$ 1767/MT
- Specific Gravity: 1.06 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 113
$ 1784/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 40 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 105
$ 1653/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 20 g/10 min
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 41.19 MPa
$ 1755/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 55 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 104
$ 2529/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 2027/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.50 - 1.0 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 35 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 2069/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 6.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 97
$ 1444/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.19 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1774/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 40 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 101
$ 1500/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 19.5 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1656/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 2408/MT
- Density: 1.07 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 7.49 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 49.0 MPa
$ 2419/MT
- Density: 1.04 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 19.76 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 48.0 MPa
$ 2200/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 104
- Tensile Strength, Yield: 36.3 MPa
$ 1618/MT
- Maximum Moisture Content: 0.010
- Melt Flow: 17 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 78
- Tensile Strength, Yield: 30.4 MPa @Thickness 3.20 mm
- Elongation at Break: 40 % @Thickness 3.20 mm
$ 1852/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 9.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 44.2 MPa
$ 1629/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 53 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 1566/MT
- Density: 1.09 g/cc
- Melt Index of Compound: 24 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 114
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 35 %
$ 1783/MT
- Density: 1.31 g/cc
- Water Absorption: 0.080 %
- Linear Mold Shrinkage: 0.012 - 0.021 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Ultimate: 56.5 MPa @Thickness 3.17 mm
$ 1469/MT
- Specific Gravity: 1.13 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 48 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 105
$ 1497/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 0.40 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Index of Compound: 1.8 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 47
$ 2211/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 85
$ 1788/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min
- Tensile Strength, Yield: 47.0 MPa @Thickness 3.20 mm
$ 2241/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 99
$ 1689/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1601/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.19 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1582/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 52 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 104
$ 1509/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 114
$ 1697/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength, Yield: 49.0 MPa
- Elongation at Break: 30 %
$ 2349/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 0.40 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Index of Compound: 6.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 65
$ 1678/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 106
$ 2512/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 105
$ 1658/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 45 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 109
$ 1536/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 48.1 MPa
$ 1519/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 32 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 72.6 MPa @Thickness 3.20 mm
$ 1585/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
- Tensile Strength, Yield: 54.0 MPa
- Elongation at Break: >= 200 %
$ 2374/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 6.2 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 123
$ 1674/MT
- Specific Gravity: 1.44 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 30 %
$ 1702/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 113
$ 1921/MT
- Specific Gravity: 1.06 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 2094/MT
- Specific Gravity: 1.06 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 1616/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 0.40 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Index of Compound: 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 40
$ 1596/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1563/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 111
$ 1893/MT
- Density: 1.09 g/cc
- Water Absorption: 0.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.006 - 0.008 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Flow: 0.007 - 0.009 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.007 - 0.009 cm/cm @Thickness 3.00 mm
$ 1693/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
- Tensile Strength, Yield: 54.0 MPa
- Elongation at Break: >= 150 %
$ 1737/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 49.1 MPa
$ 1544/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 1579/MT
- Specific Gravity: 1.12 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 62.0 MPa
$ 1483/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 1562/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 17 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1514/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1908/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 11.5 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1589/MT
- Maximum Moisture Content: 0.010
- Melt Flow: 11 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 87
- Tensile Strength, Yield: 37.3 MPa @Thickness 3.20 mm
- Elongation at Break: >= 10 % @Thickness 3.20 mm
$ 2368/MT
- Specific Gravity: 1.12 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 1676/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 0.40 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Index of Compound: 5.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 58
$ 1511/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 1.47 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 44.0 MPa
$ 1740/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 80
$ 1930/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 101
$ 1456/MT
- Specific Gravity: 0.916 g/cc
- Melt Flow: 24 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 45
- Tensile Strength at Break: 13.0 MPa
- Tensile Strength, Yield: 9.32 MPa
$ 1789/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 43 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 106
$ 1716/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 43 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 106
$ 1504/MT
- Specific Gravity: 1.12 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 42 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 93
$ 1730/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 94
$ 1646/MT
- Density: 1.31 g/cc
- Water Absorption: 0.080 %
- Linear Mold Shrinkage: 0.012 - 0.021 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Ultimate: 56.5 MPa @Thickness 3.17 mm
$ 1958/MT
- Density: 1.31 g/cc
- Water Absorption: 0.080 %
- Linear Mold Shrinkage: 0.012 - 0.021 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Ultimate: 56.5 MPa @Thickness 3.17 mm
$ 1587/MT
- Density: 1.31 g/cc
- Water Absorption: 0.080 %
- Linear Mold Shrinkage: 0.012 - 0.021 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Ultimate: 56.5 MPa @Thickness 3.17 mm
$ 1695/MT
- Density: 1.31 g/cc
- Water Absorption: 0.080 %
- Linear Mold Shrinkage: 0.012 - 0.021 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Ultimate: 56.5 MPa @Thickness 3.17 mm
$ 2232/MT
- Density: 1.31 g/cc
- Water Absorption: 0.080 %
- Linear Mold Shrinkage: 0.012 - 0.021 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Ultimate: 56.5 MPa @Thickness 3.17 mm
$ 1836/MT
- Density: 1.31 g/cc
- Water Absorption: 0.080 %
- Linear Mold Shrinkage: 0.012 - 0.021 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Ultimate: 56.5 MPa @Thickness 3.17 mm
$ 2017/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 115
$ 1510/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.4 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 102
$ 2025/MT
- Specific Gravity: 1.06 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 105
$ 1608/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 99
$ 1953/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 116
- Tensile Strength, Yield: 55.9 MPa @Thickness 3.20 mm
- Elongation at Break: 28 % @Thickness 3.20 mm
$ 1451/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 18 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 105
$ 2395/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 1461/MT
- Specific Gravity: 1.42 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Tensile Strength, Yield: 61.0 MPa
- Elongation at Break: 20 %
$ 1974/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
- Tensile Strength, Yield: 54.0 MPa
- Elongation at Break: 60 %
$ 1624/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
- Tensile Strength, Yield: 54.0 MPa
- Elongation at Break: >= 100 %
$ 1481/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 48 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 2066/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 2060/MT
- Specific Gravity: 1.44 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 cm/cm
- Tensile Strength, Yield: 132 MPa
- Elongation at Break: 4.0 %
$ 1528/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 43 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1703/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 28 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1905/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 109
- Tensile Strength, Yield: 47.1 MPa @Thickness 3.20 mm
- Elongation at Break: 30 % @Thickness 3.20 mm
$ 2554/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 37 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 2518/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 33 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 1693/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 52 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 104
$ 1464/MT
- Density: 1.07 g/cc
- Water Absorption: 0.3 % @Time 86400 sec
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Tensile Strength, Yield: 41.2 MPa @Thickness 3.20 mm
- Elongation at Break: 25 % @Thickness 3.17 mm
$ 1514/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 37 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 97
$ 1767/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 56.7 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 50.0 MPa
$ 1525/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 40 g/10 min
- Hardness, Rockwell R: 93
- Tensile Strength at Break: 37.46 MPa
$ 2217/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 40 g/10 min
- Hardness, Rockwell R: 93
- Tensile Strength at Break: 37.46 MPa
$ 1448/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 113
$ 1689/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 49.0 MPa @Thickness 3.20 mm
- Elongation at Break: 37 % @Thickness 3.20 mm
$ 1752/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1450/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1899/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 1748/MT
- Specific Gravity: 1.02 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 92
$ 2432/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 3.4 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 32 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 124
$ 1556/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 98
$ 1740/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 98
$ 1945/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 4.41 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 42.0 MPa
$ 2280/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 53 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 2036/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 109
$ 1837/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 2271/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 23 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 90
$ 1801/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 1741/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 37 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 2206/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 5.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 46.2 MPa
$ 1603/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 42 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 45.0 MPa
$ 1642/MT
- Specific Gravity: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 54.9 MPa @Thickness 3.20 mm
- Elongation at Break: 30 % @Thickness 3.20 mm
- Flexural Yield Strength: 85.3 MPa @Thickness 3.20 mm
$ 1538/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 53 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 104
$ 1857/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 99
$ 2406/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 23 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 2492/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 5.8 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 46.2 MPa
$ 1549/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1684/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 117
$ 1875/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1835/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 2.3 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 51.1 MPa
$ 1613/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 97
$ 1914/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 1957/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 23 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 2174/MT
- Density: 1.07 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 6.955 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 42.0 MPa
$ 2523/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 53 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 106
$ 1713/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 32 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1652/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 1539/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 1823/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 3.80 kg, Temperature 200 °C
- Hardness, Rockwell R: 115
$ 1996/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 cm/cm
- Tensile Strength, Yield: 93.0 MPa
- Elongation at Break: 6.0 %
$ 1661/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.5 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 108 MPa @Thickness 3.20 mm
$ 1509/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm
- Tensile Strength, Yield: 118 MPa
- Elongation at Break: 6.0 %
$ 1514/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 cm/cm
- Tensile Strength, Yield: 127 MPa
- Elongation at Break: 5.0 %
$ 1614/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1661/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1513/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1770/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 2594/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1803/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 2005/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 42 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 45.0 MPa
$ 2455/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 1581/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 22 g/10 min
- Hardness, Rockwell R: 112
- Tensile Strength at Break: 51.0 MPa
$ 1827/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 111
$ 1854/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 1460/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 1823/MT
- Specific Gravity: 1.04 - 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 40 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 109
$ 1716/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1810/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 0.40 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Index of Compound: 3.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 42
$ 1607/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 5.3 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 96
$ 1447/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 5.67 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 45.0 MPa
$ 2416/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 12.3 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 90
$ 1496/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1523/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 1748/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 96
$ 2302/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1769/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 26 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 98
$ 1656/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 1622/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 3.4 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 32 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 124
$ 2493/MT
- Specific Gravity: 0.916 g/cc
- Thickness: 50.0 - 300 microns
- Melt Flow: 24 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 43
- Tensile Strength at Break: 10.5 MPa
$ 1885/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 20 g/10 min
- Hardness, Rockwell R: 112
- Tensile Strength at Break: 47.86 MPa
$ 1741/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 1.0 g/10 min @Load 3.50 kg, Temperature 230 °C
- Hardness, Rockwell R: 97
$ 1945/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 22 g/10 min
- Hardness, Rockwell R: 112
- Tensile Strength at Break: 51.0 MPa
$ 1803/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 6.8 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 47.1 MPa
$ 2590/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.19 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1469/MT
- Density: 1.07 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 9.63 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 52.0 MPa
$ 2087/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 5.8 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 96
$ 1875/MT
- Specific Gravity: 1.02 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 93
Delivery Molded LG Chemical
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale in usa. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.