Celanese VECTRA B130 LCP, 30% Glass Reinforced

Seller in Bogotá price: $1559 per MT

Celanese VECTRA B130 LCP, 30% Glass Reinforced in Polymer, Thermoplastic, 30% Glass Fiber Filled, Liquid Crystal Polymer (LCP)

  • Physical Properties
  • Density
  • 1.60 g/cc
  • Linear Mold Shrinkage, Flow
  • 0.00 cm/cm
  • Linear Mold Shrinkage, Transverse
  • 0.0020 cm/cm
  • Mechanical Properties
  • Hardness, Rockwell M
  • 100
  • Tensile Strength at Break
  • 205 MPa
  • Tensile Stress
  • 6.97 MPa @Strain 0.110 %, Temperature 200 °C
  • Tensile Stress
  • 11.45 MPa @Strain 0.220 %, Temperature 200 °C
  • Tensile Stress
  • 13.75 MPa @Strain 0.340 %, Temperature 200 °C
  • Tensile Stress
  • 15.25 MPa @Strain 0.450 %, Temperature 200 °C
  • Tensile Stress
  • 16.5 MPa @Strain 0.570 %, Temperature 200 °C
  • Tensile Stress
  • 17.6 MPa @Strain 0.680 %, Temperature 200 °C
  • Tensile Stress
  • 18.5 MPa @Strain 0.790 %, Temperature 200 °C
  • Tensile Stress
  • 19.1 MPa @Strain 0.910 %, Temperature 200 °C
  • Tensile Stress
  • 19.4 MPa @Strain 1.02 %, Temperature 200 °C
  • Tensile Stress
  • 19.6 MPa @Strain 1.14 %, Temperature 200 °C
  • Tensile Stress
  • 20.8 MPa @Strain 0.0600 %, Temperature -40.0 °C
  • Tensile Stress
  • 26.6 MPa @Strain 0.110 %, Temperature 23.0 °C
  • Tensile Stress
  • 30.6 MPa @Strain 0.210 %, Temperature 120 °C
  • Tensile Stress
  • 34.1 MPa @Strain 0.180 %, Temperature 80.0 °C
  • Tensile Stress
  • 39.9 MPa @Strain 0.130 %, Temperature -40.0 °C
  • Tensile Stress
  • 52.4 MPa @Strain 0.230 %, Temperature 23.0 °C
  • Tensile Stress
  • 53.9 MPa @Strain 0.430 %, Temperature 120 °C
  • Tensile Stress
  • 59.9 MPa @Strain 0.200 %, Temperature -40.0 °C
  • Tensile Stress
  • 63.8 MPa @Strain 0.360 %, Temperature 80.0 °C
  • Tensile Stress
  • 70.2 MPa @Strain 0.650 %, Temperature 120 °C
  • Tensile Stress
  • 77.7 MPa @Strain 0.350 %, Temperature 23.0 °C
  • Tensile Stress
  • 80.0 MPa @Strain 0.270 %, Temperature -40.0 °C
  • Tensile Stress
  • 81.5 MPa @Strain 0.870 %, Temperature 120 °C
  • Tensile Stress
  • 88.1 MPa @Strain 0.540 %, Temperature 80.0 °C
  • Tensile Stress
  • 89.3 MPa @Strain 1.09 %, Temperature 120 °C
  • Tensile Stress
  • 94.8 MPa @Strain 1.31 %, Temperature 120 °C
  • Tensile Stress
  • 98.7 MPa @Strain 1.53 %, Temperature 120 °C
  • Tensile Stress
  • 100.16 MPa @Strain 0.340 %, Temperature -40.0 °C
  • Tensile Stress
  • 101.4 MPa @Strain 1.75 %, Temperature 120 °C
  • Tensile Stress
  • 101.5 MPa @Strain 0.470 %, Temperature 23.0 °C
  • Tensile Stress
  • 103.3 MPa @Strain 1.97 %, Temperature 120 °C
  • Tensile Stress
  • 104.4 MPa @Strain 2.19 %, Temperature 120 °C
  • Tensile Stress
  • 108 MPa @Strain 0.720 %, Temperature 80.0 °C
  • Tensile Stress
  • 119.5 MPa @Strain 0.410 %, Temperature -40.0 °C
  • Tensile Stress
  • 123.8 MPa @Strain 0.590 %, Temperature 23.0 °C
  • Tensile Stress
  • 124.4 MPa @Strain 0.910 %, Temperature 80.0 °C
  • Tensile Stress
  • 137.8 MPa @Strain 1.09 %, Temperature 80.0 °C
  • Tensile Stress
  • 138.6 MPa @Strain 0.480 %, Temperature -40.0 °C
  • Tensile Stress
  • 144.6 MPa @Strain 0.710 %, Temperature 23.0 °C
  • Tensile Stress
  • 148.6 MPa @Strain 1.27 %, Temperature 80.0 °C
  • Tensile Stress
  • 157.2 MPa @Strain 0.550 %, Temperature -40.0 °C
  • Tensile Stress
  • 157.3 MPa @Strain 1.45 %, Temperature 80.0 °C
  • Tensile Stress
  • 163.6 MPa @Strain 0.830 %, Temperature 23.0 °C
  • Tensile Stress
  • 164.2 MPa @Strain 1.63 %, Temperature 80.0 °C
  • Tensile Stress
  • 169.3 MPa @Strain 1.82 %, Temperature 80.0 °C
  • Tensile Stress
  • 175.1 MPa @Strain 0.620 %, Temperature -40.0 °C
  • Tensile Stress
  • 181.1 MPa @Strain 0.950 %, Temperature 23.0 °C
  • Tensile Stress
  • 193.7 MPa @Strain 0.690 %, Temperature -40.0 °C
  • Tensile Stress
  • 196.7 MPa @Strain 1.07 %, Temperature 23.0 °C
  • Tensile Stress
  • 211.1 MPa @Strain 1.19 %, Temperature 23.0 °C
  • Elongation at Break
  • 1.0 %
  • Tensile Modulus
  • 22.0 GPa
  • Flexural Strength
  • 300 MPa
  • Flexural Modulus
  • 20.0 GPa
  • Compressive Strength
  • 150 MPa @Strain 1.00 %
  • Compressive Modulus
  • 21.5 GPa
  • Izod Impact, Notched (ISO)
  • 14.0 kJ/m²
  • Izod Impact, Unnotched (ISO)
  • 15.0 kJ/m² @Temperature 23.0 °C
  • Charpy Impact Unnotched
  • 1.80 J/cm²
  • Charpy Impact, Notched
  • 1.20 J/cm²
  • Tensile Creep Modulus, 1 hour
  • 16000 MPa

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale history. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Celanese VECTRA B130 LCP, 30% Glass Reinforced

Seller from Bogotá – 2021-08-09:

Seller from Bogotá work with company: RTP Company, Teknor Apex Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1559 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Celanese VECTRA B130 LCP, 30% Glass Reinforced?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Appliance parts supplier in Singapore open-nearme.com