 300 %
$ 1479/MT
- Density: 1.53 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 113
- Viscosity Measurement: 70 @Temperature 290 °C
$ 1739/MT
- Density: 1.49 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 108
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
$ 2035/MT
- Density: 1.12 g/cc
- Hardness, Shore A: 87
- Tensile Strength: 2.50 MPa
- Tensile Strength: 6.00 MPa
- Tensile Strength: 11.5 MPa
$ 1558/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Tensile Strength, Ultimate: 70.0 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 6.00 GPa
$ 1870/MT
- Density: 1.11 g/cc
- Hardness, Shore A: 80
- Tensile Strength: 2.50 MPa
- Tensile Strength: 5.50 MPa
- Tensile Strength: 9.00 MPa
$ 1634/MT
- Density: 1.25 g/cc
- Hardness, Shore D: 55
- Tensile Strength: 45.0 MPa
- Tensile Strength: 13.0 MPa @Strain 20.0 %
- Tensile Strength: 16.0 MPa @Strain 100 %
$ 2130/MT
- Bulk Density: 0.600 - 0.900 g/cc
- Density: 1.55 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 105
$ 2080/MT
- Density: 1.19 g/cc
- Hardness, Shore A: 70
- Tensile Strength: 30.0 MPa
- Tensile Strength: 35.0 MPa
- Tensile Strength: 1.00 MPa @Strain 20.0 %
$ 1853/MT
- Density: 1.56 g/cc
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 1.5 %
- Flexural Modulus: 6.80 GPa
- Charpy Impact Unnotched: 1.50 J/cm² @Temperature 5.00 °C
$ 1734/MT
- Bulk Density: 0.600 - 0.900 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 95
- Linear Mold Shrinkage, Flow: 0.0013 cm/cm
$ 1605/MT
- Density: 1.16 g/cc
- Hardness, Shore D: 53
- Tensile Strength, Ultimate: 40.0 MPa
- Tensile Strength, Yield: 20.0 MPa @Strain 100 %
- Tensile Strength, Yield: 30.0 MPa @Strain 300 %
$ 1502/MT
- Density: 1.22 g/cc
- Hardness, Shore A: 89
- Tensile Strength, Ultimate: 32.0 MPa
- Tensile Strength, Yield: 9.70 MPa @Strain 100 %
- Tensile Strength, Yield: 20.9 MPa @Strain 300 %
$ 1556/MT
- Density: 1.32 g/cc
- Hardness, Shore D: 75
- Tensile Strength: 65.0 MPa
- Elongation at Break: 25 %
- Charpy Impact Unnotched: 7.00 J/cm² @Temperature -30.0 °C
$ 1708/MT
- Density: 1.38 g/cc
- Hardness, Shore D: 73
- Tensile Strength: 80.0 MPa
- Tensile Strength: 30.0 MPa @Strain 2.00 %, Temperature 60.0 °C
- Tensile Strength: 35.0 MPa @Strain 2.00 %, Temperature 40.0 °C
$ 1868/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 55
- Tensile Strength: 35.0 MPa
- Tensile Strength: 0.800 MPa @Strain 20.0 %
- Tensile Strength: 1.10 MPa @Strain 100 %
$ 2487/MT
- Density: 1.73 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 97
- Viscosity Measurement: 70 @Temperature 290 °C
$ 2050/MT
- Density: 1.20 g/cc
- Hardness, Shore A: 70
- Tensile Strength: 40.0 MPa
- Tensile Strength: 1.40 MPa @Strain 20.0 %
- Tensile Strength: 3.30 MPa @Strain 100 %
$ 1594/MT
- Density: 1.37 g/cc
- Water Absorption: 0.20 %
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Test: 116 cm³/g
$ 1815/MT
- Density: 1.31 g/cc
- Water Absorption: 0.40 %
- Moisture Absorption at Equilibrium: 0.20 %
- Viscosity Measurement: 105
- Viscosity Measurement: 70 @Temperature 290 °C
Delivery TP BASF
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.