Celanese FORTRON 1342L4 PPS, 40% Specialty price 1725 per MT

Physical Properties
Specific Gravity
1.70 g/cc
Density
1.69 g/cc
Water Absorption
0.0200 % @Temperature 22.8 °C
Water Absorption at Saturation
0.0200 %
Linear Mold Shrinkage, Flow
0.00200 cm/cm
Linear Mold Shrinkage, Flow
0.00200 - 0.00300 cm/cm
Linear Mold Shrinkage, Transverse
0.00500 cm/cm
Linear Mold Shrinkage, Transverse
0.00500 - 0.00700 cm/cm

Mechanical Properties
Tensile Strength at Break
152 MPa
Tensile Strength at Break
165 MPa
Elongation at Break
1.60 %
Elongation at Break
2.00 %
Tensile Modulus
14.4 GPa
Flexural Strength
231 MPa
Flexural Strength
245 MPa
Flexural Modulus
13.1 GPa
Flexural Modulus
13.7 GPa
Izod Impact, Unnotched
0.854 J/cm
Izod Impact, Notched (ISO)
8.50 kJ/m² @Temperature -30.0 °C
Charpy Impact Unnotched
4.40 J/cm²
Charpy Impact, Notched
0.850 J/cm²
Charpy Impact, Notched
0.850 J/cm² @Temperature -30.0 °C
Coefficient of Friction, Dynamic
0.160
Coefficient of Friction, Dynamic
0.210
Coefficient of Friction, Static
0.200
Coefficient of Friction, Static
0.200
Coefficient of Friction, Static
0.270
K (wear) Factor
334 x 10 mm³/N-M
K (wear) Factor
651 x 10 mm³/N-M
K (wear) Factor
1660 x 10 mm³/N-M

Thermal Properties
CTE, linear, Parallel to Flow
22.0 µm/m-°C
CTE, linear, Transverse to Flow
40.0 µm/m-°C
Melting Point
280 °C
Deflection Temperature at 1.8 MPa (264 psi)
268 °C
Deflection Temperature at 1.8 MPa (264 psi)
270 °C
Deflection Temperature at 8.0 MPa
215 °C
Glass Transition Temp, Tg
90.0 °C
Flammability, UL94
V-0 @Thickness 1.50 mm
Flammability, UL94
V-0 @Thickness 0.750 mm

Processing Properties
Processing Temperature
140 - 160 °C
Processing Temperature
330 - 340 °C
Feed Temperature
60.0 - 80.0 °C
Middle Barrel Temperature
20.0 - 30.0 °C
Zone 1
290 - 300 °C
Zone 2
310 - 320 °C
Zone 3
330 - 340 °C
Zone 4
330 - 340 °C
Die Temperature
310 - 330 °C
Melt Temperature
330 - 340 °C
Drying Temperature
130 - 140 °C
Dry Time
3.00 - 4.00 hour
Moisture Content
<= 0.0200 %
Injection Pressure
50.0 - 100 MPa
Hold Pressure
30.0 - 70.0 MPa
Back Pressure
<= 3.00 MPa
Screw Speed
50.0 rpm @Diameter 55.0 mm
Screw Speed
75.0 rpm @Diameter 40.0 mm
Screw Speed
120 rpm @Diameter 25.0 mm

Descriptive Properties
Injection molding
Yes
Injection Speed
fast

Alternative products

Celanese FORTRON 4184L6 PPS, 53% Mineral / Glass Reinforced accurate 46%

$ 1796/MT

Specific Gravity: 1.80 g/cc
Density: 0.00104 g/cc
Density: 1.80 g/cc
Water Absorption: 0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON 1140L7 PPS, 40% Glass Reinforced accurate 50%

$ 1622/MT

Specific Gravity: 1.64 g/cc
Density: 0.000948 g/cc
Density: 1.65 g/cc
Water Absorption: 0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON 6162A7 PPS, Mineral / Glass Reinforced accurate 46%

$ 1481/MT

Density: 1.92 g/cc
Water Absorption at Saturation: 0.0170 %
Linear Mold Shrinkage, Flow: 0.00100 - 0.00300 cm/cm
Linear Mold Shrinkage, Transverse: 0.00400 - 0.00800 cm/cm
Hardness, Rockwell M: 100

Celanese FORTRON 1131L4 ITT PPS, 30% Glass Reinforced accurate 55%

$ 1514/MT

Specific Gravity: 1.40 g/cc
Density: 0.000809 g/cc
Density: 1.56 g/cc
Water Absorption: 0.0300 % @Temperature 22.8 °C
Water Absorption at Saturation: 0.0200 %

Celanese FORTRON 1131L4 ITT PPS, 30% Glass Reinforced (Unverified Data**) accurate 50%

$ 2078/MT

Specific Gravity: 1.40 g/cc
Specific Gravity: 1.41 g/cc
Density: 1.40 g/cc
Density: 1.56 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 6450A6 PPS, 51% Specialty (Unverified Data**) accurate 43%

$ 2185/MT

Density: 1.58 g/cc
Water Absorption: 0.020 %
Tensile Strength at Break: 90.0 MPa
Elongation at Break: 1.5 %
Flexural Strength: 130 MPa

Celanese FORTRON 1342L4 PPS, 40% Specialty (Unverified Data**) accurate 97%

$ 1491/MT

Specific Gravity: 1.70 g/cc
Density: 1.69 g/cc
Water Absorption: 0.020 %
Water Absorption: 0.020 %
Thickness: 3180 microns

Celanese FORTRON 1140L7 PPS, 40% Glass Reinforced (Unverified Data**) accurate 46%

$ 2447/MT

Specific Gravity: 1.64 g/cc
Specific Gravity: 1.66 g/cc
Density: 1.64 g/cc
Density: 1.65 g/cc
Water Absorption: 0.020 %

Celanese FORTRON 1140L4 PPS, 40% Glass Reinforced accurate 43%

$ 2481/MT

Specific Gravity: 1.60 g/cc
Density: 0.000948 g/cc
Density: 1.64 g/cc
Density: 1.65 g/cc
Water Absorption: 0.0200 % @Temperature 22.8 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg tankers for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

3 prices for Celanese FORTRON 1342L4 PPS, 40% Specialty

Seller from Dongguan – 2021-04-28:

Seller from Dongguan work with company: 3M, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2411 per MT

Seller from Brasília – 2021-04-24:

Seller from Brasília work with company: 3M, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2134 per MT

Seller from Nanjing – 2021-05-14:

Seller from Nanjing work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1725 per MT