Celanese FORTRON 4184L6 PPS, 53% Mineral / Glass Reinforced price 1796 per MT

Physical Properties
Specific Gravity
1.80 g/cc
Density
0.00104 g/cc
Density
1.80 g/cc
Water Absorption
0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation
0.0200 %
Linear Mold Shrinkage, Flow
0.00100 - 0.00300 cm/cm
Linear Mold Shrinkage, Flow
0.00300 - 0.00600 cm/cm
Linear Mold Shrinkage, Transverse
0.00400 - 0.00600 cm/cm
Linear Mold Shrinkage, Transverse
0.00400 - 0.00700 cm/cm

Mechanical Properties
Hardness, Rockwell M
100
Hardness, Rockwell M
100
Tensile Strength at Break
165 MPa
Tensile Strength at Break
165 MPa
Elongation at Break
1.40 %
Elongation at Break
1.50 %
Tensile Modulus
16.6 GPa
Flexural Strength
207 MPa
Flexural Strength
250 MPa
Flexural Modulus
15.9 GPa
Flexural Modulus
16.2 GPa
Izod Impact, Notched
0.747 J/cm
Izod Impact, Unnotched
3.74 J/cm
Izod Impact, Notched (ISO)
7.00 kJ/m² @Temperature -30.0 °C
Izod Impact, Notched (ISO)
27.0 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
2.90 J/cm²
Charpy Impact Unnotched
2.90 J/cm² @Temperature -30.0 °C
Charpy Impact, Notched
0.700 J/cm²
Charpy Impact, Notched
0.700 J/cm² @Temperature -30.0 °C

Thermal Properties
CTE, linear, Parallel to Flow
24.0 µm/m-°C
CTE, linear, Transverse to Flow
32.0 µm/m-°C
Specific Heat Capacity
1.50 J/g-°C
Melting Point
280 °C
Deflection Temperature at 0.46 MPa (66 psi)
280 °C
Deflection Temperature at 1.8 MPa (264 psi)
265 °C
Deflection Temperature at 1.8 MPa (264 psi)
270 °C
Deflection Temperature at 8.0 MPa
215 °C
Glass Transition Temp, Tg
90.0 °C
Flammability, UL94
V-0 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 0.750 mm

Electrical Properties
Volume Resistivity
>= 1.00e+15 ohm-cm
Volume Resistivity
1.00e+16 ohm-cm
Surface Resistance
>= 1.00e+15 ohm
Dielectric Constant
3.80 @Frequency 1000 Hz
Dielectric Constant
3.80 @Frequency 1.00e+6 Hz
Dielectric Constant
4.70 @Frequency 1.00e+6 Hz
Dielectric Strength
27.0 kV/mm
Dissipation Factor
0.000800 @Frequency 1.00e+6 Hz
Dissipation Factor
0.00100 @Frequency 1000 Hz
Dissipation Factor
0.00200 @Frequency 1.00e+6 Hz
Arc Resistance
156 sec
Comparative Tracking Index
150 V

Processing Properties
Processing Temperature
140 - 160 °C
Processing Temperature
330 - 340 °C
Feed Temperature
60.0 - 80.0 °C
Middle Barrel Temperature
20.0 - 30.0 °C
Zone 1
290 - 300 °C
Zone 2
310 - 320 °C
Zone 3
330 - 340 °C
Zone 4
330 - 340 °C
Die Temperature
310 - 330 °C
Melt Temperature
310 - 340 °C
Melt Temperature
330 - 340 °C
Mold Temperature
135 - 160 °C
Drying Temperature
130 - 140 °C
Dry Time
3.00 - 4.00 hour
Moisture Content
<= 0.0200 %

Alternative products

Celanese FORTRON ICE 716A PPS, 65% Mineral / Glass Reinforced (Unverified Data**) accurate 63%

$ 1562/MT

Specific Gravity: 1.99 g/cc
Specific Gravity: 2.00 g/cc
Density: 1.95 g/cc
Density: 2.00 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 1140L6 PPS, 40% Glass Reinforced accurate 67%

$ 1966/MT

Specific Gravity: 1.60 g/cc
Density: 0.000926 g/cc
Density: 1.65 g/cc
Water Absorption: 0.0200 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON ICE 506L PPS, 40% Glass Reinforced accurate 65%

$ 1458/MT

Specific Gravity: 1.60 g/cc
Density: 0.000926 g/cc
Density: 1.65 g/cc
Water Absorption: 0.0200 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON ICE 716A PPS, 65% Mineral / Glass Reinforced accurate 69%

$ 1657/MT

Specific Gravity: 2.00 g/cc
Density: 0.00116 g/cc
Density: 1.95 g/cc
Water Absorption: 0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON ICE 714A PPS, 65% Mineral / Glass Reinforced accurate 67%

$ 1563/MT

Specific Gravity: 2.00 g/cc
Density: 0.00115 g/cc
Density: 1.95 g/cc
Water Absorption: 0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON 4184L6 PPS, 53% Mineral / Glass Reinforced (Unverified Data**) accurate 90%

$ 1475/MT

Specific Gravity: 1.80 g/cc
Specific Gravity: 1.80 g/cc
Density: 1.80 g/cc
Density: 1.80 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 4184L4 PPS, 53% Mineral / Glass Reinforced (Unverified Data**) accurate 85%

$ 1910/MT

Specific Gravity: 1.80 g/cc
Specific Gravity: 1.80 g/cc
Density: 1.80 g/cc
Density: 1.80 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 1140L4 PPS, 40% Glass Reinforced (Unverified Data**) accurate 63%

$ 1642/MT

Specific Gravity: 1.60 g/cc
Specific Gravity: 1.66 g/cc
Density: 1.64 g/cc
Density: 1.64 g/cc
Density: 1.65 g/cc

Celanese FORTRON 1140L4 PPS, 40% Glass Reinforced accurate 69%

$ 2481/MT

Specific Gravity: 1.60 g/cc
Density: 0.000948 g/cc
Density: 1.64 g/cc
Density: 1.65 g/cc
Water Absorption: 0.0200 % @Temperature 22.8 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg vessel for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Celanese FORTRON 4184L6 PPS, 53% Mineral / Glass Reinforced

Seller from Lahore – 2021-08-15:

Seller from Lahore work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2281 per MT

Seller from Hyderabad – 2021-05-22:

Seller from Hyderabad work with company: Solvay, SABIC Innovative Plastics (GE Plastics), LG Chemical, ALIMEX GmbH

Price: $1796 per MT

Seller from Melbourne – 2021-07-16:

Seller from Melbourne work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2364 per MT