$ 1843/MT
- Specific Gravity: 1.23 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 88.0 MPa
- Elongation at Break: 4.0 - 6.0 %
$ 2513/MT
- Specific Gravity: 1.16 g/cc
- Density: 1.17 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Water Absorption at Saturation: 3.8 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm
$ 1449/MT
- Specific Gravity: 1.17 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0050 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 68.0 MPa
- Elongation at Break: 8.0 - 10 %
$ 1492/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 53.0 MPa
- Tensile Strength, Yield: 64.0 MPa
$ 1683/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1474/MT
- Density: 1.53 g/cc
- Density: 1.54 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm @Time 86400 sec
$ 2432/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1670/MT
- Density: 1.05 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 3.80 kg, Temperature 280 °C
$ 1503/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 - 0.012 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm @Treatment Temp. 130 °C, Time 3600 sec
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.011 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 117
$ 1631/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.06 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1937/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1636/MT
- Specific Gravity: 1.33 g/cc
- Density: 1.34 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
$ 1633/MT
- Specific Gravity: 1.10 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Melt Flow: 7.4 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2383/MT
- Specific Gravity: 1.20 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.80 %
- Water Absorption at Saturation: 4.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
$ 2038/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.014 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.011 - 0.014 cm/cm @Thickness 3.20 mm
- Melt Flow: 97 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 62.0 MPa
$ 1488/MT
- Specific Gravity: 1.21 g/cc
- Tensile Strength, Yield: 88.0 MPa
- Elongation at Break: 5.0 %
- Flexural Yield Strength: 125 MPa
- Flexural Modulus: 5.20 GPa
$ 1798/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.012 cm/cm @Thickness 3.20 mm
- Melt Flow: 39 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 179 MPa
$ 1567/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.030 %
- Water Absorption at Saturation: 0.040 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm
$ 1750/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.014 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 83 %
- Flexural Yield Strength: 95.0 MPa
$ 1577/MT
- Density: 1.24 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm
$ 1736/MT
- Specific Gravity: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 3.80 kg, Temperature 260 °C
- Tensile Strength at Break: 44.0 MPa
- Tensile Strength, Yield: 55.0 MPa
$ 1778/MT
- Specific Gravity: 1.12 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 39.3 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 70.0 MPa
$ 1528/MT
- Specific Gravity: 1.35 g/cc
- Density: 1.35 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
$ 1486/MT
- Specific Gravity: 1.26 g/cc
- Density: 1.26 g/cc
- Moisture Absorption: 0.500 %
- Water Absorption at Saturation: 1.27 %
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm @Thickness 3.20 mm
$ 1485/MT
- Specific Gravity: 1.12 g/cc
- Tensile Strength at Break: 68.0 MPa
- Elongation at Break: 5.0 %
- Flexural Yield Strength: 96.0 MPa
- Flexural Modulus: 3.64 GPa
$ 1614/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Water Absorption at Saturation: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 250 °C
$ 1936/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: 50 %
$ 1505/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.40 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
$ 1453/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 42.0 MPa
- Elongation at Break: 80 %
$ 2026/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.06 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.23 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 2442/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.09 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1468/MT
- Specific Gravity: 1.29 g/cc
- Density: 1.29 g/cc
- Moisture Absorption at Equilibrium: 0.14 %
- Moisture Absorption at Equilibrium: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Time 86400 sec
$ 1454/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1546/MT
- Specific Gravity: 1.01 g/cc
- Specific Gravity: 1.12 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 6.40 mm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm @Thickness 6.40 mm
$ 1925/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength at Break: 55.0 MPa
$ 1552/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 30 %
- Flexural Yield Strength: 93.0 MPa
$ 2223/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 73.0 MPa
- Tensile Strength, Yield: 86.0 MPa
- Elongation at Break: 15 %
$ 1536/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 20.2 g/10 min @Load 5.00 kg, Temperature 280 °C
- Melt Index of Compound: 20 g/10 min @Load 5.00 kg, Temperature 280 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 37.0 MPa
$ 2280/MT
- Specific Gravity: 1.40 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.00090 - 0.0015 cm/cm @Thickness 3.20 mm
$ 2559/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.20 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 46.0 MPa
- Elongation at Break: 70 %
$ 1762/MT
- Specific Gravity: 1.10 g/cc
- Melt Index of Compound: 10 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 55.0 MPa
- Tensile Strength at Break: 55.0 MPa
- Tensile Strength, Yield: 76.0 MPa
$ 1592/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.030 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 123
- Tensile Strength, Yield: 72.0 MPa
$ 1602/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 47.0 MPa
$ 1732/MT
- Specific Gravity: 1.62 g/cc
- Density: 1.62 g/cc
- Water Absorption at Saturation: 0.020 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 300 °C
$ 1733/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 118
$ 1582/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 63.0 MPa
$ 2574/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.06 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0075 cm/cm
$ 1614/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1630/MT
- Specific Gravity: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.014 - 0.017 cm/cm
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.012 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1532/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.06 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 2462/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 4.2 %
- Linear Mold Shrinkage, Flow: 0.014 - 0.017 cm/cm @Thickness 3.20 mm
$ 1474/MT
- Specific Gravity: 1.48 g/cc
- Water Absorption: 0.020 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 43.6 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 122 MPa
$ 1575/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 140 MPa
- Elongation at Break: 10 %
$ 1511/MT
- Specific Gravity: 0.920 g/cc
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 45.0 MPa @Thickness 6.35 mm
$ 2200/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 12.1 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 52.0 MPa
$ 1686/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 26 g/10 min @Load 2.16 kg, Temperature 280 °C
- Melt Flow: 67 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Break: 66 %
$ 2251/MT
- Melt Flow: 9.1 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 54.0 MPa
- Elongation at Break: 50 %
- Izod Impact, Notched: 1.67 J/cm
- CTE, linear: 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C
$ 1601/MT
- Specific Gravity: 1.26 g/cc
- Density: 1.26 g/cc
- Moisture Absorption: 0.500 %
- Water Absorption at Saturation: 4.0 %
- Linear Mold Shrinkage, Flow: 0.0026 - 0.0030 cm/cm @Thickness 3.20 mm
$ 1547/MT
- Specific Gravity: 1.33 g/cc
- Melt Flow: 8.5 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 93
- Tensile Strength at Break: 9.00 MPa
- Tensile Strength at Break: 9.00 MPa
$ 1674/MT
- Density: 1.25 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 10.0 kg, Temperature 280 °C
$ 1600/MT
- Density: 1.43 g/cc
- Density: 1.43 g/cc
- Moisture Absorption at Equilibrium: 0.080 %
- Moisture Absorption at Equilibrium: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0028 cm/cm @Time 86400 sec
$ 1530/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 12.0 MPa
- Tensile Strength at Break: 13.0 MPa
$ 2382/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 10.0 MPa
- Tensile Strength at Break: 10.0 MPa
$ 1861/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 10.0 MPa
- Tensile Strength at Break: 10.0 MPa
$ 1626/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 10.0 MPa
- Tensile Strength at Break: 10.0 MPa
$ 1844/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 10.0 MPa
- Tensile Strength at Break: 10.0 MPa
$ 2524/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 10.0 MPa
- Tensile Strength at Break: 10.0 MPa
$ 2178/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption at Equilibrium: 0.42 %
- Water Absorption at Saturation: 0.45 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1658/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 10.0 MPa
- Tensile Strength at Break: 10.0 MPa
$ 2018/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1845/MT
- Specific Gravity: 1.03 g/cc
- Water Absorption: 0.10 % @Time 173000 sec
- Melt Flow: 5.1 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore D: 56
- Tensile Strength at Break: 23.0 MPa
$ 1549/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 140 MPa
- Elongation at Break: 10 %
$ 1565/MT
- Specific Gravity: 1.16 g/cc
- Density: 1.17 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.22 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
$ 2480/MT
- Density: 1.18 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.14 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Melt Flow: 7.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1606/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.00050 - 0.0015 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0015 - 0.0030 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 122
- Tensile Strength at Break: 71.0 MPa
$ 2025/MT
- Specific Gravity: 1.44 g/cc
- Water Absorption: 0.020 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 29.1 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 112 MPa
$ 1652/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 29.3 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 82.0 MPa
$ 2191/MT
- Specific Gravity: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 49.0 MPa
- Tensile Strength, Yield: 66.0 MPa
$ 2002/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 0.120 %
- Moisture Absorption: 0.220 %
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm @Time 86400 sec
$ 1794/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.06 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0080 - 0.0090 cm/cm @Thickness 3.20 mm
$ 1784/MT
- Density: 1.32 g/cc
- Moisture Absorption: 1.09 %
- Water Absorption at Saturation: 3.1 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0080 - 0.010 cm/cm @Thickness 3.20 mm
$ 1506/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C
- Hardness, Rockwell R: 116
- Tensile Strength at Break: 61.0 MPa
$ 2090/MT
- Specific Gravity: 1.29 g/cc
- Density: 1.30 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
$ 1650/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.10 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
$ 1998/MT
- Bulk Density: 0.462 g/cc
- Particle Size: 190 µm
- Viscosity Measurement: 0.33
- Molecular Weight: 47600 g/mol
- Transformation Temperature, Tg: 214 °C
$ 2593/MT
- Density: 1.35 g/cc
- Density: 1.35 g/cc
- Moisture Absorption: 0.0500 %
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Time 86400 sec
$ 1904/MT
- Specific Gravity: 1.32 g/cc
- Density: 1.32 g/cc
- Moisture Absorption at Equilibrium: 0.070 %
- Moisture Absorption at Equilibrium: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 1965/MT
- Density: 1.30 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Melt Index of Compound: 7.0 g/10 min @Load 10.0 kg, Temperature 280 °C
$ 1818/MT
- Specific Gravity: 1.33 g/cc
- Tensile Strength at Break: 106 MPa
- Elongation at Break: 4.0 %
- Flexural Yield Strength: 141 MPa
- Flexural Modulus: 8.46 GPa
$ 1459/MT
- Specific Gravity: 1.00 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 43.6 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 32.0 MPa
$ 1691/MT
- Density: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0023 cm/cm
- Tensile Strength at Break: 102 MPa
- Elongation at Break: 1.6 %
- Tensile Modulus: 8.50 GPa
$ 1575/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0400 %
- Water Absorption at Saturation: 0.27 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1731/MT
- Specific Gravity: 1.12 g/cc
- Density: 1.12 g/cc
- Moisture Absorption: 0.500 %
- Water Absorption at Saturation: 4.0 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.015 cm/cm @Thickness 3.20 mm
$ 1807/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1993/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.107 g/cc
- Moisture Absorption: 0.500 %
- Moisture Absorption at Equilibrium: 1.0 %
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm
$ 1697/MT
- Specific Gravity: 1.23 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Water Absorption: 0.12 % @Time 86400 sec
- Moisture Absorption: 0.0400 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
$ 2314/MT
- Specific Gravity: 1.03 g/cc
- Water Absorption: 0.10 % @Time 173000 sec
- Melt Flow: 5.1 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore D: 56
- Tensile Strength at Break: 23.0 MPa
$ 1489/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
$ 2017/MT
- Specific Gravity: 1.33 g/cc
- Density: 1.328 g/cc
- Moisture Absorption: 0.500 %
- Moisture Absorption at Equilibrium: 1.0 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
$ 1565/MT
- Specific Gravity: 1.33 g/cc
- Density: 1.328 g/cc
- Moisture Absorption: 0.500 %
- Moisture Absorption at Equilibrium: 1.0 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
$ 2066/MT
- Density: 1.10 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.37 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 3.80 kg, Temperature 280 °C
$ 2005/MT
- Specific Gravity: 0.970 g/cc
- Density: 0.970 g/cc
- Moisture Absorption at Equilibrium: 0.020 %
- Water Absorption at Saturation: 0.060 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm @Thickness 3.20 mm
$ 1975/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.40 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 3.6 %
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm
- Linear Mold Shrinkage, Flow: 0.0090 - 0.012 cm/cm @Thickness 3.20 mm
$ 1764/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 37.0 MPa
- Elongation at Break: 72 %
$ 2412/MT
- Density: 1.13 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 6.0 g/10 min @Load 1.20 kg, Temperature 280 °C
$ 1804/MT
- Specific Gravity: 1.13 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.45 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
$ 1883/MT
- Specific Gravity: 1.16 g/cc
- Density: 1.17 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Water Absorption at Saturation: 3.8 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm
$ 2271/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.22 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
$ 1601/MT
- Density: 1.12 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.42 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 20 g/10 min @Load 3.80 kg, Temperature 280 °C
$ 1679/MT
- Bulk Density: 0.465 g/cc
- Particle Size: 200 µm
- Viscosity Measurement: 0.46
- Molecular Weight: 68600 g/mol
- Transformation Temperature, Tg: 217 °C
$ 1546/MT
- Specific Gravity: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption at Equilibrium: 0.80 %
- Water Absorption at Saturation: 3.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 - 0.013 cm/cm @Thickness 3.20 mm
$ 1805/MT
- Bulk Density: 0.00100 g/cc
- Viscosity: 73400 cP
- Viscosity Measurement: 0.12
- Molecular Weight: 6300 g/mol
- Transformation Temperature, Tg: 165 °C
$ 2057/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 17.7 g/10 min @Load 2.16 kg, Temperature 300 °C
- Hardness, Rockwell M: 88
$ 1960/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption at Equilibrium: 0.10 %
- Water Absorption at Saturation: 1.1 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm
$ 2414/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 66.0 MPa
- Elongation at Break: 15 %
$ 1506/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.0094 - 0.0096 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0091 - 0.0093 cm/cm @Time 86400 sec
- Melt Index of Compound: 38 g/10 min @Load 10.0 kg, Temperature 280 °C
- Hardness, Rockwell R: 115
$ 1935/MT
- Density: 1.27 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm
- Tensile Strength at Break: 80.0 MPa
- Elongation at Break: 1.6 %
- Tensile Modulus: 6.60 GPa
$ 1911/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.0090 cm/cm @Time 86400 sec
- Tensile Strength at Break: 42.0 MPa
- Elongation at Break: 21.3 %
- Tensile Modulus: 2.35 GPa
$ 1759/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 28 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 63.0 MPa
$ 1476/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 0.0900 %
- Water Absorption at Saturation: 0.11 %
- Linear Mold Shrinkage, Flow: 0.0034 - 0.0052 cm/cm @Thickness 3.20 mm
$ 1725/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 7.5 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 87
- Tensile Strength at Break: 19.0 MPa
- Tensile Strength at Break: 20.0 MPa
$ 1720/MT
- Density: 1.15 g/cc
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0083 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0087 cm/cm @Time 86400 sec
$ 1496/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 68.0 MPa
- Elongation at Break: 25 %
$ 2427/MT
- Specific Gravity: 1.14 g/cc
- Density: 1.14 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.18 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1584/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 11 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 79
- Tensile Strength at Break: 14.0 MPa
- Tensile Strength at Break: 14.0 MPa
$ 1708/MT
- Specific Gravity: 1.02 g/cc
- Viscosity: 160 cP
- Viscosity: 298 cP
- Viscosity Measurement: 0.090
- Transformation Temperature, Tg: 140 °C
$ 1668/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 12.0 MPa
- Tensile Strength at Break: 13.0 MPa
$ 1531/MT
- Density: 1.11 g/cc
- Viscosity: 95000 cP
- Melt Index of Compound: 12 g/10 min @Load 1.20 kg, Temperature 280 °C
- Melt Index of Compound: 22 g/10 min @Load 2.16 kg, Temperature 280 °C
- Tensile Strength at Break: 49.0 MPa
$ 1476/MT
- Specific Gravity: 0.900 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm
- Melt Index of Compound: 6.0 g/10 min @Load 2.16 kg, Temperature 280 °C
- Tensile Strength at Break: 40.0 MPa
- Tensile Strength, Yield: 45.0 MPa
$ 1574/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1691/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.107 g/cc
- Moisture Absorption: 0.500 %
- Moisture Absorption at Equilibrium: 1.0 %
- Linear Mold Shrinkage, Flow: 0.016 - 0.018 cm/cm
$ 2508/MT
- Specific Gravity: 1.21 g/cc
- Density: 1.21 g/cc
- Moisture Absorption: 0.500 %
- Water Absorption at Saturation: 3.8 %
- Linear Mold Shrinkage, Flow: 0.0088 - 0.0094 cm/cm @Thickness 3.20 mm
$ 2125/MT
- Water Absorption at Saturation: 0.060 %
- Viscosity: 110000 cP
- Melt Index of Compound: 24 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 37.0 MPa
- Tensile Strength at Break: 38.0 MPa
$ 2056/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.013 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 53 %
$ 2587/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.012 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 68.0 MPa
- Elongation at Break: 40 %
$ 1800/MT
- Density: 1.05 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.22 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1776/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.07 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm
$ 1453/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
$ 2161/MT
- Specific Gravity: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
$ 2125/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.10 % @Time 173000 sec
- Linear Mold Shrinkage, Flow: 0.0048 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0109 cm/cm @Time 86400 sec
- Melt Flow: 31 g/10 min @Load 5.00 kg, Temperature 210 °C
$ 1698/MT
- Specific Gravity: 1.03 g/cc
- Density: 1.03 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.12 %
- Melt Flow: 13.8 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2043/MT
- Density: 1.37 g/cc
- Density: 1.42 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0036 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0070 cm/cm @Time 86400 sec
$ 1449/MT
- Specific Gravity: 1.29 g/cc
- Density: 1.29 g/cc
- Moisture Absorption at Equilibrium: 0.020 %
- Water Absorption at Saturation: 0.020 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
$ 1581/MT
- Density: 1.25 g/cc
- Moisture Absorption: 1.08 %
- Water Absorption at Saturation: 3.2 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm
- Melt Index of Compound: 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1557/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 2108/MT
- Specific Gravity: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 - 0.010 cm/cm @Thickness 3.20 mm
- Melt Flow: 31 g/10 min @Load 5.00 kg, Temperature 300 °C
- Hardness, Rockwell R: 123
- Tensile Strength at Break: 57.0 MPa
$ 1801/MT
- Specific Gravity: 1.35 g/cc
- Moisture Absorption at Equilibrium: 0.00 %
- Water Absorption at Saturation: 0.00 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 27 g/10 min @Load 2.16 kg, Temperature 300 °C
$ 1512/MT
- Specific Gravity: 1.02 g/cc
- Specific Gravity: 1.28 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 48.0 MPa @Thickness 6.35 mm
$ 1971/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.22 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
$ 1995/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 1.10 %
- Water Absorption at Saturation: 3.2 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm @Thickness 3.20 mm
$ 1667/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 88
- Tensile Strength at Break: 12.0 MPa
- Tensile Strength at Break: 13.0 MPa
$ 1873/MT
- Specific Gravity: 1.13 g/cc
- Density: 1.13 g/cc
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Melt Index of Compound: 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C
- Melt Index of Compound: 20 g/10 min @Load 5.00 kg, Temperature 300 °C
$ 1645/MT
- Density: 0.990 g/cc
- Melt Index of Compound: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
- Hardness, Rockwell R: 70
- Tensile Strength at Break: 34.0 MPa
- Tensile Strength, Yield: 36.0 MPa
$ 1444/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell M: 89
- Tensile Strength, Yield: 98.0 MPa
$ 1504/MT
- Specific Gravity: 1.05 g/cc
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 77
- Tensile Strength at Break: 16.0 MPa
- Tensile Strength at Break: 17.0 MPa
$ 2221/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.20 g/cc
- Moisture Absorption: 1.10 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm @Thickness 3.20 mm
$ 1446/MT
- Specific Gravity: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Hardness, Rockwell R: 117
- Tensile Strength at Break: 41.0 MPa
$ 1622/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 1.2 %
- Water Absorption at Saturation: 4.2 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.012 - 0.016 cm/cm @Thickness 3.20 mm
$ 2179/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
$ 2236/MT
- Specific Gravity: 1.16 g/cc
- Density: 1.162 g/cc
- Moisture Absorption: 0.500 %
- Moisture Absorption at Equilibrium: 1.0 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1774/MT
- Specific Gravity: 1.30 g/cc
- Density: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption at Equilibrium: 0.10 %
- Moisture Absorption at Equilibrium: 0.070 % @Time 86400 sec
$ 1938/MT
- Density: 1.41 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.015 cm/cm
- Tensile Strength at Break: 111 MPa
- Elongation at Break: 0.70 %
- Flexural Strength: 133 MPa
$ 1658/MT
- Specific Gravity: 1.19 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2260/MT
- Density: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.011 - 0.013 cm/cm
- Melt Index of Compound: 10 g/10 min @Load 5.00 kg, Temperature 280 °C
- Hardness, H358/30: 125 MPa
- Tensile Strength at Break: 65.0 MPa
$ 1865/MT
- Density: 1.05 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 3.80 kg, Temperature 280 °C
$ 1638/MT
- Specific Gravity: 1.35 g/cc
- Density: 1.35 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
$ 1686/MT
- Specific Gravity: 1.19 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2511/MT
- Specific Gravity: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 28 g/10 min @Load 3.80 kg, Temperature 260 °C
- Tensile Strength at Break: 44.0 MPa
- Tensile Strength, Yield: 55.0 MPa
$ 1719/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 2565/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 118
- Tensile Strength, Yield: 56.0 MPa
$ 1591/MT
- Specific Gravity: 1.17 g/cc
- Density: 1.17 g/cc
- Moisture Absorption: 0.0400 %
- Water Absorption at Saturation: 0.12 %
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0066 cm/cm @Thickness 3.20 mm
$ 1927/MT
- Density: 1.06 g/cc
- Tensile Strength, Yield: 65.0 MPa
- Elongation at Break: 4.5 %
- Tensile Modulus: 2.85 GPa
- Flexural Yield Strength: 105 MPa
$ 1568/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.900 %
- Water Absorption at Saturation: 3.0 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm @Thickness 3.20 mm
$ 1580/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength, Yield: 79.0 MPa
$ 1725/MT
- Specific Gravity: 1.16 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.22 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell L: 104
$ 2008/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength, Yield: 81.0 MPa
- Elongation at Break: 1.3 %
- Flexural Yield Strength: 120 MPa
$ 1567/MT
- Specific Gravity: 1.03 g/cc
- Water Absorption: 0.10 % @Time 173000 sec
- Melt Flow: 5.1 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore D: 56
- Tensile Strength at Break: 23.0 MPa
$ 1479/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm @Thickness 3.20 mm
- Melt Flow: 10.6 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 32.0 MPa
- Tensile Strength, Yield: 35.0 MPa
$ 1863/MT
- Specific Gravity: 1.09 - 1.17 g/cc
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 82
- Tensile Strength at Break: 13.0 MPa
- Tensile Strength at Break: 15.0 MPa
$ 1567/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.54 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 4.4 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.017 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 59.0 MPa
$ 1880/MT
- Specific Gravity: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength at Break: 106 MPa
$ 1643/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0200 %
- Water Absorption at Saturation: 0.13 %
- Viscosity: 66000 cP
$ 1724/MT
- Specific Gravity: 1.03 g/cc
- Melt Flow: 16 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 87
- Tensile Strength at Break: 16.0 MPa
- Tensile Strength at Break: 16.0 MPa
$ 1671/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength at Break: 46.0 MPa
- Tensile Strength, Yield: 57.0 MPa
$ 1723/MT
- Density: 1.24 g/cc
- Moisture Absorption: 1.00 %
- Water Absorption at Saturation: 2.5 %
- Melt Index of Compound: 4.0 g/10 min @Load 10.0 kg, Temperature 280 °C
- Tensile Strength at Break: 125 MPa
$ 1488/MT
- Density: 1.04 g/cc
- Density: 1.04 g/cc
- Moisture Absorption: 0.0600 %
- Moisture Absorption: 0.0700 %
- Linear Mold Shrinkage, Flow: 0.0089 cm/cm @Time 86400 sec
$ 1449/MT
- Specific Gravity: 1.31 g/cc
- Moisture Absorption: 0.0400 %
- Water Absorption at Saturation: 0.10 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.2 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1998/MT
- Specific Gravity: 1.14 g/cc
- Density: 1.14 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.18 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1809/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.18 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 2500/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: 44 %
- Flexural Yield Strength: 89.0 MPa
$ 2584/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1544/MT
- Density: 1.30 g/cc
- Melt Index of Compound: 3.0 g/10 min @Load 5.00 kg, Temperature 260 °C
- Hardness, H358/30: 100 MPa
- Tensile Strength at Break: 100 MPa
- Elongation at Break: 2.2 %
$ 1592/MT
- Density: 1.30 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
$ 1559/MT
- Specific Gravity: 1.02 g/cc
- Viscosity: 160 cP
- Viscosity: 298 cP
- Viscosity Measurement: 0.090
- Transformation Temperature, Tg: 160 °C
$ 2081/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.080 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 280 °C
- Melt Index of Compound: 23 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1557/MT
- Density: 1.95 g/cc
- Density: 1.95 g/cc
- Moisture Absorption: 0.100 %
- Linear Mold Shrinkage, Flow: 0.0064 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0056 cm/cm @Time 86400 sec
$ 1827/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0400 %
- Water Absorption at Saturation: 0.27 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1971/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 88
- Tensile Strength at Break: 12.0 MPa
- Tensile Strength at Break: 13.0 MPa
$ 1485/MT
- Density: 1.42 g/cc
- Density: 1.42 g/cc
- Moisture Absorption: 0.0800 %
- Moisture Absorption: 0.100 %
- Linear Mold Shrinkage, Flow: 0.0045 cm/cm @Time 86400 sec
$ 1510/MT
- Specific Gravity: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption at Equilibrium: 0.80 %
- Water Absorption at Saturation: 3.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 - 0.013 cm/cm @Thickness 3.20 mm
$ 1458/MT
- Density: 1.11 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 7.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1482/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 42.0 MPa
- Flexural Strength: 59.0 MPa
- Flexural Modulus: 2.24 GPa
$ 1995/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength, Yield: 44.0 MPa
$ 1833/MT
- Bulk Density: 0.00100 g/cc
- Viscosity: 73400 cP
- Viscosity Measurement: 0.12
- Molecular Weight: 6300 g/mol
- Transformation Temperature, Tg: 165 °C
$ 1706/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 66.0 MPa
$ 1584/MT
- Specific Gravity: 1.12 g/cc
- Density: 1.11 g/cc
- Water Absorption at Saturation: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 2.16 kg, Temperature 280 °C
$ 1601/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1539/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 0.0200 %
- Water Absorption at Saturation: 0.13 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1804/MT
- Specific Gravity: 1.35 g/cc
- Density: 1.35 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
$ 1706/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Index of Compound: 6.0 g/10 min @Load 2.16 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 1723/MT
- Specific Gravity: 1.38 g/cc
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 116 MPa
- Elongation at Yield: 7.0 %
- Flexural Yield Strength: 160 MPa
$ 1521/MT
- Density: 1.10 g/cc
- Moisture Absorption: 1.34 %
- Water Absorption at Saturation: 4.2 %
- Linear Mold Shrinkage, Flow: 0.016 - 0.020 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 1.20 kg, Temperature 280 °C
$ 1551/MT
- Density: 1.06 g/cc
- Moisture Absorption at Equilibrium: 0.070 %
- Water Absorption at Saturation: 0.25 % @Temperature 23.0 °C
- Melt Flow: 9.0 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 45.0 MPa
$ 2171/MT
- Density: 1.11 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.15 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 14 g/10 min @Load 1.20 kg, Temperature 280 °C
$ 1502/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
$ 1899/MT
- Specific Gravity: 1.26 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 37.7 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 98.0 MPa
$ 1822/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.09 g/cc
- Moisture Absorption: 1.21 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.016 - 0.020 cm/cm
$ 2482/MT
- Density: 1.21 g/cc
- Water Absorption: 0.15 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm
- Tensile Strength at Break: 97.0 MPa
- Elongation at Break: 2.0 %
$ 1497/MT
- Density: 1.19 g/cc
- Moisture Absorption at Equilibrium: 0.15 %
- Viscosity: 200000 cP @Temperature 282 °C
- Linear Mold Shrinkage, Flow: 0.022 - 0.026 cm/cm
- Melt Flow: 25 g/10 min @Load 10.0 kg, Temperature 280 °C
$ 2215/MT
- Density: 1.53 g/cc
- Density: 1.54 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm @Time 86400 sec
$ 2466/MT
- Bulk Density: 0.00100 g/cc
- Particle Size: <= 63 µm
- Particle Size: <= 125 µm
- Particle Size: <= 425 µm
- Particle Size: <= 710 µm
$ 2009/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.20 g/cc
- Moisture Absorption: 1.10 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm @Thickness 3.20 mm
$ 1866/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.40 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 3.6 %
- Linear Mold Shrinkage, Flow: 0.011 - 0.015 cm/cm
- Linear Mold Shrinkage, Flow: 0.0090 - 0.012 cm/cm @Thickness 3.20 mm
$ 2188/MT
- Specific Gravity: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
- Melt Flow: 36.5 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 94.0 MPa
$ 2059/MT
- Specific Gravity: 1.37 g/cc
- Density: 1.37 g/cc
- Moisture Absorption at Equilibrium: 1.2 %
- Water Absorption at Saturation: 4.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0023 - 0.0028 cm/cm @Thickness 3.20 mm
$ 2010/MT
- Density: 1.06 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.14 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 10 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1730/MT
- Specific Gravity: 1.19 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2230/MT
- Specific Gravity: 1.48 g/cc
- Water Absorption: 0.020 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 122 MPa
- Elongation at Break: 10 %
$ 1810/MT
- Density: 1.10 g/cc
- Moisture Absorption: 1.10 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.012 - 0.016 cm/cm
- Melt Index of Compound: 12 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1638/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.6 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength at Break: 86.0 MPa
$ 1573/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.900 %
- Water Absorption at Saturation: 3.0 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm @Thickness 3.20 mm
$ 1577/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 17 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 63.0 MPa
$ 1945/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 114
- Tensile Strength, Yield: 53.0 MPa
$ 1561/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.10 % @Time 173000 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0040 cm/cm @Time 86400 sec
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 250 °C
$ 2369/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0080 - 0.011 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 43.0 MPa
- Elongation at Break: 150 %
$ 2373/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Break: 100 %
$ 1778/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0024 cm/cm
- Tensile Strength at Break: 91.0 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 6.40 GPa
$ 1637/MT
- Specific Gravity: 1.23 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 11.1 g/10 min @Load 5.00 kg, Temperature 300 °C
- Hardness, Rockwell R: 124
$ 1697/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.06 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1454/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.22 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
$ 1739/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1955/MT
- Density: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.200 %
- Linear Mold Shrinkage, Flow: 0.0093 - 0.0124 cm/cm @Time 86400 sec
- Tensile Strength at Break: 56.0 MPa
$ 1973/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 13.2 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 47.0 MPa
$ 1463/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: 50 %
- Flexural Yield Strength: 75.0 MPa
$ 1469/MT
- Specific Gravity: 1.22 g/cc
- Density: 1.22 g/cc
- Moisture Absorption: 0.0200 %
- Water Absorption at Saturation: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.20 mm
$ 2192/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.10 % @Time 173000 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0040 cm/cm @Time 86400 sec
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 250 °C
$ 2120/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 20.8 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 49.0 MPa
$ 1902/MT
- Density: 2.07 g/cc
- Tensile Strength, Yield: 55.0 MPa
- Elongation at Break: 4.4 %
- Tensile Modulus: 3.40 GPa
- Flexural Yield Strength: 105 MPa
$ 1487/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 35 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength, Yield: 34.0 MPa
$ 1859/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 35 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength, Yield: 34.0 MPa
$ 2352/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 35 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength, Yield: 34.0 MPa
$ 1532/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.066 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 117
- Tensile Strength at Break: 49.0 MPa
$ 2055/MT
- Specific Gravity: 1.40 g/cc
- Density: 1.40 g/cc
- Water Absorption at Saturation: 0.20 %
- Melt Index of Compound: 20 g/10 min @Load 10.0 kg, Temperature 300 °C
- Tensile Strength at Break: 155 MPa
$ 1471/MT
- Specific Gravity: 1.52 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 68.1 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength, Yield: 114 MPa
$ 1765/MT
- Specific Gravity: 1.03 g/cc
- Melt Flow: 16 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 87
- Tensile Strength at Break: 16.0 MPa
- Tensile Strength at Break: 16.0 MPa
$ 2353/MT
- Specific Gravity: 1.08 g/cc
- Melt Flow: 23 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 84
- Tensile Strength at Break: 17.0 MPa
- Tensile Strength at Break: 18.0 MPa
$ 1990/MT
- Specific Gravity: 1.59 g/cc
- Water Absorption: 0.010 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 46.6 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 127 MPa
$ 1894/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 108 MPa
- Elongation at Break: 1.6 %
- Tensile Modulus: 9.87 GPa
$ 2550/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 2497/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.40 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
$ 1468/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Water Absorption at Saturation: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 250 °C
$ 2048/MT
- Density: 1.29 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0035 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0045 cm/cm @Time 86400 sec
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 1.8 %
$ 1714/MT
- Specific Gravity: 1.03 g/cc
- Melt Flow: 33 g/10 min @Load 5.00 kg, Temperature 280 °C
- Hardness, Shore D: 63
- Tensile Strength at Break: 25.0 MPa
- Tensile Strength at Break: 28.0 MPa
$ 1727/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 3.20 mm
- Melt Flow: 16 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1465/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.09 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.015 - 0.019 cm/cm
$ 2390/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 4.2 %
- Linear Mold Shrinkage, Flow: 0.012 - 0.016 cm/cm @Thickness 3.20 mm
$ 1757/MT
- Specific Gravity: 1.03 g/cc
- Melt Flow: 16 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 87
- Tensile Strength at Break: 16.0 MPa
- Tensile Strength at Break: 16.0 MPa
$ 2218/MT
- Density: 1.10 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.14 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 8.0 g/10 min @Load 1.20 kg, Temperature 280 °C
$ 2066/MT
- Specific Gravity: 1.08 g/cc
- Melt Flow: 23 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 84
- Tensile Strength at Break: 17.0 MPa
- Tensile Strength at Break: 18.0 MPa
$ 2364/MT
- Specific Gravity: 1.23 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0035 cm/cm @Thickness 3.20 mm
- Melt Flow: 22.1 g/10 min @Load 2.16 kg, Temperature 300 °C
- Tensile Strength, Yield: 98.0 MPa
$ 1641/MT
- Specific Gravity: 1.08 g/cc
- Moisture Absorption at Equilibrium: 1.19 %
- Moisture Absorption at Equilibrium: 3.5 %
- Linear Mold Shrinkage, Flow: 0.015 cm/cm
- Linear Mold Shrinkage, Transverse: 0.013 cm/cm
$ 1466/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 44.0 MPa
$ 2362/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 53.0 MPa
- Elongation at Break: 50 %
$ 1691/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1998/MT
- Density: 1.06 g/cc
- Moisture Absorption: 0.0300 %
- Water Absorption at Saturation: 0.14 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 9.0 g/10 min @Load 3.80 kg, Temperature 280 °C
$ 1704/MT
- Bulk Density: 0.476 g/cc
- Particle Size: 200 µm
- Viscosity Measurement: 0.40
- Molecular Weight: 56200 g/mol
- Transformation Temperature, Tg: 216 °C
$ 1717/MT
- Specific Gravity: 1.29 g/cc
- Density: 1.30 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
$ 2199/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.09 g/cc
- Moisture Absorption: 0.520 %
- Water Absorption at Saturation: 1.01 %
- Linear Mold Shrinkage, Flow: 0.0113 - 0.0126 cm/cm @Thickness 3.20 mm
$ 1461/MT
- Density: 1.10 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 7.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1577/MT
- Specific Gravity: 1.26 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 19.8 g/10 min @Load 5.00 kg, Temperature 300 °C
- Hardness, Rockwell R: 127
$ 1692/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 2236/MT
- Density: 1.07 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm
- Melt Index of Compound: 13 g/10 min @Load 1.20 kg, Temperature 280 °C
$ 2177/MT
- Specific Gravity: 1.12 g/cc
- Density: 1.12 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.18 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1514/MT
- Specific Gravity: 1.06 g/cc
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 87
- Tensile Strength at Break: 18.0 MPa
- Tensile Strength at Break: 18.0 MPa
$ 2389/MT
- Specific Gravity: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0045 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 74.0 MPa
- Tensile Strength, Yield: 74.0 MPa
$ 1455/MT
- Specific Gravity: 1.37 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 15.5 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 126 MPa
$ 2305/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 19.9 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength, Yield: 45.0 MPa
$ 1777/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 33 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 115
$ 1801/MT
- Specific Gravity: 1.02 g/cc
- Melt Flow: 3.2 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 82
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength at Break: 16.0 MPa
$ 1463/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Hardness, Rockwell R: 113
- Tensile Strength, Yield: 42.0 MPa
- Elongation at Break: 50 %
$ 1518/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 4.2 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm @Thickness 3.20 mm
$ 1832/MT
- Specific Gravity: 1.01 g/cc
- Melt Flow: 16 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 16.0 MPa
- Tensile Strength at Break: 16.0 MPa
$ 1546/MT
- Specific Gravity: 1.11 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength at Break: 55.0 MPa
$ 1488/MT
- Specific Gravity: 1.13 g/cc
- Density: 1.13 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
$ 1932/MT
- Density: 1.08 g/cc
- Tensile Strength, Yield: 86.0 MPa
- Elongation at Break: 6.0 %
- Tensile Modulus: 3.10 GPa
- Flexural Yield Strength: 130 MPa
$ 1731/MT
- Specific Gravity: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.5 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 37.0 MPa
$ 1552/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.6 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 44.0 MPa
$ 1463/MT
- Specific Gravity: 1.21 g/cc
- Density: 1.21 g/cc
- Moisture Absorption: 0.500 %
- Water Absorption at Saturation: 3.8 %
- Linear Mold Shrinkage, Flow: 0.0088 - 0.0094 cm/cm @Thickness 3.20 mm
$ 1580/MT
- Specific Gravity: 1.24 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 6.40 mm
- Melt Flow: 6.9 g/10 min @Load 5.00 kg, Temperature 300 °C
$ 1473/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 50.0 MPa
- Elongation at Break: 41 %
- Flexural Yield Strength: 55.0 MPa
$ 1536/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 35 %
$ 2580/MT
- Specific Gravity: 1.16 g/cc
- Density: 1.162 g/cc
- Moisture Absorption: 0.500 %
- Moisture Absorption at Equilibrium: 1.0 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1494/MT
- Specific Gravity: 1.19 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1675/MT
- Density: 1.20 g/cc
- Tensile Strength at Break: 55.0 MPa
- Elongation at Break: 3.2 %
- Tensile Modulus: 3.65 GPa
- Flexural Strength: 103 MPa
$ 2026/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 16.6 g/10 min @Load 5.00 kg, Temperature 300 °C
- Melt Index of Compound: 16 g/10 min @Load 5.00 kg, Temperature 300 °C
$ 2014/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.09 g/cc
- Moisture Absorption at Equilibrium: 0.30 %
- Water Absorption at Saturation: 0.55 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0113 - 0.0126 cm/cm @Thickness 3.20 mm
$ 2262/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.066 % @Time 86400 sec
- Tensile Strength, Yield: 51.0 MPa
- Elongation at Break: 25 %
- Flexural Yield Strength: 75.0 MPa
$ 2216/MT
- Density: 1.10 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1476/MT
- Density: 1.04 g/cc
- Density: 1.04 g/cc
- Moisture Absorption at Equilibrium: 0.070 %
- Moisture Absorption at Equilibrium: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0089 cm/cm @Time 86400 sec
$ 1640/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1699/MT
- Density: 1.06 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.21 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1672/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1585/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 4.2 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm @Thickness 3.20 mm
$ 1584/MT
- Density: 1.17 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2018/MT
- Density: 1.22 g/cc
- Density: 1.22 g/cc
- Moisture Absorption: 0.0900 %
- Moisture Absorption: 0.0900 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 2231/MT
- Density: 1.07 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Tensile Strength, Yield: 86.0 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 3.35 GPa
$ 1526/MT
- Specific Gravity: 1.12 g/cc
- Density: 1.12 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.18 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1857/MT
- Specific Gravity: 1.24 g/cc
- Water Absorption: 0.12 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 63.0 MPa
$ 1900/MT
- Specific Gravity: 1.02 g/cc
- Viscosity: 160 cP
- Viscosity: 298 cP
- Viscosity Measurement: 0.090
- Transformation Temperature, Tg: 140 °C
$ 1976/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
$ 1525/MT
- Specific Gravity: 1.34 g/cc
- Density: 1.34 g/cc
- Moisture Absorption: 0.800 %
- Water Absorption at Saturation: 3.0 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm @Thickness 3.20 mm
$ 1666/MT
- Specific Gravity: 1.16 g/cc
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 88
- Tensile Strength at Break: 12.0 MPa
- Tensile Strength at Break: 13.0 MPa
$ 1542/MT
- Density: 1.17 g/cc
- Tensile Strength, Yield: 34.0 MPa
- Elongation at Yield: 2.3 %
- Tensile Modulus: 2.30 GPa
- Flexural Yield Strength: 64.0 MPa
$ 1508/MT
- Specific Gravity: 1.28 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.0015 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0015 - 0.0030 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
$ 1692/MT
- Specific Gravity: 1.37 g/cc
- Density: 1.37 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 4.0 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
$ 2411/MT
- Specific Gravity: 1.20 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 12.8 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength at Break: 108 MPa
$ 2122/MT
- Specific Gravity: 1.31 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.3 g/10 min @Load 5.00 kg, Temperature 300 °C
- Hardness, Rockwell R: 121
$ 1652/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 10.0 MPa
- Tensile Strength at Break: 10.0 MPa
$ 1749/MT
- Specific Gravity: 1.23 g/cc
- Water Absorption: 0.11 % @Time 86400 sec
- Moisture Absorption: 0.0400 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.5 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1939/MT
- Specific Gravity: 0.990 g/cc
- Density: 0.990 g/cc
- Moisture Absorption: 0.0200 %
- Water Absorption at Saturation: 0.050 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 2081/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 1.10 %
- Water Absorption at Saturation: 3.2 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm @Thickness 3.20 mm
$ 1823/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.09 g/cc
- Moisture Absorption: 1.21 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.016 - 0.020 cm/cm
$ 1933/MT
- Specific Gravity: 1.22 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.1 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 88.0 MPa
$ 1460/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 24.2 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength, Yield: 157 MPa
$ 1621/MT
- Specific Gravity: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.3 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 48.0 MPa
- Tensile Strength, Yield: 55.0 MPa
$ 1689/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength, Yield: 48.0 MPa
- Elongation at Break: 35 %
$ 1705/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 0.0200 %
- Water Absorption at Saturation: 0.13 %
- Melt Flow: 42 g/10 min @Load 3.80 kg, Temperature 200 °C
$ 2106/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.3 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 41.0 MPa
$ 1499/MT
- Specific Gravity: 1.18 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.6 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength at Break: 86.0 MPa
$ 1943/MT
- Specific Gravity: 1.18 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 15.3 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 77.0 MPa
$ 2211/MT
- Specific Gravity: 1.33 g/cc
- Density: 1.34 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
$ 2392/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.13 % @Time 86400 sec
- Moisture Absorption: 0.0400 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1450/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Moisture Absorption: 0.0400 %
- Water Absorption at Saturation: 0.27 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 2098/MT
- Specific Gravity: 1.35 g/cc
- Density: 1.35 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
$ 1485/MT
- Specific Gravity: 1.33 g/cc
- Density: 1.328 g/cc
- Moisture Absorption: 0.500 %
- Moisture Absorption at Equilibrium: 1.0 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
$ 1814/MT
- Specific Gravity: 1.13 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.45 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
$ 1586/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.07 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm
$ 2211/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.06 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.23 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1493/MT
- Density: 1.14 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 25 g/10 min @Load 1.20 kg, Temperature 280 °C
- Hardness, H358/30: 100 MPa
- Tensile Strength at Break: 35.0 MPa
$ 1783/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.10 % @Time 173000 sec
- Linear Mold Shrinkage, Flow: 0.0108 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.011 cm/cm @Time 86400 sec
- Melt Flow: 14.5 g/10 min @Load 5.00 kg, Temperature 210 °C
$ 1502/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 20.2 g/10 min @Load 5.00 kg, Temperature 280 °C
- Melt Index of Compound: 20 g/10 min @Load 5.00 kg, Temperature 280 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 37.0 MPa
$ 1616/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
$ 1477/MT
- Density: 1.13 g/cc
- Moisture Absorption: 0.0100 %
- Water Absorption at Saturation: 0.090 %
- Melt Index of Compound: 10 g/10 min @Load 1.20 kg, Temperature 280 °C
- Tensile Strength at Break: 41.0 MPa
$ 1481/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.013 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 53 %
$ 1628/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0030 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 108 MPa
- Elongation at Break: 7.0 %
$ 1447/MT
- Specific Gravity: 1.62 g/cc
- Density: 1.62 g/cc
- Water Absorption at Saturation: 0.020 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 16 g/10 min @Load 2.16 kg, Temperature 300 °C
$ 1574/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 68.0 MPa
- Elongation at Break: 25 %
$ 1595/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Water Absorption at Saturation: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 250 °C
$ 1533/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 44.0 MPa
- Elongation at Break: 40 %
$ 1483/MT
- Specific Gravity: 1.31 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0040 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell L: 108
- Tensile Strength at Break: 120 MPa
$ 1576/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 44.0 MPa
- Elongation at Break: 40 %
$ 1525/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 44.0 MPa
- Elongation at Break: 40 %
$ 2515/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 44.0 MPa
- Elongation at Break: 40 %
$ 2084/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0400 %
- Water Absorption at Saturation: 0.27 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1833/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.4 g/10 min @Load 5.00 kg, Temperature 280 °C
- Melt Index of Compound: 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1501/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.08 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Viscosity: 278000 cP
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1916/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1625/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 119
- Tensile Strength, Yield: 66.0 MPa
$ 1453/MT
- Specific Gravity: 1.13 g/cc
- Density: 1.13 g/cc
- Melt Flow: 4.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Melt Index of Compound: 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C
- Melt Index of Compound: 20 g/10 min @Load 5.00 kg, Temperature 300 °C
$ 1577/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.09 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 2536/MT
- Specific Gravity: 1.15 g/cc
- Density: 1.15 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1931/MT
- Specific Gravity: 1.20 g/cc
- Density: 1.19 g/cc
- Moisture Absorption at Equilibrium: 0.050 %
- Water Absorption at Saturation: 0.25 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
$ 1524/MT
- Specific Gravity: 1.29 g/cc
- Density: 1.29 g/cc
- Moisture Absorption at Equilibrium: 0.020 %
- Water Absorption at Saturation: 0.020 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
$ 1765/MT
- Specific Gravity: 1.62 g/cc
- Density: 1.62 g/cc
- Moisture Absorption at Equilibrium: 0.00 %
- Water Absorption at Saturation: 0.020 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0080 cm/cm @Thickness 3.20 mm
$ 2271/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 0.0400 %
- Water Absorption at Saturation: 0.24 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1923/MT
- Bulk Density: 0.476 g/cc
- Particle Size: 200 µm
- Viscosity Measurement: 0.40
- Molecular Weight: 56200 g/mol
- Transformation Temperature, Tg: 216 °C
$ 2036/MT
- Bulk Density: 0.465 g/cc
- Particle Size: 200 µm
- Viscosity Measurement: 0.46
- Molecular Weight: 68600 g/mol
- Transformation Temperature, Tg: 217 °C
$ 2026/MT
- Specific Gravity: 1.35 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 22.9 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength at Break: 98.0 MPa
$ 1881/MT
- Specific Gravity: 1.53 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm
- Melt Flow: 13.3 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 129 MPa
$ 2011/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.09 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 4.2 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm @Thickness 3.20 mm
$ 2153/MT
- Specific Gravity: 1.28 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 19.6 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 108 MPa
$ 1887/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 35.0 MPa
$ 1677/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength at Break: 56.0 MPa
- Elongation at Break: 20 %
$ 1463/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 2052/MT
- Bulk Density: 0.00100 g/cc
- Particle Size: <= 63 µm
- Particle Size: <= 125 µm
- Particle Size: <= 425 µm
- Particle Size: <= 710 µm
$ 1795/MT
- Bulk Density: 0.00100 g/cc
- Viscosity: 73400 cP
- Viscosity Measurement: 0.12
- Molecular Weight: 6300 g/mol
- Transformation Temperature, Tg: 165 °C
$ 1828/MT
- Bulk Density: 0.00100 g/cc
- Particle Size: <= 63 µm
- Particle Size: <= 125 µm
- Particle Size: <= 425 µm
- Particle Size: <= 710 µm
$ 1557/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.09 g/cc
- Moisture Absorption: 1.21 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.016 - 0.020 cm/cm
$ 1679/MT
- Specific Gravity: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength at Break: 106 MPa
$ 1611/MT
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0050 cm/cm @Time 86400 sec
- Tensile Strength at Break: 86.0 MPa
- Elongation at Break: 1.8 %
$ 1681/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.06 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1970/MT
- Density: 1.14 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.30 %
- Melt Index of Compound: 10 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 55.0 MPa
$ 1979/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.23 % @Time 173000 sec
- Linear Mold Shrinkage, Flow: 0.0049 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0073 cm/cm @Time 86400 sec
- Melt Flow: 13.5 g/10 min @Load 5.00 kg, Temperature 210 °C
$ 1464/MT
- Density: 1.11 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 3.80 kg, Temperature 280 °C
$ 1704/MT
- Density: 1.25 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Melt Index of Compound: 15 g/10 min @Load 10.0 kg, Temperature 280 °C
$ 1766/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 1.10 %
- Water Absorption at Saturation: 3.2 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm @Thickness 3.20 mm
$ 2545/MT
- Specific Gravity: 1.40 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 108 MPa
$ 1688/MT
- Density: 1.08 g/cc
- Moisture Absorption: 1.14 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm
- Melt Index of Compound: 5.0 g/10 min @Load 2.16 kg, Temperature 280 °C
$ 1459/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption at Saturation: 4.2 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.013 cm/cm @Thickness 3.20 mm
- Melt Flow: 45 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1623/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0089 cm/cm
- Tensile Strength at Break: 49.0 MPa
- Elongation at Break: 4.6 %
- Tensile Modulus: 2.20 GPa
$ 1639/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0089 cm/cm
- Tensile Strength at Break: 49.0 MPa
- Elongation at Break: 4.6 %
- Tensile Modulus: 2.20 GPa
$ 1447/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0089 cm/cm
- Tensile Strength at Break: 49.0 MPa
- Elongation at Break: 4.6 %
- Tensile Modulus: 2.20 GPa
$ 2319/MT
- Specific Gravity: 1.10 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Melt Flow: 7.4 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1521/MT
- Specific Gravity: 1.21 g/cc
- Density: 1.24 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 110 MPa
$ 1613/MT
- Specific Gravity: 1.29 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.6 g/10 min @Load 5.00 kg, Temperature 300 °C
- Melt Index of Compound: 7.0 g/10 min @Load 5.00 kg, Temperature 300 °C
$ 1744/MT
- Specific Gravity: 1.29 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.6 g/10 min @Load 5.00 kg, Temperature 300 °C
- Melt Index of Compound: 7.0 g/10 min @Load 5.00 kg, Temperature 300 °C
$ 1607/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.45 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
$ 1881/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.22 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
$ 1988/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1484/MT
- Specific Gravity: 1.19 g/cc
- Specific Gravity: 1.32 g/cc
- Water Absorption: 0.080 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 6.40 mm
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm @Thickness 6.40 mm
$ 1449/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 90.0 MPa
- Elongation at Break: 4.0 %
$ 2079/MT
- Specific Gravity: 1.03 g/cc
- Melt Flow: 9.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 91
- Tensile Strength at Break: 14.0 MPa
- Tensile Strength at Break: 15.0 MPa
$ 1992/MT
- Specific Gravity: 1.08 g/cc
- Melt Flow: 23 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 84
- Tensile Strength at Break: 17.0 MPa
- Tensile Strength at Break: 18.0 MPa
$ 1959/MT
- Specific Gravity: 1.40 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.00090 - 0.0015 cm/cm @Thickness 3.20 mm
$ 1976/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: 38 %
- Flexural Yield Strength: 70.0 MPa
$ 1527/MT
- Density: 1.05 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.15 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 15 g/10 min @Load 3.80 kg, Temperature 280 °C
$ 1461/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1521/MT
- Specific Gravity: 1.21 g/cc
- Density: 1.21 g/cc
- Moisture Absorption: 0.500 %
- Water Absorption at Saturation: 3.8 %
- Linear Mold Shrinkage, Flow: 0.0088 - 0.0094 cm/cm @Thickness 3.20 mm
$ 1451/MT
- Specific Gravity: 1.37 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
- Tensile Strength, Yield: 101 MPa
$ 2322/MT
- Specific Gravity: 1.44 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm
- Melt Flow: 15.4 g/10 min @Load 2.16 kg, Temperature 300 °C
- Hardness, Rockwell M: 90
$ 1863/MT
- Specific Gravity: 1.11 g/cc
- Moisture Absorption: 0.0700 %
- Viscosity: 98000 cP
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 230 °C
- Melt Index of Compound: 22 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 2298/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.700 %
- Water Absorption at Saturation: 3.6 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
$ 1706/MT
- Specific Gravity: 1.25 g/cc
- Water Absorption: 0.13 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 29.7 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 54.0 MPa
$ 1615/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 0.120 %
- Moisture Absorption: 0.220 %
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm @Time 86400 sec
$ 2030/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 0.120 %
- Moisture Absorption: 0.220 %
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm @Time 86400 sec
$ 1548/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.06 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1606/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.09 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1856/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 4.2 %
- Linear Mold Shrinkage, Flow: 0.012 - 0.016 cm/cm @Thickness 3.20 mm
$ 1896/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 33.7 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 47.0 MPa
$ 1974/MT
- Specific Gravity: 0.930 g/cc
- Water Absorption: 0.050 % @Time 173000 sec
- Linear Mold Shrinkage, Flow: 0.0048 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0033 cm/cm @Time 86400 sec
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1523/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.6 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 119
$ 1539/MT
- Density: 1.10 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.18 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 10 g/10 min @Load 1.20 kg, Temperature 280 °C
$ 1498/MT
- Specific Gravity: 1.21 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 12.2 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 78.0 MPa
$ 1512/MT
- Specific Gravity: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption at Equilibrium: 0.80 %
- Water Absorption at Saturation: 3.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 - 0.013 cm/cm @Thickness 3.20 mm
$ 2296/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
$ 2262/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 0.080 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.025 - 0.030 cm/cm @Thickness 3.20 mm
- Melt Flow: 19.2 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 75.0 MPa
$ 1651/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 28.8 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength, Yield: 41.0 MPa
$ 1545/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 41.0 MPa
- Elongation at Break: 113 %
$ 1867/MT
- Density: 1.10 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.43 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 16 g/10 min @Load 3.80 kg, Temperature 280 °C
$ 1692/MT
- Bulk Density: 0.462 g/cc
- Particle Size: 190 µm
- Viscosity Measurement: 0.33
- Molecular Weight: 47600 g/mol
- Transformation Temperature, Tg: 214 °C
$ 2085/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.900 %
- Water Absorption at Saturation: 3.0 %
- Linear Mold Shrinkage, Flow: 0.010 - 0.014 cm/cm @Thickness 3.20 mm
$ 1614/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 39.0 MPa
- Elongation at Break: 55 %
$ 1679/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.06 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.23 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 2124/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.20 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 280 °C
- Melt Index of Compound: 15 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1471/MT
- Density: 1.09 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.15 %
- Melt Index of Compound: 9.0 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 52.0 MPa
$ 2501/MT
- Density: 1.16 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0060 cm/cm
- Tensile Strength, Yield: 127 MPa
- Elongation at Break: 5.0 %
- Tensile Modulus: 4.20 GPa
$ 1519/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength at Break: 46.0 MPa
$ 2109/MT
- Specific Gravity: 1.02 g/cc
- Viscosity: 160 cP
- Viscosity: 298 cP
- Viscosity Measurement: 0.090
- Transformation Temperature, Tg: 160 °C
$ 2291/MT
- Density: 1.06 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.14 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 13 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1669/MT
- Specific Gravity: 1.19 g/cc
- Specific Gravity: 1.32 g/cc
- Water Absorption: 0.080 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 6.40 mm
- Linear Mold Shrinkage, Transverse: 0.0030 cm/cm @Thickness 6.40 mm
$ 1667/MT
- Specific Gravity: 1.20 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.80 %
- Water Absorption at Saturation: 4.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
$ 1722/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 103
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Break: 52 %
$ 1783/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.45 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
$ 1895/MT
- Density: 1.21 g/cc
- Moisture Absorption: 0.0100 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm
- Melt Index of Compound: 25 g/10 min @Load 1.20 kg, Temperature 280 °C
$ 2325/MT
- Specific Gravity: 1.52 g/cc
- Density: 1.51 g/cc
- Density: 1.52 g/cc
- Moisture Absorption: 0.0700 %
- Moisture Absorption: 0.0900 %
$ 1475/MT
- Specific Gravity: 1.35 g/cc
- Density: 1.35 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
$ 2129/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.030 %
- Water Absorption at Saturation: 0.040 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm
$ 2076/MT
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0065 cm/cm @Thickness 3.20 mm
- Melt Flow: 15.3 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength at Break: 106 MPa
- Tensile Strength, Yield: 106 MPa
$ 1780/MT
- Specific Gravity: 1.31 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0040 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell L: 108
- Tensile Strength at Break: 120 MPa
$ 1750/MT
- Bulk Density: 0.462 g/cc
- Particle Size: 190 µm
- Viscosity Measurement: 0.33
- Molecular Weight: 47600 g/mol
- Transformation Temperature, Tg: 214 °C
$ 1575/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0023 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0076 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.6 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 79.0 MPa
$ 2345/MT
- Specific Gravity: 1.32 g/cc
- Density: 1.32 g/cc
- Moisture Absorption: 0.0600 %
- Moisture Absorption: 0.0700 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Time 86400 sec
$ 1457/MT
- Specific Gravity: 0.920 g/cc
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 45.0 MPa @Thickness 6.35 mm
$ 1455/MT
- Specific Gravity: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption: 0.0600 %
- Moisture Absorption: 0.0900 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Time 86400 sec
$ 1935/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 29.8 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 40.0 MPa
$ 1464/MT
- Specific Gravity: 1.12 g/cc
- Density: 1.12 g/cc
- Moisture Absorption: 0.500 %
- Water Absorption at Saturation: 4.0 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.015 cm/cm @Thickness 3.20 mm
$ 2378/MT
- Density: 1.11 g/cc
- Viscosity: 95000 cP
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Index of Compound: 12 g/10 min @Load 1.20 kg, Temperature 280 °C
- Melt Index of Compound: 22 g/10 min @Load 2.16 kg, Temperature 280 °C
$ 2430/MT
- Density: 1.07 g/cc
- Linear Mold Shrinkage, Flow: 0.0094 - 0.0096 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0091 - 0.0093 cm/cm @Time 86400 sec
- Melt Index of Compound: 38 g/10 min @Load 10.0 kg, Temperature 280 °C
- Hardness, Rockwell R: 115
$ 1495/MT
- Specific Gravity: 0.880 g/cc
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.17 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 6.40 mm
$ 1722/MT
- Density: 1.15 g/cc
- Density: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0083 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0087 cm/cm @Time 86400 sec
$ 1462/MT
- Specific Gravity: 1.28 g/cc
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0020 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 19.6 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 108 MPa
$ 1601/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.20 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 46.0 MPa
- Elongation at Break: 70 %
$ 1749/MT
- Specific Gravity: 1.23 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 124
- Tensile Strength, Yield: 98.0 MPa
$ 1973/MT
- Density: 1.06 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.20 % @Temperature 23.0 °C
- Melt Flow: 20 g/10 min @Load 10.0 kg, Temperature 280 °C
- Tensile Strength at Break: 30.0 MPa
$ 1859/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.700 %
- Water Absorption at Saturation: 3.6 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
$ 1727/MT
- Density: 1.06 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.19 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 12 g/10 min @Load 10.0 kg, Temperature 280 °C
$ 1736/MT
- Density: 1.06 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.30 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2073/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 3.20 mm
- Melt Flow: 16 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2198/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 4.2 %
- Linear Mold Shrinkage, Flow: 0.014 - 0.017 cm/cm @Thickness 3.20 mm
$ 2146/MT
- Specific Gravity: 1.29 g/cc
- Density: 1.29 g/cc
- Moisture Absorption: 0.0600 %
- Moisture Absorption: 0.140 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0060 cm/cm @Time 86400 sec
$ 1446/MT
- Specific Gravity: 1.03 g/cc
- Melt Flow: 33 g/10 min @Load 5.00 kg, Temperature 280 °C
- Hardness, Shore D: 63
- Tensile Strength at Break: 25.0 MPa
- Tensile Strength at Break: 28.0 MPa
$ 1984/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 37.0 MPa
- Elongation at Break: 72 %
$ 1495/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0200 %
- Water Absorption at Saturation: 0.13 %
- Viscosity: 66000 cP
$ 1717/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 43.0 MPa
- Elongation at Break: 125 %
$ 2178/MT
- Specific Gravity: 1.25 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 1.10 %
- Linear Mold Shrinkage, Flow: 0.011 cm/cm @Thickness 3.20 mm
- Melt Flow: 16 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1449/MT
- Linear Mold Shrinkage, Flow: 0.0085 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0080 - 0.010 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.010 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0090 - 0.020 cm/cm @Time 86400 sec
- Tensile Strength at Break: 47.0 MPa
$ 1692/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 66.0 MPa
- Elongation at Break: 30 %
$ 1547/MT
- Specific Gravity: 1.29 g/cc
- Density: 1.29 g/cc
- Moisture Absorption at Equilibrium: 0.020 %
- Water Absorption at Saturation: 0.020 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
$ 1527/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 43.0 MPa
- Elongation at Break: 60 %
$ 1549/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 42.0 MPa
- Elongation at Break: 60 %
$ 2070/MT
- Specific Gravity: 1.12 g/cc
- Density: 1.12 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.18 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1480/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 0.030 %
- Water Absorption at Saturation: 0.040 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm
$ 2069/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Moisture Absorption: 0.0400 %
- Water Absorption at Saturation: 0.27 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1493/MT
- Specific Gravity: 1.35 g/cc
- Density: 1.35 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
$ 2284/MT
- Specific Gravity: 1.35 g/cc
- Density: 1.35 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
$ 1743/MT
- Specific Gravity: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Melt Flow: 37 g/10 min @Load 5.00 kg, Temperature 280 °C
- Melt Index of Compound: 37 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1776/MT
- Specific Gravity: 1.30 g/cc
- Density: 1.30 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
$ 1609/MT
- Specific Gravity: 1.02 g/cc
- Viscosity: 160 cP
- Viscosity: 298 cP
- Viscosity Measurement: 0.090
- Transformation Temperature, Tg: 140 °C
$ 1613/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1991/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 16.9 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 40.0 MPa
$ 1455/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1937/MT
- Density: 1.08 g/cc
- Moisture Absorption: 1.19 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm
- Melt Index of Compound: 7.0 g/10 min @Load 2.16 kg, Temperature 280 °C
$ 1451/MT
- Specific Gravity: 1.16 g/cc
- Density: 1.17 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.22 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
$ 1465/MT
- Density: 1.08 g/cc
- Moisture Absorption: 1.19 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm
- Melt Index of Compound: 7.0 g/10 min @Load 2.16 kg, Temperature 280 °C
$ 2139/MT
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0022 cm/cm
- Tensile Strength at Break: 120 MPa
- Elongation at Break: 1.7 %
- Tensile Modulus: 9.40 GPa
$ 1466/MT
- Specific Gravity: 1.23 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell L: 106
- Tensile Strength at Break: 106 MPa
$ 1735/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 43.0 MPa
$ 1727/MT
- Density: 1.25 g/cc
- Melt Index of Compound: 17 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength at Break: 95.0 MPa
- Elongation at Break: 2.1 %
- Tensile Modulus: 6.10 GPa
$ 2071/MT
- Density: 1.25 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.50 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Melt Index of Compound: 7.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1715/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength at Break: 41.0 MPa
$ 1616/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 41.0 MPa
- Elongation at Break: 48 %
$ 1538/MT
- Specific Gravity: 1.35 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 27 g/10 min @Load 2.16 kg, Temperature 300 °C
- Tensile Strength at Break: 65.0 MPa
- Elongation at Break: 6.0 %
$ 1955/MT
- Density: 1.38 g/cc
- Density: 1.38 g/cc
- Moisture Absorption at Equilibrium: 0.070 %
- Moisture Absorption at Equilibrium: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
$ 1632/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.7 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 119
$ 1667/MT
- Density: 1.10 g/cc
- Melt Index of Compound: 30 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength, Yield: 85.0 MPa
- Elongation at Break: 15 %
$ 1605/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.54 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 4.4 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.017 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 59.0 MPa
$ 2095/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 1.2 %
- Water Absorption at Saturation: 4.2 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.012 - 0.016 cm/cm @Thickness 3.20 mm
$ 1827/MT
- Specific Gravity: 1.44 g/cc
- Water Absorption: 0.020 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 29.1 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 112 MPa
$ 1754/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.20 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 46.0 MPa
- Elongation at Break: 40 %
$ 1691/MT
- Density: 1.13 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Index of Compound: 32 g/10 min @Load 10.0 kg, Temperature 280 °C
$ 2162/MT
- Specific Gravity: 1.42 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 6.40 mm
- Melt Flow: 22 g/10 min @Load 10.0 kg, Temperature 250 °C
$ 1783/MT
- Specific Gravity: 1.62 g/cc
- Density: 1.62 g/cc
- Moisture Absorption at Equilibrium: 0.00 %
- Water Absorption at Saturation: 0.020 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0080 cm/cm @Thickness 3.20 mm
$ 2277/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1629/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 2188/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 4.2 %
- Linear Mold Shrinkage, Flow: 0.012 - 0.016 cm/cm @Thickness 3.20 mm
$ 1861/MT
- Specific Gravity: 0.970 g/cc
- Linear Mold Shrinkage, Flow: 0.0080 - 0.012 cm/cm @Thickness 3.20 mm
- Melt Flow: 10.6 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 32.0 MPa
- Tensile Strength, Yield: 35.0 MPa
$ 1719/MT
- Specific Gravity: 1.35 g/cc
- Density: 1.35 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
$ 2069/MT
- Specific Gravity: 1.32 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0030 cm/cm @Thickness 3.20 mm
- Melt Flow: 48.3 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 98.0 MPa
$ 2145/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 33 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Rockwell R: 115
$ 1609/MT
- Specific Gravity: 1.21 g/cc
- Density: 1.20 g/cc
- Moisture Absorption: 0.0700 %
- Moisture Absorption: 0.100 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Time 86400 sec
$ 2151/MT
- Specific Gravity: 1.07 g/cc
- Density: 1.06 g/cc
- Moisture Absorption: 0.110 %
- Moisture Absorption: 0.150 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Time 86400 sec
$ 1875/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
$ 1572/MT
- Water Absorption at Saturation: 0.070 %
- Viscosity: 145000 cP
- Melt Index of Compound: 16 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 42.0 MPa
- Tensile Strength at Break: 42.0 MPa
$ 1493/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 91
- Tensile Strength at Break: 22.0 MPa
- Tensile Strength at Break: 23.0 MPa
$ 1507/MT
- Specific Gravity: 1.29 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.6 g/10 min @Load 5.00 kg, Temperature 300 °C
- Melt Index of Compound: 7.0 g/10 min @Load 5.00 kg, Temperature 300 °C
$ 1606/MT
- Specific Gravity: 1.12 g/cc
- Density: 1.11 g/cc
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 260 °C
- Melt Index of Compound: 30 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 35.0 MPa
$ 1496/MT
- Specific Gravity: 1.29 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0040 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.6 g/10 min @Load 5.00 kg, Temperature 300 °C
- Melt Index of Compound: 7.0 g/10 min @Load 5.00 kg, Temperature 300 °C
$ 1938/MT
- Specific Gravity: 1.23 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 7.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 57.0 MPa
$ 1819/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.18 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
$ 2545/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.245 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Moisture Absorption: 1.00 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
$ 2053/MT
- Specific Gravity: 1.03 g/cc
- Density: 1.03 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.12 %
- Melt Flow: 13.8 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1981/MT
- Specific Gravity: 1.42 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 119 MPa
- Elongation at Break: 5.0 %
$ 1622/MT
- Specific Gravity: 1.33 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 142 MPa
- Elongation at Break: 10 %
$ 1503/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Melt Flow: 8.5 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1572/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.070 %
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
$ 1585/MT
- Density: 1.29 g/cc
- Density: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0028 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0049 cm/cm @Time 86400 sec
$ 1636/MT
- Specific Gravity: 1.09 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 115
- Tensile Strength at Break: 40.0 MPa
- Tensile Strength, Yield: 51.0 MPa
$ 2379/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.07 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm
$ 1600/MT
- Specific Gravity: 1.13 g/cc
- Water Absorption: 0.080 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 19.3 g/10 min @Load 10.0 kg, Temperature 250 °C
- Melt Index of Compound: 23 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1821/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.060 % @Time 173000 sec
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0065 cm/cm @Time 86400 sec
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 210 °C
$ 1628/MT
- Density: 1.10 g/cc
- Moisture Absorption at Equilibrium: 1.2 %
- Water Absorption at Saturation: 3.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.012 - 0.020 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 280 °C
$ 2003/MT
- Density: 1.10 g/cc
- Moisture Absorption at Equilibrium: 1.2 %
- Water Absorption at Saturation: 3.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.012 - 0.020 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 280 °C
$ 2337/MT
- Density: 1.10 g/cc
- Moisture Absorption at Equilibrium: 1.2 %
- Water Absorption at Saturation: 3.5 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.012 - 0.020 cm/cm
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 280 °C
$ 1703/MT
- Specific Gravity: 0.990 g/cc
- Density: 0.990 g/cc
- Moisture Absorption: 0.0200 %
- Water Absorption at Saturation: 0.050 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1707/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.10 % @Time 173000 sec
- Linear Mold Shrinkage, Flow: 0.0048 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0109 cm/cm @Time 86400 sec
- Melt Flow: 31 g/10 min @Load 5.00 kg, Temperature 210 °C
$ 2075/MT
- Density: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0036 cm/cm
- Tensile Strength at Break: 74.0 MPa
- Elongation at Break: 2.3 %
- Tensile Modulus: 5.30 GPa
$ 1499/MT
- Density: 1.21 g/cc
- Water Absorption: 0.11 % @Temperature 23.0 °C, Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm
- Tensile Strength at Break: 75.0 MPa
- Elongation at Break: 2.3 %
$ 2042/MT
- Specific Gravity: 1.19 g/cc
- Density: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1565/MT
- Specific Gravity: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.010 - 0.013 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength at Break: 60.0 MPa
- Tensile Strength at Break: 64.0 MPa
$ 2005/MT
- Specific Gravity: 1.14 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell M: 88
- Tensile Strength, Yield: 78.0 MPa
$ 1708/MT
- Bulk Density: 0.465 g/cc
- Particle Size: 200 µm
- Viscosity Measurement: 0.46
- Molecular Weight: 68600 g/mol
- Transformation Temperature, Tg: 217 °C
$ 1583/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption at Saturation: 4.2 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.013 cm/cm @Thickness 3.20 mm
- Melt Flow: 45 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1516/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C
- Hardness, Rockwell R: 116
- Tensile Strength at Break: 61.0 MPa
$ 1682/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 75.0 MPa
- Elongation at Break: 20 %
$ 1486/MT
- Specific Gravity: 0.930 g/cc
- Water Absorption: 0.050 % @Time 173000 sec
- Linear Mold Shrinkage, Flow: 0.0048 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0033 cm/cm @Time 86400 sec
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 1562/MT
- Specific Gravity: 1.22 g/cc
- Density: 1.22 g/cc
- Moisture Absorption: 0.0200 %
- Water Absorption at Saturation: 0.060 %
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Thickness 3.20 mm
$ 2271/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 0.400 %
- Water Absorption at Saturation: 4.0 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.015 cm/cm @Thickness 3.20 mm
$ 1625/MT
- Specific Gravity: 1.22 g/cc
- Melt Flow: 24 g/10 min @Load 2.16 kg, Temperature 300 °C
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 4.0 %
- Flexural Yield Strength: 102 MPa
$ 2265/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength at Break: 53.0 MPa
$ 1557/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
$ 1688/MT
- Density: 1.16 g/cc
- Moisture Absorption: 1.11 %
- Water Absorption at Saturation: 3.3 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.010 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1519/MT
- Density: 1.11 g/cc
- Viscosity: 95000 cP
- Melt Index of Compound: 12 g/10 min @Load 1.20 kg, Temperature 280 °C
- Melt Index of Compound: 22 g/10 min @Load 2.16 kg, Temperature 280 °C
- Tensile Strength at Break: 49.0 MPa
$ 1868/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Index of Compound: 6.0 g/10 min @Load 2.16 kg, Temperature 300 °C
- Hardness, Rockwell R: 118
$ 2303/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.20 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 40.0 MPa
- Elongation at Break: 70 %
$ 1769/MT
- Density: 0.970 g/cc
- Melt Index of Compound: 11 g/10 min @Load 5.00 kg, Temperature 260 °C
- Hardness, H358/30: 65.0 MPa
- Tensile Strength at Break: 30.0 MPa
- Tensile Strength, Yield: 34.0 MPa
$ 1751/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.066 % @Time 86400 sec
- Tensile Strength, Yield: 51.0 MPa
- Elongation at Break: 25 %
- Flexural Yield Strength: 75.0 MPa
$ 1450/MT
- Specific Gravity: 1.24 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 117 MPa
- Tensile Strength, Yield: 122 MPa
$ 1648/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 108 MPa
- Elongation at Break: 1.6 %
- Tensile Modulus: 9.87 GPa
$ 1452/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1613/MT
- Specific Gravity: 1.13 g/cc
- Density: 1.25 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.45 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
$ 1484/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 45.0 MPa
- Elongation at Break: 50 %
- Flexural Yield Strength: 75.0 MPa
$ 1543/MT
- Specific Gravity: 1.03 g/cc
- Density: 1.03 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.12 %
- Melt Flow: 13.8 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2032/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
$ 1782/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.060 % @Time 173000 sec
- Linear Mold Shrinkage, Flow: 0.0055 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0065 cm/cm @Time 86400 sec
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 210 °C
$ 1951/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1858/MT
- Specific Gravity: 1.07 g/cc
- Density: 1.07 g/cc
- Moisture Absorption at Equilibrium: 0.050 %
- Water Absorption at Saturation: 0.25 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1630/MT
- Specific Gravity: 1.06 g/cc
- Density: 1.06 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.13 %
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm
$ 1463/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Hardness, Rockwell R: 96
- Tensile Strength, Yield: 44.0 MPa
- Elongation at Break: 114 %
$ 1688/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption at Saturation: 4.2 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.010 - 0.013 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.0 g/10 min @Load 1.20 kg, Temperature 280 °C
$ 1587/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 9.5 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 85
- Tensile Strength at Break: 16.0 MPa
- Tensile Strength at Break: 17.0 MPa
$ 1651/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 89
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength at Break: 16.0 MPa
$ 1598/MT
- Specific Gravity: 1.09 g/cc
- Melt Flow: 7.7 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 50.0 MPa
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 15 %
$ 1650/MT
- Specific Gravity: 1.09 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 60.0 MPa
- Elongation at Break: 180 %
$ 1551/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.09 g/cc
- Moisture Absorption at Equilibrium: 0.30 %
- Water Absorption at Saturation: 0.55 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0113 - 0.0126 cm/cm @Thickness 3.20 mm
$ 1624/MT
- Density: 1.06 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Melt Index of Compound: 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 50.0 MPa
$ 1845/MT
- Specific Gravity: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 220 °C
- Melt Flow: 18 g/10 min @Load 3.80 kg, Temperature 260 °C
- Tensile Strength at Break: 48.0 MPa
$ 1680/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 2224/MT
- Specific Gravity: 1.30 g/cc
- Linear Mold Shrinkage, Flow: 0.0017 - 0.0018 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0027 - 0.0061 cm/cm @Thickness 3.20 mm
- Melt Flow: 1.3 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 95.0 MPa
$ 1684/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Melt Index of Compound: 13 g/10 min @Load 1.20 kg, Temperature 280 °C
- Melt Index of Compound: 34 g/10 min @Load 2.16 kg, Temperature 280 °C
- Tensile Strength at Break: 42.0 MPa
$ 1656/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.23 % @Time 173000 sec
- Linear Mold Shrinkage, Flow: 0.0049 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0073 cm/cm @Time 86400 sec
- Melt Flow: 13.5 g/10 min @Load 5.00 kg, Temperature 210 °C
$ 2414/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 114
- Tensile Strength, Yield: 49.0 MPa
$ 1889/MT
- Density: 1.13 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.37 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 13 g/10 min @Load 2.16 kg, Temperature 280 °C
$ 1482/MT
- Density: 1.08 g/cc
- Moisture Absorption at Equilibrium: 1.2 %
- Water Absorption at Saturation: 4.2 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm
- Hardness, H358/30: 80.0 MPa
$ 1630/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 35.0 MPa
$ 1540/MT
- Specific Gravity: 1.33 g/cc
- Density: 1.34 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
$ 2434/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 2285/MT
- Specific Gravity: 1.13 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 2.16 kg, Temperature 220 °C
- Melt Flow: 18 g/10 min @Load 3.80 kg, Temperature 260 °C
- Tensile Strength at Break: 48.0 MPa
$ 2249/MT
- Specific Gravity: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.0055 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0045 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.5 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 37.0 MPa
$ 1670/MT
- Density: 1.31 g/cc
- Density: 1.31 g/cc
- Moisture Absorption: 0.900 %
- Tensile Strength at Break: 53.0 MPa
- Tensile Strength at Break: 58.0 MPa
$ 1589/MT
- Density: 1.08 g/cc
- Moisture Absorption: 1.19 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm
- Melt Index of Compound: 7.0 g/10 min @Load 2.16 kg, Temperature 280 °C
$ 1452/MT
- Density: 1.08 g/cc
- Moisture Absorption: 1.19 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.014 - 0.018 cm/cm
- Melt Index of Compound: 7.0 g/10 min @Load 2.16 kg, Temperature 280 °C
$ 1990/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 13.7 g/10 min @Load 5.00 kg, Temperature 280 °C
- Hardness, Rockwell R: 114
$ 1971/MT
- Density: 1.16 g/cc
- Moisture Absorption: 1.00 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.012 - 0.016 cm/cm
- Melt Index of Compound: 13 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2032/MT
- Density: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Tensile Strength at Break: 108 MPa
- Elongation at Break: 1.6 %
- Tensile Modulus: 9.87 GPa
$ 2251/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 89
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength at Break: 16.0 MPa
$ 1505/MT
- Specific Gravity: 1.38 g/cc
- Linear Mold Shrinkage, Flow: 0.0025 - 0.0030 cm/cm
- Melt Flow: 11 g/10 min @Load 2.16 kg, Temperature 300 °C
- Tensile Strength at Break: 115 MPa
- Tensile Strength, Yield: 106 MPa
$ 1703/MT
- Specific Gravity: 1.46 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 103 MPa
- Elongation at Break: 10 %
$ 2408/MT
- Specific Gravity: 1.12 g/cc
- Density: 1.11 g/cc
- Melt Flow: 30 g/10 min @Load 5.00 kg, Temperature 260 °C
- Melt Index of Compound: 30 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 35.0 MPa
$ 1628/MT
- Specific Gravity: 0.990 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 34.0 MPa
$ 2233/MT
- Density: 1.31 g/cc
- Density: 1.31 g/cc
- Moisture Absorption: 0.900 %
- Tensile Strength at Break: 53.0 MPa
- Tensile Strength at Break: 58.0 MPa
$ 2518/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.012 - 0.014 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.011 - 0.014 cm/cm @Thickness 3.20 mm
- Melt Flow: 97 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 62.0 MPa
$ 2159/MT
- Specific Gravity: 1.06 g/cc
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 87
- Tensile Strength at Break: 18.0 MPa
- Tensile Strength at Break: 18.0 MPa
$ 1955/MT
- Specific Gravity: 1.16 g/cc
- Density: 1.17 g/cc
- Moisture Absorption: 0.0700 %
- Water Absorption at Saturation: 0.22 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
$ 1520/MT
- Specific Gravity: 1.37 g/cc
- Density: 1.37 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 4.0 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
$ 2529/MT
- Specific Gravity: 1.31 g/cc
- Linear Mold Shrinkage, Flow: 0.00080 - 0.0018 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.00090 - 0.0019 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 119 MPa
- Tensile Strength, Yield: 117 MPa
$ 1622/MT
- Specific Gravity: 1.29 g/cc
- Specific Gravity: 1.43 g/cc
- Water Absorption: 0.080 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0015 cm/cm @Thickness 6.40 mm
- Linear Mold Shrinkage, Transverse: 0.0025 cm/cm @Thickness 6.40 mm
$ 2169/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.09 g/cc
- Moisture Absorption at Equilibrium: 0.30 %
- Water Absorption at Saturation: 0.55 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0113 - 0.0126 cm/cm @Thickness 3.20 mm
$ 1451/MT
- Density: 1.10 g/cc
- Moisture Absorption: 0.0800 %
- Water Absorption at Saturation: 0.29 %
- Melt Index of Compound: 11 g/10 min @Load 10.0 kg, Temperature 280 °C
- Tensile Strength at Break: 60.0 MPa
$ 1944/MT
- Specific Gravity: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 73.0 MPa
- Tensile Strength, Yield: 86.0 MPa
- Elongation at Break: 15 %
$ 1663/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption at Equilibrium: 0.12 %
- Water Absorption at Saturation: 0.45 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
$ 1447/MT
- Specific Gravity: 1.09 g/cc
- Viscosity: 610000 cP
- Melt Flow: 12 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 71.0 MPa
- Elongation at Break: 11 %
$ 1494/MT
- Density: 1.17 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Water Absorption at Saturation: 3.0 % @Temperature 23.0 °C
- Melt Flow: 5.0 g/10 min @Load 10.0 kg, Temperature 280 °C
- Tensile Strength at Break: 95.0 MPa
$ 2457/MT
- Density: 1.45 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0040 cm/cm
- Melt Index of Compound: 19 g/10 min @Load 10.0 kg, Temperature 280 °C
$ 1574/MT
- Bulk Density: 0.476 g/cc
- Particle Size: 200 µm
- Viscosity Measurement: 0.40
- Molecular Weight: 56200 g/mol
- Transformation Temperature, Tg: 216 °C
$ 2039/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 10 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 91
- Tensile Strength at Break: 22.0 MPa
- Tensile Strength at Break: 23.0 MPa
$ 1542/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.4 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 43.0 MPa
$ 1773/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 6.4 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 43.0 MPa
$ 1645/MT
- Density: 1.06 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Melt Index of Compound: 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 50.0 MPa
$ 2315/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 14.2 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength, Yield: 81.0 MPa
$ 2098/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption: 0.700 %
- Water Absorption at Saturation: 3.6 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
$ 2508/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 300 °C
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 7.0 %
$ 1597/MT
- Specific Gravity: 1.33 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 2.16 kg, Temperature 300 °C
- Tensile Strength at Break: 70.0 MPa
- Elongation at Break: 7.0 %
$ 1705/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 13 g/10 min @Load 5.00 kg, Temperature 250 °C
- Tensile Strength, Yield: 35.0 MPa
$ 1677/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.09 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.015 - 0.019 cm/cm
$ 2268/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
$ 1596/MT
- Specific Gravity: 1.28 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 117 MPa
- Elongation at Break: 15 %
$ 1782/MT
- Specific Gravity: 1.06 g/cc
- Melt Flow: 3.8 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 48.0 MPa
- Elongation at Break: 42 %
- Flexural Strength: 76.0 MPa
$ 1575/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.10 g/cc
- Moisture Absorption at Equilibrium: 0.090 %
- Water Absorption at Saturation: 0.11 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0034 - 0.0052 cm/cm @Thickness 3.20 mm
$ 1595/MT
- Specific Gravity: 0.880 g/cc
- Density: 0.880 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 280 °C
- Tensile Strength at Break: 40.0 MPa
$ 1764/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Water Absorption at Saturation: 0.070 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2287/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 59.0 MPa
- Elongation at Break: 29 %
$ 1550/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 20.2 g/10 min @Load 5.00 kg, Temperature 280 °C
- Melt Index of Compound: 20 g/10 min @Load 5.00 kg, Temperature 280 °C
- Hardness, Shore D: 65
- Tensile Strength at Break: 37.0 MPa
$ 1797/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Hardness, Rockwell R: 121
- Tensile Strength, Yield: 59.0 MPa
- Elongation at Break: 29 %
$ 1896/MT
- Specific Gravity: 1.34 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0045 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 74.0 MPa
- Tensile Strength, Yield: 74.0 MPa
$ 2306/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 21 g/10 min @Load 2.16 kg, Temperature 260 °C
- Tensile Strength, Yield: 35.0 MPa
$ 1996/MT
- Specific Gravity: 1.31 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0025 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell M: 88
- Tensile Strength at Break: 107 MPa
$ 1584/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 4.2 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.016 cm/cm @Thickness 3.20 mm
$ 2282/MT
- Specific Gravity: 1.40 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.00090 - 0.0015 cm/cm @Thickness 3.20 mm
$ 2022/MT
- Specific Gravity: 1.12 g/cc
- Density: 1.12 g/cc
- Moisture Absorption: 0.500 %
- Water Absorption at Saturation: 4.0 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.015 cm/cm @Thickness 3.20 mm
$ 2019/MT
- Specific Gravity: 1.12 g/cc
- Density: 1.12 g/cc
- Moisture Absorption: 0.500 %
- Water Absorption at Saturation: 4.0 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.015 cm/cm @Thickness 3.20 mm
$ 2055/MT
- Specific Gravity: 1.12 g/cc
- Density: 1.12 g/cc
- Moisture Absorption: 0.500 %
- Water Absorption at Saturation: 4.0 %
- Linear Mold Shrinkage, Flow: 0.013 - 0.015 cm/cm @Thickness 3.20 mm
$ 1947/MT
- Specific Gravity: 1.14 g/cc
- Density: 1.14 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1557/MT
- Specific Gravity: 1.04 g/cc
- Water Absorption: 0.10 % @Time 173000 sec
- Linear Mold Shrinkage, Flow: 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0040 cm/cm @Time 86400 sec
- Melt Flow: 10 g/10 min @Load 2.16 kg, Temperature 250 °C
$ 1972/MT
- Density: 1.34 g/cc
- Moisture Absorption: 0.900 %
- Water Absorption at Saturation: 2.5 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.011 cm/cm @Thickness 3.20 mm
$ 1695/MT
- Specific Gravity: 1.20 g/cc
- Density: 1.20 g/cc
- Moisture Absorption at Equilibrium: 0.80 %
- Water Absorption at Saturation: 4.0 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
$ 1687/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 0.0200 %
- Water Absorption at Saturation: 0.13 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1698/MT
- Specific Gravity: 0.930 g/cc
- Water Absorption: 0.050 % @Time 173000 sec
- Linear Mold Shrinkage, Flow: 0.0048 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0033 cm/cm @Time 86400 sec
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 200 °C
$ 2002/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 20 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 89
- Tensile Strength at Break: 15.0 MPa
- Tensile Strength at Break: 16.0 MPa
$ 1483/MT
- Specific Gravity: 1.16 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Moisture Absorption at Equilibrium: 0.22 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell L: 104
$ 2218/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1533/MT
- Specific Gravity: 1.40 g/cc
- Density: 1.40 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.00090 - 0.0015 cm/cm @Thickness 3.20 mm
$ 1914/MT
- Specific Gravity: 0.990 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 34.0 MPa
$ 1858/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 40.0 MPa
- Flexural Yield Strength: 55.0 MPa
- Flexural Modulus: 2.06 GPa
$ 1571/MT
- Density: 1.06 g/cc
- Moisture Absorption at Equilibrium: 0.070 %
- Water Absorption at Saturation: 0.25 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 9.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1748/MT
- Specific Gravity: 1.29 g/cc
- Density: 1.30 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
$ 1529/MT
- Specific Gravity: 1.03 g/cc
- Melt Flow: 33 g/10 min @Load 5.00 kg, Temperature 280 °C
- Hardness, Shore D: 63
- Tensile Strength at Break: 25.0 MPa
- Tensile Strength at Break: 28.0 MPa
$ 1448/MT
- Specific Gravity: 1.07 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0050 - 0.0070 cm/cm
- Tensile Strength, Yield: 44.0 MPa
$ 2062/MT
- Specific Gravity: 1.24 g/cc
- Density: 1.24 g/cc
- Moisture Absorption at Equilibrium: 0.060 %
- Water Absorption at Saturation: 0.20 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm
$ 2506/MT
- Specific Gravity: 1.00 g/cc
- Specific Gravity: 1.11 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 6.40 mm
- Tensile Strength at Break: 28.0 MPa @Thickness 6.35 mm
$ 1590/MT
- Specific Gravity: 1.02 g/cc
- Specific Gravity: 1.28 g/cc
- Linear Mold Shrinkage, Flow: 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0015 - 0.0035 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 48.0 MPa @Thickness 6.35 mm
$ 2575/MT
- Specific Gravity: 1.10 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 48.0 MPa
- Flexural Strength: 72.0 MPa
- Flexural Modulus: 2.41 GPa
$ 1663/MT
- Specific Gravity: 1.39 g/cc
- Melt Flow: 13.4 g/10 min @Load 2.16 kg, Temperature 300 °C
- Spiral Flow: 655 cm @Thickness 3.00 mm
- Tensile Strength at Break: 97.0 MPa
- Tensile Strength, Yield: 97.0 MPa
$ 1637/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 3.8 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 54.0 MPa
$ 2197/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Moisture Absorption at Equilibrium: 0.050 %
- Water Absorption at Saturation: 0.25 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1487/MT
- Specific Gravity: 1.33 g/cc
- Melt Flow: 8.5 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 93
- Tensile Strength at Break: 9.00 MPa
- Tensile Strength at Break: 9.00 MPa
$ 2431/MT
- Density: 1.17 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0050 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2075/MT
- Specific Gravity: 0.990 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 14 g/10 min @Load 5.00 kg, Temperature 260 °C
- Melt Index of Compound: 12 g/10 min @Load 5.00 kg, Temperature 260 °C
$ 1847/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.60 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 64.0 MPa
- Elongation at Break: 120 %
$ 1456/MT
- Specific Gravity: 1.12 g/cc
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 4.2 g/10 min @Load 2.16 kg, Temperature 230 °C
- Melt Flow: 10 g/10 min @Load 3.80 kg, Temperature 230 °C
- Melt Flow: 32.1 g/10 min @Load 10.0 kg, Temperature 220 °C
$ 1527/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.25 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
$ 1498/MT
- Specific Gravity: 1.28 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.00050 - 0.0015 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0015 - 0.0030 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 120
$ 1472/MT
- Specific Gravity: 0.990 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0070 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
- Melt Flow: 10.5 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 33.0 MPa
$ 1556/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 58.0 MPa
- Elongation at Break: 30 %
$ 1812/MT
- Density: 1.06 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.22 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 10 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2312/MT
- Density: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Tensile Strength at Break: 104 MPa
- Elongation at Break: 1.6 %
- Flexural Strength: 115 MPa
$ 1597/MT
- Specific Gravity: 1.16 g/cc
- Density: 1.17 g/cc
- Moisture Absorption at Equilibrium: 1.1 %
- Water Absorption at Saturation: 3.8 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.010 - 0.012 cm/cm
$ 1968/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.10 % @Time 173000 sec
- Linear Mold Shrinkage, Flow: 0.0048 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0109 cm/cm @Time 86400 sec
- Melt Flow: 31 g/10 min @Load 5.00 kg, Temperature 210 °C
$ 1928/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell R: 115
- Tensile Strength, Yield: 43.0 MPa
$ 2120/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 30 %
$ 2043/MT
- Specific Gravity: 1.15 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0045 cm/cm @Thickness 3.20 mm
- Tensile Strength at Break: 77.0 MPa
- Elongation at Break: 2.0 %
$ 1506/MT
- Specific Gravity: 1.23 g/cc
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0045 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 26.6 g/10 min @Load 1.20 kg, Temperature 300 °C
- Tensile Strength at Break: 103 MPa
$ 1525/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Melt Index of Compound: 17 g/10 min @Load 1.20 kg, Temperature 280 °C
- Melt Index of Compound: 35 g/10 min @Load 2.16 kg, Temperature 280 °C
- Tensile Strength at Break: 45.0 MPa
$ 1620/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 11 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 80
- Tensile Strength at Break: 12.0 MPa
- Tensile Strength at Break: 13.0 MPa
$ 1786/MT
- Specific Gravity: 1.10 g/cc
- Water Absorption: 0.50 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.012 - 0.014 cm/cm @Thickness 3.20 mm
- Melt Flow: 8.9 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength, Yield: 51.0 MPa
$ 1772/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 36.0 MPa
- Elongation at Break: 125 %
$ 2350/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.10 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 62.0 MPa
- Elongation at Break: 30 %
$ 1635/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.18 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
$ 1669/MT
- Specific Gravity: 1.19 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0023 cm/cm @Thickness 3.20 mm
- Linear Mold Shrinkage, Transverse: 0.0025 - 0.0076 cm/cm @Thickness 3.20 mm
- Melt Flow: 2.6 g/10 min @Load 5.00 kg, Temperature 260 °C
- Tensile Strength at Break: 79.0 MPa
$ 2166/MT
- Density: 1.06 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 8.0 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 2292/MT
- Specific Gravity: 1.62 g/cc
- Density: 1.62 g/cc
- Moisture Absorption at Equilibrium: 0.00 %
- Water Absorption at Saturation: 0.020 % @Temperature 23.0 °C
- Linear Mold Shrinkage, Flow: 0.0030 - 0.0080 cm/cm @Thickness 3.20 mm
$ 2252/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.09 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 3.5 %
- Linear Mold Shrinkage, Flow: 0.015 - 0.019 cm/cm
$ 1577/MT
- Specific Gravity: 1.10 g/cc
- Density: 1.10 g/cc
- Viscosity: 250000 cP
- Viscosity: 390000 cP
- Viscosity: 525000 cP
$ 1453/MT
- Specific Gravity: 1.06 g/cc
- Linear Mold Shrinkage, Flow: 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 25 g/10 min @Load 5.00 kg, Temperature 300 °C
- Tensile Strength at Break: 68.0 MPa
- Tensile Strength, Yield: 72.0 MPa
$ 1583/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0500 %
- Water Absorption at Saturation: 0.15 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm
$ 2051/MT
- Specific Gravity: 1.04 g/cc
- Melt Flow: 6.0 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 83
- Tensile Strength at Break: 10.0 MPa
- Tensile Strength at Break: 10.0 MPa
$ 1539/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1642/MT
- Specific Gravity: 1.16 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm
- Hardness, Rockwell M: 88
- Tensile Strength, Yield: 83.0 MPa
$ 1857/MT
- Specific Gravity: 1.11 g/cc
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0090 cm/cm @Thickness 3.20 mm
- Melt Flow: 5.3 g/10 min @Load 5.00 kg, Temperature 280 °C
- Tensile Strength at Break: 48.0 MPa
- Tensile Strength, Yield: 55.0 MPa
$ 1828/MT
- Specific Gravity: 1.08 g/cc
- Water Absorption: 0.070 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Flow: 8.5 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength at Break: 40.0 MPa
$ 2231/MT
- Specific Gravity: 1.05 g/cc
- Density: 1.05 g/cc
- Moisture Absorption: 0.0900 %
- Moisture Absorption: 0.100 %
- Linear Mold Shrinkage, Flow: 0.0070 - 0.0090 cm/cm @Time 86400 sec
$ 1463/MT
- Specific Gravity: 1.05 g/cc
- Water Absorption: 0.20 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Tensile Strength, Yield: 53.0 MPa
- Elongation at Break: 50 %
$ 1979/MT
- Specific Gravity: 1.33 g/cc
- Melt Flow: 8.5 g/10 min @Load 10.0 kg, Temperature 250 °C
- Hardness, Shore A: 93
- Tensile Strength at Break: 9.00 MPa
- Tensile Strength at Break: 9.00 MPa
$ 1745/MT
- Specific Gravity: 1.09 g/cc
- Density: 1.10 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 4.2 %
- Linear Mold Shrinkage, Flow: 0.014 - 0.017 cm/cm @Thickness 3.20 mm
$ 1478/MT
- Specific Gravity: 1.20 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm
- Melt Flow: 9.0 g/10 min @Load 5.00 kg, Temperature 300 °C
- Melt Index of Compound: 8.0 g/10 min @Load 5.00 kg, Temperature 300 °C
$ 1781/MT
- Density: 1.29 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm
- Melt Index of Compound: 10 g/10 min @Load 10.0 kg, Temperature 300 °C
$ 1449/MT
- Specific Gravity: 1.06 g/cc
- Water Absorption: 0.060 % @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 11.1 g/10 min @Load 10.0 kg, Temperature 250 °C
- Tensile Strength, Yield: 45.0 MPa
$ 1561/MT
- Density: 1.17 g/cc
- Density: 1.17 g/cc
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0040 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Flow: 0.0030 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0040 - 0.0060 cm/cm @Time 86400 sec
$ 1486/MT
- Density: 1.30 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.20 %
- Linear Mold Shrinkage, Flow: 0.0010 - 0.0030 cm/cm
- Melt Index of Compound: 7.0 g/10 min @Load 10.0 kg, Temperature 280 °C
$ 2179/MT
- Specific Gravity: 1.08 g/cc
- Density: 1.08 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.23 %
- Linear Mold Shrinkage, Flow: 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm
$ 1613/MT
- Specific Gravity: 1.37 g/cc
- Density: 1.37 g/cc
- Moisture Absorption: 1.20 %
- Water Absorption at Saturation: 4.0 %
- Linear Mold Shrinkage, Flow: 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm
$ 1592/MT
- Density: 1.06 g/cc
- Moisture Absorption: 0.0600 %
- Water Absorption at Saturation: 0.14 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm
- Melt Index of Compound: 12 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1506/MT
- Density: 1.08 g/cc
- Linear Mold Shrinkage, Flow: 0.0082 cm/cm
- Tensile Strength, Yield: 52.0 MPa
- Elongation at Yield: 10.7 %
- Tensile Modulus: 2.30 GPa
$ 1508/MT
- Specific Gravity: 1.11 g/cc
- Density: 1.11 g/cc
- Water Absorption at Saturation: 0.070 %
- Linear Mold Shrinkage, Flow: 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm
- Melt Flow: 15 g/10 min @Load 5.00 kg, Temperature 280 °C
$ 1793/MT
- Specific Gravity: 1.10 g/cc
- Melt Flow: 10 g/10 min @Load 5.00 kg, Temperature 250 °C
- Hardness, Shore A: 86
- Tensile Strength at Break: 14.0 MPa
- Tensile Strength at Break: 15.0 MPa
$ 1569/MT
- Density: 1.66 g/cc
- Linear Mold Shrinkage, Flow: 0.0070 cm/cm @Time 86400 sec
- Linear Mold Shrinkage, Transverse: 0.0065 cm/cm @Time 86400 sec
- Melt Index of Compound: 11 g/10 min @Load 5.00 kg, Temperature 300 °C
- Flexural Strength: 90.0 - 100 MPa
Delivery Polyphenylene Ether/PPO SABIC Innovative Plastics (GE Plastics)
Below is a port-to-port container shipping rates chart for cost ranges of common international shipping destinations (from Saudi Arabia, Germany, China):| Country | 20’ Container | 40’ Container | 5,000 MT |
|---|---|---|---|
| 🇦🇺 Australia | $3345 | $4181 | $401400 |
| 🇦🇹 Austria | $2825 | $3531 | $339000 |
| 🇦🇿 Azerbaijan | $2625 | $3281 | $315000 |
| 🇦🇱 Albania | $2500 | $3125 | $300000 |
| 🇩🇿 Algeria | $2762.5 | $3453 | $331500 |
| 🇦🇴 Angola | $2762.5 | $3453 | $331500 |
| 🇦🇷 Argentina | $3230 | $4038 | $387600 |
| 🇦🇲 Armenia | $2625 | $3281 | $315000 |
| 🇦🇫 Afghanistan | $3712.5 | $4641 | $445500 |
| 🇧🇩 Bangladesh | $2625 | $3281 | $315000 |
| 🇧🇭 Bahrain | $3095 | $3869 | $371400 |
| 🇧🇾 Belarus | $2825 | $3531 | $339000 |
| 🇧🇿 Belize | $3155 | $3944 | $378600 |
| 🇧🇪 Belgium | $2575 | $3219 | $309000 |
| 🇧🇬 Bulgaria | $2400 | $3000 | $288000 |
| 🇧🇴 Bolivia | $3230 | $4038 | $387600 |
| 🇧🇦 Bosnia and Herzegovina | $2575 | $3219 | $309000 |
| 🇧🇷 Brazil | $3120 | $3900 | $374400 |
| 🇭🇺 Hungary | $2575 | $3219 | $309000 |
| 🇻🇪 Venezuela | $3230 | $4038 | $387600 |
| 🇻🇳 Vietnam | $2625 | $3281 | $315000 |
| 🇬🇭 Ghana | $2762.5 | $3453 | $331500 |
| 🇬🇹 Guatemala | $3230 | $4038 | $387600 |
| 🇬🇳 Guinea | $2762.5 | $3453 | $331500 |
| 🇩🇪 Germany | $2475 | $3094 | $297000 |
| 🇭🇳 Honduras | $3230 | $4038 | $387600 |
| 🇭🇰 Hong Kong S.A.R. | $2625 | $3281 | $315000 |
| 🇬🇷 Greece | $2575 | $3219 | $309000 |
| 🇬🇪 Georgia | $3712.5 | $4641 | $445500 |
| 🇩🇰 Denmark | $2400 | $3000 | $288000 |
| 🇩🇴 Dominican Republic | $3230 | $4038 | $387600 |
| 🇪🇬 Egypt | $2762.5 | $3453 | $331500 |
| 🇿🇲 Zambia | $2762.5 | $3453 | $331500 |
| 🇿🇼 Zimbabwe | $2762.5 | $3453 | $331500 |
| 🇮🇱 Israel | $2625 | $3281 | $315000 |
| 🇮🇳 India | $3712.5 | $4641 | $445500 |
| 🇮🇩 Indonesia | $3095 | $3869 | $371400 |
| 🇯🇴 Jordan | $2625 | $3281 | $315000 |
| 🇮🇶 Iraq | $2625 | $3281 | $315000 |
| 🇮🇷 Iran | $3095 | $3869 | $371400 |
| 🇮🇪 Ireland | $2500 | $3125 | $300000 |
| 🇮🇸 Iceland | $2575 | $3219 | $309000 |
| 🇪🇸 Spain | $2500 | $3125 | $300000 |
| 🇮🇹 Italy | $2400 | $3000 | $288000 |
| 🇾🇪 Yemen | $2625 | $3281 | $315000 |
| 🇰🇿 Kazakhstan | $2625 | $3281 | $315000 |
| 🇰🇭 Cambodia | $3095 | $3869 | $371400 |
| 🇨🇲 Cameroon | $2762.5 | $3453 | $331500 |
| 🇨🇦 Canada | $3230 | $4038 | $387600 |
| 🇶🇦 Qatar | $2625 | $3281 | $315000 |
| 🇰🇪 Kenya | $2762.5 | $3453 | $331500 |
| 🇨🇾 Cyprus | $2625 | $3281 | $315000 |
| 🇰🇬 Kyrgyzstan | $3095 | $3869 | $371400 |
| 🇨🇳 China | $3712.5 | $4641 | $445500 |
| 🇨🇴 Colombia | $3230 | $4038 | $387600 |
| 🇰🇷 Korea South | $2625 | $3281 | $315000 |
| 🇨🇷 Costa Rica | $3355 | $4194 | $402600 |
| 🇨🇮 Cote D'Ivoire (Ivory Coast) | $2762.5 | $3453 | $331500 |
| 🇨🇺 Cuba | $3230 | $4038 | $387600 |
| 🇰🇼 Kuwait | $2625 | $3281 | $315000 |
| 🇱🇻 Latvia | $2575 | $3219 | $309000 |
| 🇱🇧 Lebanon | $2625 | $3281 | $315000 |
| 🇱🇾 Libya | $2762.5 | $3453 | $331500 |
| 🇱🇹 Lithuania | $2500 | $3125 | $300000 |
| 🇱🇮 Liechtenstein | $2400 | $3000 | $288000 |
| 🇱🇺 Luxembourg | $2500 | $3125 | $300000 |
| 🇲🇾 Malaysia | $2625 | $3281 | $315000 |
| 🇲🇹 Malta | $2500 | $3125 | $300000 |
| 🇲🇦 Morocco | $2762.5 | $3453 | $331500 |
| 🇲🇽 Mexico | $3155 | $3944 | $378600 |
| 🇲🇩 Moldova | $2400 | $3000 | $288000 |
| 🇲🇨 Monaco | $2475 | $3094 | $297000 |
| 🇲🇳 Mongolia | $2625 | $3281 | $315000 |
| 🇲🇲 Myanmar | $2625 | $3281 | $315000 |
| 🇳🇦 Namibia | $2762.5 | $3453 | $331500 |
| 🇳🇵 Nepal | $2625 | $3281 | $315000 |
| 🇳🇬 Nigeria | $2762.5 | $3453 | $331500 |
| 🇳🇱 Netherlands | $2575 | $3219 | $309000 |
| 🇳🇮 Nicaragua | $3155 | $3944 | $378600 |
| 🇳🇿 New Zealand | $3345 | $4181 | $401400 |
| 🇳🇴 Norway | $2400 | $3000 | $288000 |
| 🇦🇪 United Arab Emirates | $3095 | $3869 | $371400 |
| 🇴🇲 Oman | $2625 | $3281 | $315000 |
| 🇵🇰 Pakistan | $2625 | $3281 | $315000 |
| 🇵🇦 Panama | $3230 | $4038 | $387600 |
| 🇵🇾 Paraguay | $3155 | $3944 | $378600 |
| 🇵🇪 Peru | $3230 | $4038 | $387600 |
| 🇵🇱 Poland | $2575 | $3219 | $309000 |
| 🇵🇹 Portugal | $2500 | $3125 | $300000 |
| 🇷🇺 Russia | $2575 | $3219 | $309000 |
| 🇷🇴 Romania | $2475 | $3094 | $297000 |
| 🇸🇦 Saudi Arabia | $2625 | $3281 | $315000 |
| 🇸🇳 Senegal | $2762.5 | $3453 | $331500 |
| 🇷🇸 Serbia | $2575 | $3219 | $309000 |
| 🇸🇬 Singapore | $3095 | $3869 | $371400 |
| 🇸🇾 Syria | $3095 | $3869 | $371400 |
| 🇸🇰 Slovakia | $2500 | $3125 | $300000 |
| 🇸🇮 Slovenia | $2500 | $3125 | $300000 |
| 🇬🇧 United Kingdom | $2475 | $3094 | $297000 |
| 🇸🇩 Sudan | $2762.5 | $3453 | $331500 |
| 🇺🇸 United States | $2902.5 | $3628 | $348300 |
| 🇹🇯 Tajikistan | $2625 | $3281 | $315000 |
| 🇹🇭 Thailand | $2625 | $3281 | $315000 |
| 🇹🇼 Taiwan | $3712.5 | $4641 | $445500 |
| 🇹🇿 Tanzania | $2762.5 | $3453 | $331500 |
| 🇹🇹 Trinidad And Tobago | $2675 | $3344 | $321000 |
| 🇹🇳 Tunisia | $2762.5 | $3453 | $331500 |
| 🇹🇲 Turkmenistan | $2625 | $3281 | $315000 |
| 🇹🇷 Turkey | $2625 | $3281 | $315000 |
| 🇺🇬 Uganda | $2762.5 | $3453 | $331500 |
| 🇺🇿 Uzbekistan | $2625 | $3281 | $315000 |
| 🇺🇦 Ukraine | $2500 | $3125 | $300000 |
| 🇺🇾 Uruguay | $2675 | $3344 | $321000 |
| 🇫🇴 Faroe Islands | $2575 | $3219 | $309000 |
| 🇵🇭 Philippines | $2625 | $3281 | $315000 |
| 🇫🇮 Finland | $2500 | $3125 | $300000 |
| 🇫🇷 France | $2575 | $3219 | $309000 |
| 🇭🇷 Croatia (Hrvatska) | $2575 | $3219 | $309000 |
| 🇲🇪 Montenegro | $2575 | $3219 | $309000 |
| 🇨🇿 Czech Republic | $2475 | $3094 | $297000 |
| 🇨🇱 Chile | $3355 | $4194 | $402600 |
| 🇨🇭 Switzerland | $2575 | $3219 | $309000 |
| 🇸🇪 Sweden | $2500 | $3125 | $300000 |
| 🇱🇰 Sri Lanka | $2625 | $3281 | $315000 |
| 🇪🇨 Ecuador | $3155 | $3944 | $378600 |
| 🇦🇸 American Samoa | $3345 | $4181 | $401400 |
| 🇸🇻 El Salvador | $3230 | $4038 | $387600 |
| 🇪🇪 Estonia | $2575 | $3219 | $309000 |
| 🇪🇹 Ethiopia | $2762.5 | $3453 | $331500 |
| 🇿🇦 South Africa | $2762.5 | $3453 | $331500 |
| 🇯🇵 Japan | $3095 | $3869 | $371400 |
| 🇦🇩 Andorra | $2500 | $3125 | $300000 |
| 🇦🇬 Antigua And Barbuda | $3155 | $3944 | $378600 |
| 🇧🇸 Bahamas, The | $3155 | $3944 | $378600 |
| 🇧🇧 Barbados | $3230 | $4038 | $387600 |
| 🇧🇹 Bhutan | $3095 | $3869 | $371400 |
| 🇧🇼 Botswana | $2762.5 | $3453 | $331500 |
| 🇸🇧 Solomon Islands | $3345 | $4181 | $401400 |
| 🇧🇳 Brunei | $2625 | $3281 | $315000 |
| 🇧🇮 Burundi | $2762.5 | $3453 | $331500 |
| 🇨🇻 Cabo Verde | $2762.5 | $3453 | $331500 |
| 🇨🇫 Central African Republic | $2762.5 | $3453 | $331500 |
| 🇹🇩 Chad | $2762.5 | $3453 | $331500 |
| 🇰🇲 Comoros | $2762.5 | $3453 | $331500 |
| 🇧🇯 Benin | $2762.5 | $3453 | $331500 |
| 🇩🇲 Dominica | $3230 | $4038 | $387600 |
| 🇬🇶 Equatorial Guinea | $2762.5 | $3453 | $331500 |
| 🇪🇷 Eritrea | $2762.5 | $3453 | $331500 |
| 🇫🇯 Fiji | $3345 | $4181 | $401400 |
| 🇩🇯 Djibouti | $2762.5 | $3453 | $331500 |
| 🇬🇦 Gabon | $2762.5 | $3453 | $331500 |
| 🇬🇲 Gambia, The | $2762.5 | $3453 | $331500 |
| 🇰🇮 Kiribati | $3345 | $4181 | $401400 |
| 🇬🇩 Grenada | $3355 | $4194 | $402600 |
| 🇬🇺 Guam | $3345 | $4181 | $401400 |
| 🇬🇾 Guyana | $3230 | $4038 | $387600 |
| 🇭🇹 Haiti | $3120 | $3900 | $374400 |
| 🇯🇲 Jamaica | $3230 | $4038 | $387600 |
| 🇰🇵 Korea, North | $2625 | $3281 | $315000 |
| 🇱🇸 Lesotho | $2762.5 | $3453 | $331500 |
| 🇲🇬 Madagascar | $2762.5 | $3453 | $331500 |
| 🇲🇼 Malawi | $2762.5 | $3453 | $331500 |
| 🇲🇻 Maldives | $2625 | $3281 | $315000 |
| 🇲🇱 Mali | $2762.5 | $3453 | $331500 |
| 🇲🇺 Mauritius | $2762.5 | $3453 | $331500 |
| 🇨🇼 Curaçao | $3230 | $4038 | $387600 |
| 🇦🇼 Aruba | $3120 | $3900 | $374400 |
| 🇻🇺 Vanuatu | $3345 | $4181 | $401400 |
| 🇳🇪 Niger | $2762.5 | $3453 | $331500 |
| 🇲🇵 Northern Mariana Islands | $3345 | $4181 | $401400 |
| 🇫🇲 Micronesia, Federated States Of | $3345 | $4181 | $401400 |
| 🇲🇭 Marshall Islands | $3345 | $4181 | $401400 |
| 🇵🇬 Papua New Guinea | $3345 | $4181 | $401400 |
| 🇬🇼 Guinea-Bissau | $2762.5 | $3453 | $331500 |
| 🇹🇱 Timor-Leste | $2625 | $3281 | $315000 |
| 🇷🇼 Rwanda | $2762.5 | $3453 | $331500 |
| 🇰🇳 Saint Kitts And Nevis | $3155 | $3944 | $378600 |
| 🇱🇨 Saint Lucia | $3230 | $4038 | $387600 |
| 🇻🇨 Saint Vincent And The Grenadines | $3355 | $4194 | $402600 |
| 🇸🇲 San Marino | $2500 | $3125 | $300000 |
| 🇸🇹 Sao Tome And Principe | $2762.5 | $3453 | $331500 |
| 🇸🇱 Sierra Leone | $2762.5 | $3453 | $331500 |
| 🇸🇴 Somalia | $2762.5 | $3453 | $331500 |
| 🇸🇸 South Sudan | $2762.5 | $3453 | $331500 |
| 🇸🇷 Suriname | $3230 | $4038 | $387600 |
| 🇸🇿 Swaziland | $2762.5 | $3453 | $331500 |
| 🇹🇬 Togo | $2762.5 | $3453 | $331500 |
| 🇹🇴 Tonga | $3345 | $4181 | $401400 |
| 🇹🇻 Tuvalu | $3345 | $4181 | $401400 |
| 🇧🇫 Burkina Faso | $2762.5 | $3453 | $331500 |
| 🇼🇸 Samoa | $3345 | $4181 | $401400 |
ShipsFor-Sale.com is a renowned company specializing in the sale of ships. With years of experience in the maritime industry, they have established themselves as a trusted platform for buyers and sellers worldwide. Offering an extensive range of vessels, including cargo ships, tankers, fishing boats, and luxury yachts, tankers for sale turkey. Their team of knowledgeable professionals provides expert guidance throughout the buying and selling process, ensuring smooth transactions and customer satisfaction. Whether you are a seasoned ship owner or a first-time buyer, ShipsFor-Sale.com offers a comprehensive selection of vessels and a seamless online experience, making them the go-to destination for ship sales.