$ 1767/MT
- Specific Gravity: 1.06 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 113
$ 2390/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 62.0 MPa
$ 1567/MT
- Specific Gravity: 1.25 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 65.7 MPa @Thickness 3.20 mm
- Elongation at Break: 4.0 % @Thickness 3.20 mm
$ 1459/MT
- Specific Gravity: 1.406 g/cc
- Bulk Density: 0.310 - 0.410 g/cc
- Volatiles: <= 0.30 % @Temperature 110 °C, Time 3600 sec
- Brookfield Viscosity: 10000 - 60000 cP
- Viscosity Measurement: >= 5.0 @Pressure 0.400 MPa
$ 1575/MT
- Specific Gravity: 0.921 g/cc
- Water Vapor Transmission: 10.0 g/m²/day
- Oxygen Transmission Rate: 2000 cc/m²/day
- Nitrogen Transmission: 3500 cc-mm/m²-24hr-atm
- Environmental Stress Crack Resistance: >= 500 hour
$ 1485/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 58.8 MPa @Thickness 3.20 mm
- Elongation at Break: >= 100 % @Thickness 3.20 mm
$ 1715/MT
- Specific Gravity: 1.52 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 93.2 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1707/MT
- Specific Gravity: 1.44 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.011 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 108 MPa @Thickness 3.20 mm
- Elongation at Break: 4.0 % @Thickness 3.20 mm
$ 1758/MT
- Density: 1.41 g/cc
- Water Absorption: 0.070 %
- Linear Mold Shrinkage: 0.0040 - 0.011 cm/cm
- Hardness, Rockwell R: 90
- Tensile Strength, Ultimate: 93.1 MPa @Thickness 3.17 mm
$ 1678/MT
- Specific Gravity: 1.36 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 108 MPa
$ 1656/MT
- Specific Gravity: 1.44 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 127 MPa
$ 1784/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 40 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 105
$ 2464/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1653/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 20 g/10 min
- Hardness, Rockwell R: 105
- Tensile Strength at Break: 41.19 MPa
$ 1490/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 2394/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 15.05 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 34.3 MPa
- Elongation at Break: <= 500 %
$ 1790/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1569/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 10 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1755/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 55 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 104
$ 2157/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1493/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 113
$ 1505/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2242/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1519/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1909/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1775/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1480/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1525/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1448/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1521/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1482/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1820/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1457/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1941/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2144/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2165/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2338/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1450/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2029/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1818/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1528/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2305/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 1464/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 61.0 MPa
$ 1980/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2298/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Index of Compound: 45 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 62.0 MPa
$ 1502/MT
- Specific Gravity: 1.14 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.8 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 114
$ 1738/MT
- Specific Gravity: 1.00 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 53.9 MPa @Thickness 3.20 mm
$ 2529/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1504/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 62.0 MPa
$ 1617/MT
- Specific Gravity: 1.50 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 108 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 2116/MT
- Specific Gravity: 1.25 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 13 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 124
$ 1590/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 260 °C
- Hardness, Rockwell R: 113
$ 1894/MT
- Specific Gravity: 1.38 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Hardness, Rockwell R: 100
- Tensile Strength at Break: 28.0 MPa
- Elongation at Break: 31 %
$ 1596/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.040
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 66.7 MPa @Thickness 3.20 mm
$ 1510/MT
- Specific Gravity: 0.918 - 0.922 g/cc
- Melt Flow: 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 700 %
- Film Elongation at Break, TD: 850 %
- Elmendorf Tear Strength MD: 16 g
$ 2576/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 114
$ 1944/MT
- Specific Gravity: 1.00 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 33.3 MPa @Thickness 3.20 mm
$ 1773/MT
- Specific Gravity: 1.37 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 186 MPa @Thickness 3.20 mm
$ 2509/MT
- Specific Gravity: 1.00 - 1.05 g/cc
- Solids Content: 49.5 - 50.5 % @Temperature 130 °C, Time 1800 sec
- Particle Size: 115 - 135 µm
- pH: 7.5 - 8.5
- Viscosity: <= 200 cP @Time 60.0 sec
- Surface Tension: 40 - 50 dynes/cm
$ 1855/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 17 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 34.3 MPa
- Elongation at Break: >= 500 %
$ 1532/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.040
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 18 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 59.8 MPa @Thickness 3.20 mm
$ 2234/MT
- Melt Flow: 100 g/10 min @Load 10.0 kg, Temperature 230 °C
- Hardness, Shore D: 85 - 91
- Tensile Strength at Break: 8.34 MPa @Thickness 2.00 mm
- Elongation at Break: 300 % @Thickness 2.00 mm
- Izod Impact, Notched: NB @Thickness 6.40 mm, Temperature 23.0 °C
$ 1567/MT
- Density: 1.28 g/cc
- Melt Flow: 9.5 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength, Yield: 121 MPa @Thickness 3.20 mm
- Elongation at Break: 7.0 % @Thickness 3.17 mm
- Flexural Strength: 172 MPa @Thickness 3.20 mm
$ 1610/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 8.0 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1500/MT
- Specific Gravity: 0.921 - 0.925 g/cc
- Melt Flow: 0.80 - 1.2 g/10 min @Load 2.61 kg, Temperature 190 °C
- Tensile Strength, Ultimate: 14.7 MPa
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 550 %
$ 2164/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 113
$ 1851/MT
- Specific Gravity: 1.11 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 54.9 MPa @Thickness 3.20 mm
$ 1445/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 113
$ 2027/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.50 - 1.0 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 35 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 2057/MT
- Specific Gravity: 0.935 g/cc
- Environmental Stress Crack Resistance: >= 2000 hour
- Carbon Black Loading: 2.6 %
- Melt Flow: 0.95 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 48
$ 1501/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2393/MT
- Specific Gravity: 0.950 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 60
- Tensile Strength, Yield: 23.5 MPa
- Elongation at Break: >= 800 %
$ 2270/MT
- Specific Gravity: 1.25 g/cc
- Water Absorption: 1.0 %
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 122
$ 2069/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 6.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 97
$ 2469/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 36.3 MPa
$ 1520/MT
- Specific Gravity: 1.31 g/cc
- Water Absorption: 0.080 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.018 - 0.021 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 260 °C
$ 1731/MT
- Water Absorption: 0.24 %
- Water Absorption: 0.25 %
- Water Absorption: 0.30 %
- Water Absorption: 0.30 %
- Flexural Yield Strength: 0.161 MPa
$ 1444/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.19 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1855/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1723/MT
- Specific Gravity: 1.34 g/cc
- Water Absorption: 1.0 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 117
- Tensile Strength, Yield: 152 MPa @Thickness 3.20 mm
$ 1801/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 1.7 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 78.5 MPa @Thickness 3.20 mm
$ 1564/MT
- Specific Gravity: 1.00 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0090 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 38 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 21.1 MPa @Thickness 3.20 mm
$ 1609/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 10 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 46 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 2144/MT
- Specific Gravity: 1.13 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Thickness 3.20 mm
- Melt Flow: 34 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 20.6 MPa @Thickness 3.20 mm
$ 2253/MT
- Specific Gravity: 1.406 g/cc
- Bulk Density: 0.300 - 0.400 g/cc
- Volatiles: <= 0.70 % @Temperature 110 °C, Time 3600 sec
- Brookfield Viscosity: 3500 - 8500 cP
- Viscosity Measurement: >= 2.0 @Pressure 0.400 MPa
$ 1674/MT
- Specific Gravity: 0.960 g/cc
- Hardness, Shore A: 72 - 78
- Tensile Strength at Break: 5.90 MPa
- Tensile Strength, Yield: 3.40 MPa @Strain 100 %
- Elongation at Break: 600 %
$ 1962/MT
- Specific Gravity: 1.41 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.018 - 0.021 cm/cm @Thickness 3.20 mm
- Melt Flow: 45 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 82
$ 1480/MT
- Specific Gravity: 1.20 g/cc
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 2332/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 23 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1554/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 24.5 MPa @Thickness 3.20 mm
$ 1527/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength, Yield: 44.0 MPa
- Elongation at Break: 7.0 %
$ 1714/MT
- Specific Gravity: 1.28 g/cc
- Linear Mold Shrinkage: 0.015 - 0.018 cm/cm
- Tensile Strength at Break: 36.0 MPa
- Elongation at Break: 300 %
- Flexural Strength: 32.0 MPa
$ 1929/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1919/MT
- Specific Gravity: 1.365 g/cc
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 122
$ 1551/MT
- Water Absorption: 0.45 %
- Water Absorption: 0.50 %
- Water Absorption: 0.75 %
- Water Absorption: 0.83 %
- Flexural Yield Strength: 0.186 MPa
$ 1774/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 40 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 101
$ 1465/MT
- Specific Gravity: 1.25 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 118 MPa @Thickness 3.20 mm
- Elongation at Break: 2.0 % @Thickness 3.20 mm
$ 1500/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 19.5 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1592/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 34 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 137 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1662/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 15 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 64 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 2318/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 110
$ 1469/MT
- Specific Gravity: 1.03 g/cc
- Maximum Moisture Content: 0.010
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 10 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 43 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1656/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1886/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 cm/cm
- Hardness, Rockwell R: 124
- Tensile Strength, Yield: 83.0 MPa
$ 2408/MT
- Density: 1.07 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 7.49 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 49.0 MPa
$ 2443/MT
- Specific Gravity: 1.40 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.020 - 0.022 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 80
$ 1610/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 13 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 61.8 MPa @Thickness 3.20 mm
$ 1699/MT
- Specific Gravity: 0.875 g/cc
- Mooney Viscosity: 8.0 @Temperature 121 °C
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 54
- Tensile Strength at Break: 1.80 MPa
$ 1842/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 18 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 117
$ 2268/MT
- Specific Gravity: 1.65 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength, Yield: 80.0 MPa
- Elongation at Break: 6.0 %
$ 1624/MT
- Specific Gravity: 1.01 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 52.0 MPa @Thickness 3.20 mm
$ 1996/MT
- Specific Gravity: 0.922 g/cc
- Degree of Crosslinking: >= 80 %
- Tensile Strength at Break: >= 19.7 MPa
- Tensile Strength at Break: >= 18.72 MPa @Temperature 136 °C, Time 605000 sec
- Elongation at Break: 550 %
$ 1716/MT
- Specific Gravity: 0.870 g/cc
- Mooney Viscosity: 23 @Temperature 121 °C
- Melt Flow: 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 71
- Tensile Strength at Break: 9.51 MPa
$ 1653/MT
- Specific Gravity: 1.25 g/cc
- Maximum Moisture Content: 0.040
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 60.8 MPa @Thickness 3.20 mm
$ 1719/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 58.8 MPa @Thickness 3.20 mm
- Elongation at Break: >= 100 % @Thickness 3.20 mm
$ 2120/MT
- Specific Gravity: 1.16 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 93
$ 1722/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm
- Tensile Strength, Yield: 59.0 MPa
- Elongation at Break: 7.0 %
$ 1747/MT
- Specific Gravity: 0.918 - 0.922 g/cc
- Melt Flow: 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 36.3 MPa
- Film Elongation at Break, MD: 680 %
- Film Elongation at Break, TD: 800 %
$ 2243/MT
- Specific Gravity: 1.69 g/cc
- Water Absorption: 0.70 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 130
- Tensile Strength, Yield: 206 MPa @Thickness 3.20 mm
$ 1644/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 28 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 56.9 MPa @Thickness 3.20 mm
$ 1529/MT
- Specific Gravity: 0.940 g/cc
- Volatiles: <= 0.50 %
- Viscosity: 8.6 cP
- Melt Flow: 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 84
$ 2509/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 27.5 MPa
- Elongation at Break: >= 200 %
$ 1957/MT
- Specific Gravity: 1.04 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Break: 25 %
$ 1894/MT
- Specific Gravity: 0.954 g/cc
- Melting Point: 220 - 230 °C
$ 1787/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 113
$ 1561/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm
- Hardness, Rockwell M: 87
- Tensile Strength at Break: 108 MPa
- Elongation at Break: <= 10 %
$ 1520/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2037/MT
- Specific Gravity: 1.06 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa @Thickness 3.20 mm
$ 2142/MT
- Specific Gravity: 1.10 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 103
$ 1660/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.5 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 54.9 MPa @Thickness 3.20 mm
$ 2419/MT
- Density: 1.04 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 19.76 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 48.0 MPa
$ 2255/MT
- Specific Gravity: 1.39 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.018 - 0.022 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 53.7 MPa @Thickness 3.20 mm
$ 2576/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 260 °C
- Tensile Strength, Yield: 61.8 MPa @Thickness 3.20 mm
$ 2200/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 104
- Tensile Strength, Yield: 36.3 MPa
$ 1629/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 13 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 117
$ 1513/MT
- Specific Gravity: 0.900 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0090 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 14.7 MPa @Thickness 3.20 mm
$ 1816/MT
- Specific Gravity: 1.40 g/cc
- Bulk Density: 0.480 - 0.560 g/cc
- Volatiles: <= 0.30 % @Temperature 110 °C, Time 3600 sec
- Particle Mesh Size: 45 Mesh
- Molecular Weight: 60000 - 150000 g/mol
$ 1618/MT
- Maximum Moisture Content: 0.010
- Melt Flow: 17 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 78
- Tensile Strength, Yield: 30.4 MPa @Thickness 3.20 mm
- Elongation at Break: 40 % @Thickness 3.20 mm
$ 1812/MT
- Specific Gravity: 1.25 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 18 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 117
$ 1783/MT
- Specific Gravity: 1.41 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.018 - 0.021 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 82
$ 2132/MT
- Specific Gravity: 0.944 - 0.947 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 5.4 - 6.6 g/10 min @Load 21.6 kg, Temperature 190 °C
- Tensile Strength, Yield: 23.5 MPa
- Elongation at Break: >= 600 % @Thickness 50.0 mm
$ 1852/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 9.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 44.2 MPa
$ 1706/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0090 - 0.013 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 29.4 MPa @Thickness 3.20 mm
$ 1629/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 53 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 1837/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 104
$ 1631/MT
- Specific Gravity: 0.942 - 0.945 g/cc
- Environmental Stress Crack Resistance: >= 1500 hour
- Melt Flow: 0.10 - 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 54
- Tensile Strength at Break: 35.0 MPa
$ 1756/MT
- Specific Gravity: 0.960 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0090 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 19 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 14.7 MPa @Thickness 3.20 mm
$ 1933/MT
- Specific Gravity: 0.960 g/cc
- Hardness, Shore A: 80 - 86
- Tensile Strength at Break: 9.80 MPa
- Tensile Strength, Yield: 4.90 MPa @Strain 100 %
- Elongation at Break: 600 %
$ 1895/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 30 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2226/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm
- Tensile Strength, Yield: 83.0 MPa
- Elongation at Break: 7.0 %
$ 1629/MT
- Specific Gravity: 1.406 g/cc
- Molecular Weight: 60000 - 150000 g/mol
- Melting Point: 302 °C
- Autoignition Temperature: 435°C
$ 1653/MT
- Specific Gravity: 1.52 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 cm/cm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 167 MPa
$ 2244/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1819/MT
- Specific Gravity: 1.40 g/cc
- Bulk Density: 0.460 - 0.540 g/cc
- Volatiles: <= 0.30 % @Temperature 110 °C, Time 3600 sec
- Particle Mesh Size: 45 Mesh
- Molecular Weight: 60000 - 150000 g/mol
$ 1566/MT
- Density: 1.09 g/cc
- Melt Index of Compound: 24 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 114
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 35 %
$ 2406/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1566/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 1783/MT
- Density: 1.31 g/cc
- Water Absorption: 0.080 %
- Linear Mold Shrinkage: 0.012 - 0.021 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Ultimate: 56.5 MPa @Thickness 3.17 mm
$ 2213/MT
- Specific Gravity: 0.980 g/cc
- Maximum Moisture Content: 0.010
- Melt Flow: 0.35 - 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 25.05 MPa @Thickness 3.20 mm
- Elongation at Break: 262.7 % @Thickness 3.20 mm
$ 1819/MT
- Specific Gravity: 0.914 - 0.916 g/cc
- Melt Flow: 2.2 - 2.6 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 480 %
- Film Elongation at Break, TD: 750 %
- Elmendorf Tear Strength MD: 24 g
$ 2522/MT
- Specific Gravity: 0.940 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 29.4 MPa @Thickness 3.20 mm
$ 2132/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 30 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1651/MT
- Specific Gravity: 1.50 g/cc
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
- Elongation at Break: 2.8 % @Thickness 3.20 mm
$ 1470/MT
- Specific Gravity: 0.900 g/cc
- Hardness, Shore D: 43 - 47
- Tensile Strength at Break: 13.2 MPa
- Tensile Strength, Yield: 9.80 MPa @Strain 100 %
- Elongation at Break: 750 %
$ 1865/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2288/MT
- Specific Gravity: 1.35 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 93.2 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1808/MT
- Specific Gravity: 0.930 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Thickness 3.20 mm
- Melt Flow: 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.5 MPa @Thickness 3.20 mm
$ 1631/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 16 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 2446/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
- Melt Flow: 2.0 g/10 min @Load 2.13 kg, Temperature 230 °C
$ 1806/MT
- Specific Gravity: 1.38 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.017 - 0.020 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 70
$ 2105/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1469/MT
- Specific Gravity: 1.13 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 48 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 105
$ 1726/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 1497/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 0.40 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Index of Compound: 1.8 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 47
$ 1668/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 8.0 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 2300/MT
- Specific Gravity: 1.60 g/cc
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 162 MPa @Thickness 3.20 mm
$ 1483/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 13 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 117
$ 1568/MT
- Specific Gravity: 1.16 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 90
$ 1448/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 12 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 2211/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 85
$ 1788/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min
- Tensile Strength, Yield: 47.0 MPa @Thickness 3.20 mm
$ 1541/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 96
- Tensile Strength, Yield: 26.5 MPa
$ 2241/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 99
$ 1581/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength, Yield: 36.0 MPa
- Elongation at Break: 30 %
$ 1689/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1959/MT
- Specific Gravity: 1.00 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0090 - 0.014 cm/cm @Thickness 3.20 mm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 26.5 MPa @Thickness 3.20 mm
$ 1693/MT
- Specific Gravity: 1.12 g/cc
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 2182/MT
- Specific Gravity: 1.40 g/cc
- Bulk Density: 0.430 - 0.510 g/cc
- Volatiles: <= 0.30 % @Temperature 110 °C, Time 3600 sec
- Particle Mesh Size: 45 Mesh
- Molecular Weight: 60000 - 150000 g/mol
$ 1534/MT
- Specific Gravity: 0.990 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Break: 80 %
$ 1546/MT
- Specific Gravity: 1.14 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 85.3 MPa @Thickness 3.20 mm
$ 1785/MT
- Specific Gravity: 0.921 g/cc
- Degree of Crosslinking: >= 80 %
- Tensile Strength at Break: >= 17.65 MPa
- Tensile Strength at Break: >= 16.76 MPa @Temperature 135 °C, Time 605000 sec
- Elongation at Break: 500 %
$ 1563/MT
- Specific Gravity: 1.00 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0090 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 38 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 20.6 MPa @Thickness 3.20 mm
$ 1601/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.19 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1445/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 1.7 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 76.5 MPa @Thickness 3.20 mm
$ 1541/MT
- Specific Gravity: 1.10 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.050 - 0.060 cm/cm @Thickness 3.20 mm
- Melt Flow: 21 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 16.7 MPa @Thickness 3.20 mm
$ 1582/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 52 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 104
$ 1509/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 114
$ 1697/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength, Yield: 49.0 MPa
- Elongation at Break: 30 %
$ 2058/MT
- Specific Gravity: 1.62 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 125 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1785/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 28 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1721/MT
- Specific Gravity: 1.33 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 77.5 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 2121/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 113
$ 1929/MT
- Specific Gravity: 1.59 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 85
$ 2349/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 0.40 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Index of Compound: 6.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 65
$ 1589/MT
- Specific Gravity: 1.72 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 157 MPa @Thickness 3.20 mm
- Elongation at Break: 2.0 % @Thickness 3.20 mm
$ 1678/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 106
$ 1841/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 6.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 98
- Tensile Strength, Yield: 26.5 MPa
$ 1832/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1744/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 7.35 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 50.0 MPa
$ 2512/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 105
$ 1760/MT
- Specific Gravity: 1.03 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Break: 400 %
$ 1658/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 45 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 109
$ 2227/MT
- Specific Gravity: 1.42 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Hardness, Rockwell M: 80
- Tensile Strength at Break: 59.0 MPa
- Elongation at Break: 10 %
$ 1717/MT
- Specific Gravity: 1.54 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 118 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1688/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 34.3 MPa
- Elongation at Break: <= 500 %
$ 1469/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 1993/MT
- Specific Gravity: 1.28 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Hardness, Rockwell M: 94
- Tensile Strength at Break: 118 MPa
- Elongation at Break: <= 10 %
$ 1536/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 48.1 MPa
$ 1604/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1519/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 32 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 72.6 MPa @Thickness 3.20 mm
$ 2260/MT
- Specific Gravity: 1.72 g/cc
- Water Absorption: 0.50 %
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
$ 1803/MT
- Density: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 59 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 42.0 MPa
$ 1848/MT
- Specific Gravity: 1.26 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 1957/MT
- Specific Gravity: 0.924 - 0.928 g/cc
- Melt Flow: 0.50 - 0.70 g/10 min @Load 2.61 kg, Temperature 190 °C
- Tensile Strength, Ultimate: 17.7 MPa
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 650 %
$ 1822/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 2185/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 73.5 MPa @Thickness 3.20 mm
- Elongation at Break: >= 5.0 % @Thickness 3.20 mm
$ 2435/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Index of Compound: 27 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 62.0 MPa
$ 1543/MT
- Specific Gravity: 1.48 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm
- Hardness, Rockwell M: 85
- Tensile Strength at Break: 118 MPa
- Elongation at Break: <= 10 %
$ 2278/MT
- Specific Gravity: 1.00 g/cc
- Linear Mold Shrinkage: 0.016 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Break: 80 %
$ 1661/MT
- Specific Gravity: 1.32 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0090 - 0.013 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 27.5 MPa @Thickness 3.20 mm
$ 2380/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 34.3 MPa
- Elongation at Break: <= 500 %
$ 1585/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
- Tensile Strength, Yield: 54.0 MPa
- Elongation at Break: >= 200 %
$ 1484/MT
- Specific Gravity: 1.00 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0090 - 0.014 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 28.4 MPa @Thickness 3.20 mm
$ 1885/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1855/MT
- Specific Gravity: 1.40 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 76.5 MPa @Thickness 3.20 mm
- Elongation at Break: 4.0 % @Thickness 3.20 mm
$ 2185/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 55.9 MPa @Thickness 3.20 mm
- Elongation at Break: >= 100 % @Thickness 3.20 mm
$ 1548/MT
- Specific Gravity: 1.43 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 120
$ 1931/MT
- Specific Gravity: 0.870 g/cc
- Mooney Viscosity: 18 @Temperature 121 °C
- Melt Flow: 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 63
- Tensile Strength at Break: 4.40 MPa
$ 1797/MT
- Specific Gravity: 1.22 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0060 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.5 MPa @Thickness 3.20 mm
$ 1722/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 0.35 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 99
- Tensile Strength, Yield: 64.7 MPa @Thickness 3.20 mm
$ 2374/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 6.2 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 123
$ 1617/MT
- Specific Gravity: 1.14 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.3 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 114
$ 1674/MT
- Specific Gravity: 1.44 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 30 %
$ 1702/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 113
$ 2482/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.040
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 56.9 MPa @Thickness 3.20 mm
$ 1482/MT
- Specific Gravity: 1.03 g/cc
- Melting Point: 220 - 230 °C
$ 1612/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1625/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 26.5 MPa
- Elongation at Break: >= 300 %
$ 2188/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 84
- Tensile Strength, Yield: 26.5 MPa
- Elongation at Break: <= 500 %
$ 2297/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0060 - 0.011 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 33.3 MPa @Thickness 3.20 mm
$ 1921/MT
- Specific Gravity: 1.06 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 2002/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1933/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 17 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1832/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2094/MT
- Specific Gravity: 1.06 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 1616/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 0.40 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Index of Compound: 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 40
$ 1712/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 53.0 MPa @Thickness 3.20 mm
- Elongation at Break: >= 90 % @Thickness 3.20 mm
$ 1503/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 34.3 MPa
- Elongation at Break: <= 500 %
$ 1836/MT
- Specific Gravity: 0.918 g/cc
- Water Vapor Transmission: 20.0 g/m²/day @Pressure 0.101 MPa
- Melt Flow: 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 44
- Tensile Strength at Break: 13.0 MPa
$ 1538/MT
- Specific Gravity: 1.14 g/cc
- Tensile Strength at Break: 16.8 MPa
- Tensile Strength at Break: 15.96 MPa @Temperature 121 °C, Time 605000 sec
- Elongation at Break: 230 %
- Elongation at Break: 207 % @Temperature 121 °C, Time 605000 sec
$ 1513/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 19.95 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 52.0 MPa
$ 1596/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1495/MT
- Specific Gravity: 1.13 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength, Yield: 31.0 MPa
- Elongation at Break: 140 %
$ 2128/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 17 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1446/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 17 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1580/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 28.4 MPa @Thickness 3.20 mm
- Elongation at Break: 45 % @Thickness 3.20 mm
$ 1497/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 17 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1749/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 17 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 2517/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 17 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1640/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 28.4 MPa @Thickness 3.20 mm
- Elongation at Break: 45 % @Thickness 3.20 mm
$ 1862/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 17 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1563/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 111
$ 1714/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1684/MT
- Specific Gravity: 0.903 g/cc
- Mooney Viscosity: 23 @Temperature 121 °C
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 88
- Tensile Strength at Break: 24.5 MPa
$ 1893/MT
- Density: 1.09 g/cc
- Water Absorption: 0.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.006 - 0.008 cm/cm @Thickness 3.00 mm
- Linear Mold Shrinkage, Flow: 0.007 - 0.009 cm/cm @Thickness 2.00 mm
- Linear Mold Shrinkage, Transverse: 0.007 - 0.009 cm/cm @Thickness 3.00 mm
$ 1693/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
- Tensile Strength, Yield: 54.0 MPa
- Elongation at Break: >= 150 %
$ 1459/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1560/MT
- Water Absorption: 0.20 %
- Water Absorption: 0.20 %
- Water Absorption: 0.35 %
- Water Absorption: 0.65 %
- Flexural Yield Strength: 0.197 MPa
$ 1737/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 2.8 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 49.1 MPa
$ 1544/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 1460/MT
- Specific Gravity: 0.910 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.5 MPa @Thickness 3.20 mm
$ 1605/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 47.1 MPa @Thickness 3.20 mm
- Elongation at Break: 13 % @Thickness 3.20 mm
$ 1482/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1579/MT
- Specific Gravity: 1.12 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 62.0 MPa
$ 1902/MT
- Specific Gravity: <= 0.953 g/cc
- Viscosity: 0.503 cP
- Vapor Pressure: 0.111 bar @Temperature 20.0 °C
- Melting Point: -75.0 °C
- Boiling Point: 80.3 °C
$ 1739/MT
- Maximum Moisture Content: 0.010
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 47.6 MPa @Thickness 3.20 mm
- Elongation at Break: 35 % @Thickness 3.20 mm
$ 1509/MT
- Specific Gravity: 1.48 g/cc
- Linear Mold Shrinkage: 0.017 - 0.020 cm/cm
- Hardness, Rockwell M: 70
- Tensile Strength at Break: 54.0 MPa
- Elongation at Break: 35 %
$ 1516/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 40 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 26.5 MPa
- Elongation at Break: >= 50 %
$ 1783/MT
- Specific Gravity: 0.940 g/cc
- Volatiles: <= 0.50 %
- Viscosity: 35 cP
- Melt Flow: <= 1.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 77
$ 2398/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 300 °C
- Tensile Strength, Yield: 58.8 MPa @Thickness 3.20 mm
- Elongation at Break: >= 14 % @Thickness 3.20 mm
$ 1468/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 34.3 MPa
- Elongation at Break: <= 500 %
$ 1449/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0090 - 0.013 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 29.4 MPa @Thickness 3.20 mm
$ 2428/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Tensile Strength, Yield: 14.0 MPa
- Elongation at Break: >= 500 %
$ 1584/MT
- Water Absorption: 0.70 %
- Water Absorption: 0.72 %
- Water Absorption: 0.95 %
- Water Absorption: 1.25 %
- Flexural Yield Strength: 0.186 MPa
$ 1483/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 1647/MT
- Water Absorption: 0.42 %
- Water Absorption: 0.45 %
- Water Absorption: 0.72 %
- Water Absorption: 0.75 %
- Flexural Yield Strength: 0.176 MPa
$ 1501/MT
- Specific Gravity: 1.16 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 90
$ 1998/MT
- Specific Gravity: 1.25 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 115
$ 1729/MT
- Specific Gravity: 1.14 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.5 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 116
$ 1562/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 17 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1808/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Break: 60 %
$ 1514/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1784/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 101
$ 1734/MT
- Specific Gravity: 1.48 g/cc
- Water Absorption: 0.70 %
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0040 - 0.011 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 122
$ 1908/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 11.5 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1589/MT
- Maximum Moisture Content: 0.010
- Melt Flow: 11 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 87
- Tensile Strength, Yield: 37.3 MPa @Thickness 3.20 mm
- Elongation at Break: >= 10 % @Thickness 3.20 mm
$ 2586/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2092/MT
- Specific Gravity: 1.406 g/cc
- Bulk Density: 0.280 - 0.400 g/cc
- Volatiles: <= 1.5 % @Temperature 110 °C, Time 3600 sec
- Brookfield Viscosity: 3000 - 8000 cP
- Viscosity Measurement: >= 1.0 @Pressure 0.400 MPa
$ 2368/MT
- Specific Gravity: 1.12 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 1738/MT
- Specific Gravity: 1.406 g/cc
- Bulk Density: 0.280 - 0.400 g/cc
- Volatiles: <= 1.5 % @Temperature 110 °C, Time 3600 sec
- Brookfield Viscosity: 3000 - 8000 cP
- Viscosity Measurement: >= 1.0 @Pressure 0.400 MPa
$ 1613/MT
- Specific Gravity: 0.885 g/cc
- Mooney Viscosity: 20 @Temperature 121 °C
- Melt Flow: 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 82
- Tensile Strength at Break: 17.3 MPa
$ 1521/MT
- Specific Gravity: 0.990 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 49.0 MPa @Thickness 3.20 mm
$ 1740/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1486/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 16.8 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 48.0 MPa
$ 1496/MT
- Specific Gravity: 1.52 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 70
$ 2061/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1468/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1676/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 0.40 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Index of Compound: 5.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 58
$ 1713/MT
- Specific Gravity: 0.918 - 0.922 g/cc
- Melt Flow: 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 37.3 MPa
- Film Elongation at Break, MD: 670 %
- Film Elongation at Break, TD: 770 %
$ 1511/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 1.47 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 44.0 MPa
$ 1676/MT
- Specific Gravity: 1.14 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 114
$ 1564/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Index of Compound: 27 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 62.0 MPa
$ 1532/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0010 - 0.0020 cm/cm
- Hardness, Rockwell M: 80
- Tensile Strength at Break: 98.0 MPa
- Elongation at Break: <= 10 %
$ 2318/MT
- Specific Gravity: >= 0.961 g/cc
- Environmental Stress Crack Resistance: >= 20 hour
- Melt Flow: 0.14 - 0.22 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 30.4 MPa
- Elongation at Break: >= 800 % @Thickness 50.0 mm
$ 1476/MT
- Specific Gravity: 0.960 g/cc
- Melt Flow: 40 g/10 min @Load 10.0 kg, Temperature 230 °C
- Hardness, Shore D: 72 - 78
- Tensile Strength at Break: 4.41 MPa @Thickness 2.00 mm
- Elongation at Break: 300 % @Thickness 2.00 mm
$ 1764/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: 500 %
$ 2215/MT
- Specific Gravity: 1.03 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Break: 300 %
$ 1758/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Index of Compound: 27 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 62.0 MPa
$ 1877/MT
- Specific Gravity: 0.970 - 0.990 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 17.7 MPa @Thickness 3.20 mm
$ 1963/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 99
- Tensile Strength, Yield: 27.5 MPa
$ 1486/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 2.5 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1641/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0090 - 0.011 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.5 MPa @Thickness 3.20 mm
$ 1685/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 1.7 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 98
$ 2105/MT
- Specific Gravity: 1.36 g/cc
- Maximum Moisture Content: 0.040
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 103 MPa @Thickness 3.20 mm
$ 1890/MT
- Specific Gravity: 1.32 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength, Yield: 29.0 MPa
- Elongation at Break: 20 %
$ 1462/MT
- Specific Gravity: 1.95 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 73.5 MPa @Thickness 3.20 mm
- Elongation at Break: >= 5.0 % @Thickness 3.20 mm
$ 1821/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 6.825 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 52.0 MPa
$ 2394/MT
- Specific Gravity: 1.13 g/cc
- Linear Mold Shrinkage: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Break: 35 %
$ 1730/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 24.5 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 34.3 MPa
- Elongation at Break: <= 500 %
$ 1976/MT
- Specific Gravity: 0.933 - 0.938 g/cc
- Melt Flow: 0.30 - 1.7 g/10 min @Load 2.61 kg, Temperature 190 °C
- Tensile Strength, Ultimate: 21.6 MPa
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 700 %
$ 1793/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 30 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1740/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 80
$ 1454/MT
- Specific Gravity: 1.406 g/cc
- Bulk Density: 0.290 - 0.390 g/cc
- Brookfield Viscosity: 4300 - 4700 cP
- Viscosity Measurement: >= 1.0 @Pressure 0.400 MPa
- Molecular Weight: 60000 - 150000 g/mol
$ 1598/MT
- Specific Gravity: 0.921 g/cc
- Water Vapor Transmission: 12.0 g/m²/day
- Oxygen Transmission Rate: 2000 cc/m²/day
- Nitrogen Transmission: 3500 cc-mm/m²-24hr-atm
- Environmental Stress Crack Resistance: >= 500 hour
$ 1593/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 54.9 MPa @Thickness 3.20 mm
$ 1587/MT
- Specific Gravity: 0.953 - 0.956 g/cc
- Environmental Stress Crack Resistance: >= 30 hour
- Melt Flow: 0.30 - 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 26.5 MPa
- Elongation at Break: >= 800 % @Thickness 50.0 mm
$ 1930/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 101
$ 1683/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1531/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 260 °C
- Tensile Strength, Yield: 60.8 MPa @Thickness 3.20 mm
$ 1456/MT
- Specific Gravity: 0.916 g/cc
- Melt Flow: 24 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 45
- Tensile Strength at Break: 13.0 MPa
- Tensile Strength, Yield: 9.32 MPa
$ 1789/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 43 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 106
$ 1716/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 43 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 106
$ 1617/MT
- Specific Gravity: 1.16 g/cc
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1453/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 70 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1577/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 58.8 MPa @Thickness 3.20 mm
- Elongation at Break: >= 100 % @Thickness 3.20 mm
$ 2026/MT
- Specific Gravity: 1.406 g/cc
- Bulk Density: 0.310 - 0.410 g/cc
- Volatiles: <= 0.70 % @Temperature 110 °C, Time 3600 sec
- Brookfield Viscosity: 15000 - 45000 cP
- Viscosity Measurement: >= 2.0
$ 2073/MT
- Specific Gravity: 0.970 - 1.00 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 18.6 MPa @Thickness 3.20 mm
$ 1540/MT
- Specific Gravity: 1.06 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0090 - 0.011 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa @Thickness 3.20 mm
$ 2072/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 30 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1504/MT
- Specific Gravity: 1.12 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 42 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 93
$ 1481/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2080/MT
- Specific Gravity: 1.49 g/cc
- Water Absorption: 0.90 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.011 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 127 MPa @Thickness 3.20 mm
$ 1570/MT
- Specific Gravity: 1.14 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 111
$ 1610/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 300 °C
- Tensile Strength, Yield: 167 MPa @Thickness 3.20 mm
- Elongation at Break: >= 8.0 % @Thickness 3.20 mm
$ 2299/MT
- Specific Gravity: 0.912 - 0.916 g/cc
- Melt Flow: 3.8 - 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 630 %
- Film Elongation at Break, TD: 720 %
- Elmendorf Tear Strength MD: 26 g
$ 1523/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 300 °C
- Tensile Strength, Yield: 167 MPa @Thickness 3.20 mm
- Elongation at Break: >= 8.0 % @Thickness 3.20 mm
$ 2064/MT
- Specific Gravity: 1.40 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 55.9 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1761/MT
- Specific Gravity: 0.940 g/cc
- Volatiles: <= 0.50 %
- Viscosity: 1140 cP
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 70
$ 1730/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 94
$ 1646/MT
- Density: 1.31 g/cc
- Water Absorption: 0.080 %
- Linear Mold Shrinkage: 0.012 - 0.021 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Ultimate: 56.5 MPa @Thickness 3.17 mm
$ 1958/MT
- Density: 1.31 g/cc
- Water Absorption: 0.080 %
- Linear Mold Shrinkage: 0.012 - 0.021 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Ultimate: 56.5 MPa @Thickness 3.17 mm
$ 1587/MT
- Density: 1.31 g/cc
- Water Absorption: 0.080 %
- Linear Mold Shrinkage: 0.012 - 0.021 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Ultimate: 56.5 MPa @Thickness 3.17 mm
$ 1695/MT
- Density: 1.31 g/cc
- Water Absorption: 0.080 %
- Linear Mold Shrinkage: 0.012 - 0.021 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Ultimate: 56.5 MPa @Thickness 3.17 mm
$ 2232/MT
- Density: 1.31 g/cc
- Water Absorption: 0.080 %
- Linear Mold Shrinkage: 0.012 - 0.021 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Ultimate: 56.5 MPa @Thickness 3.17 mm
$ 1898/MT
- Specific Gravity: 1.41 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.018 - 0.021 cm/cm @Thickness 3.20 mm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 82
$ 1836/MT
- Density: 1.31 g/cc
- Water Absorption: 0.080 %
- Linear Mold Shrinkage: 0.012 - 0.021 cm/cm
- Hardness, Rockwell R: 115
- Tensile Strength, Ultimate: 56.5 MPa @Thickness 3.17 mm
$ 2475/MT
- Specific Gravity: 0.890 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 80
- Tensile Strength, Yield: 22.6 MPa
- Elongation at Break: 500 %
$ 1565/MT
- Specific Gravity: 1.12 g/cc
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
- Melt Flow: 50 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1859/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2017/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 115
$ 1510/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.4 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 102
$ 2283/MT
- Specific Gravity: 0.928 - 0.932 g/cc
- Melt Flow: 0.80 - 1.2 g/10 min @Load 2.61 kg, Temperature 190 °C
- Tensile Strength, Ultimate: 19.6 MPa
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 650 %
$ 1731/MT
- Specific Gravity: 1.22 g/cc
- Water Absorption: 0.080 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 55.9 MPa @Thickness 3.20 mm
$ 2025/MT
- Specific Gravity: 1.06 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 105
$ 1688/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 21 g/10 min @Load 2.16 kg, Temperature 300 °C
- Tensile Strength, Yield: 93.2 MPa @Thickness 3.20 mm
- Elongation at Break: >= 6.0 % @Thickness 3.20 mm
$ 2174/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1608/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 99
$ 1669/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.50 % @Temperature 23.0 °C, Time 86400 sec
- Melt Flow: 1.0 g/10 min @Load 2.16 kg, Temperature 235 °C
- Tensile Strength, Yield: 41.7 MPa @Thickness 3.20 mm
- Elongation at Break: 330 % @Thickness 3.20 mm
$ 1953/MT
- Specific Gravity: 1.13 g/cc
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 116
- Tensile Strength, Yield: 55.9 MPa @Thickness 3.20 mm
- Elongation at Break: 28 % @Thickness 3.20 mm
$ 1451/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 18 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 105
$ 1736/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1744/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1549/MT
- Specific Gravity: 1.53 g/cc
- Linear Mold Shrinkage: 0.013 - 0.016 cm/cm
- Hardness, Rockwell M: 80
- Tensile Strength at Break: 61.0 MPa
- Elongation at Break: 7.0 %
$ 1537/MT
- Specific Gravity: 0.960 g/cc
- Volatiles: <= 0.50 %
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 90
- Flash Point: 288 °C
- Styrene Content: 41 %
$ 1510/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Index of Compound: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 61.0 MPa
$ 2247/MT
- Specific Gravity: 0.970 - 1.00 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 17.7 MPa @Thickness 3.20 mm
$ 1804/MT
- Specific Gravity: 1.53 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 cm/cm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 172 MPa
$ 1574/MT
- Specific Gravity: 1.52 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 57.9 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1795/MT
- Specific Gravity: 1.52 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.012 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 52.0 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1830/MT
- Specific Gravity: 1.22 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 59.8 MPa @Thickness 3.20 mm
- Elongation at Break: >= 100 % @Thickness 3.20 mm
$ 1551/MT
- Specific Gravity: 1.30 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.012 - 0.020 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 52.0 MPa @Thickness 3.20 mm
- Elongation at Break: >= 100 % @Thickness 3.20 mm
$ 2386/MT
- Specific Gravity: 1.10 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0070 - 0.012 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 34.3 MPa @Thickness 3.20 mm
$ 2351/MT
- Specific Gravity: 1.06 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 24.5 MPa @Thickness 3.20 mm
$ 1649/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 1489/MT
- Specific Gravity: 1.12 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 115
$ 1485/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 82
- Tensile Strength, Yield: 25.5 MPa
- Film Elongation at Break, MD: >= 500 %
$ 1449/MT
- Specific Gravity: 1.43 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 120
$ 1632/MT
- Specific Gravity: 1.22 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 59.8 MPa @Thickness 3.20 mm
- Elongation at Break: >= 100 % @Thickness 3.20 mm
$ 2395/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 1489/MT
- Specific Gravity: 1.40 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 113 MPa @Thickness 3.20 mm
- Elongation at Break: 2.0 % @Thickness 3.20 mm
$ 1606/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 2.5 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1973/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 105
- Tensile Strength, Yield: 30.4 MPa
- Flexural Modulus: 1.72 GPa
$ 1962/MT
- Density: 1.51 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage: 0.0030 - 0.0090 cm/cm
- Hardness, Rockwell R: 91
- Tensile Strength, Yield: 117 MPa
$ 1873/MT
- Specific Gravity: 1.38 g/cc
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.090
- Hardness, Rockwell R: 125
- Tensile Strength, Yield: 123 MPa @Thickness 3.20 mm
$ 2397/MT
- Specific Gravity: 1.31 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.020 - 0.021 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 57.9 MPa @Thickness 3.20 mm
- Elongation at Break: 100 % @Thickness 3.20 mm
$ 1460/MT
- Specific Gravity: 1.30 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 58.8 MPa @Thickness 3.20 mm
- Elongation at Break: 50 % @Thickness 3.20 mm
$ 2538/MT
- Specific Gravity: 1.30 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.018 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 58.8 MPa @Thickness 3.20 mm
- Elongation at Break: 40 % @Thickness 3.20 mm
$ 1787/MT
- Specific Gravity: 1.28 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.012 - 0.020 cm/cm @Thickness 3.20 mm
- Melt Flow: 45 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 47.1 MPa @Thickness 3.20 mm
$ 1826/MT
- Specific Gravity: 1.28 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.012 - 0.020 cm/cm @Thickness 3.20 mm
- Melt Flow: 35 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 46.1 MPa @Thickness 3.20 mm
$ 1602/MT
- Specific Gravity: 1.30 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.012 - 0.020 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 58.8 MPa @Thickness 3.20 mm
$ 1482/MT
- Specific Gravity: 1.30 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.012 - 0.020 cm/cm @Thickness 3.20 mm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 50.0 MPa @Thickness 3.20 mm
$ 1461/MT
- Specific Gravity: 1.42 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Tensile Strength, Yield: 61.0 MPa
- Elongation at Break: 20 %
$ 2099/MT
- Specific Gravity: 1.42 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.012 - 0.020 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 51.0 MPa @Thickness 3.20 mm
$ 1974/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
- Tensile Strength, Yield: 54.0 MPa
- Elongation at Break: 60 %
$ 1574/MT
- Specific Gravity: 1.47 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.012 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 58.8 MPa @Thickness 3.20 mm
- Elongation at Break: 4.0 % @Thickness 3.20 mm
$ 1614/MT
- Specific Gravity: 1.37 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0060 - 0.012 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 78.5 MPa @Thickness 3.20 mm
- Elongation at Break: 4.0 % @Thickness 3.20 mm
$ 1459/MT
- Specific Gravity: 1.52 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 118 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1965/MT
- Specific Gravity: 1.53 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 123 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1983/MT
- Specific Gravity: 1.62 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 123 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1880/MT
- Specific Gravity: 1.62 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 127 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1695/MT
- Specific Gravity: 1.62 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 118 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1473/MT
- Specific Gravity: 1.62 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 127 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1791/MT
- Specific Gravity: 1.61 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 127 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1599/MT
- Specific Gravity: 1.37 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.011 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 74.5 MPa @Thickness 3.20 mm
- Elongation at Break: 5.0 % @Thickness 3.20 mm
$ 1867/MT
- Specific Gravity: 1.39 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.011 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 83.4 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1601/MT
- Specific Gravity: 1.44 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength, Yield: 100 MPa
- Elongation at Break: 4.5 %
$ 1447/MT
- Specific Gravity: 1.30 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.012 - 0.020 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 50.0 MPa @Thickness 3.20 mm
- Elongation at Break: >= 100 % @Thickness 3.20 mm
$ 1624/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.021 cm/cm
- Tensile Strength, Yield: 54.0 MPa
- Elongation at Break: >= 100 %
$ 2032/MT
- Specific Gravity: 1.40 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 53.9 MPa @Thickness 3.20 mm
- Elongation at Break: 40 % @Thickness 3.20 mm
$ 2186/MT
- Specific Gravity: 1.60 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength, Yield: 95.0 MPa
- Elongation at Break: 7.0 %
$ 1660/MT
- Specific Gravity: 1.57 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 98.1 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1501/MT
- Density: 1.52 g/cc
- Water Absorption: 0.070 %
- Linear Mold Shrinkage: 0.0040 - 0.011 cm/cm
- Hardness, Rockwell R: 90
- Tensile Strength, Ultimate: 97.9 MPa @Thickness 3.17 mm
$ 2363/MT
- Density: 1.62 g/cc
- Water Absorption: 0.060 %
- Hardness, Rockwell R: 92
- Tensile Strength, Ultimate: 132.4 MPa @Thickness 3.17 mm
- Tensile Strength, Yield: 128 MPa
$ 1462/MT
- Density: 1.34 g/cc
- Tensile Strength, Ultimate: 124.1 MPa @Thickness 3.17 mm
- Tensile Strength, Yield: 70.3 MPa
- Elongation at Break: 7.0 %
- Flexural Yield Strength: 70.3 MPa
$ 1450/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage: 0.0080 - 0.013 cm/cm @Thickness 1.00 - 2.50 mm
- Linear Mold Shrinkage: 0.010 - 0.015 cm/cm @Thickness 2.50 - 5.00 mm
- Tensile Strength at Break: 50.3 MPa
- Elongation at Break: 25 % @Thickness 3.17 mm
$ 1998/MT
- Density: 1.34 g/cc
- Tensile Strength, Yield: 50.3 MPa
- Elongation at Break: 30 %
- Flexural Yield Strength: 78.1 MPa @Thickness 3.17 mm
- Flexural Modulus: 1.93 GPa @Thickness 3.17 mm
$ 1483/MT
- Density: 1.55 g/cc
- Water Absorption: 0.060 %
- Linear Mold Shrinkage: 0.0030 - 0.0090 cm/cm
- Hardness, Rockwell R: 91
- Tensile Strength, Yield: 117 MPa
$ 1918/MT
- Specific Gravity: 1.45 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.015 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 53.0 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1629/MT
- Specific Gravity: 1.54 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.012 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 53.9 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1541/MT
- Specific Gravity: 1.54 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.012 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 44.1 MPa @Thickness 3.20 mm
- Elongation at Break: 3.5 % @Thickness 3.20 mm
$ 1679/MT
- Specific Gravity: 1.43 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 93.2 MPa @Thickness 3.20 mm
- Elongation at Break: 4.0 % @Thickness 3.20 mm
$ 1481/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 48 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 1851/MT
- Specific Gravity: 0.928 - 0.932 g/cc
- Melt Flow: 0.80 - 1.2 g/10 min @Load 2.61 kg, Temperature 190 °C
- Tensile Strength, Ultimate: 19.6 MPa
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 650 %
$ 1768/MT
- Specific Gravity: 1.08 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 10 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 2067/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 110
$ 1806/MT
- Specific Gravity: 1.25 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 124
$ 2066/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 2060/MT
- Specific Gravity: 1.44 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 cm/cm
- Tensile Strength, Yield: 132 MPa
- Elongation at Break: 4.0 %
$ 1715/MT
- Specific Gravity: 1.35 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
$ 2321/MT
- Specific Gravity: 1.35 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
$ 1975/MT
- Specific Gravity: 1.35 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
$ 1853/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 85.3 MPa @Thickness 3.20 mm
$ 1528/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 43 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1809/MT
- Specific Gravity: 1.53 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm
- Tensile Strength, Yield: 110 MPa
- Elongation at Break: 4.0 %
$ 1460/MT
- Specific Gravity: 1.40 g/cc
- Bulk Density: 0.520 - 0.600 g/cc
- Volatiles: <= 0.30 % @Temperature 110 °C, Time 3600 sec
- Particle Mesh Size: 45 Mesh
- Molecular Weight: 60000 - 150000 g/mol
$ 2210/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 18 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1475/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 34 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 34.3 MPa
- Flexural Modulus: 1.57 GPa
$ 1919/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 1.1 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 98
$ 1648/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1661/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 113
- Tensile Strength, Yield: 40.3 MPa
$ 1517/MT
- Specific Gravity: 1.25 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 117
$ 1461/MT
- Density: 1.41 g/cc
- Water Absorption: 0.22 %
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 82
$ 1758/MT
- Specific Gravity: 1.36 - 1.38 g/cc
- Bulk Density: 0.300 - 0.400 g/cc
- Volatiles: <= 0.30 % @Temperature 110 °C, Time 3600 sec
- Brookfield Viscosity: 4000 - 20000 cP
- Viscosity Measurement: >= 1.0
$ 2354/MT
- Specific Gravity: 1.61 g/cc
- Linear Mold Shrinkage: 0.013 cm/cm
- Hardness, Rockwell R: 81
- Tensile Strength at Break: 24.0 MPa
- Elongation at Break: 58 %
$ 2477/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 109
$ 1908/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm
- Tensile Strength, Yield: 69.0 MPa
- Elongation at Break: 6.0 %
$ 1703/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 28 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1905/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 109
- Tensile Strength, Yield: 47.1 MPa @Thickness 3.20 mm
- Elongation at Break: 30 % @Thickness 3.20 mm
$ 2554/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 37 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 1675/MT
- Specific Gravity: 1.06 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 30.4 MPa @Thickness 3.20 mm
$ 1677/MT
- Specific Gravity: 1.03 g/cc
- Maximum Moisture Content: 0.010
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 15 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 65 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1785/MT
- Specific Gravity: 0.920 g/cc
- Volatiles: <= 0.50 %
- Melt Flow: 7.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 62
- Flash Point: 288 °C
$ 1679/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 2035/MT
- Specific Gravity: 1.23 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 2028/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2518/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 33 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 2165/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 59.8 MPa @Thickness 3.20 mm
- Elongation at Break: >= 100 % @Thickness 3.20 mm
$ 1989/MT
- Specific Gravity: 1.10 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 39.2 MPa @Thickness 3.20 mm
$ 1693/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 52 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 104
$ 1464/MT
- Density: 1.07 g/cc
- Water Absorption: 0.3 % @Time 86400 sec
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Tensile Strength, Yield: 41.2 MPa @Thickness 3.20 mm
- Elongation at Break: 25 % @Thickness 3.17 mm
$ 1622/MT
- Specific Gravity: 0.921 g/cc
- Water Vapor Transmission: 12.0 g/m²/day
- Oxygen Transmission Rate: 2000 cc/m²/day
- Nitrogen Transmission: 3500 cc-mm/m²-24hr-atm
- Melt Flow: 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1925/MT
- Specific Gravity: 1.52 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 95.1 MPa @Thickness 3.20 mm
- Elongation at Break: 4.0 % @Thickness 3.20 mm
$ 1580/MT
- Specific Gravity: 1.45 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 98.1 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1651/MT
- Specific Gravity: 1.00 - 1.05 g/cc
- Solids Content: 49.5 - 50.5 % @Temperature 130 °C, Time 1800 sec
- Particle Size: 115 - 135 µm
- pH: 6.5 - 7.5
- Viscosity: <= 200 cP @Time 60.0 sec
- Surface Tension: 35 - 50 dynes/cm
$ 1769/MT
- Specific Gravity: 1.14 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 29.4 MPa @Thickness 3.20 mm
$ 1514/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 37 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 97
$ 1767/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 56.7 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 50.0 MPa
$ 1525/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 40 g/10 min
- Hardness, Rockwell R: 93
- Tensile Strength at Break: 37.46 MPa
$ 2084/MT
- Specific Gravity: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 60 g/10 min @Load 2.16 kg, Temperature 300 °C
- Tensile Strength, Yield: 98.1 MPa @Thickness 3.20 mm
- Elongation at Break: >= 7.0 % @Thickness 3.20 mm
$ 2217/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 40 g/10 min
- Hardness, Rockwell R: 93
- Tensile Strength at Break: 37.46 MPa
$ 1719/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 21 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 54.9 MPa @Thickness 3.20 mm
$ 1575/MT
- Specific Gravity: 0.910 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.0 MPa @Thickness 3.20 mm
$ 1684/MT
- Specific Gravity: 1.28 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 56.9 MPa @Thickness 3.20 mm
- Elongation at Break: >= 50 % @Thickness 3.20 mm
$ 2535/MT
- Specific Gravity: 1.28 g/cc
- Water Absorption: 0.80 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.010 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 127 MPa @Thickness 3.20 mm
$ 1847/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.5 MPa @Thickness 3.20 mm
$ 1448/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 113
$ 1944/MT
- Specific Gravity: 1.66 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 108 MPa @Thickness 3.20 mm
- Elongation at Break: >= 4.0 % @Thickness 3.20 mm
$ 1623/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 93
- Tensile Strength, Yield: 27.5 MPa
$ 1938/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1594/MT
- Specific Gravity: 0.920 g/cc
- Volatiles: <= 0.50 %
- Melt Flow: 13 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 51
- Flash Point: 288 °C
$ 1643/MT
- Specific Gravity: 1.13 g/cc
- Linear Mold Shrinkage: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength, Yield: 44.0 MPa
- Elongation at Break: >= 100 %
$ 1522/MT
- Specific Gravity: 1.03 g/cc
- Maximum Moisture Content: 0.010
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 8.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 37 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1689/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 0.60 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 49.0 MPa @Thickness 3.20 mm
- Elongation at Break: 37 % @Thickness 3.20 mm
$ 1752/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1849/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 220 °C
$ 1450/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1899/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 2059/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1526/MT
- Specific Gravity: 1.59 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Hardness, Rockwell M: 85
- Tensile Strength at Break: 91.0 MPa
- Elongation at Break: 5.0 %
$ 1986/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 25.5 MPa
- Elongation at Break: >= 500 %
$ 1836/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1451/MT
- Specific Gravity: 0.940 g/cc
- Volatiles: <= 0.50 %
- Viscosity: 30.5 cP
- Melt Flow: <= 1.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 85
$ 1748/MT
- Specific Gravity: 1.02 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 92
$ 2132/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 10 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 2432/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 3.4 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 32 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 124
$ 1460/MT
- Specific Gravity: 1.27 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.012 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 103 MPa @Thickness 3.20 mm
$ 1556/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 98
$ 1717/MT
- Specific Gravity: 1.00 - 1.05 g/cc
- Solids Content: 49.5 - 50.5 % @Temperature 130 °C, Time 1800 sec
- Particle Size: 70 - 90 µm
- pH: 7.5 - 8.5
- Viscosity: <= 400 cP @Time 60.0 sec
- Surface Tension: 35 - 45 dynes/cm
$ 1461/MT
- Specific Gravity: 0.952 g/cc
- Environmental Stress Crack Resistance: >= 200 hour
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 63
- Tensile Strength, Yield: 23.5 MPa
$ 1498/MT
- Specific Gravity: 1.03 g/cc
- Melting Point: 220 - 230 °C
$ 1946/MT
- Specific Gravity: 0.922 g/cc
- Degree of Crosslinking: >= 60 %
- Tensile Strength at Break: 19.7 MPa
- Tensile Strength at Break: 18.715 MPa @Temperature 136 °C, Time 605000 sec
- Elongation at Break: 550 %
$ 1789/MT
- Specific Gravity: 1.14 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 111
$ 1582/MT
- Specific Gravity: 1.45 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.010 cm/cm
- Hardness, Rockwell M: 85
- Tensile Strength at Break: 94.0 MPa
- Elongation at Break: 5.0 %
$ 2094/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2160/MT
- Specific Gravity: 1.40 g/cc
- Bulk Density: 0.460 - 0.540 g/cc
- Volatiles: <= 0.30 % @Temperature 110 °C, Time 3600 sec
- Particle Mesh Size: 45 Mesh
- Molecular Weight: 60000 - 150000 g/mol
$ 1829/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.5 MPa @Thickness 3.20 mm
$ 1905/MT
- Specific Gravity: 1.12 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 24.5 MPa @Thickness 3.20 mm
$ 1713/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 97
- Tensile Strength, Yield: 29.5 MPa
$ 1740/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 98
$ 1945/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 4.41 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 42.0 MPa
$ 2280/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 53 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 1920/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage: 0.020 - 0.022 cm/cm
- Hardness, Rockwell M: 80
- Tensile Strength at Break: 54.0 MPa
- Elongation at Break: 70 %
$ 1808/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 99
- Tensile Strength, Yield: 28.5 MPa
$ 1834/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 34.3 MPa
- Elongation at Break: <= 500 %
$ 2589/MT
- Specific Gravity: 1.48 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.0060 - 0.011 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 83
$ 1685/MT
- Specific Gravity: 1.48 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.0060 - 0.011 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 83
$ 1925/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1487/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 28.4 MPa
- Elongation at Break: <= 500 %
$ 2036/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 109
$ 1654/MT
- Specific Gravity: 1.36 - 1.38 g/cc
- Bulk Density: 0.290 - 0.390 g/cc
- Volatiles: <= 1.5 % @Temperature 110 °C, Time 3600 sec
- Brookfield Viscosity: 5000 - 9000 cP
- Viscosity Measurement: >= 1.0 @Pressure 0.400 MPa
$ 2414/MT
- Specific Gravity: 1.406 g/cc
- Bulk Density: 0.310 - 0.410 g/cc
- Volatiles: <= 0.30 % @Temperature 110 °C, Time 3600 sec
- Brookfield Viscosity: 1500 - 5500 cP
- Viscosity Measurement: >= 3.0
$ 1837/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1471/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.012 - 0.014 cm/cm @Thickness 3.20 mm
- Melt Flow: 24 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
$ 1946/MT
- Density: 1.18 g/cc
- Melt Flow: 9.5 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength, Yield: 95.1 MPa @Thickness 3.20 mm
- Elongation at Break: 7.0 % @Thickness 3.17 mm
- Flexural Strength: 137 MPa @Thickness 3.20 mm
$ 1673/MT
- Specific Gravity: 1.43 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.010 - 0.030 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 300 °C
- Hardness, Rockwell R: 120
$ 1543/MT
- Specific Gravity: 1.00 - 1.05 g/cc
- Solids Content: 49.5 - 50.5 % @Temperature 130 °C, Time 1800 sec
- Particle Size: 105 - 135 µm
- pH: 7.5 - 8.5
- Viscosity: <= 600 cP @Time 60.0 sec
- Surface Tension: 35 - 50 dynes/cm
$ 2271/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 23 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 90
$ 1910/MT
- Specific Gravity: 1.37 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 38 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 53.9 MPa @Thickness 3.20 mm
$ 1581/MT
- Specific Gravity: 1.95 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 40 g/10 min @Load 5.00 kg, Temperature 320 °C
- Tensile Strength, Yield: 49.0 MPa @Thickness 3.20 mm
$ 1644/MT
- Specific Gravity: 1.31 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0060 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 58.8 MPa @Thickness 3.20 mm
- Elongation at Break: >= 100 % @Thickness 3.20 mm
$ 1801/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 1853/MT
- Specific Gravity: 1.406 g/cc
- Bulk Density: 0.290 - 0.390 g/cc
- Volatiles: <= 1.5 % @Temperature 110 °C, Time 3600 sec
- Brookfield Viscosity: 3000 - 4000 cP
- Viscosity Measurement: >= 1.0 @Pressure 0.400 MPa
$ 1596/MT
- Specific Gravity: 0.930 g/cc
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 230 °C
- Hardness, Shore D: <= 92
- Elongation at Break: 700 % @Thickness 2.00 mm
- Izod Impact, Notched: NB @Thickness 6.40 mm, Temperature 23.0 °C
$ 1566/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 26.5 MPa
- Elongation at Break: <= 500 %
$ 1807/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1929/MT
- Specific Gravity: 1.31 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.017 - 0.020 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 64
$ 1479/MT
- Specific Gravity: 1.45 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 290 °C
- Tensile Strength, Yield: 118 MPa @Thickness 3.20 mm
$ 1741/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 37 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 1474/MT
- Specific Gravity: 1.49 g/cc
- Water Absorption: 1.0 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 211 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 2316/MT
- Specific Gravity: 1.00 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 73.5 MPa @Thickness 3.20 mm
$ 1700/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 2424/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 59.0 MPa
$ 1802/MT
- Specific Gravity: 1.03 g/cc
- Melting Point: 220 - 230 °C
$ 1796/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 1.1 %
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 121
$ 2009/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 21 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2009/MT
- Specific Gravity: 1.03 g/cc
- Maximum Moisture Content: 0.010
- Melt Flow: 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 19 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 80 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1525/MT
- Specific Gravity: 1.406 g/cc
- Bulk Density: 0.310 - 0.410 g/cc
- Volatiles: <= 0.30 % @Temperature 110 °C, Time 3600 sec
- Brookfield Viscosity: 2000 - 6000 cP
- Viscosity Measurement: >= 2.0
$ 2191/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1556/MT
- Specific Gravity: 0.950 g/cc
- Melt Flow: 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength, Yield: 27.5 MPa
- Elongation at Break: >= 1000 %
$ 1647/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 117
$ 1560/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0035 - 0.0055 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 260 °C
- Tensile Strength, Yield: 70.1 MPa @Thickness 3.20 mm
$ 2213/MT
- Specific Gravity: 0.970 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.013 - 0.015 cm/cm @Thickness 3.20 mm
- Melt Flow: 23 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.5 MPa @Thickness 3.20 mm
$ 1843/MT
- Specific Gravity: 0.870 g/cc
- Mooney Viscosity: 9.0 @Temperature 121 °C
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 5.49 MPa
$ 1626/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 1.7 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 79.4 MPa @Thickness 3.20 mm
$ 2284/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1453/MT
- Specific Gravity: 1.35 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
$ 1706/MT
- Specific Gravity: 1.35 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.010 - 0.030 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
$ 1630/MT
- Specific Gravity: 0.953 g/cc
- Thickness: 10.0 microns
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Tensile Strength at Yield, MD: 37.3 MPa
- Film Tensile Strength at Yield, TD: 35.3 MPa
$ 1575/MT
- Specific Gravity: 1.50 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Tensile Strength, Yield: 110 MPa
- Elongation at Break: 4.0 %
$ 2206/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 5.5 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 46.2 MPa
$ 1603/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 42 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 45.0 MPa
$ 1650/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 117
$ 1798/MT
- Specific Gravity: 0.910 g/cc
- Linear Mold Shrinkage: 0.014 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Strength, Yield: 18.0 MPa
- Elongation at Break: >= 300 %
$ 1668/MT
- Specific Gravity: 1.14 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Hardness, Rockwell M: 84
- Tensile Strength at Break: 71.0 MPa
- Elongation at Break: <= 10 %
$ 2105/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C
LG Chemical LUMAX HR-5306F Heat Resistant PBT, 30% Polymer Alloy, Weather Resistant, Flame Retardant
$ 1915/MT
- Specific Gravity: 1.52 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Tensile Strength, Yield: 125 MPa
- Elongation at Break: 3.0 %
$ 1707/MT
- Specific Gravity: 1.38 g/cc
- Water Absorption: 0.70 %
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 122
$ 1851/MT
- Specific Gravity: 1.00 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 32.4 MPa @Thickness 3.20 mm
$ 1637/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength, Yield: 61.8 MPa @Thickness 3.20 mm
$ 1642/MT
- Specific Gravity: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 54.9 MPa @Thickness 3.20 mm
- Elongation at Break: 30 % @Thickness 3.20 mm
- Flexural Yield Strength: 85.3 MPa @Thickness 3.20 mm
$ 2205/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Index of Compound: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 60.0 MPa
$ 1531/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1538/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 53 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 104
$ 2581/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 84
- Tensile Strength, Yield: 26.5 MPa
- Film Elongation at Break, MD: >= 500 %
$ 2081/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 18 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1857/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 99
$ 1713/MT
- Specific Gravity: 1.38 g/cc
- Water Absorption: 0.70 %
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 122
$ 2406/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 23 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 2492/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 5.8 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 46.2 MPa
$ 1655/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.040
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 57.9 MPa @Thickness 3.20 mm
$ 2389/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 1.3 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 116
- Tensile Strength, Yield: 78.5 MPa @Thickness 3.20 mm
$ 1622/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 1.3 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.0090 - 0.016 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
$ 2284/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 1.7 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.013 - 0.020 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
$ 2321/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 1.7 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 49.0 MPa @Thickness 3.20 mm
- Elongation at Break: 250 % @Thickness 3.20 mm
$ 2544/MT
- Specific Gravity: 1.45 g/cc
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0070 - 0.012 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
$ 1858/MT
- Specific Gravity: 1.22 g/cc
- Water Absorption: 1.3 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.012 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 127 MPa @Thickness 3.20 mm
- Elongation at Break: 5.0 % @Thickness 3.20 mm
$ 2102/MT
- Specific Gravity: 1.22 g/cc
- Water Absorption: 0.090 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 113 MPa @Thickness 3.20 mm
- Elongation at Break: 8.0 % @Thickness 3.20 mm
$ 1504/MT
- Specific Gravity: 1.22 g/cc
- Water Absorption: 1.0 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0070 - 0.012 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 121
$ 1989/MT
- Specific Gravity: 1.50 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0060 - 0.011 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
$ 1588/MT
- Specific Gravity: 1.30 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.010 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 147 MPa @Thickness 3.20 mm
$ 1493/MT
- Specific Gravity: 1.30 g/cc
- Water Absorption: 1.0 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.010 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 157 MPa @Thickness 3.20 mm
$ 1679/MT
- Specific Gravity: 1.60 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0050 - 0.010 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
$ 1594/MT
- Specific Gravity: 1.60 g/cc
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 127 MPa @Thickness 3.20 mm
$ 1493/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 177 MPa @Thickness 3.20 mm
$ 1769/MT
- Specific Gravity: 1.63 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
$ 1818/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 162 MPa @Thickness 3.20 mm
$ 1822/MT
- Specific Gravity: 1.38 g/cc
- Water Absorption: 0.70 %
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0090 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 122
$ 1716/MT
- Specific Gravity: 1.50 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.90
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 122
$ 1556/MT
- Specific Gravity: 1.56 g/cc
- Water Absorption: 0.80 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 221 MPa @Thickness 3.20 mm
$ 1923/MT
- Specific Gravity: 1.57 g/cc
- Water Absorption: 0.50 %
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 122
$ 1855/MT
- Specific Gravity: 1.23 g/cc
- Water Absorption: 1.3 %
- Linear Mold Shrinkage, Flow: 0.0090 - 0.013 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 121
- Elongation at Break: 6.0 % @Thickness 3.20 mm
$ 1601/MT
- Specific Gravity: 1.28 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 73.5 MPa @Thickness 3.20 mm
$ 1462/MT
- Specific Gravity: 1.36 g/cc
- Water Absorption: 0.80 %
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0060 - 0.010 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 115
$ 1536/MT
- Specific Gravity: 1.48 g/cc
- Water Absorption: 0.70 %
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
$ 2276/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 1.4 %
- Linear Mold Shrinkage, Flow: 0.012 - 0.016 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 114
- Tensile Strength, Yield: 66.7 MPa @Thickness 3.20 mm
$ 2369/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 1.3 %
- Linear Mold Shrinkage, Flow: 0.012 - 0.016 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 113
- Tensile Strength, Yield: 63.7 MPa @Thickness 3.20 mm
$ 2364/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 1.1 %
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 110
- Tensile Strength, Yield: 51.0 MPa @Thickness 3.20 mm
$ 2257/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 1.1 %
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 110
$ 1564/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 1.2 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.010 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 96.1 MPa @Thickness 3.20 mm
$ 1508/MT
- Specific Gravity: 1.32 g/cc
- Water Absorption: 1.0 %
- Linear Mold Shrinkage, Flow: 0.0090 - 0.013 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 117
- Tensile Strength, Yield: 68.6 MPa @Thickness 3.20 mm
$ 1488/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.50 % @Temperature 23.0 °C, Time 86400 sec
- Melt Flow: 3.0 g/10 min @Load 12.5 kg, Temperature 260 °C
- Tensile Strength, Yield: 53.9 MPa @Thickness 3.20 mm
- Elongation at Break: 320 % @Thickness 3.20 mm
$ 1940/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 0.50 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.014 - 0.015 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.5 g/10 min @Load 2.16 kg, Temperature 235 °C
- Tensile Strength, Yield: 51.0 MPa @Thickness 3.20 mm
$ 2326/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.70 %
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 44.1 MPa @Thickness 3.20 mm
- Elongation at Break: 100 % @Thickness 3.20 mm
$ 2057/MT
- Specific Gravity: 0.960 g/cc
- Maximum Moisture Content: 0.010
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 12.7 MPa @Thickness 3.20 mm
- Elongation at Break: >= 200 % @Thickness 3.20 mm
$ 1786/MT
- Specific Gravity: 1.10 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.2 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 114
$ 1446/MT
- Specific Gravity: 1.72 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 87
$ 2401/MT
- Specific Gravity: 1.25 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 117
$ 2447/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 58.8 MPa @Thickness 3.20 mm
- Elongation at Break: >= 100 % @Thickness 3.20 mm
$ 2171/MT
- Specific Gravity: 1.25 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 68.6 MPa @Thickness 3.20 mm
- Elongation at Break: 9.0 % @Thickness 3.20 mm
$ 1858/MT
- Specific Gravity: 0.958 g/cc
- Environmental Stress Crack Resistance: 40 hour
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength, Yield: 29.4 MPa @Thickness 3.20 mm
$ 1790/MT
- Specific Gravity: 0.957 g/cc
- Environmental Stress Crack Resistance: 50 hour
- Melt Flow: 0.25 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength, Yield: 30.4 MPa @Thickness 3.20 mm
$ 1678/MT
- Specific Gravity: 0.952 g/cc
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength, Yield: 26.5 MPa
- Elongation at Break: >= 500 %
$ 1469/MT
- Specific Gravity: 0.961 g/cc
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 29.4 MPa
- Elongation at Break: >= 1000 %
$ 1928/MT
- Specific Gravity: 0.957 g/cc
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 65
- Tensile Strength, Yield: 28.4 MPa
- Elongation at Break: >= 1000 %
$ 1801/MT
- Specific Gravity: 0.958 g/cc
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 64
- Tensile Strength, Yield: 28.4 MPa
- Elongation at Break: >= 1000 %
$ 1997/MT
- Specific Gravity: 0.950 g/cc
- Linear Mold Shrinkage: 0.0080 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Yield: 20.0 MPa
- Elongation at Break: >= 300 %
$ 1549/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1638/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Index of Compound: 45 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 62.0 MPa
$ 1684/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 117
$ 2186/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1875/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1671/MT
- Specific Gravity: 1.25 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 1661/MT
- Specific Gravity: 1.52 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 98.1 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 1678/MT
- Specific Gravity: 1.70 g/cc
- Linear Mold Shrinkage: 0.011 cm/cm
- Hardness, Rockwell R: 90
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: <= 10 %
$ 1835/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 2.3 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 51.1 MPa
$ 1749/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1706/MT
- Specific Gravity: 1.38 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.017 - 0.020 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 60
$ 1613/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 97
$ 1529/MT
- Specific Gravity: 0.949 - 0.952 g/cc
- Melt Flow: 0.70 - 0.85 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 50
- Tensile Strength at Break: 28.0 MPa
- Tensile Strength, Yield: 24.5 MPa
$ 1914/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 1957/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 23 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 2174/MT
- Density: 1.07 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 6.955 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 42.0 MPa
$ 1664/MT
- Specific Gravity: 1.06 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0090 - 0.014 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 36.3 MPa @Thickness 3.20 mm
$ 1969/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 61.0 MPa
$ 1689/MT
- Specific Gravity: 0.918 - 0.922 g/cc
- Melt Flow: 2.7 - 3.3 g/10 min @Load 2.61 kg, Temperature 190 °C
- Tensile Strength, Ultimate: 12.3 MPa
- Film Elongation at Break, MD: 300 %
- Film Elongation at Break, TD: 550 %
$ 2523/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 53 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 106
$ 1615/MT
- Specific Gravity: 1.17 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 108
$ 2423/MT
- Specific Gravity: 0.940 g/cc
- Volatiles: <= 0.50 %
- Viscosity: 13.4 cP
- Melt Flow: <= 1.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 79
$ 1875/MT
- Specific Gravity: 1.10 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 46.1 MPa @Thickness 3.20 mm
$ 1501/MT
- Specific Gravity: 1.48 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.0060 - 0.011 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 83
$ 2029/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1713/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 32 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1644/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Hardness, Rockwell M: 95
- Tensile Strength at Break: 142 MPa
- Elongation at Break: <= 10 %
$ 1875/MT
- Specific Gravity: 1.20 g/cc
- Melt Flow: 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 68.0 MPa
- Elongation at Break: 113 %
- Elongation at Yield: 6.0 %
$ 1593/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 1670/MT
- Specific Gravity: 1.39 g/cc
- Linear Mold Shrinkage: 0.020 - 0.022 cm/cm
- Hardness, Rockwell M: 75
- Tensile Strength at Break: 54.0 MPa
- Elongation at Break: 60 %
$ 1540/MT
- Water Absorption: 0.32 %
- Water Absorption: 0.35 %
- Water Absorption: 0.40 %
- Water Absorption: 0.44 %
- Flexural Yield Strength: 0.181 MPa
$ 2537/MT
- Specific Gravity: 0.970 g/cc
- Melt Flow: 30 g/10 min @Load 10.0 kg, Temperature 230 °C
- Hardness, Shore D: 62 - 68
- Tensile Strength at Break: 4.41 MPa @Thickness 2.00 mm
- Elongation at Break: 300 % @Thickness 2.00 mm
$ 1652/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 1809/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 90
- Tensile Strength, Yield: 24.6 MPa
$ 2533/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 52.0 MPa @Thickness 3.20 mm
$ 1539/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 1508/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.015 - 0.017 cm/cm @Thickness 3.50 mm
$ 2050/MT
- Specific Gravity: 0.926 - 0.931 g/cc
- Melt Flow: 0.70 - 0.90 g/10 min @Load 2.61 kg, Temperature 190 °C
- Tensile Strength, Ultimate: 17.7 MPa
- Film Elongation at Break, MD: 400 %
- Film Elongation at Break, TD: 650 %
$ 1458/MT
- Specific Gravity: 1.25 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 37 g/10 min @Load 10.0 kg, Temperature 300 °C
- Tensile Strength, Yield: 98.1 MPa @Thickness 3.20 mm
- Elongation at Break: >= 2.5 % @Thickness 3.20 mm
$ 1570/MT
- Specific Gravity: 1.06 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 97
$ 1504/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Index of Compound: 27 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 62.0 MPa
$ 1500/MT
- Specific Gravity: 0.896 - 0.901 g/cc
- Viscosity: 0.856 cP
- Vapor Pressure: 0.00533 bar @Temperature 20.0 °C
- Melting Point: -64.0 °C
- Boiling Point: 148 °C
$ 1481/MT
- Specific Gravity: 1.65 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 152 MPa @Thickness 3.20 mm
- Elongation at Break: 1.0 - 2.0 % @Thickness 3.20 mm
$ 1723/MT
- Specific Gravity: 1.23 g/cc
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 56
$ 1842/MT
- Specific Gravity: 1.40 g/cc
- Water Absorption: 0.70 %
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0050 - 0.011 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 122
$ 1798/MT
- Specific Gravity: 1.25 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 124
$ 1823/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 3.80 kg, Temperature 200 °C
- Hardness, Rockwell R: 115
$ 1996/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 cm/cm
- Tensile Strength, Yield: 93.0 MPa
- Elongation at Break: 6.0 %
$ 1477/MT
- Specific Gravity: 1.28 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.3 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 115
$ 1661/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.5 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 108 MPa @Thickness 3.20 mm
$ 1509/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm
- Tensile Strength, Yield: 118 MPa
- Elongation at Break: 6.0 %
$ 1514/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0020 cm/cm
- Tensile Strength, Yield: 127 MPa
- Elongation at Break: 5.0 %
$ 1567/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 115
$ 1614/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1661/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1513/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1770/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 2594/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1803/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 60 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 100
$ 1652/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 0.50 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 1546/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 220 °C
- Tensile Strength, Yield: 43.1 MPa @Thickness 3.20 mm
- Elongation at Break: 10 % @Thickness 3.20 mm
$ 2103/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Hardness, Rockwell R: 117
- Tensile Strength, Yield: 59.0 MPa
$ 2108/MT
- Specific Gravity: 1.16 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
- Melt Flow: 3.0 g/10 min @Load 5.00 kg, Temperature 230 °C
$ 2005/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 42 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 45.0 MPa
$ 2455/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 108
$ 1951/MT
- Specific Gravity: 0.918 g/cc
- Water Vapor Transmission: 20.0 g/m²/day @Pressure 0.101 MPa
- Melt Flow: 7.5 g/10 min @Load 2.61 kg, Temperature 190 °C
- Hardness, Shore D: 43
- Tensile Strength at Break: 11.5 MPa
$ 2077/MT
- Specific Gravity: 1.59 g/cc
- Linear Mold Shrinkage: 0.016 - 0.019 cm/cm
- Hardness, Rockwell M: 80
- Tensile Strength at Break: 64.0 MPa
- Elongation at Break: 10 %
$ 1518/MT
- Specific Gravity: 1.24 g/cc
- Water Absorption: 0.30 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 1692/MT
- Specific Gravity: 1.37 g/cc
- Linear Mold Shrinkage: 0.017 - 0.020 cm/cm
- Hardness, Rockwell M: 65
- Tensile Strength at Break: 48.0 MPa
- Elongation at Break: 120 %
$ 2254/MT
- Specific Gravity: 1.34 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 8.0 %
$ 1581/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 22 g/10 min
- Hardness, Rockwell R: 112
- Tensile Strength at Break: 51.0 MPa
$ 2481/MT
- Specific Gravity: 1.16 - 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 88.3 MPa @Thickness 3.20 mm
$ 1631/MT
- Specific Gravity: 1.406 g/cc
- Bulk Density: 0.300 - 0.400 g/cc
- Volatiles: <= 0.30 % @Temperature 110 °C, Time 3600 sec
- Brookfield Viscosity: 1000 - 5000 cP
- Viscosity Measurement: >= 3.0
$ 1573/MT
- Specific Gravity: 1.406 g/cc
- Bulk Density: 0.290 - 0.390 g/cc
- Volatiles: <= 1.5 % @Temperature 110 °C, Time 3600 sec
- Brookfield Viscosity: 2000 - 4000 cP
- Viscosity Measurement: >= 1.0 @Pressure 0.400 MPa
$ 1827/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 111
$ 1854/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 1460/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 1823/MT
- Specific Gravity: 1.04 - 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 40 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 109
$ 1716/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1810/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 0.40 %
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Index of Compound: 3.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 42
$ 1607/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 5.3 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 96
$ 1553/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 55.9 MPa @Thickness 3.20 mm
- Elongation at Break: >= 100 % @Thickness 3.20 mm
$ 1895/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0060 cm/cm
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Break: 30 %
$ 1952/MT
- Specific Gravity: 1.29 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 81.4 MPa @Thickness 3.20 mm
- Elongation at Break: >= 6.0 % @Thickness 3.20 mm
$ 1862/MT
- Water Absorption: 0.65 %
- Water Absorption: 0.65 %
- Water Absorption: 0.80 %
- Water Absorption: 1.0 %
- Flexural Yield Strength: 0.172 MPa
$ 1472/MT
- Specific Gravity: 1.52 g/cc
- Water Absorption: 0.60 %
- Maximum Moisture Content: 0.090
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
$ 1589/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 18 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1838/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1698/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage: 0.0070 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: >= 100 %
$ 1608/MT
- Specific Gravity: 0.918 - 0.921 g/cc
- Melt Flow: 3.1 - 3.5 g/10 min @Load 2.61 kg, Temperature 190 °C
- Tensile Strength, Ultimate: 12.3 MPa
- Elongation at Break: 600 %
- 2% Secant Modulus: 1.10 GPa
$ 1447/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 5.67 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 45.0 MPa
$ 1902/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 113
$ 1547/MT
- Specific Gravity: 1.33 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.017 - 0.020 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 64
$ 1673/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1896/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 25.5 MPa @Thickness 3.20 mm
$ 2349/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 72.6 MPa @Thickness 3.20 mm
$ 1817/MT
- Specific Gravity: 1.08 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 1.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1499/MT
- Specific Gravity: 1.44 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0030 - 0.010 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 93.2 MPa @Thickness 3.20 mm
- Elongation at Break: 3.0 % @Thickness 3.20 mm
$ 2416/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 12.3 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 90
$ 1496/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1594/MT
- Specific Gravity: 0.918 - 0.922 g/cc
- Melt Flow: 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 37.3 MPa
- Film Elongation at Break, MD: 670 %
- Film Elongation at Break, TD: 770 %
$ 2095/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage: 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0040 cm/cm
- Hardness, Rockwell R: 116
- Tensile Strength, Yield: 98.0 MPa
$ 2020/MT
- Specific Gravity: 1.41 g/cc
- Maximum Moisture Content: 0.10
- Linear Mold Shrinkage, Flow: 0.018 - 0.021 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 82
$ 1523/MT
- Specific Gravity: 1.07 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 103
$ 1575/MT
- Specific Gravity: 1.47 g/cc
- Linear Mold Shrinkage: 0.016 - 0.019 cm/cm
- Hardness, Rockwell M: 83
- Tensile Strength at Break: 64.0 MPa
- Elongation at Break: 10 %
$ 1491/MT
- Specific Gravity: 1.15 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 85.8 MPa @Thickness 3.20 mm
$ 1748/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 96
$ 1657/MT
- Specific Gravity: 1.21 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 72.6 MPa @Thickness 3.20 mm
$ 1526/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 68.6 MPa @Thickness 3.20 mm
$ 1476/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.040
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 58.8 MPa @Thickness 3.20 mm
$ 1934/MT
- Specific Gravity: 1.46 g/cc
- Linear Mold Shrinkage: 0.014 - 0.017 cm/cm
- Hardness, Rockwell M: 70
- Tensile Strength at Break: 53.0 MPa
- Elongation at Break: 50 %
$ 2302/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.5 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 107
$ 1704/MT
- Specific Gravity: 1.46 g/cc
- Linear Mold Shrinkage: 0.014 - 0.017 cm/cm
- Hardness, Rockwell M: 70
- Tensile Strength at Break: 53.0 MPa
- Elongation at Break: 50 %
$ 1769/MT
- Specific Gravity: 1.19 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 26 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 98
$ 2203/MT
- Specific Gravity: 1.00 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 34.3 MPa @Thickness 3.20 mm
$ 2180/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 27 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 105
$ 1656/MT
- Specific Gravity: 1.05 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 110
$ 2152/MT
- Specific Gravity: 0.870 g/cc
- Mooney Viscosity: 13 @Temperature 121 °C
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore A: 70
- Tensile Strength at Break: 7.94 MPa
$ 2152/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 117
$ 1598/MT
- Specific Gravity: 1.21 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm
- Tensile Strength, Yield: 63.0 MPa
- Elongation at Break: 3.0 %
$ 1717/MT
- Specific Gravity: 0.918 - 0.922 g/cc
- Melt Flow: 2.7 - 3.3 g/10 min @Load 2.61 kg, Temperature 190 °C
- Tensile Strength, Ultimate: 12.3 MPa
- Elongation at Break: 600 %
- 2% Secant Modulus: 1.20 GPa
$ 1701/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 12 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2136/MT
- Specific Gravity: 1.35 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 117
$ 2399/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2189/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.60 % @Temperature 23.0 °C, Time 86400 sec
- Molecular Weight: 458.458 g/mol
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
$ 1622/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Flow: 3.4 g/10 min @Load 5.00 kg, Temperature 200 °C
- Melt Flow: 32 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 124
$ 1813/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1668/MT
- Specific Gravity: 1.09 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0090 - 0.011 cm/cm @Thickness 3.20 mm
- Melt Flow: 40 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 26.0 MPa @Thickness 3.20 mm
$ 2493/MT
- Specific Gravity: 0.916 g/cc
- Thickness: 50.0 - 300 microns
- Melt Flow: 24 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Shore D: 43
- Tensile Strength at Break: 10.5 MPa
$ 1568/MT
- Specific Gravity: 1.13 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.5 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 115
$ 1885/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 20 g/10 min
- Hardness, Rockwell R: 112
- Tensile Strength at Break: 47.86 MPa
$ 1684/MT
- Specific Gravity: 1.40 g/cc
- Bulk Density: 0.520 - 0.600 g/cc
- Volatiles: <= 0.30 % @Temperature 110 °C, Time 3600 sec
- Particle Mesh Size: 45 Mesh
- Molecular Weight: 60000 - 150000 g/mol
$ 1818/MT
- Specific Gravity: 1.04 g/cc
- Linear Mold Shrinkage: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength, Yield: 17.0 MPa
- Elongation at Break: 60 %
$ 1612/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1589/MT
- Specific Gravity: 1.20 g/cc
- Maximum Moisture Content: 0.010
- Maximum Moisture Content: 0.010
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 42
$ 2597/MT
- Specific Gravity: 0.910 - 0.913 g/cc
- Melt Flow: 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C
- Film Elongation at Break, MD: 750 %
- Film Elongation at Break, TD: 850 %
- Elmendorf Tear Strength MD: 21 g
$ 2184/MT
- Specific Gravity: 1.40 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Yield: 59.0 MPa
- Elongation at Break: 4.0 %
$ 1741/MT
- Specific Gravity: 1.04 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 1.0 g/10 min @Load 3.50 kg, Temperature 230 °C
- Hardness, Rockwell R: 97
$ 1945/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 22 g/10 min
- Hardness, Rockwell R: 112
- Tensile Strength at Break: 51.0 MPa
$ 1803/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 6.8 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 47.1 MPa
$ 2590/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.19 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1683/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2277/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Index of Compound: 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 61.0 MPa
$ 2062/MT
- Specific Gravity: 1.13 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength, Yield: 21.6 MPa @Thickness 3.20 mm
$ 1604/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2351/MT
- Specific Gravity: 1.18 g/cc
- Maximum Moisture Content: 0.040
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 66.7 MPa @Thickness 3.20 mm
$ 1516/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2205/MT
- Specific Gravity: 1.50 g/cc
- Linear Mold Shrinkage, Flow: 0.00030 - 0.0015 cm/cm @Thickness 3.20 mm
- Elongation at Break: 6.0 % @Thickness 3.20 mm
- Flexural Yield Strength: 281 MPa @Thickness 3.20 mm
- Flexural Modulus: 13.0 GPa @Thickness 3.20 mm
$ 1452/MT
- Specific Gravity: 0.900 g/cc
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Rockwell R: 100
- Tensile Strength, Yield: 26.5 MPa
- Elongation at Break: >= 100 %
$ 1604/MT
- Specific Gravity: 1.40 g/cc
- Bulk Density: 0.500 - 0.580 g/cc
- Volatiles: <= 0.30 % @Temperature 110 °C, Time 3600 sec
- Particle Mesh Size: 45 Mesh
- Molecular Weight: 60000 - 150000 g/mol
$ 1623/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 7.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 109
- Tensile Strength, Yield: 38.3 MPa
$ 1650/MT
- Specific Gravity: 1.35 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
$ 1692/MT
- Specific Gravity: 1.30 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 123
$ 1469/MT
- Density: 1.07 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0030 - 0.0060 cm/cm
- Melt Index of Compound: 9.63 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 52.0 MPa
$ 1798/MT
- Specific Gravity: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 63.7 MPa @Thickness 3.20 mm
- Elongation at Break: >= 10 % @Thickness 3.20 mm
$ 1738/MT
- Specific Gravity: 1.43 g/cc
- Linear Mold Shrinkage: 0.0010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm
- Hardness, Rockwell R: 122
- Tensile Strength, Yield: 98.0 MPa
$ 1896/MT
- Density: 1.05 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Index of Compound: 49.35 g/10 min @Load 10.0 kg, Temperature 220 °C
- Tensile Strength, Yield: 49.0 MPa
$ 2037/MT
- Specific Gravity: 0.918 g/cc
- Water Vapor Transmission: 20.0 g/m²/day @Pressure 0.101 MPa
- Melt Flow: 5.0 g/10 min @Load 2.61 kg, Temperature 190 °C
- Hardness, Shore D: 43
- Tensile Strength at Break: 12.0 MPa
$ 2473/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0080 cm/cm
- Melt Flow: 9.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Rockwell R: 95
- Tensile Strength, Yield: 26.5 MPa
$ 1888/MT
- Specific Gravity: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 108 MPa @Thickness 3.20 mm
- Elongation at Break: >= 3.0 % @Thickness 3.20 mm
- Flexural Yield Strength: 147 MPa @Thickness 6.40 mm
$ 1891/MT
- Specific Gravity: 1.41 g/cc
- Linear Mold Shrinkage: 0.018 - 0.021 cm/cm
- Melt Index of Compound: 27 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell M: 82
- Tensile Strength at Break: 62.0 MPa
$ 1704/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.00070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2419/MT
- Specific Gravity: 0.940 g/cc
- Volatiles: <= 0.50 %
- Viscosity: 2.84 cP
- Melt Flow: <= 1.0 g/10 min @Load 5.00 kg, Temperature 200 °C
- Hardness, Shore A: 84
$ 2059/MT
- Specific Gravity: 0.944 - 0.947 g/cc
- Environmental Stress Crack Resistance: >= 500 hour
- Melt Flow: 0.15 - 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Hardness, Rockwell R: 55
- Tensile Strength, Yield: 17.7 MPa
$ 1540/MT
- Specific Gravity: 1.27 g/cc
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 260 °C
- Tensile Strength, Yield: 62.8 MPa @Thickness 3.20 mm
$ 1546/MT
- Specific Gravity: 1.32 g/cc
- Linear Mold Shrinkage: 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Break: 40 %
$ 2087/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.30 %
- Linear Mold Shrinkage: 0.0020 - 0.0060 cm/cm
- Melt Index of Compound: 5.8 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell M: 96
$ 1875/MT
- Specific Gravity: 1.02 g/cc
- Maximum Moisture Content: 0.010
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 220 °C
- Hardness, Rockwell R: 93
$ 1617/MT
- Specific Gravity: 1.13 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Hardness, Rockwell R: 110
$ 1534/MT
- Specific Gravity: 1.27 g/cc
- Maximum Moisture Content: 0.040
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 2.16 kg, Temperature 250 °C
- Tensile Strength, Yield: 58.8 MPa @Thickness 3.20 mm
$ 1673/MT
- Specific Gravity: 1.43 g/cc
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.060
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0090 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 122
Delivery Thermoplastic LG Chemical
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tankers for sale in usa. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.