$ 1750/MT
- Density: 1.35 g/cc
- Tensile Strength at Break: 136 MPa
- Tensile Strength, Yield: 136 MPa
- Elongation at Break: 1.9 %
- Elongation at Yield: 1.9 %
$ 1444/MT
- Density: 1.22 g/cc
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.00080 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm @Time 86400 sec
$ 1790/MT
- Density: 1.21 g/cc
- Linear Mold Shrinkage, Flow: 0.0027 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0053 cm/cm @Time 86400 sec
$ 1567/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.030 %
- Water Absorption at Saturation: 0.040 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm
$ 2136/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Time 86400 sec
- Tensile Strength at Break: 23.0 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 2.99 GPa
$ 1446/MT
- Density: 1.33 g/cc
- Density: 1.35 g/cc
- Tensile Strength at Break: 131 MPa
- Tensile Strength at Break: 141 MPa
- Elongation at Break: 1.7 %
$ 1986/MT
- Specific Gravity: 1.04 g/cc
- Density: 1.04 g/cc
- Filler Content: 20 %
- Tensile Strength at Break: 80.0 MPa
- Tensile Strength at Break: 40.0 MPa @Temperature 120 °C
$ 2035/MT
- Density: 1.13 g/cc
- Density: 1.13 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Moisture Absorption at Equilibrium: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 - 0.030 cm/cm @Time 86400 sec
$ 1672/MT
- Density: 1.00 g/cc
- Tensile Strength at Break: 27.0 MPa
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Break: 21 %
- Elongation at Yield: 6.5 %
$ 1953/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
- Tensile Strength at Break: 87.0 MPa
- Elongation at Break: 2.7 %
- Flexural Strength: 129 MPa
$ 1447/MT
- Specific Gravity: 1.14 g/cc
- Density: 1.14 g/cc
- Moisture Absorption: 0.0100 %
- Moisture Absorption: 0.0200 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1694/MT
- Density: 1.14 g/cc
- Density: 1.14 g/cc
- Moisture Absorption: 0.0300 %
- Moisture Absorption: 0.0400 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Time 86400 sec
$ 1451/MT
- Density: 1.12 g/cc
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0151 - 0.0167 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.015 - 0.017 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0151 - 0.0167 cm/cm @Time 86400 sec
$ 1901/MT
- Density: 1.01 g/cc
- Density: 1.01 g/cc
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm @Time 86400 sec
- Tensile Strength at Break: 15.0 MPa
$ 1603/MT
- Specific Gravity: 1.21 g/cc
- Density: 1.22 g/cc
- Filler Content: 40 %
- Tensile Strength at Break: 108 MPa
- Tensile Strength at Break: 121 MPa
$ 1648/MT
- Density: 0.960 g/cc
- Water Absorption: 0.070 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Tensile Strength, Yield: 32.0 MPa
- Elongation at Break: 34 %
$ 1580/MT
- Density: 0.970 g/cc
- Density: 1.12 g/cc
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Break: 70 %
$ 1510/MT
- Density: 0.970 g/cc
- Density: 0.970 g/cc
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Break: 70 %
$ 1669/MT
- Density: 1.11 g/cc
- Tensile Strength, Yield: 81.0 MPa
- Elongation at Yield: 2.6 %
- Tensile Modulus: 5.70 GPa
- Flexural Yield Strength: 105 MPa
$ 1914/MT
- Density: 1.13 g/cc
- Water Absorption: 0.010 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Tensile Strength at Break: 56.0 MPa
- Elongation at Break: 2.5 %
$ 2113/MT
- Specific Gravity: 1.03 g/cc
- Density: 1.03 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
$ 1688/MT
- Specific Gravity: 1.03 g/cc
- Density: 1.03 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm
$ 1592/MT
- Specific Gravity: 0.960 g/cc
- Density: 0.950 g/cc
- Moisture Absorption at Equilibrium: 0.030 %
- Moisture Absorption at Equilibrium: 0.020 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 - 0.030 cm/cm @Time 86400 sec
$ 1798/MT
- Specific Gravity: 0.940 g/cc
- Density: 0.940 g/cc
- Moisture Absorption: 0.0100 %
- Moisture Absorption: 0.0600 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 1531/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 66.0 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 7.76 GPa
$ 1528/MT
- Specific Gravity: 1.13 g/cc
- Density: 1.13 g/cc
- Moisture Absorption: 0.0700 %
- Moisture Absorption: 0.130 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Time 86400 sec
$ 1475/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Time 86400 sec
- Tensile Strength at Break: 71.0 MPa
- Elongation at Break: 1.8 %
- Tensile Modulus: 9.30 GPa
$ 2005/MT
- Specific Gravity: 0.970 g/cc
- Density: 0.970 g/cc
- Moisture Absorption at Equilibrium: 0.020 %
- Water Absorption at Saturation: 0.060 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm @Thickness 3.20 mm
$ 2235/MT
- Density: 1.03 g/cc
- Density: 1.03 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.011 - 0.013 cm/cm @Time 86400 sec
$ 2148/MT
- Density: 0.930 g/cc
- Density: 0.930 g/cc
- Moisture Absorption: 0.160 %
- Moisture Absorption: 0.160 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 2309/MT
- Density: 1.12 g/cc
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0098 cm/cm @Time 86400 sec
$ 1674/MT
- Density: 0.970 g/cc
- Density: 0.980 g/cc
- Moisture Absorption: 0.0300 %
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Time 86400 sec
$ 1704/MT
- Density: 0.970 g/cc
- Linear Mold Shrinkage, Flow: 0.015 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm @Time 86400 sec
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 19.0 MPa
$ 1587/MT
- Density: 1.94 g/cc
- Density: 1.952 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0095 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Time 86400 sec
$ 1470/MT
- Specific Gravity: 0.980 g/cc
- Density: 0.980 g/cc
- Moisture Absorption: 0.0100 %
- Moisture Absorption: 0.0200 %
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
$ 1789/MT
- Density: 1.22 g/cc
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.00080 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm @Time 86400 sec
$ 1656/MT
- Density: 0.970 g/cc
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 3.7 %
- Tensile Modulus: 3.24 GPa
- Flexural Strength: 68.0 MPa
$ 1551/MT
- Specific Gravity: 0.970 g/cc
- Density: 0.970 g/cc
- Linear Mold Shrinkage, Flow: 0.0069 cm/cm
- Linear Mold Shrinkage, Flow: 0.0074 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
$ 1593/MT
- Specific Gravity: 1.59 g/cc
- Density: 1.59 g/cc
- Moisture Absorption: 0.0200 %
- Moisture Absorption: 0.0300 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Time 86400 sec
$ 1623/MT
- Density: 1.07 g/cc
- Tensile Strength at Break: 8.00 MPa
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Break: >= 100 %
- Elongation at Yield: 7.4 %
$ 1635/MT
- Density: 1.13 g/cc
- Density: 1.134 g/cc
- Moisture Absorption: 0.0200 %
- Moisture Absorption: 0.0300 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
$ 1698/MT
- Specific Gravity: 1.03 g/cc
- Density: 1.03 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.12 %
- Melt Flow: 13.8 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1611/MT
- Specific Gravity: 0.980 g/cc
- Density: 0.980 g/cc
- Moisture Absorption: 0.0100 %
- Moisture Absorption: 0.0200 %
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
$ 1645/MT
- Density: 0.990 g/cc
- Melt Index of Compound: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
- Hardness, Rockwell R: 70
- Tensile Strength at Break: 34.0 MPa
- Tensile Strength, Yield: 36.0 MPa
$ 1570/MT
- Density: 1.03 g/cc
- Tensile Strength at Break: 49.0 MPa
- Elongation at Break: 3.1 %
- Tensile Modulus: 4.77 GPa
- Flexural Strength: 77.9 MPa
$ 1658/MT
- Specific Gravity: 1.19 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1745/MT
- Density: 4.00 g/cc
- Linear Mold Shrinkage, Flow: 0.0089 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0101 cm/cm @Time 86400 sec
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 16.0 MPa
$ 1686/MT
- Specific Gravity: 1.19 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1479/MT
- Density: 1.33 g/cc
- Density: 1.33 g/cc
- Tensile Strength at Break: 131 MPa
- Tensile Strength at Break: 141 MPa
- Elongation at Break: 1.7 %
$ 1479/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm @Thickness 3.20 mm
- Melt Flow: 10.6 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 32.0 MPa
- Tensile Strength, Yield: 35.0 MPa
$ 1760/MT
- Density: 1.12 g/cc
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0027 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0059 cm/cm @Time 86400 sec
$ 1877/MT
- Density: 1.33 g/cc
- Density: 1.35 g/cc
- Tensile Strength at Break: 131 MPa
- Tensile Strength at Break: 141 MPa
- Elongation at Break: 1.7 %
$ 1544/MT
- Density: 1.30 g/cc
- Melt Index of Compound: 3.0 g/10 min @Load 5.00 kg, Temperature 260 °C
- Hardness, H358/30: 100 MPa
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 2.2 %
$ 1633/MT
- Density: 1.04 g/cc
- Filler Content: 20 %
- Tensile Strength at Break: 90.0 MPa
- Tensile Strength at Break: 45.0 MPa @Temperature 120 °C
- Tensile Strength at Break: 60.0 MPa @Temperature 80.0 °C
$ 1805/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 57.0 MPa
- Elongation at Break: 2.9 %
- Tensile Modulus: 5.27 GPa
$ 1920/MT
- Density: 1.35 g/cc
- Water Absorption: 0.010 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm
- Tensile Strength at Break: 19.0 MPa
- Tensile Strength, Yield: 22.0 MPa
$ 1675/MT
- Density: 4.00 g/cc
- Linear Mold Shrinkage, Flow: 0.0089 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0101 cm/cm @Time 86400 sec
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 16.0 MPa
$ 2401/MT
- Density: 1.01 g/cc
- Density: 1.01 g/cc
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm @Time 86400 sec
- Tensile Strength at Break: 15.0 MPa
$ 1565/MT
- Specific Gravity: 1.13 g/cc
- Density: 1.12 g/cc
- Filler Content: 30 %
- Tensile Strength at Break: 97.0 MPa
- Tensile Strength at Break: 110 MPa
$ 1517/MT
- Density: 1.33 g/cc
- Density: 1.35 g/cc
- Tensile Strength at Break: 131 MPa
- Tensile Strength at Break: 141 MPa
- Elongation at Break: 1.7 %
$ 1785/MT
- Specific Gravity: 1.04 g/cc
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm
- Melt Flow: 20 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1570/MT
- Density: 0.970 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 48.0 MPa
- Elongation at Break: 3.2 %
- Tensile Modulus: 3.61 GPa
$ 1736/MT
- Specific Gravity: 0.970 g/cc
- Density: 0.960 g/cc
- Moisture Absorption: 0.0100 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.030 cm/cm @Time 86400 sec
$ 1730/MT
- Specific Gravity: 1.19 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2342/MT
- Density: 1.48 g/cc
- Tensile Strength at Break: 137 MPa
- Tensile Modulus: 16.9 GPa
- Flexural Strength: 232 MPa
- Flexural Modulus: 15.0 GPa
$ 1456/MT
- Density: 1.22 g/cc
- Water Absorption: 0.020 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0050 cm/cm
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Break: 3.3 %
$ 1521/MT
- Density: 5.00 g/cc
- Density: 5.00 g/cc
- Moisture Absorption at Equilibrium: 0.050 %
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Time 86400 sec
$ 1456/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 9.80 GPa
$ 1923/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 9.80 GPa
$ 1994/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 9.80 GPa
$ 1736/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Time 86400 sec
- Tensile Strength at Break: 87.0 MPa
- Elongation at Break: 1.6 %
$ 1613/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Tensile Strength at Break: 71.0 MPa
- Elongation at Break: 2.9 %
- Tensile Modulus: 7.60 GPa
$ 1454/MT
- Specific Gravity: 0.950 g/cc
- Density: 0.950 g/cc
- Moisture Absorption: 0.0400 %
- Moisture Absorption: 0.0400 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Time 86400 sec
$ 1598/MT
- Density: 1.22 g/cc
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.00080 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm @Time 86400 sec
$ 2139/MT
- Density: 0.970 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 48.0 MPa
- Elongation at Break: 3.2 %
- Tensile Modulus: 3.61 GPa
$ 2129/MT
- Density: 0.970 g/cc
- Density: 0.980 g/cc
- Moisture Absorption at Equilibrium: 0.030 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Time 86400 sec
$ 1736/MT
- Density: 1.03 g/cc
- Density: 1.03 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.011 - 0.013 cm/cm @Time 86400 sec
$ 1656/MT
- Density: 5.03 g/cc
- Density: 5.04 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.017 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.016 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm @Time 86400 sec
$ 2464/MT
- Density: 1.12 g/cc
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0026 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0059 cm/cm @Time 86400 sec
$ 1494/MT
- Specific Gravity: 1.19 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1499/MT
- Density: 1.03 g/cc
- Moisture Absorption: 0.0200 %
- Moisture Absorption: 0.0200 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.020 - 0.040 cm/cm @Time 86400 sec
$ 1597/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm @Time 86400 sec
- Tensile Strength at Break: 73.0 MPa
- Elongation at Break: 2.2 %
$ 1520/MT
- Density: 1.12 g/cc
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0026 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0059 cm/cm @Time 86400 sec
$ 1627/MT
- Density: 0.960 g/cc
- Density: 0.960 g/cc
- Linear Mold Shrinkage, Flow: 0.0129 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0138 cm/cm @Time 86400 sec
$ 1534/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 9.80 GPa
$ 1667/MT
- Density: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0081 cm/cm @Time 86400 sec
- Tensile Strength at Break: 104 MPa
- Elongation at Break: 2.0 %
$ 1498/MT
- Density: 1.12 g/cc
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0027 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0059 cm/cm @Time 86400 sec
$ 1939/MT
- Specific Gravity: 0.990 g/cc
- Density: 0.990 g/cc
- Moisture Absorption: 0.0200 %
- Water Absorption at Saturation: 0.050 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 2352/MT
- Density: 1.33 g/cc
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0013 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0028 cm/cm @Time 86400 sec
- Tensile Strength at Break: 131 MPa
$ 1739/MT
- Specific Gravity: 1.01 g/cc
- Density: 1.012 g/cc
- Moisture Absorption: 0.0200 %
- Moisture Absorption: 0.0200 %
- Linear Mold Shrinkage, Flow: 0.014 cm/cm @Time 86400 sec
$ 1786/MT
- Density: 1.94 g/cc
- Density: 1.952 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0095 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Time 86400 sec
$ 2543/MT
- Density: 1.14 g/cc
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0092 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm @Time 86400 sec
$ 1717/MT
- Density: 1.00 g/cc
- Tensile Strength at Break: 16.0 MPa
- Tensile Strength, Yield: 27.0 MPa
- Elongation at Break: 24 %
- Elongation at Yield: 4.3 %
$ 2171/MT
- Density: 1.03 g/cc
- Tensile Strength at Break: 28.0 MPa
- Elongation at Break: 32 %
- Tensile Modulus: 1.58 GPa
- Flexural Strength: 34.0 MPa
$ 1687/MT
- Density: 0.950 g/cc
- Density: 0.950 g/cc
- Moisture Absorption: 0.0300 %
- Moisture Absorption: 0.0300 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm @Time 86400 sec
$ 1565/MT
- Density: 1.00 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Tensile Strength at Break: 59.0 MPa
- Elongation at Break: 3.2 %
- Elongation at Break: 5.8 %
$ 1779/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.017 cm/cm
- Tensile Strength at Break: 16.0 MPa
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Yield: 6.3 %
$ 1676/MT
- Density: 1.22 g/cc
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.00080 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm @Time 86400 sec
$ 1550/MT
- Density: 0.990 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 37.0 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 3.137 GPa
$ 2562/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength at Break: 50.0 MPa
- Elongation at Break: 3.5 %
- Tensile Modulus: 4.50 GPa
$ 2250/MT
- Specific Gravity: 1.22 g/cc
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1981/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Time 86400 sec
- Tensile Strength at Break: 23.0 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 2.99 GPa
$ 1451/MT
- Density: 0.990 g/cc
- Density: 0.990 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0052 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm @Time 86400 sec
$ 1633/MT
- Specific Gravity: 1.00 g/cc
- Density: 0.998 g/cc
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 25.0 MPa
$ 1530/MT
- Density: 1.33 g/cc
- Density: 1.33 g/cc
- Tensile Strength at Break: 131 MPa
- Tensile Strength at Break: 141 MPa
- Elongation at Break: 1.7 %
$ 1674/MT
- Density: 1.14 g/cc
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0092 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm @Time 86400 sec
$ 1459/MT
- Specific Gravity: 1.26 g/cc
- Density: 1.25 g/cc
- Melt Flow: 18 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 75
- Tensile Strength at Break: 24.0 MPa
$ 1450/MT
- Specific Gravity: 1.02 g/cc
- Density: 1.01 g/cc
- Moisture Absorption: 0.0200 %
- Moisture Absorption: 0.0200 %
- Linear Mold Shrinkage, Flow: 0.0080 - 0.020 cm/cm @Time 86400 sec
$ 2035/MT
- Density: 1.03 g/cc
- Tensile Strength at Break: 49.0 MPa
- Elongation at Break: 3.1 %
- Tensile Modulus: 4.77 GPa
- Flexural Strength: 77.9 MPa
$ 1767/MT
- Density: 1.10 g/cc
- Moisture Absorption: 0.0100 %
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 55.0 MPa
$ 2134/MT
- Density: 1.91 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm
- Tensile Strength at Break: 18.0 MPa
- Elongation at Break: 25 %
- Tensile Modulus: 4.50 GPa
$ 1631/MT
- Density: 1.33 g/cc
- Tensile Strength at Break: 118 MPa
- Elongation at Break: 1.6 %
- Tensile Modulus: 11.3 GPa
- Flexural Strength: 180 MPa
$ 1987/MT
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Tensile Strength, Yield: 78.0 MPa
- Elongation at Yield: 3.1 %
- Tensile Modulus: 4.70 GPa
$ 1639/MT
- Specific Gravity: 1.12 g/cc
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm
- Melt Flow: 12 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1499/MT
- Density: 0.970 g/cc
- Linear Mold Shrinkage, Flow: 0.015 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm @Time 86400 sec
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 19.0 MPa
$ 1654/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Tensile Strength at Break: 71.0 MPa
- Elongation at Break: 2.9 %
- Tensile Modulus: 7.60 GPa
$ 2033/MT
- Density: 1.11 g/cc
- Density: 1.12 g/cc
- Moisture Absorption: 0.0200 %
- Linear Mold Shrinkage, Flow: 0.0116 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Time 86400 sec
$ 1897/MT
- Specific Gravity: 1.16 g/cc
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0075 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0125 cm/cm
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1530/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 68.0 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 5.70 GPa
$ 1482/MT
- Specific Gravity: 1.14 g/cc
- Density: 1.13 g/cc
- Melt Flow: 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 68
- Tensile Strength at Break: 16.0 MPa
$ 1561/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 86.0 MPa
- Elongation at Break: 3.0 %
$ 2129/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.030 %
- Water Absorption at Saturation: 0.040 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm
$ 1575/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0023 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0076 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.6 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 79.0 MPa
$ 1476/MT
- Density: 1.14 g/cc
- Water Absorption: 0.020 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm
- Tensile Strength at Break: 45.0 MPa
- Tensile Strength, Yield: 47.0 MPa
$ 2051/MT
- Density: 1.22 g/cc
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.00080 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm @Time 86400 sec
$ 2092/MT
- Specific Gravity: 0.960 g/cc
- Density: 0.960 g/cc
- Moisture Absorption: 0.0200 %
- Moisture Absorption: 0.0600 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 2024/MT
- Density: 0.970 g/cc
- Density: 0.980 g/cc
- Moisture Absorption: 0.0300 %
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Time 86400 sec
$ 1509/MT
- Density: 1.15 g/cc
- Tensile Strength at Break: 35.0 MPa
- Elongation at Break: 1.0 %
- Tensile Modulus: 5.81 GPa
- Flexural Strength: 55.0 MPa
$ 1914/MT
- Density: 0.980 g/cc
- Moisture Absorption: 0.0300 %
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0158 - 0.018 cm/cm @Time 86400 sec
$ 1480/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.030 %
- Water Absorption at Saturation: 0.040 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm
$ 1872/MT
- Density: 0.950 g/cc
- Density: 0.950 g/cc
- Moisture Absorption: 0.850 %
- Linear Mold Shrinkage, Flow: 0.0135 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.014 cm/cm @Time 86400 sec
$ 1763/MT
- Specific Gravity: 1.26 g/cc
- Density: 1.26 g/cc
- Melt Flow: 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 75
- Tensile Strength at Break: 28.0 MPa
$ 1846/MT
- Density: 1.01 g/cc
- Density: 1.01 g/cc
- Moisture Absorption: 0.0500 %
- Moisture Absorption: 0.0500 %
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Time 86400 sec
$ 1597/MT
- Tensile Strength at Break: 41.0 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 65.0 MPa
- Flexural Modulus: 5.10 GPa
- Izod Impact, Notched: 0.530 J/cm
$ 1861/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm @Thickness 3.20 mm
- Melt Flow: 10.6 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 32.0 MPa
- Tensile Strength, Yield: 35.0 MPa
$ 2221/MT
- Density: 1.22 g/cc
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.00080 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm @Time 86400 sec
$ 2053/MT
- Specific Gravity: 1.03 g/cc
- Density: 1.03 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.12 %
- Melt Flow: 13.8 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1678/MT
- Specific Gravity: 1.13 g/cc
- Density: 1.12 g/cc
- Filler Content: 30 %
- Tensile Strength at Break: 97.0 MPa
- Tensile Strength at Break: 110 MPa
$ 1658/MT
- Density: 1.40 g/cc
- Tensile Strength at Break: 140 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 14.0 GPa
- Flexural Strength: 209 MPa
$ 1703/MT
- Specific Gravity: 0.990 g/cc
- Density: 0.990 g/cc
- Moisture Absorption: 0.0200 %
- Water Absorption at Saturation: 0.050 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1894/MT
- Density: 1.12 g/cc
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0026 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0059 cm/cm @Time 86400 sec
$ 2042/MT
- Specific Gravity: 1.19 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1614/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 66.0 MPa
- Elongation at Break: 3.1 %
$ 1580/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.019 cm/cm
- Tensile Strength at Break: 22.0 MPa
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 4.8 %
$ 2024/MT
- Density: 1.21 g/cc
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.014 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.013 - 0.015 cm/cm @Time 86400 sec
$ 1769/MT
- Density: 0.970 g/cc
- Melt Index of Compound: 11 g/10 min @Load 5.00 kg, Temperature 260 °C
- Hardness, H358/30: 65.0 MPa
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 34.0 MPa
$ 1543/MT
- Specific Gravity: 1.03 g/cc
- Density: 1.03 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.12 %
- Melt Flow: 13.8 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1678/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.05 g/cc
- Moisture Absorption: 0.0100 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.030 cm/cm @Time 86400 sec
$ 2031/MT
- Density: 1.01 g/cc
- Density: 1.02 g/cc
- Moisture Absorption: 0.0100 %
- Moisture Absorption: 0.0200 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 1581/MT
- Specific Gravity: 0.980 g/cc
- Density: 0.980 g/cc
- Moisture Absorption at Equilibrium: 0.010 %
- Moisture Absorption at Equilibrium: 0.020 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
$ 1723/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Tensile Strength, Yield: 23.0 MPa
- Elongation at Break: 19.6 %
- Tensile Modulus: 1.30 GPa
$ 1807/MT
- Specific Gravity: 1.00 g/cc
- Density: 0.990 g/cc
- Melt Flow: 23 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 18.0 MPa
- Tensile Strength, Yield: 25.0 MPa
$ 1821/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 66.0 MPa
- Elongation at Break: 3.1 %
$ 2224/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0017 - 0.0018 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0027 - 0.0061 cm/cm @Thickness 3.20 mm
- Melt Flow: 1.3 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 95.0 MPa
$ 2481/MT
- Specific Gravity: 1.21 g/cc
- Density: 1.22 g/cc
- Filler Content: 40 %
- Tensile Strength at Break: 108 MPa
- Tensile Strength at Break: 121 MPa
$ 1503/MT
- Density: 1.00 g/cc
- Water Absorption: 0.010 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.016 cm/cm
- Tensile Strength at Break: 25.0 MPa
- Tensile Strength, Yield: 38.0 MPa
$ 1551/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength, Yield: 120 MPa
- Elongation at Break: 2.0 %
- Elongation at Break: 2.3 %
$ 1457/MT
- Density: 1.07 g/cc
- Density: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm @Time 86400 sec
$ 1467/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 28.0 MPa
- Elongation at Break: 23.4 %
- Tensile Modulus: 2.59 GPa
$ 1444/MT
- Density: 0.970 g/cc
- Density: 0.980 g/cc
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.016 - 0.018 cm/cm @Time 86400 sec
$ 1484/MT
- Density: 2.55 g/cc
- Tensile Strength, Yield: 14.0 MPa
- Elongation at Break: >= 5.0 %
- Flexural Yield Strength: 28.0 MPa
- Flexural Modulus: 4.40 GPa
$ 1704/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 66.0 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 7.76 GPa
$ 2084/MT
- Density: 1.02 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.016 cm/cm
- Tensile Strength, Yield: 33.0 MPa
- Elongation at Yield: 4.4 %
- Tensile Modulus: 2.70 GPa
$ 1628/MT
- Specific Gravity: 0.990 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 34.0 MPa
$ 1559/MT
- Density: 1.07 g/cc
- Density: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm @Time 86400 sec
$ 1453/MT
- Density: 1.12 g/cc
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0027 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0059 cm/cm @Time 86400 sec
$ 2492/MT
- Density: 1.12 g/cc
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0098 cm/cm @Time 86400 sec
$ 1489/MT
- Density: 1.05 g/cc
- Density: 1.05 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.011 - 0.013 cm/cm @Time 86400 sec
$ 1780/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.04 g/cc
- Melt Flow: 22 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 60
- Tensile Strength at Break: 16.0 MPa
$ 1791/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.04 g/cc
- Melt Flow: 17 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 80.0 MPa
- Tensile Strength at Break: 87.0 MPa
$ 1474/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.017 cm/cm
- Tensile Strength at Break: 16.0 MPa
- Tensile Strength, Yield: 21.0 MPa
- Elongation at Yield: 6.3 %
$ 1588/MT
- Density: 1.33 g/cc
- Density: 1.33 g/cc
- Tensile Strength at Break: 131 MPa
- Tensile Strength at Break: 141 MPa
- Elongation at Break: 1.7 %
$ 1668/MT
- Specific Gravity: 0.990 g/cc
- Density: 0.990 g/cc
- Moisture Absorption: 0.0100 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.020 - 0.040 cm/cm @Time 86400 sec
$ 1897/MT
- Specific Gravity: 0.990 g/cc
- Density: 0.990 g/cc
- Moisture Absorption: 0.0100 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.020 - 0.040 cm/cm @Time 86400 sec
$ 1724/MT
- Density: 1.01 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Tensile Strength, Yield: 48.0 MPa
- Elongation at Break: 1.0 %
- Flexural Yield Strength: 65.0 MPa
$ 2016/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.021 cm/cm
- Tensile Strength at Break: 19.0 MPa
- Tensile Strength, Yield: 28.0 MPa
- Elongation at Yield: 4.8 %
$ 1504/MT
- Density: 1.00 g/cc
- Linear Mold Shrinkage, Flow: 0.00050 - 0.0025 cm/cm
- Tensile Strength at Break: 48.0 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 8.10 GPa
$ 1578/MT
- Specific Gravity: 1.02 g/cc
- Density: 1.02 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm
- Linear Mold Shrinkage, Flow: 0.010 cm/cm
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm
$ 2223/MT
- Density: 1.01 g/cc
- Density: 1.01 g/cc
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm @Time 86400 sec
- Tensile Strength at Break: 15.0 MPa
$ 1481/MT
- Density: 0.940 g/cc
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 39.0 MPa
- Elongation at Break: 4.9 %
- Tensile Modulus: 2.28 GPa
$ 1914/MT
- Specific Gravity: 0.990 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 34.0 MPa
$ 1899/MT
- Specific Gravity: 1.03 g/cc
- Density: 1.03 g/cc
- Moisture Absorption: 0.0100 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.030 cm/cm @Time 86400 sec
$ 1559/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.04 g/cc
- Melt Flow: 13 g/10 min @Load 2.16 kg, Temperature 230 °C
- Hardness, Shore D: 71
- Tensile Strength at Break: 17.0 MPa
$ 2235/MT
- Density: 1.06 g/cc
- Tensile Strength at Break: 59.0 MPa
- Elongation at Break: 0.50 %
- Flexural Strength: 85.0 MPa
- Flexural Modulus: 11.03 GPa
$ 2540/MT
- Density: 1.12 g/cc
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0065 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0098 cm/cm @Time 86400 sec
$ 1879/MT
- Density: 0.940 g/cc
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 39.0 MPa
- Elongation at Break: 4.9 %
- Tensile Modulus: 2.28 GPa
$ 2169/MT
- Specific Gravity: 0.980 g/cc
- Density: 0.974 g/cc
- Moisture Absorption: 0.0200 %
- Moisture Absorption: 0.0200 %
- Linear Mold Shrinkage, Flow: 0.017 cm/cm @Time 86400 sec
$ 2075/MT
- Specific Gravity: 0.990 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 260 °C
- Melt Index of Compound: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1671/MT
- Density: 1.48 g/cc
- Tensile Strength at Break: 41.0 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 5.58 GPa
- Flexural Strength: 68.0 MPa
$ 1491/MT
- Specific Gravity: 1.22 g/cc
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 230 °C
$ 1472/MT
- Specific Gravity: 0.990 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 10.5 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 33.0 MPa
$ 1831/MT
- Specific Gravity: 1.46 g/cc
- Density: 1.46 g/cc
- Moisture Absorption at Equilibrium: 0.030 %
- Moisture Absorption at Equilibrium: 0.020 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Time 86400 sec
$ 1480/MT
- Specific Gravity: 1.04 g/cc
- Density: 1.03 g/cc
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 230 °C
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 22.0 MPa
$ 1787/MT
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0012 cm/cm
- Tensile Strength, Yield: 81.0 MPa
- Elongation at Yield: 1.9 %
- Tensile Modulus: 6.50 GPa
$ 2470/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 57.0 MPa
- Elongation at Break: 2.9 %
- Tensile Modulus: 5.27 GPa
$ 1683/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.016 cm/cm
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 7.1 %
- Tensile Modulus: 1.90 GPa
$ 2449/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.016 cm/cm
- Tensile Strength, Yield: 25.0 MPa
- Elongation at Yield: 7.1 %
- Tensile Modulus: 1.90 GPa
$ 1619/MT
- Density: 1.09 g/cc
- Tensile Strength, Yield: 16.0 MPa
- Elongation at Yield: 4.3 %
- Tensile Modulus: 1.40 GPa
- Flexural Yield Strength: 28.0 MPa
$ 2002/MT
- Specific Gravity: 1.04 g/cc
- Density: 1.03 g/cc
- Moisture Absorption: 0.0200 %
- Moisture Absorption: 0.0200 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm @Time 86400 sec
$ 1831/MT
- Density: 0.970 g/cc
- Density: 1.12 g/cc
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength, Yield: 19.0 MPa
- Elongation at Break: 70 %
$ 1458/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.09 g/cc
- Moisture Absorption: 0.0200 %
- Moisture Absorption: 0.0300 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Time 86400 sec
$ 1613/MT
- Specific Gravity: 1.94 g/cc
- Density: 1.94 g/cc
- Moisture Absorption at Equilibrium: 0.030 %
- Moisture Absorption at Equilibrium: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 - 0.030 cm/cm @Time 86400 sec
$ 1669/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0023 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0076 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.6 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 79.0 MPa
$ 2344/MT
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 9.80 GPa
$ 2256/MT
- Density: 1.04 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 66.0 MPa
- Elongation at Break: 3.1 %
$ 1829/MT
- Specific Gravity: 1.03 g/cc
- Density: 1.03 g/cc
- Moisture Absorption: 0.0200 %
- Moisture Absorption: 0.0200 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 1726/MT
- Density: 1.48 g/cc
- Tensile Strength at Break: 41.0 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 5.58 GPa
- Flexural Strength: 68.0 MPa
$ 1893/MT
- Density: 0.990 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 37.0 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 3.137 GPa
$ 1648/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 3.9 %
- Flexural Yield Strength: 80.0 MPa
$ 1871/MT
- Density: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 28.0 MPa
- Elongation at Break: 23.4 %
- Tensile Modulus: 2.59 GPa
$ 1504/MT
- Density: 1.28 g/cc
- Water Absorption: 0.010 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0037 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0073 cm/cm @Time 86400 sec
- Tensile Strength at Break: 116 MPa
$ 1535/MT
- Density: 1.03 g/cc
- Density: 1.034 g/cc
- Moisture Absorption: 0.0300 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0072 cm/cm @Time 86400 sec
$ 1493/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0034 cm/cm
- Tensile Strength, Yield: 57.0 MPa
- Elongation at Break: 3.7 %
- Tensile Modulus: 5.30 GPa
$ 1931/MT
- Density: 1.00 g/cc
- Moisture Absorption: 0.0100 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Time 86400 sec
- Melt Flow: 34 g/10 min @Load 2.16 kg, Temperature 230 °C
Delivery Polypropylene (PP) SABIC Innovative Plastics (GE Plastics)
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, lng tanker for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.