Celanese FORTRON 1130L4 PPS, 30% Glass Reinforced price 1529 per MT

Physical Properties
Specific Gravity
1.60 g/cc
Density
0.000913 g/cc
Density
1.58 g/cc
Water Absorption
0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation
0.0200 %
Linear Mold Shrinkage, Flow
0.00300 - 0.00500 cm/cm
Linear Mold Shrinkage, Flow
0.00300 - 0.00500 cm/cm
Linear Mold Shrinkage, Transverse
0.00600 - 0.00900 cm/cm
Linear Mold Shrinkage, Transverse
0.00600 - 0.00900 cm/cm

Mechanical Properties
Hardness, Rockwell M
100
Hardness, Rockwell M
100
Tensile Strength at Break
170 MPa
Tensile Strength at Break
172 MPa
Elongation at Break
1.90 %
Elongation at Break
1.90 %
Tensile Modulus
12.0 GPa
Flexural Strength
255 MPa
Flexural Strength
260 MPa
Flexural Modulus
11.0 GPa
Flexural Modulus
11.0 GPa
Izod Impact, Notched
0.961 J/cm
Izod Impact, Unnotched
5.34 J/cm
Izod Impact, Notched (ISO)
9.00 kJ/m² @Temperature -30.0 °C
Izod Impact, Notched (ISO)
30.0 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
3.40 J/cm²
Charpy Impact Unnotched
3.40 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
0.900 J/cm²
Charpy Impact, Notched
0.900 J/cm² @Temperature -30.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
29.0 µm/m-°C
CTE, linear, Transverse to Flow
52.0 µm/m-°C
Deflection Temperature at 0.46 MPa (66 psi)
280 °C
Deflection Temperature at 1.8 MPa (264 psi)
255 °C
Deflection Temperature at 1.8 MPa (264 psi)
266 °C
Glass Transition Temp, Tg
90.0 °C
Flammability, UL94
V-0 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 0.800 mm

Electrical Properties
Volume Resistivity
>= 1.00e+15 ohm-cm
Volume Resistivity
1.00e+16 ohm-cm
Surface Resistance
>= 1.00e+15 ohm
Dissipation Factor
0.00100 @Frequency 1000 Hz
Dissipation Factor
0.00100 @Frequency 1.00e+6 Hz
Arc Resistance
127 sec
Comparative Tracking Index
150 V

Processing Properties
Processing Temperature
140 - 160 °C
Processing Temperature
330 - 340 °C
Feed Temperature
60.0 - 80.0 °C
Middle Barrel Temperature
20.0 - 30.0 °C
Zone 1
290 - 300 °C
Zone 2
310 - 320 °C
Zone 3
330 - 340 °C
Zone 4
330 - 340 °C
Die Temperature
310 - 330 °C
Melt Temperature
310 - 340 °C
Melt Temperature
330 - 340 °C
Mold Temperature
135 - 160 °C
Drying Temperature
130 - 140 °C
Dry Time
3.00 - 4.00 hour
Moisture Content
<= 0.0200 %
Injection Pressure
50.0 - 100 MPa
Hold Pressure
30.0 - 70.0 MPa
Back Pressure
<= 3.00 MPa
Screw Speed
50.0 rpm @Diameter 55.0 mm
Screw Speed
75.0 rpm @Diameter 40.0 mm
Screw Speed
120 rpm @Diameter 25.0 mm

Descriptive Properties
Injection molding
Yes
Injection Speed
fast

Alternative products

Celanese FORTRON 1130L4 PPS, 30% Glass Reinforced (Unverified Data**) accurate 85%

$ 1916/MT

Specific Gravity: 1.58 g/cc
Specific Gravity: 1.60 g/cc
Density: 1.58 g/cc
Density: 1.58 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 4184L6 PPS, 53% Mineral / Glass Reinforced accurate 61%

$ 1796/MT

Specific Gravity: 1.80 g/cc
Density: 0.00104 g/cc
Density: 1.80 g/cc
Water Absorption: 0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

SABIC Innovative Plastics Valox® ENH8560 PBT+PET (Europe-Africa-Middle East) accurate 56%

$ 2193/MT

Specific Gravity: 1.58 g/cc
Density: 1.58 g/cc
Filler Content: 30 %
Moisture Absorption: 0.0500 %
Water Absorption at Saturation: 0.30 %

Celanese FORTRON 1140L7 PPS, 40% Glass Reinforced accurate 59%

$ 1622/MT

Specific Gravity: 1.64 g/cc
Density: 0.000948 g/cc
Density: 1.65 g/cc
Water Absorption: 0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON 1131L4 ITT PPS, 30% Glass Reinforced accurate 59%

$ 1514/MT

Specific Gravity: 1.40 g/cc
Density: 0.000809 g/cc
Density: 1.56 g/cc
Water Absorption: 0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON 1140L6 PPS, 40% Glass Reinforced accurate 56%

$ 1966/MT

Specific Gravity: 1.60 g/cc
Density: 0.000926 g/cc
Density: 1.65 g/cc
Water Absorption: 0.0200 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON ICE 716A PPS, 65% Mineral / Glass Reinforced accurate 59%

$ 1657/MT

Specific Gravity: 2.00 g/cc
Density: 0.00116 g/cc
Density: 1.95 g/cc
Water Absorption: 0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON 4184L6 PPS, 53% Mineral / Glass Reinforced (Unverified Data**) accurate 56%

$ 1475/MT

Specific Gravity: 1.80 g/cc
Specific Gravity: 1.80 g/cc
Density: 1.80 g/cc
Density: 1.80 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 1140L4 PPS, 40% Glass Reinforced accurate 59%

$ 2481/MT

Specific Gravity: 1.60 g/cc
Density: 0.000948 g/cc
Density: 1.64 g/cc
Density: 1.65 g/cc
Water Absorption: 0.0200 % @Temperature 22.8 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng vessels for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Celanese FORTRON 1130L4 PPS, 30% Glass Reinforced

Seller from Atlanta – 2021-04-20:

Seller from Atlanta work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1529 per MT