Celanese FORTRON 1140L7 PPS, 40% Glass Reinforced price 1622 per MT

Physical Properties
Specific Gravity
1.64 g/cc
Density
0.000948 g/cc
Density
1.65 g/cc
Water Absorption
0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation
0.0200 %
Linear Mold Shrinkage, Flow
0.00200 cm/cm
Linear Mold Shrinkage, Flow
0.00100 - 0.00300 cm/cm
Linear Mold Shrinkage, Transverse
0.00500 cm/cm
Linear Mold Shrinkage, Transverse
0.00500 - 0.00700 cm/cm

Mechanical Properties
Hardness, Rockwell M
100
Hardness, Rockwell M
103
Tensile Strength at Break
145 MPa
Tensile Strength at Break
170 MPa
Elongation at Break
1.20 %
Elongation at Break
1.60 %
Tensile Modulus
14.5 GPa
Flexural Strength
207 MPa
Flexural Strength
260 MPa
Flexural Modulus
14.5 GPa
Flexural Modulus
14.5 GPa
Izod Impact, Notched
0.747 J/cm
Izod Impact, Unnotched
3.68 J/cm
Izod Impact, Notched (ISO)
8.00 kJ/m² @Temperature -30.0 °C

Thermal Properties
Melting Point
280 °C
Deflection Temperature at 0.46 MPa (66 psi)
280 °C
Deflection Temperature at 1.8 MPa (264 psi)
265 °C
Deflection Temperature at 1.8 MPa (264 psi)
270 °C
Deflection Temperature at 8.0 MPa
200 °C
Glass Transition Temp, Tg
90.0 °C
Flammability, UL94
V-0 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 0.380 mm

Electrical Properties
Volume Resistivity
>= 1.00e+15 ohm-cm
Surface Resistance
>= 1.00e+15 ohm
Dielectric Constant
3.70 @Frequency 1000 Hz
Dielectric Constant
3.70 @Frequency 1.00e+6 Hz
Dielectric Strength
26.0 kV/mm
Dissipation Factor
0.00100 @Frequency 1000 Hz
Dissipation Factor
0.00100 @Frequency 1.00e+6 Hz
Arc Resistance
134 sec
Comparative Tracking Index
125 V
Comparative Tracking Index
150 V

Processing Properties
Processing Temperature
140 - 160 °C
Processing Temperature
330 - 340 °C
Feed Temperature
60.0 - 80.0 °C
Middle Barrel Temperature
20.0 - 30.0 °C
Zone 1
290 - 300 °C
Zone 2
310 - 320 °C
Zone 3
330 - 340 °C
Zone 4
330 - 340 °C
Die Temperature
310 - 330 °C
Melt Temperature
310 - 340 °C
Melt Temperature
330 - 340 °C
Mold Temperature
135 - 160 °C
Drying Temperature
130 - 140 °C
Dry Time
3.00 - 4.00 hour
Moisture Content
<= 0.0200 %
Injection Pressure
50.0 - 100 MPa
Hold Pressure
30.0 - 70.0 MPa
Back Pressure
<= 3.00 MPa
Screw Speed
50.0 rpm @Diameter 55.0 mm
Screw Speed
75.0 rpm @Diameter 40.0 mm
Screw Speed
120 rpm @Diameter 25.0 mm

Descriptive Properties
Injection molding
Yes
Injection Speed
fast

Alternative products

Celanese FORTRON 1342L4 PPS, 40% Specialty accurate 58%

$ 1725/MT

Specific Gravity: 1.70 g/cc
Density: 1.69 g/cc
Water Absorption: 0.0200 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %
Linear Mold Shrinkage, Flow: 0.00200 cm/cm

Celanese FORTRON 1131L4 ITT PPS, 30% Glass Reinforced accurate 58%

$ 1514/MT

Specific Gravity: 1.40 g/cc
Density: 0.000809 g/cc
Density: 1.56 g/cc
Water Absorption: 0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON 1140L6 PPS, 40% Glass Reinforced accurate 60%

$ 1966/MT

Specific Gravity: 1.60 g/cc
Density: 0.000926 g/cc
Density: 1.65 g/cc
Water Absorption: 0.0200 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON ICE 506L PPS, 40% Glass Reinforced accurate 58%

$ 1458/MT

Specific Gravity: 1.60 g/cc
Density: 0.000926 g/cc
Density: 1.65 g/cc
Water Absorption: 0.0200 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON 1140L6 PPS, 40% Glass Reinforced (Unverified Data**) accurate 56%

$ 1551/MT

Specific Gravity: 1.60 g/cc
Specific Gravity: 1.61 g/cc
Density: 1.60 g/cc
Density: 1.65 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 1140L7 PPS, 40% Glass Reinforced (Unverified Data**) accurate 90%

$ 2447/MT

Specific Gravity: 1.64 g/cc
Specific Gravity: 1.66 g/cc
Density: 1.64 g/cc
Density: 1.65 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 1130L4 PPS, 30% Glass Reinforced accurate 56%

$ 1529/MT

Specific Gravity: 1.60 g/cc
Density: 0.000913 g/cc
Density: 1.58 g/cc
Water Absorption: 0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON 1140L4 PPS, 40% Glass Reinforced (Unverified Data**) accurate 56%

$ 1642/MT

Specific Gravity: 1.60 g/cc
Specific Gravity: 1.66 g/cc
Density: 1.64 g/cc
Density: 1.64 g/cc
Density: 1.65 g/cc

Celanese FORTRON 1140L4 PPS, 40% Glass Reinforced accurate 60%

$ 2481/MT

Specific Gravity: 1.60 g/cc
Density: 0.000948 g/cc
Density: 1.64 g/cc
Density: 1.65 g/cc
Water Absorption: 0.0200 % @Temperature 22.8 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale europe. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for Celanese FORTRON 1140L7 PPS, 40% Glass Reinforced

Seller from Chicago – 2021-08-12:

Seller from Chicago work with company: Celanese Corporation, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1622 per MT

Seller from Chennai – 2021-03-30:

Seller from Chennai work with company: Solvay, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2194 per MT

Seller from Luanda – 2021-07-11:

Seller from Luanda work with company: Celanese Corporation, SABIC Innovative Plastics (GE Plastics), BASF, ALIMEX GmbH

Price: $1978 per MT

Seller from Miami – 2021-07-22:

Seller from Miami work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1694 per MT