$ 2513/MT
- Specific Gravity: 1.16 g/cc
- Density: 1.17 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Water Absorption at Saturation: 3.8 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm
$ 1501/MT
- Density: 1.36 g/cc
- Water Absorption: 3.0 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Tensile Strength, Yield: 170 MPa
- Elongation at Yield: 3.3 %
$ 1804/MT
- Specific Gravity: 1.49 g/cc
- Density: 1.49 g/cc
- Density: 1.50 g/cc
- Moisture Absorption: 0.400 %
- Moisture Absorption: 0.560 %
$ 2229/MT
- Density: 1.37 g/cc
- Tensile Strength, Yield: 220 MPa
- Elongation at Break: 1.6 %
- Flexural Yield Strength: 315 MPa
- Flexural Modulus: 17.6 GPa
$ 1607/MT
- Density: 1.22 g/cc
- Tensile Strength at Break: 218 MPa
- Elongation at Break: 1.6 %
- Flexural Strength: 305 MPa
- Flexural Modulus: 12.3 GPa
$ 1542/MT
- Density: 1.48 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 119 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 10.4 GPa
$ 1455/MT
- Specific Gravity: 1.33 g/cc
- Density: 1.33 g/cc
- Moisture Absorption: 0.670 %
- Moisture Absorption: 0.950 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 2383/MT
- Specific Gravity: 1.20 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.80 %
- Water Absorption at Saturation: 4.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
$ 1534/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0090 cm/cm
- Tensile Strength at Break: 129 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 8.70 GPa
$ 2015/MT
- Density: 1.43 g/cc
- Tensile Strength at Break: 185 MPa
- Elongation at Break: 3.3 %
- Flexural Strength: 275 MPa
- Flexural Modulus: 9.30 GPa
$ 2210/MT
- Specific Gravity: 1.72 g/cc
- Density: 1.72 g/cc
- Moisture Absorption: 0.530 %
- Moisture Absorption: 0.670 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 2166/MT
- Specific Gravity: 1.42 g/cc
- Density: 1.42 g/cc
- Moisture Absorption: 0.730 %
- Moisture Absorption: 1.00 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Time 86400 sec
$ 1454/MT
- Density: 1.55 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 140 MPa
- Tensile Strength at Break: 140 MPa
$ 2419/MT
- Density: 1.50 g/cc
- Tensile Strength at Break: 185 MPa
- Elongation at Break: 2.9 %
- Flexural Strength: 258 MPa
- Flexural Modulus: 8.30 GPa
$ 2582/MT
- Density: 1.36 g/cc
- Density: 1.37 g/cc
- Moisture Absorption: 0.600 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0064 cm/cm @Time 86400 sec
$ 1586/MT
- Linear Mold Shrinkage, Flow: 0.010 - 0.030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.030 cm/cm @Time 86400 sec
$ 2095/MT
- Density: 1.54 g/cc
- Density: 1.54 g/cc
- Moisture Absorption: 0.400 %
- Linear Mold Shrinkage, Flow: 0.0018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 1629/MT
- Density: 1.50 g/cc
- Tensile Strength at Break: 228 MPa
- Elongation at Break: 0.90 %
- Tensile Modulus: 35.25 GPa
- Flexural Strength: 351 MPa
$ 1466/MT
- Density: 1.72 g/cc
- Density: 1.72 g/cc
- Moisture Absorption: 0.300 %
- Linear Mold Shrinkage, Flow: 0.0029 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
$ 1624/MT
- Specific Gravity: 1.12 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.400 %
- Moisture Absorption: 0.600 %
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm @Time 86400 sec
$ 1606/MT
- Specific Gravity: 1.34 g/cc
- Density: 1.34 g/cc
- Moisture Absorption: 0.580 %
- Moisture Absorption: 0.790 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 2468/MT
- Specific Gravity: 1.50 g/cc
- Density: 1.51 g/cc
- Density: 1.54 g/cc
- Moisture Absorption at Equilibrium: 0.93 %
- Moisture Absorption at Equilibrium: 0.64 % @Time 86400 sec
$ 1769/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.017 cm/cm
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 110 MPa
$ 2115/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Tensile Strength at Break: 184 MPa
- Elongation at Break: 2.0 %
- Flexural Strength: 264 MPa
$ 1784/MT
- Density: 1.44 g/cc
- Moisture Absorption: 0.400 %
- Linear Mold Shrinkage, Flow: 0.0089 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0129 cm/cm @Time 86400 sec
$ 1645/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength at Break: 150 MPa
- Elongation at Break: 0.90 %
- Flexural Strength: 236 MPa
$ 1746/MT
- Density: 1.02 g/cc
- Density: 1.02 g/cc
- Moisture Absorption: 0.300 %
- Moisture Absorption: 0.430 %
- Linear Mold Shrinkage, Flow: 0.0257 cm/cm @Time 86400 sec
$ 2293/MT
- Density: 1.71 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Time 86400 sec
- Tensile Strength at Break: 279 MPa
$ 2108/MT
- Density: 1.48 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Time 86400 sec
- Tensile Strength, Yield: 131 MPa
$ 1903/MT
- Density: 1.42 g/cc
- Density: 1.42 g/cc
- Moisture Absorption: 0.970 %
- Tensile Strength at Break: 204 MPa
- Tensile Strength at Break: 214 MPa
$ 2025/MT
- Density: 1.66 g/cc
- Moisture Absorption at Equilibrium: 0.20 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0039 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0119 cm/cm @Time 86400 sec
$ 1820/MT
- Specific Gravity: 1.68 g/cc
- Density: 1.67 g/cc
- Moisture Absorption: 0.400 %
- Moisture Absorption: 0.570 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Time 86400 sec
$ 1482/MT
- Tensile Strength at Break: 267 MPa
- Tensile Strength at Break: 293 MPa
- Elongation at Break: 1.7 %
- Elongation at Break: 1.9 %
- Tensile Modulus: 29.5 GPa
$ 1577/MT
- Density: 2.04 g/cc
- Moisture Absorption: 0.300 %
- Moisture Absorption: 0.300 %
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0093 cm/cm @Time 86400 sec
$ 1740/MT
- Specific Gravity: 1.27 g/cc
- Density: 1.27 g/cc
- Density: 1.278 g/cc
- Moisture Absorption: 0.650 %
- Moisture Absorption: 1.14 %
$ 2116/MT
- Density: 1.65 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 174 MPa
- Elongation at Break: 1.9 %
- Tensile Modulus: 13.77 GPa
$ 2048/MT
- Density: 1.69 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 234 MPa
- Elongation at Break: 2.3 %
- Tensile Modulus: 18.8 GPa
$ 1686/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 280 °C
- Melt Flow: 67 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Break: 66 %
$ 1833/MT
- Density: 1.35 g/cc
- Density: 1.35 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
$ 2328/MT
- Density: 1.59 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Tensile Strength at Break: 157 MPa
- Elongation at Break: 2.4 %
- Tensile Modulus: 10.54 GPa
$ 2099/MT
- Density: 1.42 g/cc
- Tensile Strength at Break: 214 MPa
- Elongation at Break: 2.1 %
- Flexural Strength: 309 MPa
- Flexural Modulus: 10.2 GPa
$ 1961/MT
- Density: 1.28 g/cc
- Density: 1.28 g/cc
- Moisture Absorption: 0.610 %
- Moisture Absorption: 0.930 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 1470/MT
- Density: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.350 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0032 - 0.0044 cm/cm @Time 86400 sec
$ 1458/MT
- Density: 1.28 g/cc
- Water Absorption: 0.93 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0060 cm/cm
- Tensile Strength, Yield: 95.0 MPa
- Elongation at Break: 2.7 %
$ 1511/MT
- Density: 1.41 g/cc
- Density: 1.42 g/cc
- Tensile Strength at Break: 198 MPa
- Tensile Strength at Break: 202 MPa
- Elongation at Break: 2.3 %
$ 2122/MT
- Specific Gravity: 1.62 g/cc
- Density: 1.62 g/cc
- Moisture Absorption: 0.320 %
- Moisture Absorption: 0.490 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 2244/MT
- Density: 1.58 g/cc
- Density: 1.58 g/cc
- Linear Mold Shrinkage, Flow: 0.0018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0022 cm/cm @Time 86400 sec
$ 1676/MT
- Density: 1.60 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Time 86400 sec
- Tensile Strength at Break: 276 MPa
$ 1790/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.015 cm/cm @Time 86400 sec
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 40 %
$ 1600/MT
- Density: 1.18 g/cc
- Density: 1.18 g/cc
- Moisture Absorption: 0.800 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0074 cm/cm @Time 86400 sec
$ 1451/MT
- Density: 1.72 g/cc
- Density: 1.72 g/cc
- Moisture Absorption at Equilibrium: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0029 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
$ 1540/MT
- Density: 1.19 g/cc
- Water Absorption at Saturation: 5.5 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Hardness, Rockwell L: 105
- Tensile Strength at Break: 170 MPa
$ 1924/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 166 MPa
- Elongation at Break: 2.6 %
- Flexural Strength: 277 MPa
$ 1797/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 240 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 13.85 GPa
$ 1568/MT
- Specific Gravity: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption: 0.690 %
- Moisture Absorption: 0.960 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 1614/MT
- Density: 1.23 g/cc
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 - 0.013 cm/cm
- Linear Mold Shrinkage, Flow: 0.017 - 0.018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.020 - 0.021 cm/cm @Time 86400 sec
$ 1459/MT
- Density: 1.55 g/cc
- Moisture Absorption: 0.430 %
- Moisture Absorption: 0.820 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.030 cm/cm @Time 86400 sec
$ 2132/MT
- Density: 1.57 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0024 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0079 cm/cm @Time 86400 sec
- Tensile Strength at Break: 268 MPa
$ 1694/MT
- Density: 1.51 g/cc
- Density: 1.51 g/cc
- Moisture Absorption at Equilibrium: 1.0 %
- Moisture Absorption at Equilibrium: 0.61 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
$ 2152/MT
- Density: 1.42 g/cc
- Density: 1.42 g/cc
- Moisture Absorption: 0.970 %
- Tensile Strength at Break: 204 MPa
- Tensile Strength at Break: 214 MPa
$ 1465/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Tensile Strength, Yield: 190 MPa
- Elongation at Break: 3.0 %
- Flexural Yield Strength: 265 MPa
$ 1803/MT
- Density: 1.34 g/cc
- Density: 1.34 g/cc
- Moisture Absorption: 0.930 %
- Moisture Absorption: 1.35 %
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Time 86400 sec
$ 1449/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.020 cm/cm
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: 8.2 %
- Tensile Modulus: 2.30 GPa
$ 1514/MT
- Specific Gravity: 1.15 g/cc
- Density: 1.15 g/cc
- Moisture Absorption: 0.490 %
- Moisture Absorption: 0.730 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 1452/MT
- Density: 1.50 g/cc
- Tensile Strength at Break: 185 MPa
- Elongation at Break: 2.9 %
- Flexural Strength: 258 MPa
- Flexural Modulus: 8.30 GPa
$ 1473/MT
- Density: 1.35 g/cc
- Water Absorption: 0.81 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 117 MPa
- Elongation at Break: 3.8 %
$ 1474/MT
- Density: 1.51 g/cc
- Tensile Strength at Break: 138 MPa
- Tensile Strength at Break: 139 MPa
- Elongation at Break: 2.1 %
- Elongation at Break: 2.1 %
$ 1546/MT
- Specific Gravity: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption at Equilibrium: 0.80 %
- Water Absorption at Saturation: 3.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 - 0.013 cm/cm @Thickness 3.20 mm
$ 1483/MT
- Density: 1.71 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0041 cm/cm @Time 86400 sec
- Tensile Strength at Break: 261 MPa
- Elongation at Break: 1.6 %
$ 1492/MT
- Density: 1.15 g/cc
- Tensile Strength at Break: 46.0 MPa
- Elongation at Break: 13.5 %
- Tensile Modulus: 2.38 GPa
- Flexural Strength: 82.0 MPa
$ 1734/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 122 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 9.03 GPa
$ 2159/MT
- Density: 1.41 g/cc
- Water Absorption: 1.3 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0043 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm @Time 86400 sec
- Tensile Strength at Break: 195 MPa
$ 1879/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm @Time 86400 sec
- Tensile Strength at Break: 132 MPa
- Tensile Strength at Break: 139 MPa
$ 1611/MT
- Density: 1.29 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 4.30 GPa
$ 1597/MT
- Density: 1.41 g/cc
- Density: 1.42 g/cc
- Tensile Strength at Break: 198 MPa
- Tensile Strength at Break: 202 MPa
- Elongation at Break: 2.3 %
$ 1631/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 159 MPa
- Elongation at Break: 3.1 %
- Flexural Strength: 235 MPa
$ 1448/MT
- Density: 1.39 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.870 %
- Moisture Absorption: 1.07 %
- Linear Mold Shrinkage, Flow: 0.0029 cm/cm @Time 86400 sec
$ 1820/MT
- Density: 1.12 g/cc
- Density: 1.12 g/cc
- Moisture Absorption: 0.880 %
- Moisture Absorption: 1.18 %
- Linear Mold Shrinkage, Flow: 0.023 - 0.025 cm/cm @Time 86400 sec
$ 1758/MT
- Density: 1.53 g/cc
- Moisture Absorption at Equilibrium: 0.30 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.015 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0152 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0167 cm/cm @Time 86400 sec
$ 1897/MT
- Density: 1.16 g/cc
- Density: 1.17 g/cc
- Tensile Strength at Break: 69.0 MPa
- Tensile Strength at Break: 84.0 MPa
- Tensile Strength, Yield: 69.0 MPa
$ 2534/MT
- Density: 1.27 g/cc
- Density: 1.27 g/cc
- Tensile Strength at Break: 78.0 MPa
- Tensile Strength at Break: 83.0 MPa
- Flexural Modulus: 3.57 GPa
$ 1584/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm
- Tensile Strength, Yield: 79.0 MPa
- Elongation at Break: 45 %
$ 1710/MT
- Specific Gravity: 1.52 g/cc
- Density: 1.52 g/cc
- Moisture Absorption: 0.690 %
- Moisture Absorption: 1.00 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Time 86400 sec
$ 1663/MT
- Density: 1.59 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Tensile Strength at Break: 157 MPa
- Elongation at Break: 2.4 %
- Tensile Modulus: 10.54 GPa
$ 1723/MT
- Density: 2.04 g/cc
- Moisture Absorption: 0.300 %
- Moisture Absorption: 0.300 %
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0093 cm/cm @Time 86400 sec
$ 2053/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.016 cm/cm
- Tensile Strength at Break: 80.0 MPa
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: 4.0 %
$ 1922/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 110 MPa
- Elongation at Break: 1.8 %
- Flexural Strength: 141 MPa
$ 1844/MT
- Density: 1.40 g/cc
- Moisture Absorption: 0.500 %
- Tensile Strength at Break: 131 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 193 MPa
$ 1515/MT
- Density: 1.37 g/cc
- Moisture Absorption at Equilibrium: 1.3 %
- Water Absorption at Saturation: 4.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Hardness, Rockwell L: 113
$ 1655/MT
- Density: 1.53 g/cc
- Tensile Strength at Break: 185 MPa
- Elongation at Break: 2.3 %
- Tensile Modulus: 11.2 GPa
- Flexural Strength: 275 MPa
$ 2042/MT
- Specific Gravity: 1.70 g/cc
- Density: 1.69 g/cc
- Moisture Absorption: 0.340 %
- Moisture Absorption: 0.510 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Time 86400 sec
$ 1719/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.39 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.690 %
- Moisture Absorption: 1.20 %
$ 2085/MT
- Density: 1.71 g/cc
- Tensile Strength at Break: 151 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 16.54 GPa
- Flexural Strength: 248 MPa
$ 1634/MT
- Density: 1.74 g/cc
- Density: 1.74 g/cc
- Moisture Absorption at Equilibrium: 0.40 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0037 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
$ 2173/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.840 %
- Moisture Absorption: 1.20 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 1784/MT
- Density: 1.22 g/cc
- Tensile Strength at Break: 157 MPa
- Elongation at Break: 2.4 %
- Tensile Modulus: 16.37 GPa
- Flexural Strength: 241 MPa
$ 1926/MT
- Density: 1.48 g/cc
- Density: 1.48 g/cc
- Moisture Absorption: 0.700 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0021 cm/cm @Time 86400 sec
$ 1557/MT
- Density: 1.03 g/cc
- Density: 1.03 g/cc
- Moisture Absorption: 0.250 %
- Linear Mold Shrinkage, Flow: 0.018 - 0.022 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.021 - 0.031 cm/cm @Time 86400 sec
$ 1568/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.900 %
- Water Absorption at Saturation: 3.0 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm @Thickness 3.20 mm
$ 2582/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Time 86400 sec
- Tensile Strength at Break: 119 MPa
- Elongation at Break: 2.8 %
- Tensile Modulus: 6.24 GPa
$ 1485/MT
- Density: 1.45 g/cc
- Density: 1.46 g/cc
- Moisture Absorption: 1.20 %
- Moisture Absorption: 1.55 %
- Linear Mold Shrinkage, Flow: 0.018 - 0.020 cm/cm @Time 86400 sec
$ 2040/MT
- Density: 1.09 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm @Time 86400 sec
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 70 %
- Tensile Modulus: 2.20 GPa
$ 2426/MT
- Density: 1.43 g/cc
- Tensile Strength at Break: 185 MPa
- Elongation at Break: 3.3 %
- Flexural Strength: 275 MPa
- Flexural Modulus: 9.30 GPa
$ 2095/MT
- Density: 1.60 g/cc
- Density: 1.60 g/cc
- Moisture Absorption: 0.400 %
- Linear Mold Shrinkage, Flow: 0.0037 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1519/MT
- Density: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.014 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.015 cm/cm @Time 86400 sec
- Tensile Strength at Break: 68.0 MPa
- Elongation at Break: 4.3 %
$ 2346/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.860 %
- Moisture Absorption: 1.20 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 1849/MT
- Density: 1.48 g/cc
- Density: 1.485 g/cc
- Moisture Absorption at Equilibrium: 0.65 %
- Moisture Absorption at Equilibrium: 0.93 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0023 - 0.0043 cm/cm @Time 86400 sec
$ 2092/MT
- Density: 1.32 g/cc
- Density: 1.32 g/cc
- Moisture Absorption: 0.600 %
- Linear Mold Shrinkage, Flow: 0.0036 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1535/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 240 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 13.85 GPa
$ 2156/MT
- Density: 1.325 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 93.0 MPa
- Elongation at Break: 3.2 %
- Tensile Modulus: 6.27 GPa
$ 1481/MT
- Density: 1.24 g/cc
- Moisture Absorption: 0.380 %
- Moisture Absorption: 0.660 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm @Time 86400 sec
$ 1786/MT
- Density: 1.57 g/cc
- Water Absorption: 0.70 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength at Break: 213 MPa
$ 2201/MT
- Density: 1.25 g/cc
- Density: 1.26 g/cc
- Moisture Absorption: 1.10 %
- Moisture Absorption: 1.60 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Time 86400 sec
$ 2214/MT
- Density: 1.498 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Moisture Absorption at Equilibrium: 0.72 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.010 cm/cm @Time 86400 sec
$ 1562/MT
- Density: 1.36 g/cc
- Tensile Strength, Yield: 141 MPa
- Elongation at Yield: 2.9 %
- Tensile Modulus: 9.00 GPa
- Flexural Yield Strength: 215 MPa
$ 1945/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Time 86400 sec
- Tensile Strength, Yield: 254 MPa
- Elongation at Break: 2.7 %
$ 1660/MT
- Specific Gravity: 1.12 g/cc
- Density: 1.13 g/cc
- Density: 1.13 g/cc
- Tensile Strength at Break: 87.0 MPa
- Tensile Strength at Break: 90.0 MPa
$ 1489/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength at Break: 200 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 269 MPa
$ 1875/MT
- Density: 1.23 g/cc
- Tensile Strength at Break: 77.0 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 5.01 GPa
- Flexural Strength: 124 MPa
$ 1536/MT
- Density: 1.38 g/cc
- Density: 1.389 g/cc
- Moisture Absorption at Equilibrium: 1.2 %
- Moisture Absorption at Equilibrium: 0.66 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0029 - 0.0049 cm/cm @Time 86400 sec
$ 1778/MT
- Density: 1.32 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength at Break: 189 MPa
- Elongation at Break: 3.1 %
- Flexural Strength: 250 MPa
$ 2505/MT
- Density: 1.39 g/cc
- Density: 1.394 g/cc
- Moisture Absorption at Equilibrium: 0.75 %
- Moisture Absorption at Equilibrium: 0.52 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0017 cm/cm @Time 86400 sec
$ 1532/MT
- Density: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.790 %
- Moisture Absorption: 1.20 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 1496/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Time 86400 sec
- Tensile Strength at Break: 278 MPa
- Elongation at Break: 1.6 %
$ 2333/MT
- Density: 2.04 g/cc
- Moisture Absorption: 0.300 %
- Moisture Absorption: 0.300 %
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0093 cm/cm @Time 86400 sec
$ 1909/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.015 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 88.0 MPa
- Elongation at Break: 4.5 %
$ 2018/MT
- Density: 1.09 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm @Time 86400 sec
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 70 %
- Tensile Modulus: 2.20 GPa
$ 1573/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.900 %
- Water Absorption at Saturation: 3.0 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm @Thickness 3.20 mm
$ 2087/MT
- Density: 1.10 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 0.730 %
- Moisture Absorption: 1.12 %
- Linear Mold Shrinkage, Flow: 0.024 - 0.026 cm/cm @Time 86400 sec
$ 1921/MT
- Density: 1.43 g/cc
- Tensile Strength at Break: 183 MPa
- Elongation at Break: 3.2 %
- Flexural Strength: 268 MPa
- Flexural Modulus: 9.30 GPa
$ 1648/MT
- Density: 1.40 g/cc
- Tensile Strength at Break: 159 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 10.27 GPa
- Flexural Modulus: 10.3 GPa
$ 1552/MT
- Density: 1.51 g/cc
- Moisture Absorption: 0.590 %
- Moisture Absorption: 0.810 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.020 cm/cm @Time 86400 sec
$ 1706/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength at Break: 178 MPa
- Elongation at Break: 2.4 %
- Flexural Strength: 235 MPa
$ 1780/MT
- Density: 1.09 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm @Time 86400 sec
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 70 %
- Tensile Modulus: 2.20 GPa
$ 1599/MT
- Density: 1.65 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 174 MPa
- Elongation at Break: 1.9 %
- Tensile Modulus: 13.77 GPa
$ 1955/MT
- Density: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.200 %
- Linear Mold Shrinkage, Flow: 0.0093 - 0.0124 cm/cm @Time 86400 sec
- Tensile Strength at Break: 56.0 MPa
$ 1905/MT
- Specific Gravity: 1.54 g/cc
- Density: 1.53 g/cc
- Moisture Absorption: 0.640 %
- Moisture Absorption: 0.990 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1609/MT
- Density: 1.02 g/cc
- Density: 1.02 g/cc
- Moisture Absorption: 0.300 %
- Moisture Absorption: 0.430 %
- Linear Mold Shrinkage, Flow: 0.0257 cm/cm @Time 86400 sec
$ 2036/MT
- Density: 1.34 g/cc
- Density: 1.34 g/cc
- Moisture Absorption: 0.930 %
- Moisture Absorption: 1.35 %
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Time 86400 sec
$ 2133/MT
- Density: 1.41 g/cc
- Density: 1.41 g/cc
- Moisture Absorption: 0.650 %
- Moisture Absorption: 1.14 %
- Linear Mold Shrinkage, Flow: 0.0028 cm/cm @Time 86400 sec
$ 1456/MT
- Density: 1.47 g/cc
- Density: 1.48 g/cc
- Moisture Absorption: 0.700 %
- Linear Mold Shrinkage, Flow: 0.0029 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 1786/MT
- Density: 1.15 g/cc
- Moisture Absorption at Equilibrium: 0.80 % @Time 86400 sec
- Tensile Strength at Break: 64.0 MPa
- Tensile Strength, Yield: 66.0 MPa
- Elongation at Break: 4.1 %
$ 2475/MT
- Specific Gravity: 1.49 g/cc
- Density: 1.49 g/cc
- Moisture Absorption: 0.410 %
- Moisture Absorption: 0.580 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 1605/MT
- Density: 1.48 g/cc
- Density: 1.48 g/cc
- Moisture Absorption: 0.780 %
- Moisture Absorption: 1.22 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
$ 1938/MT
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.94 %
- Moisture Absorption at Equilibrium: 0.62 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 - 0.030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.030 cm/cm @Time 86400 sec
$ 2164/MT
- Density: 1.34 g/cc
- Density: 1.346 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0034 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm @Time 86400 sec
$ 1521/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.740 %
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Time 86400 sec
$ 1928/MT
- Density: 1.60 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Time 86400 sec
- Tensile Strength at Break: 276 MPa
$ 2139/MT
- Density: 1.29 g/cc
- Density: 1.295 g/cc
- Moisture Absorption: 0.800 %
- Linear Mold Shrinkage, Flow: 0.0047 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
$ 1503/MT
- Density: 1.32 g/cc
- Density: 1.32 g/cc
- Moisture Absorption: 0.600 %
- Linear Mold Shrinkage, Flow: 0.0036 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 2332/MT
- Density: 1.41 g/cc
- Tensile Strength at Break: 155 MPa
- Elongation at Break: 2.5 %
- Tensile Modulus: 9.99 GPa
- Flexural Strength: 227 MPa
$ 1727/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 3.20 mm
- Melt Flow: 16 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1909/MT
- Density: 1.71 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: 0.0026 cm/cm
- Linear Mold Shrinkage, Transverse: 0.0061 cm/cm
$ 2200/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Time 86400 sec
- Tensile Strength at Break: 82.0 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 8.67 GPa
$ 1516/MT
- Density: 1.46 g/cc
- Tensile Strength at Break: 185 MPa
- Elongation at Break: 3.3 %
- Flexural Strength: 262 MPa
- Flexural Strength: 275 MPa
$ 2223/MT
- Density: 1.14 g/cc
- Density: 1.15 g/cc
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Time 86400 sec
$ 1628/MT
- Density: 1.48 g/cc
- Density: 1.48 g/cc
- Moisture Absorption: 0.780 %
- Moisture Absorption: 1.22 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
$ 1726/MT
- Specific Gravity: 1.34 g/cc
- Density: 1.34 g/cc
- Moisture Absorption: 0.640 %
- Moisture Absorption: 0.970 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Time 86400 sec
$ 1534/MT
- Density: 1.42 g/cc
- Density: 1.42 g/cc
- Moisture Absorption: 0.970 %
- Tensile Strength at Break: 204 MPa
- Tensile Strength at Break: 214 MPa
$ 1693/MT
- Density: 1.45 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm
- Tensile Strength at Break: 99.0 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 5.80 GPa
$ 2096/MT
- Density: 1.24 g/cc
- Moisture Absorption: 0.380 %
- Moisture Absorption: 0.660 %
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.012 cm/cm @Time 86400 sec
$ 1489/MT
- Density: 1.10 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 0.700 %
- Moisture Absorption: 1.12 %
- Linear Mold Shrinkage, Flow: 0.024 - 0.026 cm/cm @Time 86400 sec
$ 1742/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 173 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 9.70 GPa
$ 1544/MT
- Density: 1.27 g/cc
- Density: 1.27 g/cc
- Moisture Absorption: 0.600 %
- Tensile Strength at Break: 48.0 MPa
- Tensile Strength at Break: 55.0 MPa
$ 2199/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.09 g/cc
- Moisture Absorption: 0.520 %
- Water Absorption at Saturation: 1.01 %
- Linear Mold Shrinkage, Flow: 0.0113 - 0.0126 cm/cm @Thickness 3.20 mm
$ 1811/MT
- Density: 1.37 g/cc
- Density: 1.38 g/cc
- Moisture Absorption: 0.630 %
- Linear Mold Shrinkage, Flow: 0.0027 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
$ 2317/MT
- Specific Gravity: 1.21 g/cc
- Density: 1.21 g/cc
- Moisture Absorption: 0.620 %
- Moisture Absorption: 0.950 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0040 cm/cm @Time 86400 sec
$ 1480/MT
- Density: 1.26 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Water Absorption at Saturation: 4.5 %
- Linear Mold Shrinkage, Flow: 0.00040 - 0.00080 cm/cm
- Linear Mold Shrinkage, Flow: 0.00050 - 0.010 cm/cm
$ 1916/MT
- Specific Gravity: 1.04 g/cc
- Density: 1.05 g/cc
- Moisture Absorption: 0.200 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.030 cm/cm @Time 86400 sec
$ 1888/MT
- Density: 1.16 g/cc
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0101 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0103 cm/cm @Time 86400 sec
- Tensile Strength at Break: 69.0 MPa
$ 2281/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 2.8 %
- Tensile Modulus: 8.35 GPa
$ 1541/MT
- Density: 1.66 g/cc
- Moisture Absorption: 0.200 %
- Moisture Absorption: 0.430 %
- Linear Mold Shrinkage, Flow: 0.0039 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
$ 2195/MT
- Density: 1.51 g/cc
- Density: 1.51 g/cc
- Moisture Absorption: 0.620 %
- Linear Mold Shrinkage, Flow: 0.0032 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
$ 2119/MT
- Density: 1.37 g/cc
- Water Absorption: 1.2 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Tensile Strength at Break: 147 MPa
- Elongation at Break: 3.4 %
$ 1849/MT
- Density: 1.38 g/cc
- Density: 1.38 g/cc
- Moisture Absorption: 0.860 %
- Moisture Absorption: 1.40 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Time 86400 sec
$ 1799/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0024 cm/cm
- Tensile Strength at Break: 173 MPa
- Elongation at Break: 2.5 %
- Elongation at Break: 3.3 %
$ 1490/MT
- Specific Gravity: 3.79 g/cc
- Density: 3.78 g/cc
- Moisture Absorption: 0.450 %
- Moisture Absorption: 0.510 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1470/MT
- Specific Gravity: 1.53 g/cc
- Density: 1.52 g/cc
- Moisture Absorption: 0.430 %
- Moisture Absorption: 0.540 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 2003/MT
- Density: 1.51 g/cc
- Density: 1.51 g/cc
- Moisture Absorption: 0.620 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm @Time 86400 sec
$ 2352/MT
- Specific Gravity: 1.23 g/cc
- Density: 1.23 g/cc
- Moisture Absorption: 0.890 %
- Moisture Absorption: 1.20 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 1452/MT
- Density: 1.03 g/cc
- Density: 1.03 g/cc
- Moisture Absorption: 0.250 %
- Linear Mold Shrinkage, Flow: 0.018 - 0.022 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.021 - 0.031 cm/cm @Time 86400 sec
$ 1748/MT
- Density: 1.23 g/cc
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.017 - 0.018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.020 - 0.021 cm/cm @Time 86400 sec
- Tensile Strength at Break: 85.0 MPa
$ 2176/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 168 MPa
- Elongation at Break: 2.7 %
- Tensile Modulus: 12.5 GPa
$ 2534/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.014 cm/cm @Time 86400 sec
- Tensile Strength at Break: 60.0 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 4.93 GPa
$ 1703/MT
- Density: 1.71 g/cc
- Density: 1.71 g/cc
- Moisture Absorption: 0.440 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
$ 1963/MT
- Specific Gravity: 1.50 g/cc
- Density: 1.48 g/cc
- Moisture Absorption: 0.660 %
- Moisture Absorption: 1.00 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 2250/MT
- Density: 1.39 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.870 %
- Moisture Absorption: 1.07 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 2427/MT
- Density: 1.60 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength at Break: 194 MPa
- Elongation at Break: 2.7 %
- Tensile Modulus: 12.9 GPa
$ 1518/MT
- Specific Gravity: 1.29 g/cc
- Density: 1.29 g/cc
- Density: 1.30 g/cc
- Moisture Absorption: 0.610 %
- Moisture Absorption: 0.900 %
$ 1982/MT
- Density: 1.48 g/cc
- Density: 1.48 g/cc
- Moisture Absorption: 0.780 %
- Moisture Absorption: 1.22 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
$ 1571/MT
- Density: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.350 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0032 - 0.0044 cm/cm @Time 86400 sec
$ 1740/MT
- Density: 1.60 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 155 MPa
- Elongation at Break: 1.9 %
- Flexural Strength: 178 MPa
$ 1525/MT
- Specific Gravity: 1.34 g/cc
- Density: 1.34 g/cc
- Moisture Absorption: 0.800 %
- Water Absorption at Saturation: 3.0 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm @Thickness 3.20 mm
$ 2470/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.640 %
- Moisture Absorption: 0.940 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Time 86400 sec
$ 1486/MT
- Density: 1.72 g/cc
- Density: 1.72 g/cc
- Moisture Absorption: 0.300 %
- Linear Mold Shrinkage, Flow: 0.0029 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
$ 1760/MT
- Specific Gravity: 1.48 g/cc
- Density: 1.48 g/cc
- Moisture Absorption: 0.0600 %
- Moisture Absorption: 0.630 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 1553/MT
- Density: 1.66 g/cc
- Moisture Absorption: 0.200 %
- Moisture Absorption: 0.430 %
- Linear Mold Shrinkage, Flow: 0.0039 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
$ 1787/MT
- Density: 1.51 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0023 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0083 cm/cm @Time 86400 sec
- Tensile Strength at Break: 188 MPa
$ 1627/MT
- Specific Gravity: 1.39 g/cc
- Density: 1.38 g/cc
- Moisture Absorption: 0.750 %
- Moisture Absorption: 1.20 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 1611/MT
- Specific Gravity: 1.30 g/cc
- Density: 1.29 g/cc
- Moisture Absorption: 0.890 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.030 cm/cm @Time 86400 sec
$ 1596/MT
- Density: 1.38 g/cc
- Density: 1.38 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0011 cm/cm @Time 86400 sec
$ 2127/MT
- Density: 1.57 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0024 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0079 cm/cm @Time 86400 sec
- Tensile Strength at Break: 268 MPa
$ 1511/MT
- Density: 1.54 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Tensile Strength at Break: 214 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 15.9 GPa
$ 1708/MT
- Density: 1.36 g/cc
- Density: 1.37 g/cc
- Moisture Absorption: 0.600 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0064 cm/cm @Time 86400 sec
$ 1557/MT
- Specific Gravity: 1.49 g/cc
- Density: 1.49 g/cc
- Moisture Absorption: 0.980 %
- Hardness, Rockwell M: 92
- Tensile Strength at Break: 168 MPa
$ 1956/MT
- Density: 1.53 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.012 cm/cm @Time 86400 sec
- Tensile Strength at Break: 136 MPa
- Elongation at Break: 3.3 %
$ 1899/MT
- Density: 1.69 g/cc
- Tensile Strength at Break: 165 MPa
- Elongation at Break: 2.2 %
- Tensile Modulus: 13.78 GPa
- Flexural Strength: 241 MPa
$ 1876/MT
- Specific Gravity: 1.40 g/cc
- Density: 1.39 g/cc
- Density: 1.39 g/cc
- Moisture Absorption: 0.500 %
- Moisture Absorption: 0.750 %
$ 1619/MT
- Specific Gravity: 1.70 g/cc
- Density: 1.72 g/cc
- Moisture Absorption: 0.480 %
- Moisture Absorption: 0.730 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1495/MT
- Density: 1.23 g/cc
- Density: 1.23 g/cc
- Moisture Absorption: 0.740 %
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Time 86400 sec
$ 1598/MT
- Specific Gravity: 1.15 g/cc
- Density: 1.14 g/cc
- Moisture Absorption: 1.20 %
- Moisture Absorption: 1.50 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 1477/MT
- Density: 1.69 g/cc
- Tensile Strength at Break: 213 MPa
- Elongation at Break: 1.8 %
- Tensile Modulus: 15.07 GPa
- Flexural Strength: 298 MPa
$ 2244/MT
- Density: 1.46 g/cc
- Density: 1.471 g/cc
- Moisture Absorption: 0.770 %
- Linear Mold Shrinkage, Flow: 0.0017 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
$ 2448/MT
- Density: 1.24 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.900 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Time 86400 sec
$ 2137/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Time 86400 sec
- Tensile Strength at Break: 82.0 MPa
- Elongation at Break: 3.3 %
- Tensile Modulus: 8.67 GPa
$ 1800/MT
- Density: 1.29 g/cc
- Density: 1.295 g/cc
- Moisture Absorption: 0.800 %
- Linear Mold Shrinkage, Flow: 0.0047 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
$ 1561/MT
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 1.5 %
- Water Absorption at Saturation: 5.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm
- Hardness, Rockwell R: 112
$ 1802/MT
- Density: 1.69 g/cc
- Density: 1.69 g/cc
- Moisture Absorption: 0.590 %
- Moisture Absorption: 0.750 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1969/MT
- Density: 1.39 g/cc
- Moisture Absorption: 0.900 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 136 MPa
- Elongation at Break: 2.4 %
$ 1454/MT
- Density: 1.44 g/cc
- Linear Mold Shrinkage, Flow: 0.014 cm/cm
- Tensile Strength, Yield: 83.0 MPa
- Elongation at Break: 4.0 %
- Tensile Modulus: 5.20 GPa
$ 1588/MT
- Density: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.800 %
- Linear Mold Shrinkage, Flow: 0.019 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.019 cm/cm @Time 86400 sec
$ 1899/MT
- Density: 1.34 g/cc
- Density: 1.34 g/cc
- Moisture Absorption: 0.930 %
- Moisture Absorption: 1.35 %
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Time 86400 sec
$ 1545/MT
- Density: 1.71 g/cc
- Density: 1.71 g/cc
- Moisture Absorption: 0.440 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
$ 1664/MT
- Density: 1.29 g/cc
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
- Flexural Strength: 161 MPa
- Flexural Modulus: 5.58 GPa
- Flexural Modulus: 5.99 GPa
$ 1715/MT
- Density: 1.05 g/cc
- Tensile Strength at Break: 56.0 MPa
- Flexural Modulus: 27.3 GPa
- Izod Impact, Notched: 0.740 J/cm
- Deflection Temperature at 1.8 MPa (264 psi): 102 °C @Thickness 3.20 mm
$ 2202/MT
- Specific Gravity: 1.22 g/cc
- Density: 1.20 g/cc
- Moisture Absorption: 0.570 %
- Moisture Absorption: 0.910 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 1730/MT
- Specific Gravity: 1.40 g/cc
- Density: 1.40 g/cc
- Density: 1.43 g/cc
- Moisture Absorption: 0.570 %
- Moisture Absorption: 0.880 %
$ 1592/MT
- Density: 1.38 g/cc
- Density: 1.38 g/cc
- Moisture Absorption: 0.530 %
- Moisture Absorption: 0.840 %
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
$ 1455/MT
- Density: 1.71 g/cc
- Density: 1.71 g/cc
- Moisture Absorption: 0.440 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
$ 1500/MT
- Density: 1.57 g/cc
- Moisture Absorption: 0.800 %
- Linear Mold Shrinkage, Flow: 0.0024 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0079 cm/cm @Time 86400 sec
- Tensile Strength at Break: 268 MPa
$ 1635/MT
- Density: 1.40 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.670 %
- Moisture Absorption: 0.990 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1553/MT
- Density: 1.65 g/cc
- Tensile Strength at Break: 231 MPa
- Elongation at Break: 2.3 %
- Flexural Yield Strength: 362 MPa
- Flexural Modulus: 14.1 GPa
$ 2512/MT
- Specific Gravity: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption at Equilibrium: 1.6 %
- Moisture Absorption at Equilibrium: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Time 86400 sec
$ 2327/MT
- Density: 1.22 g/cc
- Density: 1.22 g/cc
- Moisture Absorption: 0.720 %
- Moisture Absorption: 1.17 %
- Linear Mold Shrinkage, Flow: 0.019 cm/cm @Time 86400 sec
$ 1934/MT
- Specific Gravity: 1.41 g/cc
- Moisture Absorption: 0.600 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm
- Tensile Strength at Break: 158 MPa
- Elongation at Break: 3.0 - 4.0 %
$ 1566/MT
- Density: 1.53 g/cc
- Moisture Absorption: 0.380 %
- Moisture Absorption: 0.550 %
- Linear Mold Shrinkage, Flow: 0.015 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0152 cm/cm @Time 86400 sec
$ 1551/MT
- Density: 1.53 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 217 MPa
- Elongation at Break: 2.8 %
- Flexural Strength: 324 MPa
$ 2140/MT
- Density: 1.61 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm
- Tensile Strength at Break: 226 MPa
- Elongation at Break: 2.2 %
- Tensile Modulus: 17.4 GPa
$ 1455/MT
- Density: 1.51 g/cc
- Linear Mold Shrinkage, Flow: 0.0022 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0087 cm/cm @Time 86400 sec
- Tensile Strength at Break: 197 MPa
- Elongation at Break: 2.4 %
$ 1935/MT
- Density: 1.20 g/cc
- Tensile Strength at Break: 107 MPa
- Elongation at Break: 4.1 %
- Tensile Modulus: 4.82 GPa
- Flexural Strength: 158 MPa
$ 1955/MT
- Density: 1.46 g/cc
- Tensile Strength at Break: 148 MPa
- Elongation at Break: 3.9 %
- Flexural Strength: 211 MPa
- Flexural Modulus: 7.00 GPa
$ 1922/MT
- Density: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.350 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0032 - 0.0044 cm/cm @Time 86400 sec
$ 2332/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Yield: 3.6 %
- Tensile Modulus: 4.30 GPa
$ 1927/MT
- Specific Gravity: 1.54 g/cc
- Density: 1.54 g/cc
- Moisture Absorption: 0.370 %
- Moisture Absorption: 0.580 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Time 86400 sec
$ 1797/MT
- Density: 1.57 g/cc
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Time 86400 sec
- Tensile Strength at Break: 52.0 MPa
- Elongation at Break: 1.8 %
- Tensile Modulus: 5.24 GPa
$ 2196/MT
- Density: 1.34 g/cc
- Density: 1.34 g/cc
- Moisture Absorption: 0.270 %
- Moisture Absorption: 0.400 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
$ 1767/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.010 - 0.015 cm/cm
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Break: >= 40 %
- Tensile Modulus: 2.20 GPa
$ 1725/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 189 MPa
- Elongation at Break: 2.3 %
- Flexural Strength: 276 MPa
$ 1633/MT
- Density: 1.60 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Time 86400 sec
- Tensile Strength at Break: 276 MPa
$ 1523/MT
- Density: 1.42 g/cc
- Density: 1.42 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.013 cm/cm @Time 86400 sec
$ 1715/MT
- Density: 1.22 g/cc
- Density: 1.224 g/cc
- Moisture Absorption: 1.26 %
- Moisture Absorption: 1.94 %
- Linear Mold Shrinkage, Flow: 0.0077 cm/cm @Time 86400 sec
$ 1618/MT
- Density: 1.22 g/cc
- Density: 1.22 g/cc
- Moisture Absorption: 0.860 %
- Moisture Absorption: 1.20 %
- Linear Mold Shrinkage, Flow: 0.0090 - 0.020 cm/cm @Time 86400 sec
$ 2028/MT
- Density: 1.57 g/cc
- Water Absorption: 0.70 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength, Yield: 210 MPa
- Elongation at Break: 2.4 %
$ 1761/MT
- Density: 1.59 g/cc
- Tensile Strength at Break: 206 MPa
- Elongation at Break: 2.0 %
- Flexural Strength: 310 MPa
- Flexural Modulus: 14.54 GPa
$ 1522/MT
- Specific Gravity: 1.42 g/cc
- Density: 1.42 g/cc
- Moisture Absorption: 0.730 %
- Moisture Absorption: 1.00 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Time 86400 sec
$ 1581/MT
- Density: 1.07 g/cc
- Density: 1.073 g/cc
- Moisture Absorption: 0.800 %
- Moisture Absorption: 1.37 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.015 cm/cm @Time 86400 sec
$ 1873/MT
- Density: 1.65 g/cc
- Tensile Strength at Break: 231 MPa
- Elongation at Break: 2.3 %
- Flexural Strength: 362 MPa
- Flexural Modulus: 14.1 GPa
$ 2085/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.900 %
- Water Absorption at Saturation: 3.0 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm @Thickness 3.20 mm
$ 1626/MT
- Density: 1.17 g/cc
- Density: 1.17 g/cc
- Moisture Absorption at Equilibrium: 1.4 %
- Moisture Absorption at Equilibrium: 0.94 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.020 - 0.040 cm/cm @Time 86400 sec
$ 1601/MT
- Specific Gravity: 1.33 g/cc
- Density: 1.322 g/cc
- Moisture Absorption: 0.590 %
- Moisture Absorption: 0.920 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 1758/MT
- Density: 1.20 g/cc
- Density: 1.203 g/cc
- Moisture Absorption at Equilibrium: 1.47 %
- Moisture Absorption at Equilibrium: 0.93 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0017 - 0.0026 cm/cm @Time 86400 sec
$ 1521/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 128 MPa
- Elongation at Break: 2.5 %
- Flexural Strength: 179 MPa
$ 2163/MT
- Density: 1.23 g/cc
- Tensile Strength at Break: 77.0 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 5.01 GPa
- Flexural Strength: 124 MPa
$ 1691/MT
- Specific Gravity: 1.50 g/cc
- Density: 1.47 g/cc
- Density: 1.478 g/cc
- Moisture Absorption: 0.600 %
- Moisture Absorption: 0.970 %
$ 1564/MT
- Specific Gravity: 1.59 g/cc
- Density: 1.59 g/cc
- Moisture Absorption: 0.640 %
- Moisture Absorption: 1.20 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 1518/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 - 0.013 cm/cm
- Tensile Strength at Break: 71.0 MPa
- Tensile Strength, Yield: 72.0 MPa
- Elongation at Break: 8.4 %
$ 1695/MT
- Density: 1.49 g/cc
- Moisture Absorption at Equilibrium: 0.80 % @Time 86400 sec
- Tensile Strength at Break: 124 MPa
- Elongation at Break: 1.6 %
- Tensile Modulus: 11.0 GPa
$ 1612/MT
- Density: 1.56 g/cc
- Density: 1.573 g/cc
- Moisture Absorption: 0.400 %
- Moisture Absorption: 0.740 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
$ 1969/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.018 - 0.020 cm/cm
- Tensile Strength at Break: 59.0 MPa
- Elongation at Break: 4.9 %
- Tensile Modulus: 2.70 GPa
$ 1576/MT
- Density: 1.28 g/cc
- Density: 1.28 g/cc
- Moisture Absorption: 0.610 %
- Moisture Absorption: 0.930 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 2102/MT
- Specific Gravity: 1.43 g/cc
- Density: 1.43 g/cc
- Moisture Absorption at Equilibrium: 1.3 %
- Moisture Absorption at Equilibrium: 0.84 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0040 cm/cm @Time 86400 sec
$ 1523/MT
- Density: 1.43 g/cc
- Tensile Strength at Break: 183 MPa
- Elongation at Break: 3.2 %
- Flexural Strength: 268 MPa
- Flexural Modulus: 9.30 GPa
$ 1534/MT
- Density: 1.18 g/cc
- Density: 1.19 g/cc
- Moisture Absorption: 0.630 %
- Moisture Absorption: 0.630 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 1679/MT
- Density: 1.48 g/cc
- Density: 1.48 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.0098 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0090 - 0.011 cm/cm @Time 86400 sec
$ 1624/MT
- Specific Gravity: 1.27 g/cc
- Density: 1.27 g/cc
- Moisture Absorption: 0.720 %
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 1445/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 168 MPa
- Elongation at Break: 2.7 %
- Tensile Modulus: 12.5 GPa
$ 1472/MT
- Density: 1.22 g/cc
- Density: 1.22 g/cc
- Moisture Absorption: 0.700 %
- Linear Mold Shrinkage, Flow: 0.019 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0192 cm/cm @Time 86400 sec
$ 1938/MT
- Density: 1.69 g/cc
- Tensile Strength at Break: 270 MPa
- Flexural Modulus: 17.16 GPa
- Izod Impact, Notched: 4.80 J/cm
- Deflection Temperature at 1.8 MPa (264 psi): 252 °C @Thickness 3.20 mm
$ 1719/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 154 MPa
- Elongation at Break: 1.6 %
- Tensile Modulus: 14.2 GPa
$ 1556/MT
- Density: 1.71 g/cc
- Density: 1.71 g/cc
- Moisture Absorption: 0.440 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
$ 1622/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.016 cm/cm @Time 86400 sec
- Tensile Strength at Break: 56.0 MPa
- Elongation at Break: 2.7 %
- Tensile Modulus: 5.21 GPa
$ 2056/MT
- Density: 1.71 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Moisture Absorption at Equilibrium: 1.1 %
- Linear Mold Shrinkage, Flow: 0.0026 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0061 cm/cm @Time 86400 sec
$ 2369/MT
- Density: 1.36 g/cc
- Tensile Strength, Yield: 220 MPa
- Elongation at Break: 1.6 %
- Flexural Yield Strength: 315 MPa
- Flexural Modulus: 16.8 GPa
$ 1839/MT
- Density: 1.54 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0034 cm/cm
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm
- Tensile Strength, Yield: 217 MPa
$ 1515/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.980 %
- Moisture Absorption: 1.50 %
- Linear Mold Shrinkage, Flow: 0.0090 - 0.020 cm/cm @Time 86400 sec
$ 2073/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 3.20 mm
- Melt Flow: 16 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1736/MT
- Density: 1.58 g/cc
- Moisture Absorption at Equilibrium: 0.85 %
- Water Absorption at Saturation: 2.75 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0025 cm/cm
- Hardness, Rockwell L: 114
$ 2178/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 3.20 mm
- Melt Flow: 16 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1641/MT
- Density: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Time 86400 sec
$ 1616/MT
- Density: 1.47 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 9.00 GPa
$ 1850/MT
- Density: 1.12 g/cc
- Density: 1.12 g/cc
- Moisture Absorption: 0.880 %
- Moisture Absorption: 1.18 %
- Linear Mold Shrinkage, Flow: 0.023 - 0.025 cm/cm @Time 86400 sec
$ 1765/MT
- Specific Gravity: 1.33 g/cc
- Density: 1.32 g/cc
- Moisture Absorption: 0.670 %
- Moisture Absorption: 0.960 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Time 86400 sec
$ 1759/MT
- Density: 1.43 g/cc
- Tensile Strength at Break: 183 MPa
- Elongation at Break: 3.2 %
- Flexural Strength: 270 MPa
- Flexural Modulus: 9.30 GPa
$ 1809/MT
- Density: 1.75 g/cc
- Moisture Absorption: 0.250 %
- Moisture Absorption: 0.410 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.030 cm/cm @Time 86400 sec
$ 1995/MT
- Density: 1.23 g/cc
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.017 - 0.018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.020 - 0.021 cm/cm @Time 86400 sec
- Tensile Strength at Break: 85.0 MPa
$ 2101/MT
- Specific Gravity: 1.69 g/cc
- Density: 1.68 g/cc
- Density: 1.69 g/cc
- Moisture Absorption: 0.360 %
- Moisture Absorption: 0.540 %
$ 1934/MT
- Density: 1.23 g/cc
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 73.0 MPa
- Tensile Strength at Break: 73.0 MPa
$ 1861/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage, Flow: 0.015 - 0.020 cm/cm
- Tensile Strength, Yield: 63.0 MPa
- Elongation at Break: 7.0 %
- Tensile Modulus: 2.70 GPa
$ 1679/MT
- Density: 1.38 g/cc
- Tensile Strength at Break: 78.0 MPa
- Elongation at Break: 3.4 %
- Tensile Modulus: 4.96 GPa
- Flexural Strength: 131 MPa
$ 1640/MT
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.018 - 0.023 cm/cm
- Tensile Strength at Break: 53.0 MPa
- Elongation at Break: 4.9 %
- Tensile Modulus: 2.50 GPa
$ 1886/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.246 g/cc
- Moisture Absorption: 0.810 %
- Moisture Absorption: 1.20 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1485/MT
- Density: 1.02 g/cc
- Density: 1.02 g/cc
- Moisture Absorption: 0.300 %
- Moisture Absorption: 0.430 %
- Linear Mold Shrinkage, Flow: 0.0257 cm/cm @Time 86400 sec
$ 1660/MT
- Specific Gravity: 1.48 g/cc
- Density: 1.48 g/cc
- Moisture Absorption: 0.0600 %
- Moisture Absorption: 0.630 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 1489/MT
- Density: 1.54 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Melt Index of Compound: 70 g/10 min @Load 5.00 kg, Temperature 275 °C
- Tensile Strength at Break: 170 MPa
- Elongation at Break: 2.3 %
$ 1595/MT
- Density: 1.41 g/cc
- Density: 1.42 g/cc
- Tensile Strength at Break: 198 MPa
- Tensile Strength at Break: 202 MPa
- Elongation at Break: 2.3 %
$ 1652/MT
- Density: 1.58 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0022 cm/cm @Time 86400 sec
- Tensile Strength at Break: 265 MPa
- Elongation at Break: 1.9 %
$ 1700/MT
- Moisture Absorption at Equilibrium: 0.87 %
- Moisture Absorption at Equilibrium: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.030 - 0.050 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.030 - 0.050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 46.0 MPa
$ 2370/MT
- Density: 1.29 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.014 cm/cm
- Tensile Strength at Break: 71.0 MPa
- Tensile Strength, Yield: 43.0 MPa
- Elongation at Break: 5.3 %
$ 1870/MT
- Moisture Absorption: 0.600 %
- Moisture Absorption: 0.870 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.030 - 0.050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 46.0 MPa
$ 1459/MT
- Specific Gravity: 1.40 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.640 %
- Moisture Absorption: 0.890 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Time 86400 sec
$ 1487/MT
- Density: 1.11 g/cc
- Tensile Strength at Break: 45.0 MPa
- Elongation at Break: 97 %
- Tensile Modulus: 1.60 GPa
- Flexural Yield Strength: 49.0 MPa
$ 1954/MT
- Density: 1.39 g/cc
- Moisture Absorption: 0.850 %
- Moisture Absorption: 1.40 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.040 cm/cm @Time 86400 sec
$ 1759/MT
- Density: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.015 cm/cm @Time 86400 sec
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 40 %
$ 2375/MT
- Density: 1.47 g/cc
- Density: 1.478 g/cc
- Moisture Absorption: 0.600 %
- Moisture Absorption: 0.970 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 1557/MT
- Density: 1.72 g/cc
- Density: 1.72 g/cc
- Moisture Absorption: 0.300 %
- Linear Mold Shrinkage, Flow: 0.0029 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
$ 1515/MT
- Density: 1.29 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 115 MPa
- Tensile Strength at Break: 117 MPa
- Elongation at Break: 3.6 %
$ 1993/MT
- Specific Gravity: 1.50 g/cc
- Density: 1.48 g/cc
- Moisture Absorption: 0.660 %
- Moisture Absorption: 1.00 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 1538/MT
- Density: 1.27 g/cc
- Density: 1.28 g/cc
- Moisture Absorption: 0.600 %
- Linear Mold Shrinkage, Flow: 0.00080 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
$ 1478/MT
- Density: 1.38 g/cc
- Density: 1.38 g/cc
- Moisture Absorption: 0.530 %
- Moisture Absorption: 0.840 %
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
$ 1534/MT
- Density: 1.48 g/cc
- Density: 1.487 g/cc
- Moisture Absorption: 0.490 %
- Linear Mold Shrinkage, Flow: 0.0089 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Time 86400 sec
$ 1776/MT
- Density: 1.65 g/cc
- Tensile Strength at Break: 231 MPa
- Elongation at Break: 2.3 %
- Flexural Strength: 362 MPa
- Flexural Modulus: 14.1 GPa
$ 1878/MT
- Density: 1.38 g/cc
- Tensile Strength at Break: 78.0 MPa
- Elongation at Break: 3.4 %
- Tensile Modulus: 4.96 GPa
- Flexural Strength: 131 MPa
$ 1766/MT
- Density: 1.27 g/cc
- Density: 1.27 g/cc
- Moisture Absorption: 0.600 %
- Moisture Absorption: 0.970 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 2120/MT
- Density: 1.59 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Tensile Strength at Break: 157 MPa
- Elongation at Break: 2.4 %
- Tensile Modulus: 10.54 GPa
$ 1724/MT
- Density: 1.76 g/cc
- Tensile Strength at Break: 237 MPa
- Elongation at Break: 2.0 %
- Tensile Modulus: 23.23 GPa
- Flexural Strength: 358 MPa
$ 1486/MT
- Density: 1.22 g/cc
- Density: 1.23 g/cc
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Yield: 10 %
- Tensile Modulus: 3.40 GPa
$ 1585/MT
- Density: 1.47 g/cc
- Density: 1.48 g/cc
- Moisture Absorption: 0.600 %
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm @Time 86400 sec
$ 1533/MT
- Density: 1.23 g/cc
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.017 - 0.018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.020 - 0.021 cm/cm @Time 86400 sec
- Tensile Strength at Break: 85.0 MPa
$ 1865/MT
- Density: 1.57 g/cc
- Density: 1.58 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0033 cm/cm @Time 86400 sec
$ 2028/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 2.2 %
- Tensile Modulus: 10.54 GPa
$ 1717/MT
- Density: 1.56 g/cc
- Tensile Strength at Break: 206 MPa
- Flexural Modulus: 11.92 GPa
- Izod Impact, Notched: 2.74 J/cm
- Deflection Temperature at 1.8 MPa (264 psi): 251 °C @Thickness 3.20 mm
$ 1708/MT
- Specific Gravity: 1.38 g/cc
- Density: 1.36 g/cc
- Density: 1.38 g/cc
- Moisture Absorption: 0.720 %
- Moisture Absorption: 0.720 %
$ 2202/MT
- Density: 1.10 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 0.730 %
- Moisture Absorption: 1.12 %
- Linear Mold Shrinkage, Flow: 0.024 - 0.026 cm/cm @Time 86400 sec
$ 1811/MT
- Density: 1.23 g/cc
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.017 - 0.018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.020 - 0.021 cm/cm @Time 86400 sec
- Tensile Strength at Break: 85.0 MPa
$ 1466/MT
- Specific Gravity: 1.29 g/cc
- Density: 1.28 g/cc
- Moisture Absorption: 0.620 %
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 2309/MT
- Density: 1.14 g/cc
- Tensile Strength at Break: 57.0 MPa
- Tensile Strength, Yield: 69.0 MPa
- Elongation at Break: 58 %
- Elongation at Yield: 23 %
$ 1537/MT
- Specific Gravity: 1.33 g/cc
- Density: 1.34 g/cc
- Moisture Absorption: 0.540 %
- Moisture Absorption: 0.780 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 1741/MT
- Density: 1.37 g/cc
- Density: 1.38 g/cc
- Moisture Absorption: 0.630 %
- Linear Mold Shrinkage, Flow: 0.0027 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
$ 1785/MT
- Specific Gravity: 1.28 g/cc
- Density: 1.274 g/cc
- Moisture Absorption: 0.750 %
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 2353/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.840 %
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 1530/MT
- Density: 1.16 g/cc
- Tensile Strength at Break: 77.0 MPa
- Elongation at Break: 6.6 %
- Elongation at Yield: 5.4 %
- Tensile Modulus: 3.20 GPa
$ 1968/MT
- Density: 1.54 g/cc
- Density: 1.54 g/cc
- Moisture Absorption: 0.400 %
- Linear Mold Shrinkage, Flow: 0.0018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 1716/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 2.2 %
- Tensile Modulus: 10.54 GPa
$ 1839/MT
- Density: 1.46 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 189 MPa
- Elongation at Break: 2.3 %
- Flexural Strength: 276 MPa
$ 1860/MT
- Density: 1.36 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Tensile Strength at Break: 127 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 6.70 GPa
$ 1859/MT
- Density: 1.39 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.690 %
- Moisture Absorption: 1.20 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1811/MT
- Density: 1.12 g/cc
- Water Absorption: 0.37 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 99.0 MPa
- Elongation at Break: 3.5 %
$ 2144/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 154 MPa
- Elongation at Break: 1.6 %
- Tensile Modulus: 14.2 GPa
$ 1958/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 154 MPa
- Elongation at Break: 1.6 %
- Tensile Modulus: 14.2 GPa
$ 1580/MT
- Density: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.840 %
- Moisture Absorption: 0.840 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1591/MT
- Density: 1.52 g/cc
- Density: 1.52 g/cc
- Moisture Absorption: 0.400 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0053 cm/cm @Time 86400 sec
$ 2357/MT
- Density: 1.40 g/cc
- Tensile Strength at Break: 145 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 7.80 GPa
- Flexural Strength: 215 MPa
$ 1821/MT
- Density: 1.48 g/cc
- Water Absorption: 1.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0044 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm @Time 86400 sec
- Tensile Strength at Break: 190 MPa
$ 1774/MT
- Specific Gravity: 1.68 g/cc
- Density: 1.68 g/cc
- Moisture Absorption: 0.420 %
- Moisture Absorption: 0.600 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1654/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.640 %
- Moisture Absorption: 0.940 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Time 86400 sec
$ 1597/MT
- Density: 1.22 g/cc
- Density: 1.22 g/cc
- Moisture Absorption: 0.700 %
- Linear Mold Shrinkage, Flow: 0.019 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0192 cm/cm @Time 86400 sec
$ 1469/MT
- Density: 1.22 g/cc
- Density: 1.22 g/cc
- Moisture Absorption: 0.720 %
- Moisture Absorption: 1.17 %
- Linear Mold Shrinkage, Flow: 0.019 cm/cm @Time 86400 sec
$ 1496/MT
- Specific Gravity: 1.42 g/cc
- Density: 1.42 g/cc
- Moisture Absorption: 0.660 %
- Moisture Absorption: 1.00 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
$ 1886/MT
- Specific Gravity: 1.41 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.640 %
- Moisture Absorption: 0.940 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Time 86400 sec
$ 1698/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 126 MPa
- Elongation at Break: 3.5 %
- Tensile Modulus: 5.90 GPa
$ 1670/MT
- Density: 1.31 g/cc
- Density: 1.31 g/cc
- Moisture Absorption: 0.900 %
- Tensile Strength at Break: 53.0 MPa
- Tensile Strength at Break: 58.0 MPa
$ 1763/MT
- Density: 1.65 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 161 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 13.85 GPa
$ 1927/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 154 MPa
- Elongation at Break: 1.6 %
- Tensile Modulus: 14.2 GPa
$ 2233/MT
- Density: 1.31 g/cc
- Density: 1.31 g/cc
- Moisture Absorption: 0.900 %
- Tensile Strength at Break: 53.0 MPa
- Tensile Strength at Break: 58.0 MPa
$ 1457/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 173 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 9.70 GPa
$ 1534/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm @Time 86400 sec
- Tensile Strength at Break: 132 MPa
- Tensile Strength at Break: 139 MPa
$ 2315/MT
- Density: 1.57 g/cc
- Water Absorption: 0.80 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0024 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0079 cm/cm @Time 86400 sec
- Tensile Strength at Break: 268 MPa
$ 2038/MT
- Density: 1.53 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 217 MPa
- Elongation at Break: 2.8 %
- Flexural Strength: 324 MPa
$ 2051/MT
- Density: 1.65 g/cc
- Tensile Strength at Break: 231 MPa
- Elongation at Break: 2.3 %
- Flexural Strength: 362 MPa
- Flexural Modulus: 14.1 GPa
$ 2001/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 2.8 %
- Tensile Modulus: 8.35 GPa
$ 1897/MT
- Density: 1.49 g/cc
- Density: 1.50 g/cc
- Moisture Absorption: 0.500 %
- Moisture Absorption: 0.740 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Time 86400 sec
$ 1528/MT
- Specific Gravity: 1.40 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.860 %
- Moisture Absorption: 1.40 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1449/MT
- Density: 1.60 g/cc
- Density: 1.60 g/cc
- Moisture Absorption: 0.400 %
- Linear Mold Shrinkage, Flow: 0.0037 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 2293/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm
- Tensile Strength at Break: 77.0 MPa
- Elongation at Break: 4.2 %
- Tensile Modulus: 6.30 GPa
$ 1766/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Flow: 0.018 - 0.023 cm/cm
- Tensile Strength at Break: 58.0 MPa
- Elongation at Break: 3.8 %
- Tensile Modulus: 2.80 GPa
$ 1716/MT
- Density: 1.23 g/cc
- Tensile Strength at Break: 59.0 MPa
- Elongation at Break: 7.0 %
- Flexural Strength: 83.0 MPa
- Flexural Modulus: 2.30 GPa
$ 1666/MT
- Density: 1.47 g/cc
- Tensile Strength at Break: 171 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 13.99 GPa
- Flexural Strength: 220 MPa
$ 2099/MT
- Density: 1.46 g/cc
- Tensile Strength at Break: 108 MPa
- Elongation at Break: 2.7 %
- Tensile Modulus: 7.74 GPa
- Flexural Strength: 186 MPa
$ 1511/MT
- Density: 1.51 g/cc
- Linear Mold Shrinkage, Flow: 0.012 cm/cm
- Tensile Strength, Yield: 54.0 MPa
- Elongation at Yield: 2.1 %
- Tensile Modulus: 4.80 GPa
$ 1817/MT
- Density: 1.52 g/cc
- Density: 1.53 g/cc
- Moisture Absorption at Equilibrium: 0.86 %
- Moisture Absorption at Equilibrium: 0.61 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.010 - 0.030 cm/cm @Time 86400 sec
$ 1472/MT
- Density: 1.41 g/cc
- Density: 1.41 g/cc
- Moisture Absorption: 0.650 %
- Moisture Absorption: 1.14 %
- Linear Mold Shrinkage, Flow: 0.0028 cm/cm @Time 86400 sec
$ 1634/MT
- Density: 1.19 g/cc
- Water Absorption at Saturation: 5.5 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm
- Hardness, Rockwell L: 105
- Tensile Strength at Break: 170 MPa
$ 1710/MT
- Density: 1.58 g/cc
- Density: 1.58 g/cc
- Linear Mold Shrinkage, Flow: 0.0018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0022 cm/cm @Time 86400 sec
$ 1753/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 8.17 GPa
$ 1706/MT
- Specific Gravity: 1.38 g/cc
- Density: 1.37 g/cc
- Moisture Absorption: 0.600 %
- Moisture Absorption: 0.900 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Time 86400 sec
$ 1498/MT
- Density: 2.19 g/cc
- Density: 2.19 g/cc
- Moisture Absorption at Equilibrium: 2.0 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0128 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0108 cm/cm @Time 86400 sec
$ 1571/MT
- Density: 1.53 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.012 cm/cm @Time 86400 sec
- Tensile Strength at Break: 136 MPa
- Elongation at Break: 3.3 %
$ 1547/MT
- Specific Gravity: 1.67 g/cc
- Density: 1.66 g/cc
- Moisture Absorption: 0.400 %
- Moisture Absorption: 0.790 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 2139/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 135 MPa
- Tensile Strength, Yield: 82.0 MPa
- Elongation at Break: 3.5 %
$ 1649/MT
- Density: 1.39 g/cc
- Density: 1.39 g/cc
- Moisture Absorption: 0.460 %
- Moisture Absorption: 0.700 %
- Linear Mold Shrinkage, Flow: 0.0189 cm/cm @Time 86400 sec
$ 1881/MT
- Density: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Time 86400 sec
$ 1460/MT
- Density: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Time 86400 sec
$ 2148/MT
- Density: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Time 86400 sec
$ 1849/MT
- Density: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Time 86400 sec
$ 1857/MT
- Density: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Time 86400 sec
$ 1464/MT
- Density: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Time 86400 sec
$ 1453/MT
- Density: 1.29 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 115 MPa
- Tensile Strength at Break: 117 MPa
- Elongation at Break: 3.6 %
$ 1839/MT
- Density: 1.22 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Tensile Strength at Break: 200 MPa
- Elongation at Break: 3.0 %
- Flexural Strength: 269 MPa
$ 1662/MT
- Density: 1.49 g/cc
- Density: 1.49 g/cc
- Moisture Absorption at Equilibrium: 0.47 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.020 cm/cm @Time 86400 sec
$ 1739/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.016 cm/cm @Time 86400 sec
- Tensile Strength at Break: 56.0 MPa
- Elongation at Break: 2.7 %
- Tensile Modulus: 5.21 GPa
$ 2364/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.023 - 0.025 cm/cm @Time 86400 sec
- Tensile Strength at Break: 40.0 MPa
- Elongation at Break: 40 %
- Tensile Modulus: 1.70 GPa
$ 2139/MT
- Density: 1.20 g/cc
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 8.0 %
- Tensile Modulus: 3.24 GPa
- Flexural Strength: 110 MPa
$ 1493/MT
- Density: 1.54 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm
- Tensile Strength at Break: 221 MPa
- Elongation at Break: 2.4 %
- Tensile Modulus: 14.5 GPa
$ 1494/MT
- Density: 1.21 g/cc
- Density: 1.21 g/cc
- Moisture Absorption: 0.730 %
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: >= 0.020 cm/cm @Time 86400 sec
$ 1972/MT
- Density: 1.34 g/cc
- Moisture Absorption: 0.900 %
- Water Absorption at Saturation: 2.5 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.011 cm/cm @Thickness 3.20 mm
$ 1939/MT
- Specific Gravity: 1.57 g/cc
- Density: 1.56 g/cc
- Moisture Absorption: 0.630 %
- Moisture Absorption: 0.920 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Time 86400 sec
$ 1945/MT
- Density: 1.45 g/cc
- Density: 1.46 g/cc
- Moisture Absorption: 1.20 %
- Moisture Absorption: 1.55 %
- Linear Mold Shrinkage, Flow: 0.018 - 0.020 cm/cm @Time 86400 sec
$ 1560/MT
- Density: 1.45 g/cc
- Density: 1.46 g/cc
- Moisture Absorption: 1.20 %
- Moisture Absorption: 1.55 %
- Linear Mold Shrinkage, Flow: 0.018 - 0.020 cm/cm @Time 86400 sec
$ 1793/MT
- Density: 1.45 g/cc
- Density: 1.46 g/cc
- Moisture Absorption: 1.20 %
- Moisture Absorption: 1.55 %
- Linear Mold Shrinkage, Flow: 0.018 - 0.020 cm/cm @Time 86400 sec
$ 1657/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.00050 - 0.0015 cm/cm
- Tensile Strength at Break: 238 MPa
- Elongation at Break: 1.0 %
- Tensile Modulus: 33.4 GPa
$ 2077/MT
- Density: 1.29 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 113 MPa
- Elongation at Break: 2.7 %
- Tensile Modulus: 6.39 GPa
$ 2288/MT
- Density: 1.10 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 0.730 %
- Moisture Absorption: 1.12 %
- Linear Mold Shrinkage, Flow: 0.024 - 0.026 cm/cm @Time 86400 sec
$ 1991/MT
- Density: 1.34 g/cc
- Density: 1.34 g/cc
- Moisture Absorption: 0.270 %
- Moisture Absorption: 0.400 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
$ 2165/MT
- Density: 1.41 g/cc
- Density: 1.41 g/cc
- Moisture Absorption: 0.620 %
- Moisture Absorption: 0.920 %
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0090 cm/cm @Time 86400 sec
$ 2332/MT
- Density: 1.53 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 - 0.012 cm/cm @Time 86400 sec
- Tensile Strength at Break: 136 MPa
- Elongation at Break: 3.3 %
$ 1772/MT
- Density: 1.21 g/cc
- Density: 1.215 g/cc
- Moisture Absorption: 0.800 %
- Moisture Absorption: 1.70 %
- Linear Mold Shrinkage, Flow: 0.0076 cm/cm @Time 86400 sec
$ 1902/MT
- Specific Gravity: 1.46 g/cc
- Density: 1.46 g/cc
- Moisture Absorption: 0.630 %
- Moisture Absorption: 0.950 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Time 86400 sec
$ 1576/MT
- Density: 1.49 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Tensile Strength, Yield: 171 MPa
- Elongation at Break: 3.1 %
- Flexural Yield Strength: 247 MPa
$ 1462/MT
- Density: 1.65 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 170 MPa
- Elongation at Break: 3.0 %
$ 1523/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Tensile Strength at Break: 175 MPa
- Elongation at Break: 3.0 %
- Tensile Modulus: 10.9 GPa
$ 1913/MT
- Density: 1.25 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 122 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 9.03 GPa
$ 1760/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm
- Tensile Strength at Break: 162 MPa
- Elongation at Break: 2.6 %
- Flexural Strength: 232 MPa
$ 1949/MT
- Density: 1.47 g/cc
- Water Absorption: 1.1 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm
- Tensile Strength, Yield: 131 MPa
- Elongation at Break: 2.6 %
$ 1865/MT
- Density: 1.60 g/cc
- Water Absorption: 0.90 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Time 86400 sec
- Tensile Strength at Break: 276 MPa
$ 1575/MT
- Specific Gravity: 1.48 g/cc
- Density: 1.48 g/cc
- Moisture Absorption: 0.550 %
- Moisture Absorption: 0.810 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1726/MT
- Density: 1.22 g/cc
- Density: 1.23 g/cc
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Yield: 10 %
- Tensile Modulus: 3.40 GPa
$ 1673/MT
- Density: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption at Equilibrium: 0.35 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0032 - 0.0044 cm/cm @Time 86400 sec
$ 2354/MT
- Density: 1.57 g/cc
- Linear Mold Shrinkage, Flow: 0.012 cm/cm @Time 86400 sec
- Tensile Strength at Break: 52.0 MPa
- Elongation at Break: 1.8 %
- Tensile Modulus: 5.24 GPa
$ 2584/MT
- Specific Gravity: 1.69 g/cc
- Density: 1.69 g/cc
- Moisture Absorption: 0.390 %
- Moisture Absorption: 0.510 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Time 86400 sec
$ 1640/MT
- Density: 1.71 g/cc
- Density: 1.71 g/cc
- Moisture Absorption: 0.440 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
$ 1656/MT
- Density: 1.60 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Time 86400 sec
- Tensile Strength at Break: 276 MPa
$ 2089/MT
- Density: 1.40 g/cc
- Linear Mold Shrinkage, Flow: 0.0024 cm/cm
- Tensile Strength at Break: 156 MPa
- Elongation at Break: 2.2 %
- Elongation at Break: 3.8 %
$ 1715/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 204 MPa
- Elongation at Break: 2.3 %
- Tensile Modulus: 14.9 GPa
$ 2420/MT
- Density: 1.20 g/cc
- Tensile Strength at Break: 107 MPa
- Elongation at Break: 4.1 %
- Tensile Modulus: 4.82 GPa
- Flexural Strength: 158 MPa
$ 2573/MT
- Density: 1.24 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.900 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Time 86400 sec
$ 1673/MT
- Density: 1.58 g/cc
- Water Absorption at Saturation: 4.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm
- Hardness, Rockwell L: 108
- Tensile Strength at Break: 165 MPa
$ 1547/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 8.17 GPa
$ 2152/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 115 MPa
- Elongation at Break: 2.6 %
- Tensile Modulus: 8.17 GPa
$ 1806/MT
- Density: 1.64 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.014 cm/cm
- Tensile Strength at Break: 58.0 MPa
- Elongation at Break: 1.3 %
- Tensile Modulus: 7.70 GPa
$ 1667/MT
- Density: 1.51 g/cc
- Tensile Strength at Break: 138 MPa
- Tensile Strength at Break: 139 MPa
- Elongation at Break: 2.1 %
- Elongation at Break: 2.1 %
$ 1913/MT
- Density: 1.44 g/cc
- Moisture Absorption: 0.550 %
- Moisture Absorption: 0.870 %
- Linear Mold Shrinkage, Flow: 0.0017 - 0.0026 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Time 86400 sec
$ 2235/MT
- Density: 1.51 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0035 cm/cm
- Tensile Strength at Break: 219 MPa
- Elongation at Break: 2.8 %
- Tensile Modulus: 13.3 GPa
$ 1461/MT
- Density: 1.15 g/cc
- Moisture Absorption at Equilibrium: 0.80 % @Time 86400 sec
- Tensile Strength at Break: 64.0 MPa
- Tensile Strength, Yield: 66.0 MPa
- Elongation at Break: 4.1 %
$ 2337/MT
- Density: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Time 86400 sec
$ 1953/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.017 - 0.019 cm/cm
- Tensile Strength at Break: 74.0 MPa
- Elongation at Break: 4.5 %
- Tensile Modulus: 3.00 GPa
$ 2048/MT
- Density: 1.45 g/cc
- Tensile Strength at Break: 175 MPa
- Elongation at Break: 2.7 %
- Tensile Modulus: 10.34 GPa
- Flexural Strength: 255 MPa
$ 1685/MT
- Density: 1.71 g/cc
- Water Absorption: 0.90 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0080 cm/cm @Time 86400 sec
- Tensile Strength at Break: 279 MPa
$ 1865/MT
- Density: 1.35 g/cc
- Density: 1.35 g/cc
- Moisture Absorption: 0.500 %
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
$ 1563/MT
- Density: 1.44 g/cc
- Water Absorption: 1.1 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0090 cm/cm @Time 86400 sec
- Tensile Strength at Break: 205 MPa
$ 1786/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 - 0.014 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.9 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength, Yield: 51.0 MPa
$ 1489/MT
- Density: 1.39 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
- Tensile Strength at Break: 130 MPa
- Elongation at Break: 2.4 %
- Tensile Modulus: 9.40 GPa
$ 1486/MT
- Density: 1.32 g/cc
- Tensile Strength at Break: 260 MPa
- Elongation at Break: 1.5 %
- Tensile Modulus: 27.4 GPa
- Flexural Strength: 358 MPa
$ 1945/MT
- Density: 1.71 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm @Time 86400 sec
- Tensile Strength at Break: 165 MPa
- Elongation at Break: 2.7 %
$ 1591/MT
- Density: 1.14 g/cc
- Density: 1.15 g/cc
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Time 86400 sec
$ 1618/MT
- Density: 1.58 g/cc
- Density: 1.58 g/cc
- Linear Mold Shrinkage, Flow: 0.0018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0022 cm/cm @Time 86400 sec
$ 1594/MT
- Density: 1.23 g/cc
- Density: 1.24 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 - 0.013 cm/cm
- Linear Mold Shrinkage, Flow: 0.017 - 0.018 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.020 - 0.021 cm/cm @Time 86400 sec
$ 1902/MT
- Density: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Time 86400 sec
- Tensile Strength at Break: 119 MPa
- Elongation at Break: 2.8 %
- Tensile Modulus: 6.24 GPa
$ 1620/MT
- Density: 1.27 g/cc
- Density: 1.27 g/cc
- Moisture Absorption: 0.550 %
- Linear Mold Shrinkage, Flow: 0.0188 - 0.0329 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.019 - 0.033 cm/cm @Time 86400 sec
$ 1626/MT
- Density: 1.38 g/cc
- Density: 1.38 g/cc
- Moisture Absorption: 0.840 %
- Linear Mold Shrinkage, Flow: 0.0046 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
$ 1723/MT
- Density: 1.16 g/cc
- Tensile Strength at Break: 84.0 MPa
- Elongation at Break: 4.0 %
- Flexural Strength: 117 MPa
- Flexural Modulus: 3.41 GPa
$ 2315/MT
- Density: 1.70 g/cc
- Moisture Absorption: 0.320 %
- Moisture Absorption: 0.470 %
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0024 cm/cm @Time 86400 sec
$ 2267/MT
- Density: 1.42 g/cc
- Density: 1.42 g/cc
- Moisture Absorption: 0.970 %
- Tensile Strength at Break: 204 MPa
- Tensile Strength at Break: 214 MPa
$ 2013/MT
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.014 cm/cm @Time 86400 sec
- Tensile Strength at Break: 195 MPa
- Elongation at Break: 2.9 %
$ 2170/MT
- Density: 1.37 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength, Yield: 175 MPa
- Elongation at Break: 2.0 - 4.0 %
- Tensile Modulus: 9.50 GPa
Delivery Nylon 66 SABIC Innovative Plastics (GE Plastics)
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):
Country | 20’ Container | 40’ Container | 5,000 MT |
🇦🇺 Australia | $3345 | $4181 | $401400 |
🇦🇹 Austria | $2825 | $3531 | $339000 |
🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
🇦🇱 Albania | $2500 | $3125 | $300000 |
🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
🇦🇴 Angola | $2762.5 | $3453 | $331500 |
🇦🇷 Argentina | $3230 | $4038 | $387600 |
🇦🇲 Armenia | $2625 | $3281 | $315000 |
🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
🇧🇭 Bahrain | $3095 | $3869 | $371400 |
🇧🇾 Belarus | $2825 | $3531 | $339000 |
🇧🇿 Belize | $3155 | $3944 | $378600 |
🇧🇪 Belgium | $2575 | $3219 | $309000 |
🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
🇧🇴 Bolivia | $3230 | $4038 | $387600 |
🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
🇧🇷 Brazil | $3120 | $3900 | $374400 |
🇭🇺 Hungary | $2575 | $3219 | $309000 |
🇻🇪 Venezuela | $3230 | $4038 | $387600 |
🇻🇳 Vietnam | $2625 | $3281 | $315000 |
🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
🇬🇹 Guatemala | $3230 | $4038 | $387600 |
🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
🇩🇪 Germany | $2475 | $3094 | $297000 |
🇭🇳 Honduras | $3230 | $4038 | $387600 |
🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
🇬🇷 Greece | $2575 | $3219 | $309000 |
🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
🇩🇰 Denmark | $2400 | $3000 | $288000 |
🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
🇮🇱 Israel | $2625 | $3281 | $315000 |
🇮🇳 India | $3712.5 | $4641 | $445500 |
🇮🇩 Indonesia | $3095 | $3869 | $371400 |
🇯🇴 Jordan | $2625 | $3281 | $315000 |
🇮🇶 Iraq | $2625 | $3281 | $315000 |
🇮🇷 Iran | $3095 | $3869 | $371400 |
🇮🇪 Ireland | $2500 | $3125 | $300000 |
🇮🇸 Iceland | $2575 | $3219 | $309000 |
🇪🇸 Spain | $2500 | $3125 | $300000 |
🇮🇹 Italy | $2400 | $3000 | $288000 |
🇾🇪 Yemen | $2625 | $3281 | $315000 |
🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
🇰🇭 Cambodia | $3095 | $3869 | $371400 |
🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
🇨🇦 Canada | $3230 | $4038 | $387600 |
🇶🇦 Qatar | $2625 | $3281 | $315000 |
🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
🇨🇾 Cyprus | $2625 | $3281 | $315000 |
🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
🇨🇳 China | $3712.5 | $4641 | $445500 |
🇨🇴 Colombia | $3230 | $4038 | $387600 |
🇰🇷 Korea South | $2625 | $3281 | $315000 |
🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
🇨🇺 Cuba | $3230 | $4038 | $387600 |
🇰🇼 Kuwait | $2625 | $3281 | $315000 |
🇱🇻 Latvia | $2575 | $3219 | $309000 |
🇱🇧 Lebanon | $2625 | $3281 | $315000 |
🇱🇾 Libya | $2762.5 | $3453 | $331500 |
🇱🇹 Lithuania | $2500 | $3125 | $300000 |
🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
🇲🇾 Malaysia | $2625 | $3281 | $315000 |
🇲🇹 Malta | $2500 | $3125 | $300000 |
🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
🇲🇽 Mexico | $3155 | $3944 | $378600 |
🇲🇩 Moldova | $2400 | $3000 | $288000 |
🇲🇨 Monaco | $2475 | $3094 | $297000 |
🇲🇳 Mongolia | $2625 | $3281 | $315000 |
🇲🇲 Myanmar | $2625 | $3281 | $315000 |
🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
🇳🇵 Nepal | $2625 | $3281 | $315000 |
🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
🇳🇱 Netherlands | $2575 | $3219 | $309000 |
🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
🇳🇿 New Zealand | $3345 | $4181 | $401400 |
🇳🇴 Norway | $2400 | $3000 | $288000 |
🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
🇴🇲 Oman | $2625 | $3281 | $315000 |
🇵🇰 Pakistan | $2625 | $3281 | $315000 |
🇵🇦 Panama | $3230 | $4038 | $387600 |
🇵🇾 Paraguay | $3155 | $3944 | $378600 |
🇵🇪 Peru | $3230 | $4038 | $387600 |
🇵🇱 Poland | $2575 | $3219 | $309000 |
🇵🇹 Portugal | $2500 | $3125 | $300000 |
🇷🇺 Russia | $2575 | $3219 | $309000 |
🇷🇴 Romania | $2475 | $3094 | $297000 |
🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
🇷🇸 Serbia | $2575 | $3219 | $309000 |
🇸🇬 Singapore | $3095 | $3869 | $371400 |
🇸🇾 Syria | $3095 | $3869 | $371400 |
🇸🇰 Slovakia | $2500 | $3125 | $300000 |
🇸🇮 Slovenia | $2500 | $3125 | $300000 |
🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
🇺🇸 United States | $2902.5 | $3628 | $348300 |
🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
🇹🇭 Thailand | $2625 | $3281 | $315000 |
🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
🇹🇷 Turkey | $2625 | $3281 | $315000 |
🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
🇺🇦 Ukraine | $2500 | $3125 | $300000 |
🇺🇾 Uruguay | $2675 | $3344 | $321000 |
🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
🇵🇭 Philippines | $2625 | $3281 | $315000 |
🇫🇮 Finland | $2500 | $3125 | $300000 |
🇫🇷 France | $2575 | $3219 | $309000 |
🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
🇲🇪 Montenegro | $2575 | $3219 | $309000 |
🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
🇨🇱 Chile | $3355 | $4194 | $402600 |
🇨🇭 Switzerland | $2575 | $3219 | $309000 |
🇸🇪 Sweden | $2500 | $3125 | $300000 |
🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
🇪🇨 Ecuador | $3155 | $3944 | $378600 |
🇦🇸 American Samoa | $3345 | $4181 | $401400 |
🇸🇻 El Salvador | $3230 | $4038 | $387600 |
🇪🇪 Estonia | $2575 | $3219 | $309000 |
🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
🇯🇵 Japan | $3095 | $3869 | $371400 |
🇦🇩 Andorra | $2500 | $3125 | $300000 |
🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
🇧🇧 Barbados | $3230 | $4038 | $387600 |
🇧🇹 Bhutan | $3095 | $3869 | $371400 |
🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
🇧🇳 Brunei | $2625 | $3281 | $315000 |
🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
🇹🇩 Chad | $2762.5 | $3453 | $331500 |
🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
🇧🇯 Benin | $2762.5 | $3453 | $331500 |
🇩🇲 Dominica | $3230 | $4038 | $387600 |
🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
🇫🇯 Fiji | $3345 | $4181 | $401400 |
🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
🇰🇮 Kiribati | $3345 | $4181 | $401400 |
🇬🇩 Grenada | $3355 | $4194 | $402600 |
🇬🇺 Guam | $3345 | $4181 | $401400 |
🇬🇾 Guyana | $3230 | $4038 | $387600 |
🇭🇹 Haiti | $3120 | $3900 | $374400 |
🇯🇲 Jamaica | $3230 | $4038 | $387600 |
🇰🇵 Korea, North | $2625 | $3281 | $315000 |
🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
🇲🇻 Maldives | $2625 | $3281 | $315000 |
🇲🇱 Mali | $2762.5 | $3453 | $331500 |
🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
🇨🇼 Curaçao | $3230 | $4038 | $387600 |
🇦🇼 Aruba | $3120 | $3900 | $374400 |
🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
🇳🇪 Niger | $2762.5 | $3453 | $331500 |
🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
🇸🇲 San Marino | $2500 | $3125 | $300000 |
🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
🇸🇷 Suriname | $3230 | $4038 | $387600 |
🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
🇹🇬 Togo | $2762.5 | $3453 | $331500 |
🇹🇴 Tonga | $3345 | $4181 | $401400 |
🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts,
chemical carrier for sale. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.