Physical Properties
Density
1.67 g/cc
Moisture Absorption
0.00200 %
Water Absorption at Saturation
0.0150 %
Linear Mold Shrinkage, Flow
0.00100 cm/cm
Linear Mold Shrinkage, Transverse
0.00500 cm/cm

Mechanical Properties
Hardness, Rockwell M
55.0
Tensile Strength at Break
130 MPa
Elongation at Break
2.50 %
Elongation at Break
2.50 %
Tensile Modulus
13.8 GPa
Flexural Strength
180 MPa
Flexural Modulus
13.5 GPa
Compressive Strength
82.0 MPa @Strain 1.00 %
Compressive Modulus
11.0 GPa
Izod Impact, Notched (ISO)
14.0 kJ/m²
Izod Impact, Notched (ISO)
60.0 kJ/m² @Temperature 23.0 °C
Charpy Impact Unnotched
5.50 J/cm²
Charpy Impact, Notched
3.00 J/cm²

Thermal Properties
CTE, linear, Parallel to Flow
6.00 µm/m-°C
CTE, linear, Transverse to Flow
18.0 µm/m-°C
Melting Point
335 °C
Deflection Temperature at 1.8 MPa (264 psi)
265 °C
Deflection Temperature at 8.0 MPa
220 °C
Vicat Softening Point
200 °C
Flammability, UL94
V-0

Electrical Properties
Volume Resistivity
1.00e+16 ohm-cm
Surface Resistance
>= 1.00e+15 ohm
Dielectric Constant
3.80 @Frequency 1.00e+6 Hz
Dielectric Strength
53.0 kV/mm
Dissipation Factor
0.0310 @Frequency 1.00e+6 Hz

Processing Properties
Processing Temperature
80.0 - 120 °C
Processing Temperature
335 - 345 °C
Feed Temperature
60.0 - 80.0 °C
Middle Barrel Temperature
20.0 - 30.0 °C
Zone 1
315 - 325 °C
Zone 2
320 - 330 °C
Zone 3
325 - 335 °C
Zone 4
330 - 340 °C
Die Temperature
335 - 345 °C
Melt Temperature
335 - 345 °C
Drying Temperature
150 - 170 °C
Dry Time
4.00 - 6.00 hour
Moisture Content
<= 0.0100 %
Injection Pressure
50.0 - 150 MPa
Hold Pressure
50.0 - 150 MPa
Back Pressure
<= 3.00 MPa
Screw Speed
80.0 rpm @Diameter 40.0 mm
Screw Speed
140 rpm @Diameter 25.0 mm
Screw Speed
200 rpm @Diameter 16.0 mm

Descriptive Properties
Injection Speed
very fast

Alternative products

Celanese Celstran® PP-GF30-0405 P10/10 PP, 30% Glass Reinforced accurate 57%

$ 1711/MT

Density: 1.13 g/cc
Tensile Strength at Break: 110 MPa
Tensile Strength: 70.0 MPa @Temperature 80.0 °C
Elongation at Break: 2.20 %
Elongation at Break: 2.30 % @Temperature 80.0 °C

Celanese Celstran® PP-GF30-0455 P10/16 PP, 30% Glass Reinforced accurate 57%

$ 1545/MT

Density: 1.13 g/cc
Tensile Strength at Break: 110 MPa
Tensile Strength: 70.0 MPa @Temperature 80.0 °C
Elongation at Break: 2.20 %
Elongation at Break: 2.30 % @Temperature 80.0 °C

Celanese VECTRA E471i LCP, 35% Specialty (Unverified Data**) accurate 87%

$ 1581/MT

Density: 1.67 g/cc
Linear Mold Shrinkage, Flow: 0.0010 cm/cm
Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
Hardness, Rockwell M: 55
Tensile Strength at Break: 130 MPa

Celanese FORTRON 1140L7 PPS, 40% Glass Reinforced (Unverified Data**) accurate 64%

$ 2447/MT

Specific Gravity: 1.64 g/cc
Specific Gravity: 1.66 g/cc
Density: 1.64 g/cc
Density: 1.65 g/cc
Water Absorption: 0.020 %

Celanese Celstran® PP-GF30-0405 P10/16 PP, 30% Glass Reinforced accurate 57%

$ 1820/MT

Density: 1.13 g/cc
Tensile Strength at Break: 110 MPa
Tensile Strength: 70.0 MPa @Temperature 80.0 °C
Elongation at Break: 2.20 %
Elongation at Break: 2.30 % @Temperature 80.0 °C

Celanese FORTRON ICE 504L PPS, 40% Specialty accurate 57%

$ 1452/MT

Density: 1.65 g/cc
Water Absorption at Saturation: 0.0200 %
Linear Mold Shrinkage, Flow: 0.00200 - 0.00600 cm/cm
Linear Mold Shrinkage, Transverse: 0.00400 - 0.00600 cm/cm
Hardness, Rockwell M: 100

Celanese Celstran® +PP-GF60-04CN15/10 PP, 60% Glass Reinforced accurate 57%

$ 1891/MT

Density: 1.43 g/cc
Tensile Strength at Break: 135 MPa
Tensile Strength: 80.0 MPa @Temperature 80.0 °C
Elongation at Break: 1.80 %
Elongation at Break: 2.00 % @Temperature 80.0 °C

Celanese Celstran® PP-GF30-0403 P10/10 PP, 30% Glass Reinforced accurate 64%

$ 1541/MT

Density: 1.13 g/cc
Viscosity Test: 119 cm³/g
Linear Mold Shrinkage, Flow: 0.00220 cm/cm
Linear Mold Shrinkage, Transverse: 0.00350 cm/cm
Tensile Strength at Break: 110 MPa

Celanese FORTRON 1140L4 PPS, 40% Glass Reinforced (Unverified Data**) accurate 57%

$ 1642/MT

Specific Gravity: 1.60 g/cc
Specific Gravity: 1.66 g/cc
Density: 1.64 g/cc
Density: 1.64 g/cc
Density: 1.65 g/cc

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, used cruise ship for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

4 prices for Celanese VECTRA E471i LCP, 35% Specialty

Seller from Shenzhen – 2021-05-05:

Seller from Shenzhen work with company: Solvay, RTP Company, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1651 per MT

Seller from Xi’an – 2021-08-03:

Seller from Xi’an work with company: Solvay, SABIC Innovative Plastics (GE Plastics), Lehmann & Voss & Co., ALIMEX GmbH

Price: $1841 per MT

Seller from Ōsaka – 2021-07-12:

Seller from Ōsaka work with company: Celanese Corporation, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2339 per MT

Seller from Bangkok – 2021-07-16:

Seller from Bangkok work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1932 per MT