$ 1469/MT
- Density: 1.34 g/cc
- Water Absorption: 0.90 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.019 cm/cm
$ 2276/MT
- Density: 0.932 g/cc
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.7 %
$ 1846/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.3 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 2.6 cP
$ 1903/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.3 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 2.6 cP
$ 2108/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 4.0 cP
- Viscosity Test: 250 cm³/g
$ 1817/MT
- Density: 1.16 g/cc
- Water Absorption: 6.5 - 7.5 %
- Moisture Absorption at Equilibrium: 1.6 - 2.0 %
- Viscosity Measurement: 130
- Linear Mold Shrinkage: 0.0060 cm/cm
$ 2422/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.7 %
- Relative Viscosity: 2.81 - 3.0 cP
- Viscosity Test: 165 cm³/g
$ 1515/MT
- Relative Viscosity: 5.0 cP
- Linear Mold Shrinkage: 0.0090 cm/cm
- Melting Point: 220 °C
$ 1623/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 145 MPa
$ 1907/MT
- Bulk Density: 0.850 g/cc
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.021 cm/cm
$ 1817/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 5.0 cP
- Viscosity Test: 320 cm³/g
$ 1621/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage: 0.019 cm/cm
- Tensile Strength, Yield: 63.0 MPa
$ 2014/MT
- Density: 1.13 g/cc
- Relative Viscosity: 2.7 cP
- Viscosity Test: 150 cm³/g
- Melt Flow: 145 g/10 min @Load 5.00 kg, Temperature 275 °C
- Tensile Strength, Yield: 79.0 MPa
$ 1745/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage: 0.020 cm/cm
- Linear Mold Shrinkage, Flow: 0.021 cm/cm
$ 1527/MT
- Density: 1.16 g/cc
- Water Absorption: 6.5 - 7.5 %
- Moisture Absorption at Equilibrium: 1.6 - 2.0 %
- Viscosity Measurement: 130
- Linear Mold Shrinkage: 0.0060 cm/cm
$ 1455/MT
- Bulk Density: 0.690 - 0.710 g/cc
- Density: 1.12 g/cc
- Water Absorption: 10.5 %
- Moisture Absorption at Equilibrium: 3.2 %
- Viscosity Measurement: 3.19 - 3.41
$ 1788/MT
- Density: 1.30 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.25 %
- Viscosity Test: 160 cm³/g
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
$ 1480/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 5.0 cP
- Viscosity Test: 320 cm³/g
$ 1464/MT
- Density: 1.13 g/cc
- Tensile Strength at Break: 48.0 MPa
- Elongation at Break: 200 %
- Elongation at Yield: 30 %
- Tensile Modulus: 1.18 GPa
$ 1527/MT
- Density: 1.41 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 12.9 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 155 MPa
$ 1824/MT
- Bulk Density: 0.850 g/cc
- Density: 1.35 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 9.45 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1994/MT
- Density: 1.13 g/cc
- Water Absorption: 9.0 - 10 %
- Moisture Absorption at Equilibrium: 2.6 - 3.4 %
- Viscosity Measurement: 145
- Linear Mold Shrinkage: 0.0055 cm/cm
$ 1730/MT
- Density: 1.39 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 125 MPa
$ 1984/MT
- Density: 1.13 g/cc
- Moisture Absorption at Equilibrium: 1.6 %
- Moisture Absorption at Equilibrium: 2.7 %
- Moisture Absorption at Equilibrium: 9.5 %
- Tensile Strength, Yield: 80.0 MPa
$ 1596/MT
- Bulk Density: 0.700 g/cc
- Density: 1.12 - 1.15 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: <= 0.40 %
- Moisture Absorption at Equilibrium: 2.2 %
$ 1635/MT
- Density: 1.05 g/cc
- Water Absorption: 0.10 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1521/MT
- Density: 1.37 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 8.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 105 MPa @Load 36.5 kg, Time 30.0 sec
$ 2489/MT
- Density: 1.13 g/cc
- Water Absorption: 8.0 - 9.0 %
- Moisture Absorption at Equilibrium: 2.5 - 3.1 %
- Viscosity Measurement: 150
- Linear Mold Shrinkage: 0.0085 cm/cm
$ 2508/MT
- Bulk Density: 0.850 g/cc
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
$ 1548/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Moisture Absorption at Equilibrium: 1.9 %
- Moisture Absorption at Equilibrium: 6.7 %
- Linear Mold Shrinkage: 0.03556 cm/cm
$ 1502/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 3.3 cP
- Viscosity Test: 195 cm³/g
$ 1892/MT
- Density: 1.14 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.5 %
- Linear Mold Shrinkage: 0.016 cm/cm
- Tensile Strength, Yield: 69.0 MPa
$ 1576/MT
- Density: 1.30 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.25 %
- Viscosity Test: 130 cm³/g
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
$ 2239/MT
- Density: 1.08 g/cc
- Tensile Strength, Yield: 46.0 MPa
- Elongation at Break: 50 %
- Flexural Modulus: 1.703 GPa
- Izod Impact, Notched (ISO): 22.0 kJ/m² @Temperature -40.0 °C
$ 1566/MT
- Bulk Density: 0.640 - 0.740 g/cc
- Density: 1.12 - 1.15 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Viscosity Measurement: 3.89 - 4.17
$ 1796/MT
- Density: 1.15 g/cc
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 20 %
- Tensile Modulus: 1.50 GPa
$ 2119/MT
- Bulk Density: 0.640 - 0.740 g/cc
- Density: 1.12 - 1.15 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Viscosity Measurement: 3.89 - 4.17
$ 1587/MT
- Density: 1.30 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.25 %
- Viscosity Test: 107 cm³/g
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
$ 1522/MT
- Density: 1.04 g/cc
- Tensile Strength at Break: 48.0 MPa
- Elongation at Break: 200 %
- Flexural Modulus: 0.750 GPa
- Izod Impact, Notched (ISO): 104 kJ/m²
$ 1862/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 3.2 cP
- Viscosity Test: 184 cm³/g
$ 2186/MT
- Density: 1.10 g/cc
- Moisture Absorption at Equilibrium: 2.4 %
- Moisture Absorption at Equilibrium: 8.6 %
- Tensile Strength, Yield: 36.0 MPa
- Elongation at Break: >= 100 %
$ 1971/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 135 MPa @Load 36.5 kg, Time 30.0 sec
$ 1608/MT
- Bulk Density: 0.450 - 0.800 g/cc
- Density: 1.16 g/cc
- Water Absorption: 6.5 - 7.5 %
- Moisture Absorption at Equilibrium: 1.6 - 2.0 %
- Viscosity Measurement: 130
$ 1467/MT
- Density: 1.10 g/cc
- Water Absorption: 8.5 - 9.5 %
- Moisture Absorption at Equilibrium: 2.1 - 2.9 %
- Linear Mold Shrinkage: 0.0065 cm/cm
- Melt Flow: 121 g/10 min @Load 5.00 kg, Temperature 275 °C
$ 1601/MT
- Bulk Density: 0.640 - 0.740 g/cc
- Density: 1.12 - 1.15 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Viscosity Measurement: 3.49 - 3.71
$ 1774/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 145 MPa
$ 1615/MT
- Density: 1.16 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.9 %
- Linear Mold Shrinkage: 0.0080 cm/cm
- Tensile Strength, Yield: 84.0 MPa
$ 1949/MT
- Bulk Density: 0.850 g/cc
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.023 cm/cm
$ 2164/MT
- Density: 1.33 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 8.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 65.0 MPa @Load 36.5 kg, Time 30.0 sec
$ 1699/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage: 0.020 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 61.0 MPa
- Tensile Strength, Yield: 61.0 MPa
$ 1845/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Moisture Absorption at Equilibrium: 1.9 %
- Moisture Absorption at Equilibrium: 6.7 %
- Linear Mold Shrinkage: 0.03556 cm/cm
$ 1685/MT
- Bulk Density: 0.640 - 0.740 g/cc
- Density: 1.12 - 1.15 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Viscosity Measurement: 3.49 - 3.71
$ 1631/MT
- Density: 1.06 g/cc
- Moisture Absorption at Equilibrium: 2.1 %
- Moisture Absorption at Equilibrium: 7.3 %
- Linear Mold Shrinkage: 0.04572 cm/cm
- Melt Temperature: 270 - 300 °C
$ 1908/MT
- Bulk Density: 0.690 - 0.710 g/cc
- Density: 1.12 g/cc
- Water Absorption: 10.5 %
- Moisture Absorption at Equilibrium: 3.2 %
- Viscosity Measurement: 2.96 - 3.15
$ 1583/MT
- Density: 1.13 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.2 %
- Viscosity Test: 150 cm³/g
- Linear Mold Shrinkage: 0.010 cm/cm
$ 1783/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 2.7 cP
- Viscosity Test: 150 cm³/g
$ 1711/MT
- Density: 1.14 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.5 %
- Linear Mold Shrinkage: 0.016 cm/cm
- Tensile Strength, Yield: 83.0 MPa
$ 2023/MT
- Density: 1.13 g/cc
- Water Absorption: 9.0 - 10 %
- Moisture Absorption at Equilibrium: 2.6 - 3.4 %
- Viscosity Measurement: 150
- Linear Mold Shrinkage: 0.0065 cm/cm
$ 1543/MT
- Density: 1.09 g/cc
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Break: >= 50 %
- Elongation at Yield: 20 %
- Tensile Modulus: 1.20 GPa
$ 1703/MT
- Bulk Density: 0.500 - 0.800 g/cc
- Density: 1.10 g/cc
- Moisture Absorption at Equilibrium: 4.5 - 5.0 %
- Viscosity Measurement: 125
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
$ 1450/MT
- Density: 1.10 g/cc
- Water Absorption: 8.5 - 9.5 %
- Moisture Absorption at Equilibrium: 2.1 - 2.9 %
- Linear Mold Shrinkage: 0.0065 cm/cm
- Melt Flow: 121 g/10 min @Load 5.00 kg, Temperature 275 °C
$ 1500/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
$ 1658/MT
- Density: 1.13 g/cc
- Moisture Absorption at Equilibrium: 1.3 %
- Moisture Absorption at Equilibrium: 2.7 %
- Moisture Absorption at Equilibrium: 9.5 %
- Linear Mold Shrinkage: 0.0508 cm/cm
$ 1484/MT
- Density: 1.16 g/cc
- Water Absorption: 8.0 - 9.0 %
- Moisture Absorption at Equilibrium: 2.6 - 3.2 %
- Viscosity Test: 150 cm³/g
- Linear Mold Shrinkage: 0.0080 cm/cm
$ 1529/MT
- Density: 1.05 g/cc
- Water Absorption: 0.10 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm
- Melt Flow: 1.2 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2252/MT
- Density: 1.05 g/cc
- Water Absorption: 0.10 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1454/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Moisture Absorption at Equilibrium: 1.9 %
- Moisture Absorption at Equilibrium: 6.7 %
- Linear Mold Shrinkage: 0.03556 cm/cm
$ 1518/MT
- Bulk Density: 0.640 - 0.740 g/cc
- Density: 1.12 - 1.15 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Viscosity Measurement: 2.19 - 3.41
$ 1560/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 8.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 130 MPa @Load 36.5 kg, Time 30.0 sec
$ 2130/MT
- Density: 1.12 g/cc
- Water Absorption: 10.5 %
- Moisture Absorption at Equilibrium: 3.2 %
- Relative Viscosity: 4.0 cP
- Viscosity Test: 250 cm³/g
$ 1591/MT
- Bulk Density: 0.500 - 0.800 g/cc
- Density: 1.10 g/cc
- Moisture Absorption at Equilibrium: 4.5 - 5.0 %
- Viscosity Measurement: 125
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
$ 1706/MT
- Density: 1.13 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.2 %
- Relative Viscosity: 3.5 cP
- Viscosity Test: 205 cm³/g
$ 2196/MT
- Density: 1.12 g/cc
- Water Absorption: 10.5 %
- Moisture Absorption at Equilibrium: 3.2 %
- Relative Viscosity: 4.0 cP
- Viscosity Test: 250 cm³/g
$ 1656/MT
- Density: 1.12 g/cc
- Water Absorption: 10.5 %
- Moisture Absorption at Equilibrium: 3.2 %
- Relative Viscosity: 4.0 cP
- Viscosity Test: 250 cm³/g
$ 1773/MT
- Bulk Density: 0.890 g/cc
- Density: 1.40 g/cc
- Melt Flow: 35 g/10 min @Load 10.0 kg, Temperature 190 °C
- Melting Point: 165 °C
- Decomposition Temperature: >= 240 °C
$ 1848/MT
- Density: 1.35 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 8.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 80.0 MPa @Load 36.5 kg, Time 30.0 sec
$ 1622/MT
- Bulk Density: 0.650 - 0.900 g/cc
- Density: 1.42 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.021 cm/cm
$ 1831/MT
- Density: 1.13 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.8 %
- Relative Viscosity: 2.73 cP
- Viscosity Test: 151 cm³/g
$ 2404/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.7 %
- Relative Viscosity: 2.6 cP
$ 1512/MT
- Bulk Density: 0.650 - 0.900 g/cc
- Density: 1.48 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
$ 2286/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 3.6 cP
- Viscosity Test: 218 cm³/g
$ 1466/MT
- Density: 1.13 g/cc
- Moisture Absorption at Equilibrium: 1.6 %
- Moisture Absorption at Equilibrium: 2.6 %
- Moisture Absorption at Equilibrium: 9.2 %
- Hardness, Rockwell R: 99
$ 2071/MT
- Bulk Density: 0.650 - 0.850 g/cc
- Density: 1.37 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
$ 1653/MT
- Density: 1.14 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.5 %
- Linear Mold Shrinkage: 0.016 cm/cm
- Tensile Strength, Yield: 54.0 MPa
$ 2099/MT
- Density: 1.14 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.5 %
- Linear Mold Shrinkage: 0.016 cm/cm
- Tensile Strength, Yield: 54.0 MPa
$ 2299/MT
- Density: 1.14 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.5 %
- Linear Mold Shrinkage: 0.016 cm/cm
- Tensile Strength, Yield: 90.0 MPa
$ 1620/MT
- Bulk Density: 0.500 - 0.800 g/cc
- Density: 1.10 g/cc
- Ball Indentation Hardness: 115 MPa
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Yield: 5.0 %
$ 1606/MT
- Bulk Density: 0.500 - 0.800 g/cc
- Density: 1.10 g/cc
- Ball Indentation Hardness: 115 MPa
- Tensile Modulus: 2.40 GPa
- Flexural Strength: 100 MPa
$ 2083/MT
- Density: 1.13 g/cc
- Moisture Absorption at Equilibrium: 1.6 %
- Moisture Absorption at Equilibrium: 2.7 %
- Moisture Absorption at Equilibrium: 9.5 %
- Tensile Strength, Yield: 39.0 MPa
$ 1945/MT
- Density: 1.13 g/cc
- Moisture Absorption at Equilibrium: 1.6 %
- Moisture Absorption at Equilibrium: 2.7 %
- Moisture Absorption at Equilibrium: 9.5 %
- Tensile Strength, Yield: 80.0 MPa
$ 1481/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.7 %
- Relative Viscosity: 2.6 cP
$ 2331/MT
- Density: 0.932 g/cc
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.7 %
$ 1640/MT
- Density: 0.932 g/cc
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.7 %
$ 2485/MT
- Density: 1.30 g/cc
- Moisture Absorption at Equilibrium: 1.6 %
- Moisture Absorption at Equilibrium: 2.7 %
- Moisture Absorption at Equilibrium: 9.5 %
- Linear Mold Shrinkage: 0.0305 cm/cm
$ 1473/MT
- Density: 1.30 g/cc
- Moisture Absorption at Equilibrium: 1.6 %
- Moisture Absorption at Equilibrium: 2.7 %
- Moisture Absorption at Equilibrium: 9.5 %
- Linear Mold Shrinkage: 0.0305 cm/cm
$ 1824/MT
- Density: 0.932 g/cc
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.7 %
$ 1667/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.3 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 2.6 cP
$ 1552/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.3 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 2.6 cP
$ 1611/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.3 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 2.6 cP
$ 1565/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.3 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 2.6 cP
$ 1517/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.2 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 2.6 cP
$ 1674/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.2 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 2.6 cP
$ 1637/MT
- Density: 1.13 g/cc
- Water Absorption: 9.0 - 10 %
- Moisture Absorption at Equilibrium: 2.6 - 3.4 %
- Viscosity Measurement: 150
- Linear Mold Shrinkage: 0.0065 cm/cm
$ 2451/MT
- Bulk Density: 0.500 - 0.800 g/cc
- Density: 1.13 g/cc
- Water Absorption: 8.0 - 9.0 %
- Moisture Absorption at Equilibrium: 2.5 - 3.1 %
- Viscosity Measurement: 190
$ 1620/MT
- Density: 1.13 g/cc
- Moisture Absorption at Equilibrium: 1.6 %
- Moisture Absorption at Equilibrium: 2.6 %
- Moisture Absorption at Equilibrium: 9.2 %
- Tensile Strength, Yield: 46.0 MPa @Temperature 23.0 °C
$ 2259/MT
- Density: 1.14 g/cc
- Moisture Absorption at Equilibrium: 2.5 %
- Moisture Absorption at Equilibrium: 8.5 %
- Tensile Strength, Yield: 54.0 MPa
- Elongation at Break: >= 50 %
$ 1643/MT
- Density: 1.12 g/cc
- Water Absorption: 10.5 %
- Moisture Absorption at Equilibrium: 3.2 %
- Relative Viscosity: 3.3 cP
- Viscosity Test: 195 cm³/g
$ 2208/MT
- Density: 1.13 g/cc
- Moisture Absorption at Equilibrium: 1.3 %
- Moisture Absorption at Equilibrium: 2.7 %
- Moisture Absorption at Equilibrium: 9.5 %
- Linear Mold Shrinkage: 0.0508 cm/cm
$ 2003/MT
- Density: 1.12 g/cc
- Water Absorption: 10.5 %
- Moisture Absorption at Equilibrium: 3.2 %
- Relative Viscosity: 3.3 cP
- Viscosity Test: 195 cm³/g
$ 1769/MT
- Density: 1.14 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.5 %
- Linear Mold Shrinkage: 0.016 cm/cm
- Tensile Strength, Yield: 83.0 MPa
$ 1553/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
$ 2041/MT
- Bulk Density: 0.850 g/cc
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.021 cm/cm
$ 1770/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 29.4 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 145 MPa
$ 1696/MT
- Bulk Density: 0.850 g/cc
- Density: 1.33 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 9.31 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1459/MT
- Bulk Density: 0.690 - 0.710 g/cc
- Density: 1.12 g/cc
- Water Absorption: 10.5 %
- Moisture Absorption at Equilibrium: 3.2 %
- Viscosity Measurement: 3.19 - 3.41
$ 1566/MT
- Density: 1.12 g/cc
- Water Absorption: 10.5 %
- Moisture Absorption at Equilibrium: 3.2 %
- Relative Viscosity: 3.3 cP
- Viscosity Test: 195 cm³/g
$ 1816/MT
- Density: 1.16 g/cc
- Water Absorption: 8.0 - 9.0 %
- Moisture Absorption at Equilibrium: 2.6 - 3.2 %
- Viscosity Test: 150 cm³/g
- Linear Mold Shrinkage: 0.0080 cm/cm
$ 1468/MT
- Density: 1.05 g/cc
- Water Absorption: 0.10 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2196/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.2 %
- Moisture Absorption at Equilibrium: 2.6 %
- Viscosity Measurement: 220
$ 1814/MT
- Bulk Density: 0.850 g/cc
- Density: 1.43 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 7.579 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1853/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 8.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 145 MPa
$ 1941/MT
- Density: 1.13 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.2 %
- Relative Viscosity: 3.5 cP
- Viscosity Test: 205 cm³/g
$ 2254/MT
- Bulk Density: 0.850 g/cc
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.021 cm/cm
$ 1887/MT
- Density: 1.10 g/cc
- Moisture Absorption at Equilibrium: 2.4 %
- Moisture Absorption at Equilibrium: 8.6 %
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: 70 %
$ 2051/MT
- Bulk Density: 0.640 - 0.740 g/cc
- Density: 1.12 - 1.15 g/cc
- Melting Point: 220 °C
- Decomposition Temperature: >= 300 °C
- Commercial Status: Europe
- Ignition Temperature: >400°C
$ 2125/MT
- Bulk Density: 0.640 - 0.740 g/cc
- Density: 1.12 - 1.15 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Viscosity Measurement: 3.89 - 4.17
$ 2505/MT
- Density: 1.06 g/cc
- Moisture Absorption at Equilibrium: 2.1 %
- Moisture Absorption at Equilibrium: 7.3 %
- Linear Mold Shrinkage: 0.04572 cm/cm
- Tensile Strength at Break: 45.0 MPa
$ 1485/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 3.08 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 130 MPa @Load 36.5 kg, Time 30.0 sec
$ 1765/MT
- Density: 1.04 g/cc
- Tensile Strength at Break: 38.0 MPa
- Elongation at Break: 160 %
- Tensile Modulus: 0.494 GPa
- Flexural Modulus: 0.480 GPa
$ 1696/MT
- Density: 1.30 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.25 %
- Water Vapor Transmission: 10.0 g/m²/day
- Viscosity Test: 130 cm³/g
$ 1455/MT
- Bulk Density: 0.850 g/cc
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
$ 2245/MT
- Bulk Density: 0.700 g/cc
- Density: 1.12 - 1.15 g/cc
- Melting Point: 260 °C
- Decomposition Temperature: >= 300 °C
- Commercial Status: Europe
- Ignition Temperature: >400°C
$ 1511/MT
- Density: 1.13 g/cc
- Moisture Absorption at Equilibrium: 2.8 %
- Moisture Absorption at Equilibrium: 8.5 %
- Tensile Strength, Yield: 85.0 MPa
- Elongation at Break: 20 %
$ 1909/MT
- Bulk Density: 0.450 - 0.800 g/cc
- Density: 1.16 g/cc
- Water Absorption: 6.5 - 7.5 %
- Moisture Absorption at Equilibrium: 1.6 - 2.0 %
- Viscosity Measurement: 130
$ 1768/MT
- Density: 1.14 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.5 %
- Linear Mold Shrinkage: 0.016 cm/cm
- Tensile Strength, Yield: 54.0 MPa
$ 1505/MT
- Density: 1.05 g/cc
- Water Absorption: 0.10 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm
- Melt Flow: 2.5 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1451/MT
- Density: 1.12 g/cc
- Water Absorption: 10.5 %
- Moisture Absorption at Equilibrium: 3.2 %
- Relative Viscosity: 3.3 cP
- Viscosity Test: 195 cm³/g
$ 1895/MT
- Density: 1.06 g/cc
- Moisture Absorption at Equilibrium: 2.1 %
- Moisture Absorption at Equilibrium: 7.3 %
- Linear Mold Shrinkage: 0.04572 cm/cm
- Melt Temperature: 270 - 300 °C
$ 2013/MT
- Density: 1.13 g/cc
- Water Absorption: 9.0 - 10 %
- Moisture Absorption at Equilibrium: 2.6 - 3.4 %
- Viscosity Test: 150 cm³/g
- Linear Mold Shrinkage: 0.0065 cm/cm
$ 1813/MT
- Density: 1.13 g/cc
- Water Absorption: 9.0 - 10 %
- Moisture Absorption at Equilibrium: 2.6 - 3.4 %
- Viscosity Test: 150 cm³/g
- Linear Mold Shrinkage: 0.0065 cm/cm
$ 1484/MT
- Density: 1.05 g/cc
- Water Absorption: 0.10 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm
- Melt Flow: 28 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2299/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 3.4 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 135 MPa @Load 36.5 kg, Time 30.0 sec
$ 1547/MT
- Density: 1.30 g/cc
- Water Absorption: 0.90 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
$ 1703/MT
- Bulk Density: 0.640 - 0.740 g/cc
- Density: 1.12 - 1.15 g/cc
- Melting Point: 220 °C
- Decomposition Temperature: >= 300 °C
- Commercial Status: Europe
- Ignition Temperature: >400°C
$ 2551/MT
- Bulk Density: 0.690 - 0.710 g/cc
- Density: 1.12 g/cc
- Water Absorption: 10.5 %
- Moisture Absorption at Equilibrium: 3.2 %
- Water Vapor Transmission: 50.0 g/m²/day
$ 1619/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.021 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
$ 1668/MT
- Density: 1.06 g/cc
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Yield: 3.7 %
- Flexural Modulus: 1.75 GPa
- Charpy Impact Unnotched: NB
$ 2262/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 3.3 cP
- Viscosity Test: 195 cm³/g
$ 1951/MT
- Density: 1.14 g/cc
- Water Absorption: 8.5 %
- Moisture Absorption at Equilibrium: 2.5 %
- Linear Mold Shrinkage: 0.016 cm/cm
- Tensile Strength, Yield: 54.0 MPa
$ 1565/MT
- Density: 1.13 g/cc
- Water Absorption: 8.0 - 9.0 %
- Moisture Absorption at Equilibrium: 2.5 - 3.1 %
- Viscosity Measurement: 150
- Linear Mold Shrinkage: 0.0085 cm/cm
$ 1593/MT
- Bulk Density: 0.850 g/cc
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.021 cm/cm
$ 1727/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage: 0.020 cm/cm
- Linear Mold Shrinkage, Flow: 0.021 cm/cm
$ 1589/MT
- Density: 1.40 g/cc
- Water Absorption: 0.80 %
- Moisture Absorption at Equilibrium: 0.20 %
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 130 MPa @Load 36.5 kg, Time 30.0 sec
$ 1603/MT
- Density: 1.13 g/cc
- Water Absorption: 9.0 - 10 %
- Moisture Absorption at Equilibrium: 2.6 - 3.4 %
- Viscosity Measurement: 145
- Linear Mold Shrinkage: 0.0055 cm/cm
$ 1521/MT
- Density: 1.13 g/cc
- Water Absorption: 9.5 %
- Moisture Absorption at Equilibrium: 2.6 %
- Relative Viscosity: 4.0 cP
- Viscosity Test: 250 cm³/g
$ 1885/MT
- Density: 1.15 g/cc
- Water Absorption: 8.0 %
- Moisture Absorption at Equilibrium: 2.8 %
- Tensile Strength, Yield: 95.0 MPa
- Elongation at Break: 50 %
$ 1794/MT
- Bulk Density: 0.650 - 0.850 g/cc
- Density: 1.27 g/cc
- Water Absorption: 0.50 %
- Moisture Absorption at Equilibrium: 0.20 %
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
$ 1605/MT
- Density: 1.05 g/cc
- Water Absorption: 0.10 %
- Moisture Absorption at Equilibrium: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm
- Melt Flow: 1.8 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2182/MT
- Density: 1.13 g/cc
- Water Absorption: 1.6 %
- Water Absorption: 9.2 %
- Moisture Absorption at Equilibrium: 2.6 %
- Viscosity Measurement: 220
$ 2044/MT
- Density: 1.09 g/cc
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Yield: 2.6 %
- Tensile Modulus: 1.79 GPa
$ 1446/MT
- Bulk Density: 0.640 - 0.740 g/cc
- Density: 1.12 - 1.15 g/cc
- Viscosity Measurement: 2.67 - 2.73
- Viscosity Measurement: 146 - 151
- Melting Point: 220 °C
Delivery Unreinforced BASF
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
bulk cargo ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.