$ 1681/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 71.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1687/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
- Tensile Strength, Ultimate: 65.5 MPa
$ 1506/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 71.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 2011/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm
- Melt Flow: 18 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 57.9 MPa
- Tensile Strength, Yield: 58.0 MPa
$ 2210/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 71.0 MPa
- Tensile Strength, Yield: 62.1 MPa
$ 1755/MT
- Density: 1.10 g/cc
- Water Absorption: 0.20 - 0.60 %
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm
- Melt Flow: 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 9.5 g/10 min @Load 5.00 kg, Temperature 250 °C
$ 1938/MT
- Density: 1.20 g/cc
- Water Absorption: 0.25 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2183/MT
- Specific Gravity: 1.37 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 79.3 MPa
$ 2259/MT
- Density: 1.20 g/cc
- Melt Density: 1.00 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0060 cm/cm
$ 1454/MT
- Density: 1.20 g/cc
- Melt Flow: 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 65.0 MPa
- Tensile Strength, Yield: 66.0 MPa
- Elongation at Break: 100 %
$ 2570/MT
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 120 %
- Elongation at Yield: 6.0 %
- Tensile Modulus: 2.30 GPa
$ 2351/MT
- Density: 1.14 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0070 cm/cm
- Melt Flow: 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1544/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
- Tensile Strength, Ultimate: 71.0 MPa
$ 1501/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Flow: 18 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 57.9 MPa
- Elongation at Break: 110 %
$ 1500/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 0.050 %
- Water Absorption at Saturation: 0.18 %
- Linear Mold Shrinkage: 0.0065 cm/cm
- Melt Flow: 1.5 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1538/MT
- Density: 1.12 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0070 cm/cm
- Melt Flow: 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1784/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1624/MT
- Density: 1.20 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1663/MT
- Density: 1.13 g/cc
- Melt Density: 0.962 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0070 cm/cm
$ 1466/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1805/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1586/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1984/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
- Tensile Strength, Ultimate: 71.0 MPa
$ 1924/MT
- Density: 1.20 g/cc
- Water Absorption: 0.20 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 58 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 48.0 MPa
$ 2263/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 55.8 MPa
- Elongation at Break: 130 %
$ 2145/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 123
- Tensile Strength, Ultimate: 65.5 MPa
$ 2271/MT
- Density: 1.20 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1848/MT
- Density: 1.12 g/cc
- Melt Density: 1.01 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0070 cm/cm
$ 2512/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1953/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 71.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 2256/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Melt Flow: 20 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 95 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 47.0 MPa @Thickness 4.00 mm
$ 1634/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage: 0.0070 cm/cm
- Melt Flow: 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 48.3 MPa
- Tensile Strength, Yield: 51.7 MPa
$ 2069/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Flow: 18 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 57.9 MPa
- Elongation at Break: 110 %
$ 1591/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
- Tensile Strength, Ultimate: 72.4 MPa
$ 2305/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.53 %
- Linear Mold Shrinkage: >= 0.0060 cm/cm
- Melt Flow: 4.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 52.7 MPa
$ 1747/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 73
- Hardness, Rockwell R: 118
$ 2223/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1448/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1712/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 123
- Tensile Strength, Ultimate: 58.6 MPa
$ 1632/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0050 cm/cm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 58.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1801/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0060 - 0.0080 cm/cm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 55.8 MPa
- Elongation at Break: 130 %
$ 2090/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1474/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 66.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1854/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1560/MT
- Density: 1.14 g/cc
- Melt Density: 1.02 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0070 cm/cm
$ 1494/MT
- Density: 1.27 g/cc
- Melt Density: 1.17 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
$ 1525/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Melt Flow: 10.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 46 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1661/MT
- Specific Gravity: 1.36 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
- Tensile Strength, Ultimate: 82.7 MPa
$ 1457/MT
- Density: 1.20 g/cc
- Water Absorption: 0.20 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 58 g/10 min @Load 1.20 kg, Temperature 300 °C
- Izod Impact, Notched: 5.80 J/cm @Temperature 23.0 °C
$ 1516/MT
- Density: 1.20 g/cc
- Melt Flow: 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 64.8 MPa
- Tensile Strength, Yield: 65.5 MPa
- Elongation at Break: 100 %
$ 1509/MT
- Specific Gravity: 1.27 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
$ 1452/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1526/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1762/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2359/MT
- Density: 1.13 g/cc
- Water Absorption: 0.53 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 53.0 MPa
$ 1857/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 71.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 2079/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 71.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 2479/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1506/MT
- Density: 1.14 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0070 cm/cm
- Melt Flow: 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1738/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Melt Flow: 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 100 MPa
- Elongation at Break: 4.0 %
$ 1998/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 5.6 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1535/MT
- Density: 1.33 g/cc
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 82.7 MPa
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 4.0 %
$ 1491/MT
- Density: 1.14 g/cc
- Melt Density: 1.02 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Melt Flow: 1.3 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Yield: 51.7 MPa
$ 1959/MT
- Density: 1.20 g/cc
- Melt Density: 1.00 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0060 cm/cm
$ 2251/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 71.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1548/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0080 cm/cm
- Melt Flow: 8.5 g/10 min @Load 5.00 kg, Temperature 260 °C
- Hardness, Rockwell R: 111 @Thickness 3.20 mm
$ 2192/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1686/MT
- Density: 1.10 g/cc
- Melt Flow: 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength at Break: 180 MPa
- Tensile Strength, Yield: 47.6 MPa
- Flexural Modulus: 2.18 GPa
$ 1981/MT
- Density: 1.27 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.25 %
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
$ 1465/MT
- Density: 1.20 g/cc
- Melt Density: 1.03 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0060 cm/cm
$ 1477/MT
- Density: 1.20 g/cc
- Melt Density: 1.01 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0060 cm/cm
$ 2562/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 123
- Tensile Strength, Ultimate: 58.6 MPa
$ 1651/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Maximum Moisture Content: 0.020
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
$ 1755/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Melt Flow: 12 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
- Tensile Strength at Break: 82.7 MPa
$ 2028/MT
- Density: 1.29 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0095 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 260 °C
- Melt Flow: 13 g/10 min @Load 5.00 kg, Temperature 265 °C
$ 1623/MT
- Melt Flow: 3.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 17 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 44.0 MPa
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 100 %
$ 2146/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0050 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 57.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1637/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0050 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 57.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 2211/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0050 cm/cm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 58.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1993/MT
- Density: 1.13 g/cc
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 18 g/10 min
- Melt Flow: 18 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1477/MT
- Density: 1.16 g/cc
- Water Absorption: 0.20 - 0.60 %
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm
- Ball Indentation Hardness: 105 MPa
- Tensile Strength at Break: 53.0 MPa
$ 1556/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 19 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 123
- Tensile Strength, Ultimate: 58.6 MPa
$ 1463/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 123
- Tensile Strength, Ultimate: 65.5 MPa
$ 1907/MT
- Density: 1.14 g/cc
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Melt Flow: 1.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength at Break: 48.3 MPa
$ 1652/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 72.4 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 2526/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1445/MT
- Density: 1.20 g/cc
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Transmission, Visible: 60 %
- Transmission, Visible: 67 %
- Solar Heat Reduction: 10-11°C
- Solar Heat Reduction: 10-11°C
$ 1459/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
- Tensile Strength, Ultimate: 71.0 MPa
$ 1709/MT
- Density: 1.20 g/cc
- Melt Density: 1.01 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0060 cm/cm
$ 1610/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1782/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 19 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2457/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2535/MT
- Density: 1.27 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.25 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2570/MT
- Density: 1.27 g/cc
- Water Absorption: 0.25 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1502/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1731/MT
- Density: 1.20 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1517/MT
- Density: 1.20 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2360/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0050 cm/cm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 58.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1697/MT
- Density: 1.19 g/cc
- Melt Density: 1.04 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 18 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 57.9 MPa
$ 1600/MT
- Density: 1.13 g/cc
- Melt Density: 0.998 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0070 cm/cm
$ 1899/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Melt Flow: 19 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 118 @Thickness 3.20 mm
- Tensile Strength at Break: 44.1 MPa @Thickness 3.20 mm
$ 1507/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2026/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 71.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 2221/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1599/MT
- Density: 1.12 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0070 cm/cm
- Melt Flow: 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 2314/MT
- Density: 1.18 g/cc
- Melt Density: 1.05 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0040 cm/cm
$ 1467/MT
- Density: 1.27 g/cc
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 59.0 MPa
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 6.0 %
$ 1569/MT
- Density: 1.18 g/cc
- Melt Density: 1.02 g/cc
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 55.8 MPa
$ 1570/MT
- Density: 1.20 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1716/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 123
- Tensile Strength, Ultimate: 58.6 MPa
$ 1460/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 4.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 53.8 MPa
$ 2591/MT
- Melt Flow: 25 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 120 %
- Elongation at Yield: 6.0 %
- Tensile Modulus: 2.30 GPa
$ 1831/MT
- Density: 1.20 g/cc
- Melt Density: 1.00 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0060 cm/cm
$ 1767/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 7.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Tensile Strength, Ultimate: 54.5 MPa
$ 1518/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1519/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 72.4 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1900/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
- Tensile Strength at Break: 82.7 MPa
$ 1666/MT
- Density: 1.20 g/cc
- Water Absorption: 0.25 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2203/MT
- Density: 1.20 g/cc
- Water Absorption: 0.25 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1622/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1574/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 123
- Tensile Strength, Ultimate: 65.5 MPa
$ 1529/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 66.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1496/MT
- Density: 1.20 g/cc
- Water Absorption: 0.25 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2405/MT
- Density: 1.12 g/cc
- Water Absorption: 0.20 - 0.60 %
- Linear Mold Shrinkage: 0.0030 - 0.0070 cm/cm
- Melt Flow: 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 250 °C
$ 1573/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 71.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1590/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 0.15 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 24 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 47.0 MPa
$ 2384/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1624/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1923/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1900/MT
- Specific Gravity: 1.27 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 13 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
$ 1502/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
- Tensile Strength, Ultimate: 65.5 MPa
$ 1965/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1493/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0050 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 57.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1771/MT
- Density: 1.20 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1482/MT
- Density: 1.18 g/cc
- Melt Flow: 18 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 65.3 MPa @Thickness 3.20 mm
- Tensile Strength, Yield: 64.8 MPa @Thickness 3.20 mm
- Elongation at Break: 49 % @Thickness 3.20 mm
$ 1677/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1584/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1580/MT
- Density: 1.20 g/cc
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 59
$ 1577/MT
- Density: 1.09 g/cc
- Linear Mold Shrinkage: 0.0040 - 0.0070 cm/cm
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 80.0 MPa
- Tensile Strength, Yield: 43.0 MPa
$ 1731/MT
- Bulk Density: 0.665 g/cc
- Density: 1.17 g/cc
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 3.80 kg, Temperature 230 °C
$ 1539/MT
- Density: 1.22 g/cc
- Melt Density: 0.962 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0025 cm/cm
$ 1814/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1595/MT
- Density: 1.27 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.25 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1447/MT
- Specific Gravity: 1.20 g/cc
- Melt Flow: 80 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 58
- Hardness, Rockwell R: 124
- Tensile Strength, Ultimate: 48.3 MPa
$ 2463/MT
- Specific Gravity: 1.36 g/cc
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
- Tensile Strength, Ultimate: 82.7 MPa
$ 1491/MT
- Density: 1.20 g/cc
- Water Absorption: 0.25 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min
$ 2009/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm
- Melt Flow: 11 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 55.8 MPa
- Tensile Strength, Yield: 56.0 MPa
$ 1678/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 66.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1688/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 20 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 123
- Tensile Strength at Break: 58.0 MPa @Thickness 4.00 mm
$ 1548/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage: 0.0050 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: 6.0 %
$ 1567/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Melt Flow: 11 g/10 min @Load 3.80 kg, Temperature 230 °C
- Hardness, Rockwell R: 120 @Thickness 3.20 mm
- Tensile Strength at Break: 48.3 MPa @Thickness 3.20 mm
$ 2085/MT
- Specific Gravity: 1.37 g/cc
- Filler Content: 20 %
- Linear Mold Shrinkage: 0.0020 - 0.0040 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 79.3 MPa
$ 1456/MT
- Density: 1.20 g/cc
- Water Absorption: 0.15 %
- Moisture Absorption at Equilibrium: 0.32 %
- Linear Mold Shrinkage: 0.0060 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1639/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1454/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0050 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength, Ultimate: 57.0 MPa
- Tensile Strength, Yield: 60.0 MPa
$ 1644/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.15 %
- Water Absorption at Saturation: 0.32 %
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1494/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1658/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 2290/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
- Tensile Strength, Ultimate: 71.0 MPa
$ 1696/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 46.9 MPa
- Tensile Strength, Yield: 64.1 MPa
$ 1910/MT
- Specific Gravity: 1.27 g/cc
- Filler Content: 10 %
- Linear Mold Shrinkage: 0.0020 - 0.0050 cm/cm
- Melt Flow: 13 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 122
$ 2094/MT
- Density: 1.18 g/cc
- Linear Mold Shrinkage: 0.0030 cm/cm
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength, Yield: 75.0 MPa
- Tensile Modulus: 4.00 GPa
$ 1490/MT
- Density: 1.20 g/cc
- Water Absorption: 0.32 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 22 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1813/MT
- Density: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 4.5 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 260 °C
- Hardness, Rockwell R: 112 @Thickness 3.20 mm
$ 1590/MT
- Density: 1.27 g/cc
- Water Absorption: 0.25 % @Temperature 23.0 °C
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 300 °C
$ 1942/MT
- Density: 1.20 g/cc
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell M: 59
$ 1776/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage: 0.0050 - 0.0070 cm/cm
- Melt Flow: 19 g/10 min @Load 1.20 kg, Temperature 300 °C
- Hardness, Rockwell R: 123
- Tensile Strength, Ultimate: 58.6 MPa
$ 1648/MT
- Density: 1.13 g/cc
- Water Absorption: 0.15 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
- Melt Flow: 4.5 g/10 min @Load 3.80 kg, Temperature 230 °C
Delivery Polycarbonate (PC) Styron
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, ships for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.