$ 2120/MT
- Density: 1.64 g/cc
- Water Absorption: 1.0 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 2.5 %
$ 1554/MT
- Density: 1.31 g/cc
- Water Absorption at Saturation: 6.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 3.5 %
$ 2485/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.014 cm/cm
- Tensile Strength at Break: 69.0 MPa
- Elongation at Break: 3.1 %
- Flexural Strength: 102 MPa
$ 1870/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Time 86400 sec
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 6.20 GPa
$ 1748/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 8.10 GPa
$ 1738/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 95.0 MPa
- Elongation at Break: >= 3.0 %
- Tensile Modulus: 5.80 GPa
$ 1670/MT
- Density: 1.37 g/cc
- Moisture Absorption: 1.80 % @Temperature 23.0 °C
- Water Absorption at Saturation: 6.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
$ 1817/MT
- Density: 1.27 g/cc
- Moisture Absorption: 1.40 % @Temperature 23.0 °C
- Water Absorption at Saturation: 6.8 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
- Hardness, Rockwell L: 123
$ 1517/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm
- Hardness, Rockwell L: 112
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 6.0 %
$ 1608/MT
- Density: 1.31 g/cc
- Water Absorption at Saturation: 6.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 3.5 %
$ 1627/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: >= 8.0 %
- Tensile Modulus: 3.60 GPa
$ 1677/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: >= 8.0 %
- Tensile Modulus: 3.60 GPa
$ 1682/MT
- Density: 1.23 g/cc
- Water Absorption at Saturation: 8.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0085 cm/cm
- Hardness, Rockwell L: 110
- Tensile Strength at Break: 125 MPa
$ 1696/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.017 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Yield: 3.7 %
- Tensile Modulus: 1.40 GPa
$ 1615/MT
- Density: 1.29 g/cc
- Water Absorption: 1.6 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 67.0 MPa
- Tensile Strength, Yield: 57.0 MPa
$ 2478/MT
- Density: 1.13 g/cc
- Moisture Absorption: 2.35 % @Temperature 23.0 °C
- Water Absorption at Saturation: 10 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm
- Hardness, Rockwell R: 121
$ 1659/MT
- Density: 1.13 g/cc
- Moisture Absorption: 2.60 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.012 - 0.016 cm/cm
- Hardness, Rockwell R: 122
- Tensile Strength at Break: 80.0 MPa
$ 1606/MT
- Density: 1.42 g/cc
- Moisture Absorption: 1.60 % @Temperature 23.0 °C
- Water Absorption at Saturation: 6.2 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm
- Hardness, Rockwell L: 112
$ 2055/MT
- Density: 1.37 g/cc
- Moisture Absorption: 1.70 % @Temperature 23.0 °C
- Water Absorption at Saturation: 6.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Hardness, Rockwell L: 113
$ 1771/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 68.0 MPa
- Elongation at Break: 1.5 %
- Flexural Yield Strength: 101 MPa
$ 1566/MT
- Density: 2.99 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 74.0 MPa
- Elongation at Break: 0.90 %
- Flexural Strength: 102 MPa
$ 1680/MT
- Density: 1.55 g/cc
- Moisture Absorption: 0.600 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Tensile Strength at Break: 220 MPa
$ 2089/MT
- Density: 1.48 g/cc
- Water Absorption: 5.1 % @Temperature 23.0 °C, Time 86400 sec
- Moisture Absorption: 1.50 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 115 MPa
$ 1860/MT
- Density: 1.67 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 95.0 MPa
- Tensile Modulus: 11.6 GPa
- Flexural Strength: 150 MPa
$ 1552/MT
- Density: 1.14 g/cc
- Moisture Absorption: 2.60 % @Temperature 23.0 °C
- Water Absorption at Saturation: 10 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm
- Hardness, Rockwell R: 120
$ 2012/MT
- Density: 1.52 g/cc
- Water Absorption: 1.3 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 121 MPa
- Tensile Strength, Yield: 121 MPa
$ 1553/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 74.0 MPa
- Elongation at Break: 7.3 %
- Flexural Yield Strength: 95.0 MPa
$ 1450/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.019 - 0.021 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.019 - 0.021 cm/cm @Time 86400 sec
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 100 %
$ 1714/MT
- Density: 1.55 g/cc
- Water Absorption: 1.6 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 64.0 MPa
- Elongation at Break: 2.3 %
$ 1550/MT
- Density: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: >= 100 %
$ 1803/MT
- Density: 1.36 g/cc
- Moisture Absorption: 1.80 % @Temperature 23.0 °C
- Water Absorption at Saturation: 6.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Hardness, Rockwell L: 112
$ 2256/MT
- Density: 1.14 g/cc
- Moisture Absorption: 2.60 % @Temperature 23.0 °C
- Water Absorption at Saturation: 10 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm
- Hardness, Rockwell R: 120
$ 1753/MT
- Density: 1.37 g/cc
- Water Absorption at Saturation: 6.5 % @Temperature 23.0 °C
- Hardness, Rockwell L: 105
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 2.0 %
$ 1604/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Flow: 0.0034 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 110 MPa
- Tensile Strength, Yield: 117 MPa
- Elongation at Break: 3.0 %
$ 1583/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.019 - 0.021 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: >= 50.0 MPa
- Tensile Strength, Yield: 45.0 MPa
- Flexural Yield Strength: 56.0 MPa
$ 2218/MT
- Density: 2.30 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.014 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 77.0 MPa
- Elongation at Break: 1.3 %
- Flexural Strength: 103 MPa
$ 1867/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 78.0 MPa
- Elongation at Break: 5.6 %
- Elongation at Yield: 3.7 %
$ 1639/MT
- Density: 1.43 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 93.0 MPa
- Elongation at Break: 2.1 %
- Flexural Yield Strength: 136 MPa
$ 1925/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm
- Tensile Strength at Break: 95.0 MPa
- Elongation at Break: 3.2 %
- Tensile Modulus: 6.20 GPa
$ 1709/MT
- Density: 1.36 g/cc
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Yield: 2.5 %
- Tensile Modulus: 3.40 GPa
- Flexural Yield Strength: 83.0 MPa
$ 1716/MT
- Density: 1.27 g/cc
- Moisture Absorption: 1.40 % @Temperature 23.0 °C
- Water Absorption at Saturation: 6.8 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
- Hardness, Rockwell L: 123
$ 2054/MT
- Density: 1.54 g/cc
- Water Absorption: 1.0 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 64.0 MPa
- Elongation at Break: 1.9 %
$ 1723/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 3.5 %
- Tensile Modulus: 7.50 GPa
$ 1599/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 165 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 8.50 GPa
$ 2059/MT
- Density: 1.37 g/cc
- Water Absorption: 1.9 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0035 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 81.0 MPa
- Tensile Strength, Yield: 84.0 MPa
$ 1820/MT
- Density: 4.00 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Thickness 4.00 mm
- Ash: 82 % @Temperature 650 °C
- Flexural Strength: 90.0 MPa
- Flexural Modulus: 5.40 GPa
$ 2446/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.015 cm/cm @Time 86400 sec
- Tensile Strength at Break: 75.0 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 3.40 GPa
$ 1646/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0055 cm/cm
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 6.20 GPa
$ 2292/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.0090 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: >= 3.2 %
- Tensile Modulus: 6.20 GPa
$ 1975/MT
- Density: 1.54 g/cc
- Water Absorption at Saturation: 5.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 3.0 %
$ 1726/MT
- Density: 1.38 g/cc
- Moisture Absorption: 1.05 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Time 86400 sec
- Tensile Strength at Break: 82.0 MPa
- Tensile Strength at Break: 103 MPa
$ 1963/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 95.0 MPa
- Elongation at Break: 4.0 %
- Flexural Strength: 140 MPa
$ 1956/MT
- Density: 1.35 g/cc
- Water Absorption: 1.9 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0044 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 93.0 MPa
- Elongation at Break: 2.6 %
$ 1697/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 56.0 MPa
- Elongation at Break: >= 100 %
$ 2120/MT
- Density: 1.14 g/cc
- Moisture Absorption: 2.60 % @Temperature 23.0 °C
- Water Absorption at Saturation: 10 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm
- Hardness, Rockwell R: 120
$ 1492/MT
- Density: 1.66 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 63.0 MPa
- Elongation at Break: 1.5 %
$ 1688/MT
- Density: 1.18 g/cc
- Moisture Absorption: 2.20 % @Temperature 23.0 °C
- Water Absorption at Saturation: 9.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm
- Hardness, Rockwell R: 120
$ 1825/MT
- Density: 1.37 g/cc
- Water Absorption: 1.2 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Tensile Strength at Break: 147 MPa
- Elongation at Break: 3.4 %
$ 2245/MT
- Density: 1.21 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength, Yield: 105 MPa
- Elongation at Yield: 3.0 %
- Tensile Modulus: 4.90 GPa
$ 1462/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0025 cm/cm
- Tensile Strength at Break: 195 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 13.5 GPa
$ 2284/MT
- Density: 1.37 g/cc
- Moisture Absorption: 1.80 % @Temperature 23.0 °C
- Water Absorption at Saturation: 6.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
$ 1517/MT
- Density: 1.10 g/cc
- Water Absorption: 2.3 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.014 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Yield: 4.1 %
$ 1755/MT
- Density: 1.48 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 156 MPa
- Elongation at Break: 3.3 %
- Flexural Strength: 215 MPa
$ 2288/MT
- Density: 1.40 g/cc
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 6.00 GPa
- Izod Impact, Notched (ISO): 2.00 kJ/m² @Temperature -40.0 °C
$ 1492/MT
- Density: 1.55 g/cc
- Water Absorption at Saturation: 4.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0030 cm/cm
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 2.0 %
$ 1630/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm
- Tensile Strength at Break: 140 MPa
- Izod Impact, Notched (ISO): 10.0 kJ/m²
- CTE, linear, Parallel to Flow: 18.0 µm/m-°C @Temperature 23.0 - 60.0 °C
$ 1593/MT
- Density: 1.23 g/cc
- Water Absorption at Saturation: 8.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0045 - 0.0085 cm/cm
- Hardness, Rockwell L: 110
- Tensile Strength at Break: 125 MPa
$ 1453/MT
- Density: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.023 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 44.0 MPa
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Yield: 3.8 %
$ 2403/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.018 - 0.022 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 18 %
- Flexural Strength: 79.0 MPa
$ 1769/MT
- Density: 1.31 g/cc
- Water Absorption at Saturation: 6.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 3.0 %
$ 2533/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 190 MPa
- Elongation at Break: 3.0 %
- Flexural Yield Strength: 265 MPa
$ 2000/MT
- Density: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.013 cm/cm @Time 86400 sec
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 3.0 %
$ 1446/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.018 - 0.022 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: 3.5 %
- Flexural Strength: 91.0 MPa
$ 1557/MT
- Density: 1.20 g/cc
- Water Absorption at Saturation: 5.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm
- Tensile Strength, Yield: 94.0 MPa
- Elongation at Break: 8.0 %
$ 1565/MT
- Density: 1.55 g/cc
- Moisture Absorption: 0.600 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Tensile Strength at Break: 224 MPa
$ 1601/MT
- Density: 1.08 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Hardness, Rockwell R: 111
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: >= 100 %
$ 1746/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Yield: 4.0 %
- Flexural Yield Strength: 100 MPa
$ 1676/MT
- Density: 1.55 g/cc
- Moisture Absorption: 0.600 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
$ 2294/MT
- Density: 1.17 g/cc
- Water Absorption at Saturation: 6.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0095 - 0.0135 cm/cm
- Tensile Strength at Break: 75.0 MPa
- Elongation at Break: 10 %
$ 1665/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 123 MPa
- Tensile Strength, Yield: 125 MPa
- Elongation at Break: 3.0 %
$ 1640/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.014 - 0.016 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 40.0 MPa
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: 80 %
$ 1684/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Ash: 30 % @Temperature 650 °C
- Tensile Strength, Yield: 160 MPa
- Elongation at Yield: 2.0 - 3.0 %
$ 2075/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Time 86400 sec
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 6.40 GPa
$ 1598/MT
- Density: 1.42 g/cc
- Moisture Absorption: 1.60 % @Temperature 23.0 °C
- Water Absorption at Saturation: 6.2 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm
- Hardness, Rockwell L: 112
$ 1444/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 78.0 MPa
- Elongation at Break: 5.6 %
- Elongation at Yield: 3.7 %
$ 1499/MT
- Density: 1.35 g/cc
- Water Absorption: 1.9 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0044 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 93.0 MPa
- Elongation at Break: 2.6 %
$ 2436/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm
- Tensile Strength at Break: 138 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 7.90 GPa
$ 1525/MT
- Density: 1.37 g/cc
- Moisture Absorption: 1.80 % @Temperature 23.0 °C
- Water Absorption at Saturation: 6.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
$ 1868/MT
- Density: 1.35 g/cc
- Water Absorption at Saturation: 6.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 - 0.015 cm/cm
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 10 %
$ 2534/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 78.0 MPa
- Elongation at Break: 5.6 %
- Elongation at Yield: 3.7 %
$ 2404/MT
- Density: 1.16 g/cc
- Moisture Absorption: 2.20 % @Temperature 23.0 °C
- Water Absorption at Saturation: 9.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm
- Hardness, Rockwell R: 120
$ 1575/MT
- Density: 1.34 g/cc
- Moisture Absorption: 1.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Hardness, Rockwell L: 110
- Tensile Strength at Break: 85.0 MPa
$ 1622/MT
- Density: 1.55 g/cc
- Moisture Absorption: 0.600 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
$ 1841/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 57.0 MPa
- Tensile Strength, Yield: 69.0 MPa
- Elongation at Yield: 3.5 %
$ 1585/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm @Thickness 3.00 mm
- Tensile Strength, Yield: 131 MPa
- Elongation at Break: 3.7 %
- Tensile Modulus: 5.70 GPa
$ 1643/MT
- Density: 1.55 g/cc
- Moisture Absorption: 0.600 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
$ 1504/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.020 cm/cm
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: >= 100 %
- Elongation at Yield: 3.8 %
$ 1979/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.020 cm/cm
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: >= 100 %
- Elongation at Yield: 3.8 %
$ 1795/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.020 cm/cm
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: >= 100 %
- Elongation at Yield: 3.8 %
$ 2233/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.020 cm/cm
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: >= 100 %
- Elongation at Yield: 3.8 %
$ 1725/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.020 cm/cm
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: >= 100 %
- Elongation at Yield: 3.8 %
$ 1982/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.020 cm/cm
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: >= 100 %
- Elongation at Yield: 3.8 %
$ 1616/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.020 cm/cm
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: >= 100 %
- Elongation at Yield: 3.8 %
$ 1589/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.020 cm/cm
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: >= 100 %
- Elongation at Yield: 3.8 %
$ 1591/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.020 cm/cm
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: >= 100 %
- Elongation at Yield: 3.8 %
$ 1786/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 155 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 195 MPa
$ 1817/MT
- Density: 1.40 g/cc
- Water Absorption: 2.2 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength at Break: 44.0 MPa
- Elongation at Break: 6.7 %
- Elongation at Yield: 3.9 %
$ 1528/MT
- Density: 1.40 g/cc
- Water Absorption: 2.2 % @Temperature 23.0 °C, Time 86400 sec
- Tensile Strength at Break: 44.0 MPa
- Elongation at Break: 6.7 %
- Elongation at Yield: 3.9 %
$ 1519/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 93.0 MPa
- Elongation at Break: 2.5 %
- Flexural Yield Strength: 142 MPa
$ 2571/MT
- Density: 1.20 g/cc
- Moisture Absorption: 1.40 % @Temperature 23.0 °C
- Water Absorption at Saturation: 6.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm
- Hardness, H358/30: 101 MPa
$ 1730/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 170 MPa
- Elongation at Break: 2.5 %
- Flexural Strength: 240 MPa
$ 1549/MT
- Density: 1.21 g/cc
- Water Absorption at Saturation: 5.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 10 %
$ 1465/MT
- Density: 1.50 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 71.0 MPa
- Elongation at Break: 2.7 %
Delivery Nylon 6 Eurostar Engineering Plastics
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
ships for sale in greece. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.