$ 1965/MT
- Linear Mold Shrinkage, Flow: 0.0072 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0074 cm/cm
- Tensile Strength at Break: 44.0 MPa
- Elongation at Break: 0.40 %
- Tensile Modulus: 16.45 GPa
$ 2098/MT
- Density: 1.22 g/cc
- Density: 1.22 g/cc
- Moisture Absorption: 1.30 %
- Linear Mold Shrinkage, Flow: 0.0072 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm @Time 86400 sec
$ 1688/MT
- Density: 1.48 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 236 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 18.28 GPa
$ 1486/MT
- Specific Gravity: 1.26 g/cc
- Density: 1.26 g/cc
- Moisture Absorption: 0.500 %
- Water Absorption at Saturation: 1.27 %
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm @Thickness 3.20 mm
$ 1771/MT
- Density: 1.55 g/cc
- Moisture Absorption at Equilibrium: 0.60 %
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
$ 1549/MT
- Density: 1.22 g/cc
- Density: 1.22 g/cc
- Moisture Absorption: 1.30 %
- Linear Mold Shrinkage, Flow: 0.0072 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm @Time 86400 sec
$ 1549/MT
- Density: 1.24 g/cc
- Tensile Strength at Break: 177 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 29.16 GPa
- Flexural Strength: 303 MPa
$ 1500/MT
- Density: 1.40 g/cc
- Tensile Strength at Break: 158 MPa
- Elongation at Break: 2.8 %
- Tensile Modulus: 10.41 GPa
- Flexural Strength: 255 MPa
$ 2344/MT
- Density: 1.64 g/cc
- Water Absorption: 1.0 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 2.5 %
$ 1569/MT
- Density: 1.74 g/cc
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 12.5 GPa
- Flexural Yield Strength: 170 MPa
$ 1718/MT
- Density: 1.56 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength, Yield: 155 MPa
- Elongation at Break: 2.7 %
- Tensile Modulus: 10.9 GPa
$ 1847/MT
- Density: 4.00 g/cc
- Density: 4.00 g/cc
- Moisture Absorption: 0.170 %
- Moisture Absorption: 0.260 %
- Linear Mold Shrinkage, Flow: 0.0044 - 0.0046 cm/cm @Time 86400 sec
$ 1575/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 140 MPa
- Elongation at Break: 10 %
$ 1825/MT
- Density: 1.76 g/cc
- Tensile Strength at Break: 102 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 12.5 GPa
- Flexural Yield Strength: 164 MPa
$ 1481/MT
- Density: 1.70 g/cc
- Tensile Strength at Break: 235 MPa
- Elongation at Break: 1.8 %
- Flexural Strength: 335 MPa
- Flexural Modulus: 19.0 GPa
$ 1549/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 140 MPa
- Elongation at Break: 10 %
$ 1548/MT
- Density: 11.0 g/cc
- Tensile Strength at Break: 43.0 MPa
- Tensile Strength, Yield: 43.0 MPa
- Elongation at Break: 0.40 %
- Elongation at Yield: 0.40 %
$ 2048/MT
- Density: 1.40 g/cc
- Tensile Strength at Break: 174 MPa
- Tensile Strength at Break: 190 MPa
- Elongation at Break: 2.6 %
- Elongation at Break: 2.8 %
$ 1600/MT
- Specific Gravity: 1.26 g/cc
- Tensile Strength at Break: 233 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 24.9 GPa
- Flexural Strength: 345 MPa
$ 1460/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm @Time 86400 sec
- Tensile Strength at Break: 84.0 MPa
- Elongation at Break: 14.7 %
$ 2020/MT
- Specific Gravity: 7.81 g/cc
- Density: 7.79 g/cc
- Moisture Absorption: 0.110 %
- Moisture Absorption: 0.180 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 2175/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Time 86400 sec
- Tensile Strength at Break: 59.0 MPa
- Elongation at Break: 2.3 %
- Tensile Modulus: 5.12 GPa
$ 1477/MT
- Density: 1.39 g/cc
- Density: 1.39 g/cc
- Moisture Absorption: 5.10 %
- Linear Mold Shrinkage, Flow: 0.0028 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 1859/MT
- Density: 1.17 g/cc
- Tensile Strength at Break: 88.0 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 3.97 GPa
- Flexural Strength: 131 MPa
$ 1643/MT
- Density: 1.33 g/cc
- Water Absorption: 2.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.014 - 0.016 cm/cm
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Yield: 5.0 - 7.0 %
$ 1467/MT
- Density: 1.55 g/cc
- Water Absorption: 1.6 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
- Tensile Strength at Break: 64.0 MPa
- Elongation at Break: 2.3 %
$ 2251/MT
- Density: 1.47 g/cc
- Water Absorption: 0.42 % @Time 86400 sec
- Moisture Absorption: 0.0600 %
- Linear Mold Shrinkage, Flow: 0.0029 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0032 cm/cm @Time 86400 sec
$ 1642/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Tensile Strength, Yield: 42.0 MPa
- Elongation at Break: 10 %
- Flexural Yield Strength: 56.0 MPa
$ 1908/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Tensile Strength, Yield: 42.0 MPa
- Elongation at Break: 10 %
- Flexural Yield Strength: 56.0 MPa
$ 1672/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Tensile Strength at Break: 168 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 9.90 GPa
$ 2033/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Tensile Strength at Break: 82.0 MPa
- Elongation at Break: 3.1 %
- Tensile Modulus: 4.87 GPa
$ 2245/MT
- Density: 1.35 g/cc
- Density: 1.354 g/cc
- Moisture Absorption: 0.310 %
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 1658/MT
- Density: 6.78 g/cc
- Moisture Absorption at Equilibrium: 0.090 % @Time 86400 sec
- Tensile Strength at Break: 41.0 MPa
- Tensile Strength, Yield: 42.0 MPa
- Elongation at Break: 10.5 %
$ 1465/MT
- Density: 1.74 g/cc
- Water Absorption: 0.25 % @Time 86400 sec
- Moisture Absorption: 0.0400 %
- Linear Mold Shrinkage, Flow: 0.0033 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0048 cm/cm @Time 86400 sec
$ 1867/MT
- Density: 1.72 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Tensile Strength, Yield: 206 MPa
- Elongation at Break: 3.0 %
- Elongation at Break: 3.7 %
$ 1829/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage, Flow: 0.018 cm/cm
- Tensile Strength, Yield: 42.0 MPa
- Elongation at Break: 10 %
- Flexural Yield Strength: 56.0 MPa
$ 1462/MT
- Density: 3.80 g/cc
- Density: 3.812 g/cc
- Moisture Absorption at Equilibrium: 0.43 %
- Moisture Absorption at Equilibrium: 0.18 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0109 cm/cm @Time 86400 sec
$ 1592/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Tensile Strength at Break: 128 MPa
- Elongation at Break: 2.9 %
- Tensile Modulus: 7.37 GPa
$ 1694/MT
- Density: 1.57 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Time 86400 sec
- Tensile Strength at Break: 62.0 MPa
- Tensile Strength at Break: 62.0 MPa
- Elongation at Break: 2.7 %
$ 1691/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 1.10 %
- Moisture Absorption: 1.70 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 1683/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption at Equilibrium: 1.8 %
- Moisture Absorption at Equilibrium: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 - 0.030 cm/cm @Time 86400 sec
$ 2080/MT
- Density: 1.24 g/cc
- Tensile Strength at Break: 177 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 29.16 GPa
- Flexural Strength: 303 MPa
$ 1551/MT
- Density: 3.06 g/cc
- Density: 3.071 g/cc
- Moisture Absorption: 0.360 %
- Moisture Absorption: 0.490 %
- Linear Mold Shrinkage, Flow: 0.0108 cm/cm @Time 86400 sec
$ 2136/MT
- Density: 1.35 g/cc
- Water Absorption: 1.9 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0044 cm/cm
- Tensile Strength at Break: 93.0 MPa
- Elongation at Break: 2.6 %
$ 1646/MT
- Density: 1.36 g/cc
- Density: 1.37 g/cc
- Moisture Absorption: 0.860 %
- Moisture Absorption: 1.53 %
- Linear Mold Shrinkage, Flow: 0.0017 - 0.0050 cm/cm @Time 86400 sec
$ 1524/MT
- Density: 1.37 g/cc
- Moisture Absorption at Equilibrium: 1.8 %
- Water Absorption at Saturation: 6.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm
$ 1585/MT
- Density: 1.40 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 1.30 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
$ 1466/MT
- Density: 1.63 g/cc
- Tensile Strength at Break: 150 MPa
- Flexural Strength: 248 MPa
- Flexural Modulus: 12.27 GPa
- Izod Impact, Notched: 1.65 J/cm
$ 1555/MT
- Density: 4.49 g/cc
- Density: 4.51 g/cc
- Moisture Absorption: 0.100 %
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Time 86400 sec
$ 1497/MT
- Density: 1.47 g/cc
- Density: 1.47 g/cc
- Moisture Absorption: 0.980 %
- Moisture Absorption: 1.26 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 2230/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 82.0 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 5.04 GPa
$ 2380/MT
- Density: 1.71 g/cc
- Tensile Strength at Break: 210 MPa
- Elongation at Break: 2.4 %
- Tensile Modulus: 22.38 GPa
- Flexural Strength: 365 MPa
$ 1641/MT
- Density: 1.43 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Time 86400 sec
- Tensile Strength at Break: 173 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 11.96 GPa
$ 1715/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Tensile Strength at Break: 123 MPa
- Tensile Strength, Yield: 125 MPa
- Elongation at Break: 3.0 %
$ 1666/MT
- Density: 1.17 g/cc
- Tensile Strength at Break: 88.0 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 3.97 GPa
- Flexural Strength: 131 MPa
$ 2369/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0080 - 0.011 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 43.0 MPa
- Elongation at Break: 150 %
$ 2373/MT
- Density: 1.61 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 228 MPa
- Elongation at Break: 2.2 %
- Tensile Modulus: 17.44 GPa
$ 2217/MT
- Density: 1.46 g/cc
- Density: 1.47 g/cc
- Moisture Absorption: 0.980 %
- Moisture Absorption: 1.26 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Time 86400 sec
$ 2373/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Break: 100 %
$ 1494/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 124 MPa
- Elongation at Break: 2.4 %
- Tensile Modulus: 8.33 GPa
$ 1883/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.0090 cm/cm @Time 86400 sec
- Tensile Strength at Break: 94.0 MPa
- Tensile Strength, Yield: 97.0 MPa
$ 1562/MT
- Density: 1.35 g/cc
- Water Absorption: 1.9 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0044 cm/cm
- Tensile Strength at Break: 93.0 MPa
- Elongation at Break: 2.6 %
$ 2365/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0138 cm/cm
- Tensile Strength at Break: 54.0 MPa
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: 1.4 %
$ 1471/MT
- Specific Gravity: 1.52 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 68.1 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength, Yield: 114 MPa
$ 1723/MT
- Density: 1.32 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Tensile Strength, Yield: 107 MPa
- Elongation at Break: 2.6 %
$ 1608/MT
- Density: 1.49 g/cc
- Tensile Strength at Break: 181 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 12.1 GPa
- Flexural Strength: 250 MPa
$ 2030/MT
- Density: 1.54 g/cc
- Density: 1.54 g/cc
- Moisture Absorption: 0.870 %
- Moisture Absorption: 1.07 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 2030/MT
- Density: 1.43 g/cc
- Moisture Absorption: 0.500 %
- Moisture Absorption: 0.910 %
- Linear Mold Shrinkage, Flow: 0.0038 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
$ 2016/MT
- Specific Gravity: 2.03 g/cc
- Moisture Absorption: 0.400 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0072 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0118 cm/cm @Time 86400 sec
$ 1778/MT
- Density: 1.27 g/cc
- Tensile Strength at Break: 123 MPa
- Elongation at Break: 3.2 %
- Tensile Modulus: 6.35 GPa
- Flexural Strength: 179 MPa
$ 1446/MT
- Density: 1.57 g/cc
- Density: 1.57 g/cc
- Moisture Absorption: 0.830 %
- Moisture Absorption: 0.970 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 1473/MT
- Density: 1.52 g/cc
- Water Absorption: 0.39 % @Time 86400 sec
- Moisture Absorption: 0.0600 %
- Linear Mold Shrinkage, Flow: 0.0024 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0028 cm/cm @Time 86400 sec
$ 2174/MT
- Density: 1.72 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Tensile Strength, Yield: 206 MPa
- Elongation at Break: 3.0 %
- Elongation at Break: 3.7 %
$ 1484/MT
- Density: 1.17 g/cc
- Water Absorption: 6.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm
- Tensile Strength at Break: 44.0 MPa
- Tensile Strength, Yield: 56.0 MPa
$ 1519/MT
- Density: 1.63 g/cc
- Tensile Strength at Break: 150 MPa
- Flexural Strength: 248 MPa
- Flexural Modulus: 12.27 GPa
- Izod Impact, Notched: 1.65 J/cm
$ 2424/MT
- Density: 1.27 g/cc
- Tensile Strength at Break: 123 MPa
- Elongation at Break: 3.2 %
- Tensile Modulus: 6.35 GPa
- Flexural Strength: 179 MPa
$ 1684/MT
- Density: 1.21 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength, Yield: 105 MPa
- Elongation at Yield: >= 3.0 %
- Tensile Modulus: 4.90 GPa
$ 1634/MT
- Density: 1.43 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Time 86400 sec
- Tensile Strength at Break: 173 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 11.96 GPa
$ 2358/MT
- Specific Gravity: 1.35 g/cc
- Density: 1.35 g/cc
- Density: 1.37 g/cc
- Moisture Absorption: 0.830 %
- Moisture Absorption: 0.830 %
$ 1505/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 143 MPa
- Elongation at Break: 2.4 %
- Tensile Modulus: 13.1 GPa
$ 2317/MT
- Density: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 156 MPa
- Tensile Strength at Break: 156 MPa
- Elongation at Break: 2.7 %
$ 1650/MT
- Density: 3.06 g/cc
- Density: 3.071 g/cc
- Moisture Absorption: 0.360 %
- Moisture Absorption: 0.490 %
- Linear Mold Shrinkage, Flow: 0.0108 cm/cm @Time 86400 sec
$ 1734/MT
- Density: 1.36 g/cc
- Moisture Absorption: 1.80 %
- Water Absorption at Saturation: 6.5 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Hardness, Rockwell L: 112
$ 1672/MT
- Density: 1.19 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 52.0 MPa
$ 1763/MT
- Density: 1.26 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength at Break: 182 MPa
- Elongation at Break: 2.2 %
- Flexural Strength: 275 MPa
$ 1510/MT
- Density: 1.52 g/cc
- Water Absorption: 0.39 % @Time 86400 sec
- Moisture Absorption: 0.0600 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0045 cm/cm @Time 86400 sec
$ 1492/MT
- Density: 1.40 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 1.30 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
$ 2377/MT
- Density: 1.52 g/cc
- Water Absorption: 0.39 % @Time 86400 sec
- Moisture Absorption: 0.0600 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0045 cm/cm @Time 86400 sec
$ 1542/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 155 MPa
- Elongation at Break: 2.9 %
- Tensile Modulus: 9.56 GPa
$ 1920/MT
- Density: 1.46 g/cc
- Density: 1.47 g/cc
- Moisture Absorption: 0.980 %
- Moisture Absorption: 1.26 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Time 86400 sec
$ 2298/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.700 %
- Water Absorption at Saturation: 3.6 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
$ 1720/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.013 cm/cm @Time 86400 sec
- Tensile Strength at Break: 165 MPa
- Elongation at Break: 3.0 - 5.0 %
$ 1561/MT
- Density: 1.22 g/cc
- Density: 1.22 g/cc
- Moisture Absorption: 1.30 %
- Linear Mold Shrinkage, Flow: 0.0072 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm @Time 86400 sec
$ 1593/MT
- Density: 1.61 g/cc
- Water Absorption: 0.34 % @Time 86400 sec
- Moisture Absorption: 0.0600 %
- Linear Mold Shrinkage, Flow: 0.0046 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0039 cm/cm @Time 86400 sec
$ 2358/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 107 MPa
- Tensile Strength at Break: 107 MPa
- Elongation at Break: 2.5 %
$ 1606/MT
- Specific Gravity: 1.59 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm
- Tensile Strength at Break: 152 MPa
- Elongation at Break: 2.5 %
$ 1583/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 106 MPa
- Elongation at Break: 3.8 %
$ 1910/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.017 cm/cm
- Tensile Strength, Yield: 35.0 MPa
- Elongation at Yield: 3.7 %
- Tensile Modulus: 1.40 GPa
$ 2332/MT
- Density: 6.00 g/cc
- Tensile Strength at Break: 62.0 MPa
- Elongation at Break: 3.6 %
- Flexural Strength: 96.0 MPa
- Flexural Modulus: 11.5 GPa
$ 1645/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 124 MPa
- Elongation at Break: 2.4 %
- Tensile Modulus: 8.33 GPa
$ 2443/MT
- Specific Gravity: 5.90 g/cc
- Density: 5.90 g/cc
- Density: 6.00 g/cc
- Moisture Absorption at Equilibrium: 0.10 %
- Moisture Absorption at Equilibrium: 0.080 % @Time 86400 sec
$ 1859/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.700 %
- Water Absorption at Saturation: 3.6 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
$ 2329/MT
- Density: 1.61 g/cc
- Water Absorption: 0.34 % @Time 86400 sec
- Moisture Absorption: 0.0600 %
- Linear Mold Shrinkage, Flow: 0.0046 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0039 cm/cm @Time 86400 sec
$ 1487/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.019 - 0.021 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.019 - 0.021 cm/cm @Time 86400 sec
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 100 %
$ 1479/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 3.2 %
- Tensile Modulus: 4.95 GPa
$ 2138/MT
- Specific Gravity: 1.22 g/cc
- Density: 1.22 g/cc
- Moisture Absorption: 1.10 %
- Moisture Absorption: 1.60 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Time 86400 sec
$ 1652/MT
- Density: 1.37 g/cc
- Moisture Absorption: 1.70 %
- Water Absorption at Saturation: 6.5 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Hardness, Rockwell L: 113
$ 1766/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Tensile Strength at Break: 128 MPa
- Elongation at Break: 2.9 %
- Tensile Modulus: 7.37 GPa
$ 1581/MT
- Density: 4.49 g/cc
- Density: 4.51 g/cc
- Moisture Absorption: 0.100 %
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Time 86400 sec
$ 1553/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.014 cm/cm @Time 86400 sec
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 6.0 - 8.0 %
- Tensile Modulus: 3.20 GPa
$ 1452/MT
- Density: 1.57 g/cc
- Density: 1.57 g/cc
- Moisture Absorption: 0.830 %
- Moisture Absorption: 0.970 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 2063/MT
- Density: 1.14 g/cc
- Moisture Absorption: 1.30 %
- Tensile Strength at Break: 76.0 MPa
- Tensile Strength, Yield: 76.0 MPa
- Elongation at Break: 4.5 %
$ 1609/MT
- Density: 1.46 g/cc
- Density: 1.46 g/cc
- Moisture Absorption: 0.640 %
- Moisture Absorption: 1.02 %
- Linear Mold Shrinkage, Flow: 0.0017 cm/cm @Time 86400 sec
$ 1554/MT
- Density: 1.51 g/cc
- Tensile Strength at Break: 109 MPa
- Tensile Strength at Break: 113 MPa
- Tensile Strength, Yield: 110 MPa
- Tensile Strength, Yield: 113 MPa
$ 1541/MT
- Density: 1.18 g/cc
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0041 cm/cm @Time 86400 sec
$ 2166/MT
- Density: 1.10 g/cc
- Water Absorption: 2.3 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Yield: 4.1 %
$ 1664/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.019 - 0.021 cm/cm
- Tensile Strength at Break: >= 50.0 MPa
- Tensile Strength, Yield: 45.0 MPa
- Flexural Yield Strength: 56.0 MPa
$ 1698/MT
- Density: 1.61 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 228 MPa
- Elongation at Break: 2.2 %
- Tensile Modulus: 17.44 GPa
$ 1808/MT
- Density: 1.17 g/cc
- Water Absorption: 1.5 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 114 MPa
- Elongation at Break: 3.6 %
$ 1577/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.24 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 6.60 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Time 86400 sec
$ 1578/MT
- Density: 1.57 g/cc
- Density: 1.57 g/cc
- Moisture Absorption: 0.830 %
- Moisture Absorption: 0.970 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 1457/MT
- Density: 1.47 g/cc
- Density: 1.47 g/cc
- Moisture Absorption: 0.980 %
- Moisture Absorption: 1.26 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 1565/MT
- Specific Gravity: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.010 - 0.013 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength at Break: 64.0 MPa
$ 1553/MT
- Density: 1.43 g/cc
- Moisture Absorption: 0.500 %
- Moisture Absorption: 0.910 %
- Linear Mold Shrinkage, Flow: 0.0038 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
$ 1721/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.014 cm/cm @Time 86400 sec
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 6.0 - 8.0 %
- Tensile Modulus: 3.20 GPa
$ 1450/MT
- Specific Gravity: 1.24 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 117 MPa
- Tensile Strength, Yield: 122 MPa
$ 2266/MT
- Density: 1.58 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength at Break: 233 MPa
- Elongation at Break: 2.3 %
- Flexural Strength: 315 MPa
$ 1686/MT
- Density: 1.63 g/cc
- Density: 1.63 g/cc
- Moisture Absorption: 0.750 %
- Moisture Absorption: 0.980 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1912/MT
- Specific Gravity: 1.46 g/cc
- Moisture Absorption: 0.900 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm @Time 86400 sec
- Tensile Strength at Break: 163 MPa
$ 1909/MT
- Density: 1.36 g/cc
- Density: 1.369 g/cc
- Moisture Absorption: 0.860 %
- Moisture Absorption: 1.53 %
- Linear Mold Shrinkage, Flow: 0.0017 - 0.0050 cm/cm @Time 86400 sec
$ 1535/MT
- Density: 1.54 g/cc
- Water Absorption: 1.0 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Tensile Strength at Break: 64.0 MPa
- Elongation at Break: 1.9 %
$ 1657/MT
- Density: 1.47 g/cc
- Tensile Strength at Break: 112 MPa
- Elongation at Break: 2.3 %
- Tensile Modulus: 8.50 GPa
- Flexural Modulus: 7.29 GPa
$ 1452/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Tensile Strength, Yield: 95.0 MPa
- Elongation at Break: >= 3.0 %
- Tensile Modulus: 5.80 GPa
$ 1650/MT
- Density: 1.48 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 236 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 18.28 GPa
$ 2127/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Tensile Strength at Break: 82.0 MPa
- Elongation at Break: 3.1 %
- Tensile Modulus: 4.87 GPa
$ 1879/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.014 cm/cm @Time 86400 sec
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 6.0 - 8.0 %
- Tensile Modulus: 3.20 GPa
$ 2583/MT
- Density: 1.32 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 87.0 MPa
- Tensile Strength, Yield: 107 MPa
$ 1669/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: >= 8.0 %
- Flexural Yield Strength: 70.0 MPa
$ 1650/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 180 %
$ 2231/MT
- Density: 1.38 g/cc
- Tensile Strength at Break: 188 MPa
- Elongation at Break: 2.7 %
- Tensile Modulus: 9.51 GPa
- Flexural Strength: 249 MPa
$ 1729/MT
- Density: 1.79 g/cc
- Melt Index of Compound: 21 g/10 min @Load 10.0 kg, Temperature 300 °C
- Tensile Strength at Break: 105 MPa
- Elongation at Break: 1.3 %
- Tensile Modulus: 15.0 GPa
$ 2192/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.014 cm/cm @Time 86400 sec
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 6.0 - 8.0 %
- Tensile Modulus: 3.20 GPa
$ 1703/MT
- Specific Gravity: 1.46 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 103 MPa
- Elongation at Break: 10 %
$ 1596/MT
- Density: 1.66 g/cc
- Water Absorption: 0.80 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Tensile Strength at Break: 63.0 MPa
- Elongation at Break: 1.5 %
$ 1641/MT
- Density: 1.31 g/cc
- Water Absorption at Saturation: 6.5 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 3.5 %
$ 2098/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.700 %
- Water Absorption at Saturation: 3.6 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
$ 2097/MT
- Density: 6.00 g/cc
- Tensile Strength, Yield: 51.0 MPa
- Elongation at Yield: 3.5 %
- Tensile Modulus: 0.710 GPa
- Flexural Strength: 68.0 MPa
$ 1926/MT
- Density: 2.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 - 0.011 cm/cm
- Tensile Strength, Yield: 66.0 MPa
- Elongation at Yield: 1.2 %
- Flexural Yield Strength: 99.0 MPa
$ 1725/MT
- Density: 1.32 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Tensile Strength, Yield: 107 MPa
- Elongation at Break: 2.6 %
$ 1596/MT
- Specific Gravity: 1.28 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 117 MPa
- Elongation at Break: 15 %
$ 1620/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: 2.0 - 3.0 %
- Tensile Modulus: 4.80 GPa
$ 1942/MT
- Density: 1.55 g/cc
- Water Absorption: 0.40 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm
- Tensile Strength at Break: 212 MPa
- Elongation at Break: 3.4 %
$ 1619/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.019 - 0.021 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.019 - 0.021 cm/cm @Time 86400 sec
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 100 %
$ 2214/MT
- Density: 1.52 g/cc
- Moisture Absorption: 0.0600 %
- Linear Mold Shrinkage, Flow: 0.0058 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0053 cm/cm
- Tensile Strength at Break: 51.0 MPa
$ 2516/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm @Time 86400 sec
- Tensile Strength at Break: 84.0 MPa
- Elongation at Break: 14.7 %
$ 2467/MT
- Density: 1.36 g/cc
- Density: 1.369 g/cc
- Moisture Absorption: 0.860 %
- Moisture Absorption: 1.53 %
- Linear Mold Shrinkage, Flow: 0.0017 - 0.0050 cm/cm @Time 86400 sec
$ 1918/MT
- Specific Gravity: 1.33 g/cc
- Density: 1.33 g/cc
- Moisture Absorption: 0.750 %
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 2032/MT
- Density: 1.71 g/cc
- Tensile Strength at Break: 210 MPa
- Elongation at Break: 2.4 %
- Tensile Modulus: 22.38 GPa
- Flexural Strength: 365 MPa
$ 1476/MT
- Density: 1.56 g/cc
- Tensile Strength at Break: 230 MPa
- Flexural Strength: 324 MPa
- Flexural Modulus: 12.96 GPa
- Izod Impact, Notched: 2.88 J/cm @Temperature 23.0 °C
- Deflection Temperature at 1.8 MPa (264 psi): 216 °C @Thickness 3.20 mm
$ 1830/MT
- Density: 1.79 g/cc
- Water Absorption: 0.23 % @Time 86400 sec
- Moisture Absorption: 0.0400 %
- Linear Mold Shrinkage, Flow: 0.0042 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0058 cm/cm @Time 86400 sec
$ 2049/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Tensile Strength at Break: 2.00 MPa
- Tensile Strength, Yield: 136 MPa
- Elongation at Break: 3.9 %
$ 1917/MT
- Density: 1.32 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 87.0 MPa
$ 1731/MT
- Density: 1.18 g/cc
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0041 cm/cm @Time 86400 sec
$ 1847/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Break: 120 %
$ 1619/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Tensile Strength at Break: 95.0 MPa
- Elongation at Break: 4.0 %
- Flexural Strength: 140 MPa
$ 1460/MT
- Density: 1.54 g/cc
- Density: 1.54 g/cc
- Moisture Absorption: 0.870 %
- Moisture Absorption: 1.07 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 1449/MT
- Density: 1.39 g/cc
- Tensile Strength at Break: 175 MPa
- Tensile Strength at Break: 178 MPa
- Elongation at Break: 2.6 %
- Elongation at Break: 2.8 %
$ 1544/MT
- Specific Gravity: 1.48 g/cc
- Tensile Strength at Break: 53.0 MPa
- Elongation at Break: 1.0 %
- Tensile Modulus: 9.69 GPa
- Flexural Strength: 82.0 MPa
$ 2250/MT
- Density: 1.51 g/cc
- Tensile Strength at Break: 109 MPa
- Tensile Strength at Break: 113 MPa
- Tensile Strength, Yield: 110 MPa
- Tensile Strength, Yield: 113 MPa
$ 1943/MT
- Density: 1.40 g/cc
- Density: 1.40 g/cc
- Moisture Absorption at Equilibrium: 0.89 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
$ 1624/MT
- Density: 1.52 g/cc
- Water Absorption: 1.3 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm
- Tensile Strength at Break: 121 MPa
- Tensile Strength, Yield: 121 MPa
$ 1789/MT
- Density: 1.13 g/cc
- Tensile Strength at Break: 43.0 MPa
- Tensile Strength, Yield: 70.0 MPa
- Elongation at Break: 6.6 %
- Tensile Modulus: 2.50 GPa
$ 1534/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Time 86400 sec
- Tensile Strength at Break: 59.0 MPa
- Elongation at Break: 2.3 %
- Tensile Modulus: 5.12 GPa
$ 2311/MT
- Density: 1.27 g/cc
- Moisture Absorption: 1.40 %
- Water Absorption at Saturation: 6.8 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm
- Hardness, Rockwell L: 123
$ 2093/MT
- Water Absorption: 2.2 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Tensile Strength at Break: 44.0 MPa
- Elongation at Break: 6.7 %
- Elongation at Yield: 3.9 %
$ 1448/MT
- Density: 2.35 g/cc
- Density: 2.36 g/cc
- Moisture Absorption: 0.190 %
- Moisture Absorption: 0.340 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 1563/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 143 MPa
- Elongation at Break: 2.4 %
- Tensile Modulus: 13.1 GPa
$ 2234/MT
- Density: 1.61 g/cc
- Water Absorption: 0.34 % @Time 86400 sec
- Moisture Absorption: 0.0600 %
- Linear Mold Shrinkage, Flow: 0.0019 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0021 cm/cm @Time 86400 sec
$ 1699/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Tensile Strength at Break: 168 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 9.90 GPa
Delivery Nylon 6 SABIC Innovative Plastics (GE Plastics)
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
lng tankers for sale in usa. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.