Premix Thermoplastics PRE-ELEC® PC 1431 price 1581 per MT

Physical Properties
Density
1.24 g/cc
Thickness
406 microns
Linear Mold Shrinkage
<= 0.0060 cm/cm
Melt Flow
1.0 g/10 min @Load 1.20 kg, Temperature 300 °C
Melt Flow
4.0 g/10 min @Load 2.16 kg, Temperature 300 °C

Mechanical Properties
Hardness, Shore D
85
Film Tensile Strength at Yield, MD
50.0 MPa
Film Tensile Strength at Yield, TD
45.0 MPa
Film Elongation at Break, MD
20 %
Film Elongation at Break, TD
15 %
Film Elongation at Yield, MD
6.0 %
Film Elongation at Yield, TD
6.0 %
Modulus of Elasticity
2.50 GPa
Izod Impact, Notched
0.800 J/cm @Thickness 4.00 mm, Temperature -20.0 °C
Izod Impact, Notched
1.75 J/cm @Thickness 4.00 mm, Temperature 23.0 °C
Izod Impact, Unnotched
8.80 J/cm @Thickness 4.00 mm, Temperature -20.0 °C
Izod Impact, Unnotched
8.80 J/cm @Thickness 4.00 mm, Temperature 23.0 °C
Film Tensile Strength at Break, MD
47.0 MPa
Film Tensile Strength at Break, TD
44.0 MPa

Thermal Properties
Deflection Temperature at 0.46 MPa (66 psi)
134 °C
Deflection Temperature at 1.8 MPa (264 psi)
120 °C
Vicat Softening Point
140 °C
Vicat Softening Point
147 °C

Electrical Properties
Volume Resistivity
<= 1e+05
Surface Resistance
<= 1.00e+7 ohm

Processing Properties
Middle Barrel Temperature
250 °C
Middle Barrel Temperature
260 °C
Middle Barrel Temperature
260 °C
Middle Barrel Temperature
260 °C
Middle Barrel Temperature
270 °C
Middle Barrel Temperature
270 °C
Die Temperature
260 °C
Die Temperature
280 °C
Die Temperature
280 °C
Die Temperature
280 °C
Die Temperature
280 °C
Roll Temperature
70.0 °C
Roll Temperature
80.0 °C
Roll Temperature
90.0 °C
Drying Temperature
100 - 120 °C @Time 7200 - 14400 sec
Moisture Content
<= 0.15 %
Shelf Life
12.0 Month

Descriptive Properties
Appearance
Granule
Color
Black

Alternative products

Tipco Tipcofil® KMX 800 FR - UL94-V0 Flame Retardant, Highly Filled PBT/PC Alloy, with High Heat Stability accurate 22%

$ 1458/MT

Density: 1.90 g/cc
Linear Mold Shrinkage: 0.010 cm/cm
Melt Flow: 45 g/10 min
Tensile Strength, Yield: 60.0 MPa
Elongation at Break: >= 5.0 %

Kraiburg TPE THERMOLAST® K TC8NYN Thermoplastic Elastomer, Adhesion to PA accurate 19%

$ 2174/MT

Density: 1.15 g/cc
Hardness, Shore A: 78
Tensile Strength: 3.80 MPa
Elongation at Break: 320 %
Tear Strength: 21.0 kN/m

Kraiburg TPE THERMOLAST® K TC4PCN Thermoplastic Elastomer, Adhesion to PA, optimized compression set accurate 19%

$ 2162/MT

Density: 1.10 g/cc
Hardness, Shore A: 39
Tensile Strength: 2.50 MPa
Elongation at Break: 300 %
Tear Strength: 9.00 kN/m

Premix Thermoplastics PRE-ELEC® ABS 1410 accurate 19%

$ 1659/MT

Density: 1.10 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.0050 - 0.0080 cm/cm @Thickness 4.00 mm
Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 220 °C
Hardness, Shore D: 76 @Thickness 4.00 mm

Premix Thermoplastics PRE-ELEC® PC/ABS 1420 accurate 22%

$ 1970/MT

Density: 1.14 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.0070 - 0.0090 cm/cm
Melt Flow: 0.50 g/10 min @Load 5.00 kg, Temperature 240 °C
Melt Flow: 1.0 g/10 min @Load 1.20 kg, Temperature 300 °C

SABIC Innovative Plastics LNP THERMOCOMP NF001XXX PC+ABS accurate 22%

$ 1547/MT

Density: 1.18 g/cc
Density: 1.19 g/cc
Moisture Absorption: 0.170 %
Moisture Absorption: 0.250 %
Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec

Kraiburg TPE THERMOLAST® K TC7PCZ Thermoplastic Elastomer, Adhesion to PA, optimized compression set accurate 19%

$ 2000/MT

Density: 1.10 g/cc
Hardness, Shore A: 66
Tensile Strength: 7.50 MPa
Elongation at Break: 550 %
Tear Strength: 19.0 kN/m

Premix Thermoplastics PRE-ELEC® PPE 1461 (discontinued **) accurate 56%

$ 1922/MT

Density: 1.15 g/cc
Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
Melt Flow: 2.0 g/10 min @Load 5.00 kg, Temperature 240 °C
High Load Melt Index: 10 g/10 min @Load 21.6 kg, Temperature 240 °C
Hardness, Shore D: 85

Premix Thermoplastics PRE-ELEC® PS 1324 accurate 22%

$ 1584/MT

Density: 1.08 g/cc
Thickness: 406 microns
Linear Mold Shrinkage: 0.0040 - 0.0060 cm/cm
Melt Flow: 0.20 g/10 min @Load 5.00 kg, Temperature 200 °C
High Load Melt Index: 18 g/10 min @Load 21.6 kg, Temperature 200 °C

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

2 prices for Premix Thermoplastics PRE-ELEC® PC 1431

Seller from Luanda – 2021-06-12:

Seller from Luanda work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1581 per MT

Seller from Delhi – 2021-07-10:

Seller from Delhi work with company: 3M, Solvay, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $1944 per MT