Hexion Bakelite™ PF 13 Phenolic Formaldehyde Resin, UL Listed  (discontinued **)

Seller in Hong Kong price: $2057 per MT

Hexion Bakelite™ PF 13 Phenolic Formaldehyde Resin, UL Listed  (discontinued **) in Polymer, Thermoset, Phenolic, Filled/Reinforced Thermoset

  • Physical Properties
  • Density
  • 1.85 g/cc
  • Apparent Bulk Density
  • 0.650 g/cc
  • Linear Mold Shrinkage, Flow
  • -0.000100 cm/cm
  • Mechanical Properties
  • Ball Indentation Hardness
  • 425 MPa
  • Flexural Strength
  • 85.0 MPa
  • Flexural Modulus
  • 25.0 GPa
  • Compressive Strength
  • 135 MPa
  • Charpy Impact Unnotched
  • 0.300 J/cm² @Temperature 23.0 °C
  • Charpy Impact, Notched
  • 0.200 J/cm² @Temperature 23.0 °C
  • Thermal Properties
  • Maximum Service Temperature, Air
  • 150 °C
  • Maximum Service Temperature, Air
  • 200 °C
  • Deflection Temperature at 8.0 MPa
  • 160 °C
  • UL RTI, Electrical
  • 150 °C @Thickness 0.750 mm
  • UL RTI, Mechanical with Impact
  • 150 °C @Thickness 0.750 mm
  • UL RTI, Mechanical without Impact
  • 150 °C @Thickness 0.750 mm
  • Flammability, UL94
  • V-1 @Thickness 0.750 mm
  • Flammability, UL94
  • V-0 @Thickness 3.00 mm
  • Shrinkage
  • 0.0200 % @Temperature 110 °C
  • Electrical Properties
  • Volume Resistivity
  • 1.00e+12 ohm-cm
  • Surface Resistance
  • 1.00e+11 ohm
  • Dielectric Constant
  • 5.0 @Frequency 100 Hz
  • Dielectric Strength
  • 30.0 kV/mm @Thickness 1.00 mm
  • Dissipation Factor
  • 0.040 @Frequency 100 Hz
  • Arc Resistance
  • 180 - 240 sec @Thickness 3.00 mm
  • High Voltage Arc Resistance to Ignition (HVAR)
  • >= 300 sec @Thickness 0.750 mm
  • Comparative Tracking Index
  • 175 V
  • Hot Wire Ignition, HWI
  • 30 - 60 sec @Thickness 0.750 mm
  • Hot Wire Ignition, HWI
  • >= 120 sec @Thickness 1.50 mm
  • High Amp Arc Ignition, HAI
  • 30 - 60 arcs @Thickness 0.750 mm
  • High Voltage Arc-Tracking Rate, HVTR
  • 0.000 - 10.0 mm/min @Thickness 3.00 mm
  • Processing Properties
  • Feed Temperature
  • 60.0 - 75.0 °C
  • Nozzle Temperature
  • 80.0 - 100 °C
  • Melt Temperature
  • 80.0 - 100 °C
  • Mold Temperature
  • 160 - 190 °C
  • Mold Temperature
  • 160 - 190 °C
  • Injection Pressure
  • >= 15.0 MPa
  • Back Pressure
  • 0.500 - 2.00 MPa
  • Cure Time
  • 0.167 - 0.333 min
  • Cure Time
  • 0.333 - 0.667 min
  • Descriptive Properties
  • Chromatic Spectrum
  • All Colors
  • Creep Rupture Strength
  • Very Good
  • Holding Pressure
  • Approximately 40-60% of injection pressure
  • Media Resistance
  • Very Good
  • Moisture Absorption
  • 10 mg
  • Reserves by Peak Temperature
  • Very High
  • Thermal Expansion
  • Very Slight

Alternative products

ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lpg carrier for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.

Andrey Kutuzov

University of Córdoba (Spain), email: [email protected]

Work with plastics from August, 2015

1 prices for Hexion Bakelite™ PF 13 Phenolic Formaldehyde Resin, UL Listed  (discontinued **)

Seller from Hong Kong – 2021-03-08:

Seller from Hong Kong work with company: Solvay, PolyOne Corporation, SABIC Innovative Plastics (GE Plastics), ALIMEX GmbH

Price: $2057 per MT

Share on Pinterest
Share on LinkedIn
Share on Reddit

Would you like to sell Hexion Bakelite™ PF 13 Phenolic Formaldehyde Resin, UL Listed  (discontinued **)?

Plastic warehouse

Find a direct plastic supplier if you're interested in a supplier or Pet food and animal feeds in Singapore open-nearme.com