$ 1656/MT
- Density: 1.40 g/cc
- Density of Compound: 1.165 g/cc
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0170 cm/cm
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1724/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
- Tensile Strength, Yield: 58.0 MPa
- Tensile Modulus: 2.45 GPa
$ 1651/MT
- Density: 1.37 g/cc
- Water Absorption at Saturation: 0.800 %
- Linear Mold Shrinkage, Flow: 0.0160 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0150 cm/cm
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1496/MT
- Density: 1.36 g/cc
- Melt Flow: 17.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 40.0 %
- Elongation at Yield: 8.50 %
$ 1660/MT
- Density: 1.39 g/cc
- Water Absorption at Saturation: 0.800 %
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 6.50 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2092/MT
- Density: 1.37 g/cc
- Water Absorption at Saturation: 0.800 %
- Linear Mold Shrinkage, Flow: 0.0160 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0150 cm/cm
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1605/MT
- Density: 1.36 g/cc
- Water Absorption at Saturation: 0.650 %
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 41.0 MPa
- Elongation at Yield: 13.0 %
$ 2145/MT
- Density: 1.43 g/cc
- Density: 1.50 g/cc
- Linear Mold Shrinkage: 0.022 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Tensile Strength, Yield: 48.0 MPa
$ 2065/MT
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 63.0 MPa
$ 2070/MT
- Density: 1.43 g/cc
- Water Absorption: 0.20 %
- Moisture Absorption at Equilibrium: 0.80 %
- Linear Mold Shrinkage: 0.0030 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
$ 1981/MT
- Density: 1.42 g/cc
- Melt Flow: 17.04 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 30 %
- Elongation at Yield: 11 %
$ 2050/MT
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0220 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 1463/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.650 %
- Melt Flow: 0.900 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Break: 25.0 %
$ 1628/MT
- Density: 1.43 g/cc
- Water Absorption at Saturation: 0.75 %
- Linear Mold Shrinkage, Flow: 0.023 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength, Yield: 54.0 MPa
$ 1933/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.20 % @Temperature 23.0 °C
- Water Absorption at Saturation: 0.65 % @Temperature 23.0 °C
- Melt Flow: 16.92 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 143 MPa
$ 1853/MT
- Density: 1.60 g/cc
- Tensile Strength at Break: 160 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 9.50 GPa
- Flexural Modulus: 9.50 GPa
$ 1868/MT
- Density: 1.43 g/cc
- Water Absorption at Saturation: 0.750 %
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 56.0 MPa
- Elongation at Yield: 10.0 %
$ 1447/MT
- Density: 1.44 g/cc
- Tensile Strength at Break: 151 MPa
- Elongation at Break: 2.4 %
- Flexural Modulus: 11.78 GPa
- Izod Impact, Notched (ISO): 6.50 kJ/m²
$ 1567/MT
- Density: 1.48 g/cc
- Water Absorption at Saturation: 0.850 %
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 90.0 MPa
- Elongation at Break: 4.00 %
$ 2382/MT
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Water Absorption at Saturation: 0.650 %
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 62.0 MPa
$ 2159/MT
- Density: 1.42 g/cc
- Melt Flow: 7.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 52.0 MPa
- Elongation at Break: 16.0 %
- Elongation at Yield: 7.00 %
$ 1479/MT
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 1452/MT
- Specific Gravity: 1.40 g/cc
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0220 cm/cm
- Linear Mold Shrinkage, Flow: 0.0230 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 1631/MT
- Density: 1.41 g/cc
- Water Absorption: 0.22 %
- Moisture Absorption at Equilibrium: 0.80 %
- Linear Mold Shrinkage: 0.022 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
$ 1597/MT
- Density: 1.46 g/cc
- Tensile Strength at Break: 93.0 MPa
- Elongation at Break: 6.0 %
- Izod Impact, Notched (ISO): 4.40 kJ/m²
- Deflection Temperature at 1.8 MPa (264 psi): 110 °C
$ 2406/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.20 % @Temperature 23.0 °C
- Water Absorption at Saturation: 0.65 % @Temperature 23.0 °C
- Melt Flow: 3.1 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 144 MPa
$ 1456/MT
- Density: 1.34 g/cc
- Water Absorption at Saturation: 0.800 %
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 44.0 MPa
- Elongation at Break: 15.0 %
$ 1792/MT
- Density: 1.60 g/cc
- Density of Compound: 1.35 g/cc
- Water Absorption at Saturation: 0.900 %
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 135 MPa
$ 1601/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 8.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 63.0 MPa
$ 1759/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.750 %
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Yield: 9.00 %
$ 2440/MT
- Density: 1.43 g/cc
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0230 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0140 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1532/MT
- Density: 1.52 g/cc
- Water Absorption at Saturation: 0.200 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0170 cm/cm
- Melt Flow: 6.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2483/MT
- Density: 1.42 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Melt Flow: 25.8 g/10 min
- Tensile Strength, Yield: 53.0 MPa
$ 1494/MT
- Density: 1.59 g/cc
- Water Absorption at Saturation: 0.900 %
- Melt Flow: 16.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 38.0 MPa
- Elongation at Break: 12.0 %
$ 1750/MT
- Density: 1.57 g/cc
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 2.50 %
- Tensile Modulus: 7.70 GPa
$ 2043/MT
- Density: 1.59 g/cc
- Density of Compound: 1.37 g/cc
- Water Absorption at Saturation: 0.900 %
- Melt Flow: 7.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 38.0 MPa
$ 2438/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0250 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0230 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 65.0 MPa
$ 2147/MT
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 1796/MT
- Density: 1.40 g/cc
- Tensile Strength, Yield: 41.0 MPa
- Tensile Modulus: 3.03 GPa
- Flexural Modulus: 2.82 GPa
- Izod Impact, Notched (ISO): 2.50 kJ/m²
$ 1720/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1487/MT
- Density: 1.48 g/cc
- Melt Flow: 8.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 58.0 MPa
- Elongation at Yield: 9.50 %
- Tensile Modulus: 2.80 GPa
$ 1817/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage: 0.022 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Tensile Strength, Yield: 66.0 MPa
- Flexural Modulus: 2.75 GPa
$ 1526/MT
- Specific Gravity: 1.48 g/cc
- Density: 1.48 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
$ 1625/MT
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 1563/MT
- Density: 1.51 g/cc
- Water Absorption at Saturation: 0.65 %
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Tensile Strength, Yield: 47.0 MPa
$ 2119/MT
- Density: 1.33 g/cc
- Water Absorption at Saturation: 1.0 %
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Tensile Strength, Yield: 44.0 MPa
$ 1949/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0170 cm/cm
- Linear Mold Shrinkage, Flow: 0.0220 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
$ 1516/MT
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 1630/MT
- Density: 1.40 g/cc
- Tensile Strength, Yield: 64.0 MPa
- Tensile Modulus: 2.445 GPa
- Flexural Modulus: 2.402 GPa
- Izod Impact, Notched (ISO): 7.70 kJ/m²
$ 1562/MT
- Density: 1.47 g/cc
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Yield: 10.0 %
- Tensile Modulus: 3.00 GPa
- Charpy Impact, Notched: 0.400 J/cm²
$ 1575/MT
- Density: 1.37 g/cc
- Water Absorption: 0.20 %
- Moisture Absorption at Equilibrium: 0.80 %
- Linear Mold Shrinkage: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm
$ 1918/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.20 % @Temperature 23.0 °C
- Water Absorption at Saturation: 0.65 % @Temperature 23.0 °C
- Melt Flow: 33.84 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 147 MPa
$ 1523/MT
- Density: 1.44 g/cc
- Density of Compound: 1.23 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 1561/MT
- Density: 1.34 g/cc
- Water Absorption at Saturation: 0.800 %
- Linear Mold Shrinkage, Flow: 0.0230 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 5.50 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1501/MT
- Density: 1.63 g/cc
- Melt Flow: 7.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 38.0 MPa
- Elongation at Break: 13.0 %
- Elongation at Yield: 5.00 %
$ 1810/MT
- Density: 1.42 g/cc
- Water Absorption: 0.75 %
- Melt Flow: 8.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Break: 20 %
$ 1981/MT
- Density: 1.40 g/cc
- Melt Flow: 8.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 30.0 %
- Elongation at Yield: 9.00 %
$ 1470/MT
- Density: 1.62 g/cc
- Water Absorption: 0.27 %
- Moisture Absorption at Equilibrium: 0.80 %
- Linear Mold Shrinkage: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
$ 1938/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.20 % @Temperature 23.0 °C
- Water Absorption at Saturation: 0.65 % @Temperature 23.0 °C
- Melt Flow: 1.27 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 150 MPa
$ 2447/MT
- Density: 1.43 g/cc
- Melt Flow: 16 g/10 min
- Tensile Strength, Yield: 56.0 MPa
- Flexural Modulus: 2.39 GPa
- Izod Impact, Notched (ISO): 4.60 kJ/m²
$ 2219/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Linear Mold Shrinkage: 0.022 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
$ 1741/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Melt Flow: 54.99 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 148 MPa
$ 1955/MT
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 1997/MT
- Density: 1.46 g/cc
- Tensile Strength at Break: 77.0 MPa
- Tensile Modulus: 4.60 GPa
- Flexural Modulus: 4.30 GPa
- Izod Impact, Notched (ISO): 6.20 kJ/m²
$ 1502/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
$ 1621/MT
- Specific Gravity: 1.48 g/cc
- Density: 1.48 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
$ 1513/MT
- Density: 1.54 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.800 %
- Tensile Strength at Break: 99.0 MPa
- Elongation at Break: 2.20 %
$ 1709/MT
- Density: 1.33 g/cc
- Water Absorption at Saturation: 1.0 %
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Tensile Strength, Yield: 44.0 MPa
$ 2337/MT
- Density: 1.37 g/cc
- Water Absorption: 0.65 %
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0017 cm/cm
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2476/MT
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 2476/MT
- Density: 1.35 g/cc
- Density: 1.37 g/cc
- Linear Mold Shrinkage: 0.018 cm/cm
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm
- Melt Flow: 7.0 g/10 min
$ 2163/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 24.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1503/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0220 cm/cm
$ 2105/MT
- Density: 1.38 g/cc
- Linear Mold Shrinkage: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
- Tensile Strength, Yield: 50.0 MPa
- Tensile Modulus: 2.40 GPa
$ 1646/MT
- Density: 1.40 g/cc
- Water Absorption at Saturation: 0.600 %
- Linear Mold Shrinkage, Flow: 0.0185 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0175 cm/cm
- Melt Flow: 25.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2399/MT
- Density: 1.38 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0180 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1840/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1710/MT
- Density: 1.54 g/cc
- Linear Mold Shrinkage, Flow: 0.00300 cm/cm
- Linear Mold Shrinkage, Transverse: 0.00800 cm/cm
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 110 MPa
$ 2066/MT
- Specific Gravity: 1.40 g/cc
- Density: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Flow: 0.0220 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
$ 2067/MT
- Density: 1.42 g/cc
- Tensile Strength, Yield: 61.0 MPa
- Tensile Modulus: 2.65 GPa
- Charpy Impact, Notched: 0.460 J/cm²
- Deflection Temperature at 1.8 MPa (264 psi): 94.0 °C
$ 2080/MT
- Specific Gravity: 1.43 g/cc
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0180 cm/cm
$ 1562/MT
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 2100/MT
- Density: 1.38 g/cc
- Melt Flow: 1.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 44.0 MPa
- Elongation at Break: 15.0 %
- Elongation at Yield: 11.0 %
$ 1503/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0160 cm/cm
- Linear Mold Shrinkage, Flow: 0.0220 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 2091/MT
- Density: 1.42 g/cc
- Water Absorption at Saturation: 1.20 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 6.50 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1453/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0170 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 64.0 MPa
$ 2113/MT
- Density: 1.43 g/cc
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0230 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0140 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2130/MT
- Density: 1.37 g/cc
- Water Absorption at Saturation: 0.80 %
- Tensile Strength, Yield: 43.0 MPa
- Elongation at Yield: 16 %
- Tensile Modulus: 1.65 GPa
$ 1699/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0170 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Yield: 10.0 %
$ 1466/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 32.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 68.0 MPa
$ 1571/MT
- Density: 1.40 g/cc
- Water Absorption: 0.21 %
- Moisture Absorption at Equilibrium: 0.80 %
- Linear Mold Shrinkage: 0.022 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
$ 1656/MT
- Density: 1.33 g/cc
- Melt Flow: 13.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 41.0 MPa
- Elongation at Yield: 10.0 %
- Tensile Modulus: 1.90 GPa
$ 1913/MT
- Density: 1.41 g/cc
- Water Absorption: 0.22 %
- Moisture Absorption at Equilibrium: 0.80 %
- Linear Mold Shrinkage: 0.022 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
$ 1535/MT
- Density: 1.37 g/cc
- Moisture Absorption at Equilibrium: 0.25 %
- Water Absorption at Saturation: 0.65 %
- Melt Flow: 9.59 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 86.0 MPa
$ 2578/MT
- Density: 1.39 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.70 %
- Melt Flow: 25.02 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 115 MPa
$ 1749/MT
- Density: 1.53 g/cc
- Water Absorption at Saturation: 0.800 %
- Melt Flow: 8.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 46.0 MPa
- Elongation at Break: 15.0 %
$ 1871/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 12.5 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1491/MT
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0210 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 2105/MT
- Density: 1.46 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.800 %
- Linear Mold Shrinkage, Flow: 0.00900 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0120 cm/cm
$ 1490/MT
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Water Absorption at Saturation: 0.650 %
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 62.0 MPa
$ 1986/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1713/MT
- Melting Point: 165 °C
- Pellets: Yes
$ 1649/MT
- Specific Gravity: 1.54 g/cc
- Density: 1.502 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.800 %
- Linear Mold Shrinkage, Flow: 0.00400 cm/cm
$ 2058/MT
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 2321/MT
- Density: 1.59 g/cc
- Tensile Strength at Break: 177 MPa
- Elongation at Break: 2.35 %
- Tensile Modulus: 10.3 GPa
- Flexural Strength: 265 MPa
$ 1674/MT
- Density: 1.27 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 1.2 %
- Melt Flow: 1.78 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 80.0 MPa
$ 1753/MT
- Density: 1.44 g/cc
- Linear Mold Shrinkage, Flow: 0.00800 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0100 cm/cm
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 70.0 MPa
$ 1598/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0190 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 66.0 MPa
$ 1566/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.750 %
- Melt Flow: 2.20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Yield: 12.0 %
$ 1582/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0210 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0200 cm/cm
- Melt Flow: 1.70 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2199/MT
- Density: 1.42 g/cc
- Tensile Strength, Yield: 59.0 MPa
- Flexural Modulus: 2.47 GPa
- Izod Impact, Notched (ISO): 4.30 kJ/m²
- Deflection Temperature at 1.8 MPa (264 psi): 99.0 °C
$ 2082/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0105 cm/cm
- Linear Mold Shrinkage, Transverse: 0.00950 cm/cm
- Melt Flow: 1.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 105 MPa
$ 1529/MT
- Density: 1.42 g/cc
- Melt Flow: 12.5 g/10 min
- Tensile Strength, Yield: 63.0 MPa
- Tensile Modulus: 2.84 GPa
- Charpy Impact, Notched: 0.650 J/cm²
$ 1513/MT
- Density: 1.42 g/cc
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 8.50 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1810/MT
- Density: 1.39 g/cc
- Water Absorption: 0.65 %
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1752/MT
- Specific Gravity: 1.62 g/cc
- Density: 1.58 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0150 cm/cm
$ 1610/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0220 cm/cm
$ 2123/MT
- Density: 1.39 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1456/MT
- Density: 1.37 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0180 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0170 cm/cm
- Melt Flow: 19.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1823/MT
- Density: 1.33 g/cc
- Water Absorption at Saturation: 1.00 %
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1749/MT
- Density: 1.39 g/cc
- Water Absorption at Saturation: 0.800 %
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 6.50 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1481/MT
- Density: 1.38 g/cc
- Water Absorption at Saturation: 0.650 %
- Melt Flow: 7.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 49.0 MPa
- Elongation at Yield: 12.0 %
$ 1451/MT
- Density: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.0210 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0190 cm/cm
- Melt Flow: 13.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 49.0 MPa
$ 1826/MT
- Density: 1.33 g/cc
- Water Absorption at Saturation: 0.800 %
- Linear Mold Shrinkage, Flow: 0.0140 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0120 cm/cm
- Melt Flow: 1.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1496/MT
- Density: 1.33 g/cc
- Water Absorption at Saturation: 1.00 %
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1541/MT
- Density: 1.26 g/cc
- Water Absorption at Saturation: 1.20 %
- Linear Mold Shrinkage, Flow: 0.0170 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
- Melt Flow: 1.40 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1600/MT
- Density: 1.26 g/cc
- Water Absorption at Saturation: 1.20 %
- Linear Mold Shrinkage, Flow: 0.0170 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
- Melt Flow: 1.40 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1471/MT
- Density: 1.38 g/cc
- Water Absorption at Saturation: 0.800 %
- Linear Mold Shrinkage, Flow: 0.0180 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
- Melt Flow: 5.50 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1658/MT
- Density: 1.38 g/cc
- Water Absorption at Saturation: 0.800 %
- Linear Mold Shrinkage, Flow: 0.0180 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
- Melt Flow: 5.50 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1903/MT
- Density: 1.37 g/cc
- Water Absorption at Saturation: 0.800 %
- Melt Flow: 0.600 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 43.0 MPa
- Elongation at Yield: 16.0 %
$ 1949/MT
- Density: 1.32 g/cc
- Water Absorption at Saturation: 0.800 %
- Linear Mold Shrinkage, Flow: 0.0120 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0110 cm/cm
- Melt Flow: 2.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1721/MT
- Density: 1.37 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0180 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0170 cm/cm
- Melt Flow: 18.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2284/MT
- Density: 1.39 g/cc
- Water Absorption at Saturation: 0.700 %
- Melt Flow: 21.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 46.0 MPa
- Elongation at Break: 35.0 %
$ 2116/MT
- Density: 1.41 g/cc
- Tensile Strength, Yield: 52.0 MPa
- Tensile Modulus: 2.37 GPa
- Flexural Modulus: 2.35 GPa
- Izod Impact, Notched (ISO): 5.00 kJ/m²
$ 2295/MT
- Density: 1.41 g/cc
- Tensile Strength, Yield: 52.0 MPa
- Tensile Modulus: 2.37 GPa
- Flexural Modulus: 2.35 GPa
- Izod Impact, Notched (ISO): 5.00 kJ/m²
$ 1663/MT
- Density: 1.39 g/cc
- Water Absorption: 0.65 %
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1483/MT
- Specific Gravity: 1.60 g/cc
- Density: 1.57 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0150 cm/cm
$ 1856/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Melt Flow: 16.92 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 143 MPa
$ 1991/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.65 %
- Tensile Strength, Yield: 63.0 MPa
- Elongation at Break: 30 %
- Elongation at Yield: 9.0 %
$ 1686/MT
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 2312/MT
- Density: 1.42 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1674/MT
- Density: 1.48 g/cc
- Linear Mold Shrinkage, Flow: 0.0145 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0100 cm/cm
- Melt Flow: 3.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 110 MPa
$ 1556/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0180 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 65.0 MPa
$ 1503/MT
- Density: 1.44 g/cc
- Melt Flow: 8.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 58.0 MPa
- Elongation at Break: 28.0 %
- Elongation at Yield: 9.00 %
$ 1590/MT
- Density: 1.41 g/cc
- Melt Flow: 24.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 66.0 MPa
- Elongation at Yield: 7.00 %
- Tensile Modulus: 2.75 GPa
$ 1648/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0210 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0190 cm/cm
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 53.0 MPa
$ 1633/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage: 0.022 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Tensile Strength, Yield: 65.0 MPa
- Flexural Modulus: 2.52 GPa
$ 1474/MT
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0170 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
$ 1599/MT
- Density: 1.44 g/cc
- Melt Flow: 21.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 58.0 MPa
- Elongation at Break: 25.0 %
- Tensile Modulus: 2.60 GPa
$ 2001/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 49.0 MPa
$ 1708/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.70 %
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Tensile Strength, Yield: 63.0 MPa
$ 1814/MT
- Specific Gravity: 1.58 g/cc
- Density: 1.57 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.800 %
- Linear Mold Shrinkage, Flow: 0.00400 cm/cm
$ 1660/MT
- Density: 1.39 g/cc
- Water Absorption: 0.21 %
- Moisture Absorption at Equilibrium: 0.80 %
- Linear Mold Shrinkage: 0.021 cm/cm
- Linear Mold Shrinkage, Transverse: 0.017 cm/cm
$ 1636/MT
- Density: 1.40 g/cc
- Water Absorption at Saturation: 0.600 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0165 cm/cm
- Melt Flow: 13.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2152/MT
- Density: 1.38 g/cc
- Water Absorption at Saturation: 0.80 %
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Yield: 12 %
- Tensile Modulus: 2.00 GPa
$ 1517/MT
- Density: 1.65 g/cc
- Tensile Strength at Break: 182 MPa
- Elongation at Break: 2.05 %
- Tensile Modulus: 11.99 GPa
- Flexural Strength: 285 MPa
$ 2416/MT
- Density: 1.26 g/cc
- Water Absorption at Saturation: 1.2 %
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Strength, Yield: 33.0 MPa
$ 2234/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0250 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0240 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 64.0 MPa
$ 2156/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2112/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
$ 1949/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0250 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0200 cm/cm
- Melt Flow: 4.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 63.0 MPa
$ 1752/MT
- Density: 1.40 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 63.0 MPa
- Elongation at Break: 32.0 %
- Elongation at Yield: 19.0 %
$ 1623/MT
- Density: 1.35 g/cc
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 40 %
- Elongation at Yield: 8.5 %
- Tensile Modulus: 2.20 GPa
$ 1801/MT
- Density: 1.44 g/cc
- Water Absorption at Saturation: 0.650 %
- Melt Flow: 8.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 58.0 MPa
- Elongation at Yield: 9.00 %
$ 2303/MT
- Density: 1.37 g/cc
- Water Absorption at Saturation: 0.800 %
- Melt Flow: 4.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 41.0 MPa
- Elongation at Yield: 20.0 %
$ 1884/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0220 cm/cm
$ 1663/MT
- Density: 1.52 g/cc
- Linear Mold Shrinkage, Flow: 0.00800 cm/cm
- Linear Mold Shrinkage, Transverse: 0.00900 cm/cm
- Melt Flow: 1.50 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength at Break: 135 MPa
$ 1876/MT
- Density: 1.39 g/cc
- Water Absorption at Saturation: 0.700 %
- Melt Flow: 21.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 46.0 MPa
- Elongation at Break: 35.0 %
$ 1611/MT
- Density: 1.41 g/cc
- Tensile Strength, Yield: 52.0 MPa
- Tensile Modulus: 2.37 GPa
- Flexural Modulus: 2.35 GPa
- Izod Impact, Notched (ISO): 5.00 kJ/m²
$ 1465/MT
- Density: 1.41 g/cc
- Tensile Strength, Yield: 52.0 MPa
- Tensile Modulus: 2.37 GPa
- Flexural Modulus: 2.35 GPa
- Izod Impact, Notched (ISO): 5.00 kJ/m²
$ 1838/MT
- Density: 1.39 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Melt Flow: 11.12 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 110 MPa
$ 1472/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0220 cm/cm
$ 1852/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0260 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0220 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 65.0 MPa
$ 2121/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0160 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0150 cm/cm
- Melt Flow: 13.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 41.0 MPa
$ 1612/MT
- Density: 1.41 g/cc
- Melt Density: 1.20 g/cc
- Water Absorption: 0.65 %
- Melt Flow: 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Stress: 18.0 MPa @Strain 2.00 %, Temperature 80.0 °C
$ 1690/MT
- Density: 1.34 g/cc
- Tensile Strength, Yield: 37.0 MPa
- Tensile Modulus: 1.22 GPa
- Flexural Modulus: 1.20 GPa
- Izod Impact, Notched (ISO): 11.8 kJ/m²
$ 1452/MT
- Density: 1.38 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0210 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0190 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1459/MT
- Density: 1.42 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.75 %
- Melt Flow: 12.07 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 140 MPa
$ 1570/MT
- Density: 1.39 g/cc
- Water Absorption at Saturation: 0.80 %
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Yield: 10 %
- Tensile Modulus: 2.30 GPa
$ 1519/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0220 cm/cm
$ 1730/MT
- Density: 1.41 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Melt Flow: 11.28 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 144 MPa
$ 1609/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Flow: 0.0220 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0170 cm/cm
$ 1514/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 1.70 %
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 30.0 %
$ 2129/MT
- Density: 1.41 g/cc
- Melt Flow: 2.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 61.0 MPa
- Elongation at Yield: 11.0 %
- Tensile Modulus: 2.40 GPa
$ 2560/MT
- Density: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
- Melt Flow: 20.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 56.0 MPa
$ 1740/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage: 0.022 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
- Tensile Strength, Yield: 64.0 MPa
- Flexural Modulus: 2.77 GPa
$ 2293/MT
- Density: 1.51 g/cc
- Linear Mold Shrinkage, Flow: 0.00900 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0110 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 44.0 MPa
$ 1530/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.650 %
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 63.0 MPa
- Elongation at Break: 30.0 %
$ 2151/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0140 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 55.0 MPa
$ 1735/MT
- Density: 1.41 g/cc
- Melt Flow: 2.10 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 63.0 MPa
- Elongation at Yield: 10.0 %
- Tensile Modulus: 2.60 GPa
$ 1838/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1963/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0160 cm/cm
- Melt Flow: 17.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 55.0 MPa
$ 1956/MT
- Density: 1.42 g/cc
- Melt Density: 1.16 g/cc
- Water Absorption at Saturation: 0.75 %
- Linear Mold Shrinkage, Flow: 0.022 cm/cm
- Linear Mold Shrinkage, Transverse: 0.018 cm/cm
$ 1721/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.650 %
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Break: 25.0 %
$ 2057/MT
- Density: 1.39 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.65 %
- Melt Flow: 27.8 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 115 MPa
$ 1454/MT
- Density: 1.50 g/cc
- Water Absorption at Saturation: 0.850 %
- Linear Mold Shrinkage, Flow: 0.00700 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0120 cm/cm
- Tensile Strength at Break: 75.0 MPa
$ 1824/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2503/MT
- Density: 1.57 g/cc
- Water Absorption at Saturation: 0.850 %
- Melt Flow: 4.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 3.00 %
$ 1536/MT
- Density: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 56.0 MPa
$ 1553/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1913/MT
- Density: 1.41 g/cc
- Water Absorption: 0.65 %
- Melt Flow: 24 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Break: 17 %
$ 1739/MT
- Density: 1.26 g/cc
- Water Absorption at Saturation: 1.2 %
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
- Linear Mold Shrinkage, Transverse: 0.016 cm/cm
- Tensile Strength, Yield: 33.0 MPa
$ 1527/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0220 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0190 cm/cm
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 62.0 MPa
$ 1911/MT
- Density: 1.37 g/cc
- Melt Flow: 7.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 51.0 MPa
- Elongation at Break: 35.0 %
- Elongation at Yield: 15.0 %
$ 2268/MT
- Density: 1.40 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0165 cm/cm
- Melt Flow: 13.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 2084/MT
- Density: 1.59 g/cc
- Linear Mold Shrinkage, Flow: 0.00600 cm/cm
- Linear Mold Shrinkage, Transverse: 0.00950 cm/cm
- Melt Flow: 4.80 g/10 min @Load 5.00 kg, Temperature 190 °C
- Tensile Strength at Break: 155 MPa
$ 2038/MT
- Density: 1.40 g/cc
- Melt Flow: 9.50 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 61.0 MPa
- Elongation at Break: 28.0 %
- Elongation at Yield: 8.00 %
$ 1671/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
$ 2450/MT
- Density: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.0210 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0190 cm/cm
- Melt Flow: 32.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 53.0 MPa
$ 2198/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0190 cm/cm
$ 1596/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0200 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1473/MT
- Density: 1.33 g/cc
- Melt Flow: 13.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 41.0 MPa
- Elongation at Yield: 10.0 %
- Tensile Modulus: 1.90 GPa
$ 1681/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0220 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0220 cm/cm
- Melt Flow: 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 65.0 MPa
$ 1477/MT
- Density: 1.40 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0185 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0175 cm/cm
- Melt Flow: 26.0 g/10 min @Load 2.16 kg, Temperature 190 °C
$ 1989/MT
- Density: 1.41 g/cc
- Water Absorption at Saturation: 0.650 %
- Melt Flow: 12.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Break: 25.0 %
$ 2493/MT
- Density: 1.41 g/cc
- Tensile Strength, Yield: 64.0 MPa
- Flexural Modulus: 2.52 GPa
- Izod Impact, Notched (ISO): 5.70 kJ/m²
- Deflection Temperature at 1.8 MPa (264 psi): 88.0 °C
$ 1464/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.41 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0170 cm/cm
$ 1539/MT
- Density: 1.42 g/cc
- Melt Flow: 17.04 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 30 %
- Elongation at Yield: 11 %
$ 1850/MT
- Density: 1.44 g/cc
- Moisture Absorption at Equilibrium: 0.20 %
- Water Absorption at Saturation: 0.80 %
- Melt Flow: 25.92 g/10 min @Load 2.16 kg, Temperature 190 °C
- Ball Indentation Hardness: 110 MPa
$ 1809/MT
- Specific Gravity: 1.60 g/cc
- Density: 1.57 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0150 cm/cm
$ 1736/MT
- Specific Gravity: 1.58 g/cc
- Density: 1.575 g/cc
- Moisture Absorption: 0.200 %
- Water Absorption at Saturation: 0.800 %
- Linear Mold Shrinkage, Flow: 0.00400 cm/cm
$ 1937/MT
- Density: 1.41 g/cc
- Melt Flow: 12 g/10 min
- Tensile Strength, Yield: 66.0 MPa
- Flexural Modulus: 2.65 GPa
- Izod Impact, Notched (ISO): 5.50 kJ/m²
$ 1860/MT
- Density: 1.41 g/cc
- Density of Compound: 1.20 g/cc
- Water Absorption at Saturation: 0.650 %
- Linear Mold Shrinkage, Flow: 0.0210 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0180 cm/cm
$ 2502/MT
- Density: 1.47 g/cc
- Density of Compound: 1.25 g/cc
- Water Absorption at Saturation: 0.800 %
- Melt Flow: 9.00 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 52.0 MPa
$ 1926/MT
- Density: 1.51 g/cc
- Melt Flow: 17.0 g/10 min @Load 2.16 kg, Temperature 190 °C
- Tensile Strength, Yield: 48.0 MPa
- Elongation at Break: 15.0 %
- Elongation at Yield: 8.00 %
Delivery Acetal (POM) Celanese Corporation
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng carrier vessel for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.