$ 2056/MT
- Density: 1.35 g/cc
- Water Absorption at Saturation: 6.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 - 0.015 cm/cm
- Hardness, Rockwell R: 120
- Tensile Strength at Break: 80.0 MPa
$ 1807/MT
- Density: 1.45 g/cc
- Moisture Absorption: 0.0900 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0090 - 0.013 cm/cm
- Hardness, Rockwell L: 92
- Tensile Strength at Break: 75.0 MPa
$ 1774/MT
- Density: 1.29 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 4.30 GPa
$ 2057/MT
- Density: 1.46 g/cc
- Moisture Absorption: 0.900 % @Temperature 23.0 °C
- Water Absorption at Saturation: 3.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0025 cm/cm
- Hardness, Rockwell L: 114
$ 1518/MT
- Density: 1.41 g/cc
- Moisture Absorption: 1.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0030 cm/cm
- Hardness, Rockwell L: 115
$ 1876/MT
- Density: 1.58 g/cc
- Water Absorption at Saturation: 4.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm
- Hardness, Rockwell L: 108
- Tensile Strength at Break: 165 MPa
$ 1498/MT
- Density: 1.56 g/cc
- Moisture Absorption: 0.600 % @Temperature 23.0 °C
- Water Absorption at Saturation: 5.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 118
$ 1581/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 4.80 GPa
$ 1604/MT
- Density: 1.58 g/cc
- Water Absorption at Saturation: 4.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm
- Hardness, Rockwell L: 108
- Tensile Strength at Break: 165 MPa
$ 2164/MT
- Density: 1.07 g/cc
- Moisture Absorption: 1.50 % @Temperature 23.0 °C
- Water Absorption at Saturation: 5.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm
- Hardness, Rockwell R: 112
$ 1612/MT
- Density: 1.56 g/cc
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 2.0 %
$ 2235/MT
- Density: 1.24 g/cc
- Water Absorption at Saturation: 5.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 3.0 %
$ 1652/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 165 MPa
- Elongation at Break: 2.0 %
- Flexural Strength: 219 MPa
$ 2069/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.020 cm/cm
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 20 %
- Elongation at Yield: 4.5 %
$ 2370/MT
- Density: 1.55 g/cc
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 2.0 %
$ 1557/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 171 MPa
- Elongation at Break: 3.1 %
- Flexural Strength: 247 MPa
$ 1564/MT
- Density: 1.37 g/cc
- Moisture Absorption: 1.20 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Hardness, Rockwell L: 113
$ 1836/MT
- Density: 1.37 g/cc
- Moisture Absorption: 1.30 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Hardness, Rockwell L: 113
$ 1489/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 133 MPa
- Elongation at Break: 2.0 %
- Flexural Strength: 188 MPa
$ 2443/MT
- Density: 1.14 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Water Absorption at Saturation: 8.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.016 - 0.020 cm/cm
- Hardness, Rockwell L: 118
$ 1529/MT
- Density: 1.14 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Water Absorption at Saturation: 8.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.016 - 0.020 cm/cm
- Tensile Strength, Yield: 85.0 MPa
$ 2348/MT
- Density: 1.44 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 165 MPa
- Elongation at Break: 2.7 %
- Flexural Strength: 210 MPa
$ 1703/MT
- Density: 1.23 g/cc
- Water Absorption at Saturation: 7.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm
- Tensile Strength at Break: 125 MPa
- Elongation at Break: 3.0 %
$ 1946/MT
- Density: 1.41 g/cc
- Moisture Absorption: 1.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0030 cm/cm
- Hardness, Rockwell L: 115
$ 1692/MT
- Density: 1.56 g/cc
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 2.0 %
$ 1480/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.028 - 0.034 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 71.0 MPa
- Elongation at Break: 5.0 %
- Flexural Strength: 94.0 MPa
$ 1976/MT
- Density: 1.37 g/cc
- Moisture Absorption: 1.20 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Hardness, Rockwell L: 113
$ 2394/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 6.20 GPa
$ 1610/MT
- Density: 1.19 g/cc
- Tensile Strength at Break: 135 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 8.00 GPa
- Flexural Yield Strength: 230 MPa
$ 2219/MT
- Density: 1.27 g/cc
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: >= 0.00080 cm/cm
- Hardness, Rockwell L: 108
- Tensile Strength at Break: 250 MPa
$ 1764/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0040 cm/cm @Thickness 4.00 mm
- Ash: 33 % @Temperature 650 °C
- Tensile Strength, Yield: 115 MPa
- Elongation at Break: 4.0 - 6.0 %
$ 2396/MT
- Density: 1.07 g/cc
- Moisture Absorption: 1.50 % @Temperature 23.0 °C
- Water Absorption at Saturation: 5.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.019 - 0.021 cm/cm
- Hardness, Rockwell R: 112
$ 1887/MT
- Density: 1.08 g/cc
- Moisture Absorption: 1.60 % @Temperature 23.0 °C
- Water Absorption at Saturation: 6.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.013 - 0.020 cm/cm
- Hardness, Rockwell R: 108
$ 1655/MT
- Density: 1.14 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Water Absorption at Saturation: 8.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.016 - 0.020 cm/cm
- Hardness, Rockwell L: 118
$ 1614/MT
- Density: 1.37 g/cc
- Moisture Absorption: 1.20 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Melt Flow: 25 - 50 g/10 min @Load 5.00 kg, Temperature 275 °C
$ 1476/MT
- Density: 1.21 g/cc
- Linear Mold Shrinkage, Flow: 0.024 - 0.030 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 69.0 MPa
- Elongation at Break: 8.0 %
- Flexural Strength: 89.0 MPa
$ 1859/MT
- Density: 1.47 g/cc
- Water Absorption: 1.1 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 131 MPa
- Elongation at Break: 2.6 %
$ 2085/MT
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 208 MPa
- Elongation at Break: 1.8 %
- Flexural Strength: 275 MPa
- Flexural Modulus: 16.0 GPa
$ 1770/MT
- Density: 1.41 g/cc
- Moisture Absorption: 1.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0030 cm/cm
- Hardness, Rockwell L: 114
$ 2484/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 5.80 GPa
$ 1949/MT
- Density: 1.24 g/cc
- Water Absorption at Saturation: 5.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0015 cm/cm
- Tensile Strength at Break: 190 MPa
- Elongation at Break: 2.0 %
$ 1632/MT
- Density: 1.09 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm @Time 86400 sec
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 70 %
- Tensile Modulus: 2.20 GPa
$ 1699/MT
- Density: 1.56 g/cc
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm
- Tensile Strength at Break: 85.0 MPa
- Elongation at Break: 2.5 %
$ 1579/MT
- Density: 1.09 g/cc
- Water Absorption at Saturation: 5.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 60.0 MPa
$ 2075/MT
- Density: 1.36 g/cc
- Moisture Absorption: 1.30 % @Temperature 23.0 °C
- Water Absorption at Saturation: 6.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell L: 108
$ 1527/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 84.0 MPa
- Elongation at Break: 2.2 %
- Tensile Modulus: 5.70 GPa
$ 1744/MT
- Density: 1.58 g/cc
- Moisture Absorption: 0.700 % @Temperature 23.0 °C
- Water Absorption at Saturation: 2.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0025 cm/cm
- Hardness, Rockwell L: 114
$ 1647/MT
- Density: 1.16 g/cc
- Water Absorption at Saturation: 6.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.016 - 0.020 cm/cm
- Hardness, Rockwell R: 117
- Elongation at Break: >= 30 %
$ 2133/MT
- Density: 1.43 g/cc
- Moisture Absorption: 1.10 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm
- Hardness, Rockwell L: 108
$ 1831/MT
- Density: 1.59 g/cc
- Water Absorption at Saturation: 4.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0035 cm/cm
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 2.0 %
$ 1841/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 10 %
- Tensile Modulus: 5.50 GPa
$ 2596/MT
- Density: 1.37 g/cc
- Moisture Absorption: 1.20 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Hardness, Rockwell L: 114
$ 1514/MT
- Density: 1.48 g/cc
- Water Absorption at Saturation: 5.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 2.5 %
$ 1455/MT
- Density: 1.37 g/cc
- Moisture Absorption: 1.30 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Hardness, Rockwell L: 113
$ 1666/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 4.00 mm
- Ash: 14 %
- Tensile Strength, Yield: 90.0 MPa
- Elongation at Break: 4.0 %
$ 1501/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 170 MPa
- Elongation at Break: 2.3 %
- Flexural Strength: 221 MPa
$ 1737/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 4.00 mm
- Tensile Strength at Break: 175 MPa
- Elongation at Break: 2.7 %
- Flexural Strength: 175 MPa
$ 1545/MT
- Density: 1.16 g/cc
- Moisture Absorption: 1.30 % @Temperature 23.0 °C
- Water Absorption at Saturation: 6.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm
- Hardness, Rockwell L: 121
$ 1490/MT
- Density: 1.37 g/cc
- Water Absorption at Saturation: 5.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 9.0 %
$ 2125/MT
- Density: 1.60 g/cc
- Tensile Strength at Break: 76.0 MPa
- Elongation at Break: 1.6 %
- Tensile Modulus: 8.70 GPa
- Flexural Strength: 118 MPa
$ 2181/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 2.8 %
- Flexural Strength: 200 MPa
$ 2121/MT
- Density: 1.58 g/cc
- Moisture Absorption: 0.700 % @Temperature 23.0 °C
- Water Absorption at Saturation: 2.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0025 cm/cm
- Hardness, Rockwell L: 114
$ 1741/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 4.00 mm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.011 cm/cm
- Tensile Strength at Break: 155 MPa
- Elongation at Break: 2.1 %
$ 1896/MT
- Density: 1.14 g/cc
- Moisture Absorption: 2.00 % @Temperature 23.0 °C
- Water Absorption at Saturation: 8.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.016 - 0.020 cm/cm
- Tensile Strength, Yield: 85.0 MPa
$ 1732/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 5.80 GPa
$ 1628/MT
- Density: 1.45 g/cc
- Water Absorption at Saturation: 0.50 % @Temperature 23.0 °C
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: 10 %
- Tensile Modulus: 4.80 GPa
$ 1460/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 161 MPa
- Elongation at Break: 2.5 %
- Flexural Strength: 215 MPa
$ 1488/MT
- Density: 1.60 g/cc
- Moisture Absorption: 0.600 % @Temperature 23.0 °C
- Water Absorption at Saturation: 5.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm
- Hardness, Rockwell R: 118
$ 1654/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 200 MPa
- Elongation at Break: 1.5 %
- Flexural Strength: 245 MPa
$ 2149/MT
- Density: 1.37 g/cc
- Moisture Absorption: 1.20 % @Temperature 23.0 °C
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Hardness, Rockwell L: 113
$ 1456/MT
- Density: 1.26 g/cc
- Water Absorption at Saturation: 5.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Hardness, Rockwell L: 112
- Tensile Strength at Break: 130 MPa
$ 1830/MT
- Density: 1.57 g/cc
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 210 MPa
- Elongation at Break: 2.4 %
$ 1644/MT
- Density: 1.39 g/cc
- Water Absorption: 0.20 % @Temperature 23.0 °C, Time 86400 sec
- Moisture Absorption: 2.64 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.015 - 0.025 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.012 cm/cm @Time 86400 sec
$ 2494/MT
- Density: 1.26 g/cc
- Water Absorption at Saturation: 5.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Hardness, Rockwell L: 112
- Tensile Strength at Break: 130 MPa
$ 1672/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.016 cm/cm
- Tensile Strength at Break: 80.0 MPa
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: 4.0 %
$ 1854/MT
- Density: 1.33 g/cc
- Moisture Absorption: 1.20 % @Temperature 23.0 °C
- Water Absorption at Saturation: 6.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Hardness, Rockwell L: 108
$ 1605/MT
- Density: 1.19 g/cc
- Water Absorption at Saturation: 5.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Hardness, Rockwell L: 105
- Tensile Strength at Break: 170 MPa
$ 1589/MT
- Density: 1.57 g/cc
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 4.00 mm
- Tensile Strength, Yield: 210 MPa
- Elongation at Break: 2.4 %
$ 1914/MT
- Density: 1.23 g/cc
- Water Absorption at Saturation: 7.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm
- Tensile Strength at Break: 125 MPa
- Elongation at Break: 3.0 %
$ 1902/MT
- Density: 1.14 g/cc
- Tensile Strength at Break: 88.0 MPa
- Elongation at Break: >= 5.0 %
- Flexural Strength: 130 MPa
- Flexural Modulus: 3.40 GPa
Delivery Nylon 66 Eurostar Engineering Plastics
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
commercial ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.